To predict and evaluate metallurgical and mechanical behavior of th welds, it is essential to understand solidification behavior and microstructural evolution experienced in the welds, neither of which follows the equilibrium phase diagram because of rapid heating and cooling conditions. Metallurgical phenomena in austenitic stainless steel fusion welds, types 304, 309S, 316L, 321 and 304N, were investigated in this study. Autogenous GTA welding was performed on weld coupons, and primary solidification mode and phase distribution were investigated from the welds. Varestraint test was employed to evaluate solidification cracking susceptibilities of the alloys. GTA weld fusion zones in type 304, 321 and 304N stainless steels experienced primary ferrite solidification while those in type 309S primary austenite solidification. Type 316L exhibited a mixed type of primary ferrite and primary austenite solidification. The primary solidification mode strongly depended on $Cr_{eq}/Ni_{eq}$ ratio. In terms of solidification cracking susceptibility, type 309S that solidified as primary austenite exhibited high cracking susceptibility while the alloys experienced primary ferrite solidification showed low cracking susceptibility. The relative ranking in solidification cracking susceptibility was type 304=type 304N < type 321 < type 316L < type 309S.

• Journal of Welding and Joining
• /
• v.18 no.1
• /
• pp.59-69
• /
• 2000

The purpose of the present study was to investigate weld metallurgical phenomena such as primary solidification mode, microstructural evolution and hot cracking susceptibility in nitrogen-bearing austenitic stainless steel GTA welds. Eight experimental heats varying nitrogen content from 0.007 to 0.23 wt.% were used in this study. Autogenous GTA welding was performed on weld coupons and the primary solidification mode and their microstructural characteristics were investigated from the fusion welds. Varestraint test was employed to evaluate the solidification cracking susceptibility of the heats and TCL(Total Crack Length) was used as cracking susceptibility index. The solidification mode shifted from primary ferrite to primary austenite with an increase in nitrogen content. Retained delta ferrite exhibited a variety of morphology as nitrogen content varied. The weld fusion zone exhibited duplex structure(austenite+ferrite) at nitrogen contents less than 0.10 wt.% but fully austenitic structure at nitrogen contents more than 0.20 wt.%. The weld fusion zone in alloys with about 0.15 wt.% nitrogen experienced primary austenite + primary ferrite solidification (mode AF) and contained delta ferrite less than 1% at room temperature. Regarding to solidification cracking susceptibility, the welds with fully austenitic structure exhibited high cracking susceptibility while those with duplex structure low susceptibility. The cracking susceptibility increased slowly with an increase in nitrogen content up to 0.20 wt.% but sharply as nitrogen content exceeded 0.20 wt.%, which was attributed to solidification mode shift fro primary ferrite to primary austenite single phase solidification.

• Journal of Welding and Joining
• /
• v.16 no.6
• /
• pp.59-68
• /
• 1998

In this study, effects of solidification modes (primary $\delta$-ferrite, primary ${\gamma}$-austenite) on the pit initiation and propagation in the 304L and 316L austenitic stainless steel weld metals were investigated. The solidification mode of weld metal was controlled by the addition of nitrogen to Ar shielding gas. Through the electrochemical experiments (potentiodynamic anodic polarization and potentiostatic time-current transient test) and metallographic examination (microstructure and elemental distribution), the following results were obtained. The more the volume content of nitrogen in the shielding gas were, the lower critical current density for passivity was observed. In comparison with weldments solidified through the primary $\delta$-ferrite solidification mode and the primary ${\gamma}$-solidification mode, the former showed higher critical pitting potential and a longer incubation time for stable pit initiation than the latter. However, in the pit propagation stage the former exhibited a faster dissolution rate than the latter. These results were believed to ee related to the distribution of alloying elements such as Cr, Mo, Ni and S.

• Journal of the Korean Society for Heat Treatment
• /
• v.31 no.6
• /
• pp.290-299
• /
• 2018

The microstructure of a newly developed alloy tool steel (KV1) for casting cold-work press dies was analyzed using advanced scanning electron microscopy. Its mechanical properties and durability in use as piercing inserts were tested. It contained a continuous network structure which originated from the micro-segregation during solidification and was composed of retained austenite and primary carbides. However, after quenching and tempering, its continuity was destroyed due to the decomposition of austenite. The discontinuous spatial distribution and the smaller amount of primary carbide in the network presented KV1 enhanced ductility compared to the common alloy (HK700). The reduced C and Cr, the addition of V resulted in a small amount of primary carbides which primarily consisted of MC, as well as fine and uniform dispersion of precipitates. Owing to these features, KV1 exhibited delayed initiation of chipping when used for piercing inserts.

• Korean Journal of Materials Research
• /
• v.10 no.2
• /
• pp.144-147
• /
• 2000

10%C-5%Mo-5%W-10%Cr 및 10%C-5%Mo-5%W-10%V 백주철의 응고거동을 열분석을 통하여 연구하였다. 15Kg 용량의 고주파 유도옹해로에 선철, 고철, Fe-Mo, Fe-W, Fe-Cr, Fe-V 등을 장입시켜 용해시킨 후 슬래그를 제거시키고 $1550^{\circ}C$에서 Y블럭의 펩 주형에 주입하였다. 응고거동을 조사하기 위하여 50g을 Y블럭에서 채취한 뒤 알루미나 도가니에 넣어 재용해시킨 후 1$0^{\circ}C$/min의 냉각속도로 냉각시키면서 여섯 종류의 다른 온도에서 도중에 급냉시켜 응고조직을 광학현미경으로 관찰하였다. 10%C-5%Mo-5%W-10%Cr 백주철의 경우 초정 오스테나이트, 오스테나이트와 M(sub)7C(sob)3의 공정, 오스테나이트와 M(sub)6C의 공정으로, 10%C-5%Mo-5%W-10%V 백주철의 경우 초정 MC, 오스테나이트와 MC의 공정, 오스테나이트와 M(sub)2C의 공정으로 각각 순차적으로 정출하였다. 정출하였다.

• Journal of the Korean Society for Heat Treatment
• /
• v.35 no.4
• /
• pp.211-219
• /
• 2022

It is known that superplastic materials with ultrafine grains have high elongation mainly due to grain boundary sliding. Therefore, in the present study we examined the influence of grain refinement, caused by a repetitive cold rolling and annealing process, on both superplastic elongation and superplastic deformation mechanism. The cold rolling and annealing process was repetitively applied up to 4 times using Fe-10Mn-3.5Si alloy. High-temperature tensile tests were conducted at 763 K with an initial strain rate of 1 × 10^-3 s^-1 using the specimens. The superplastic elongation increased with the number of the repetitive cold rolling and annealing process; in particular, the 4 cycled specimen exhibited the highest elongation of 372%. The primary deformation mechanism of all specimens was grain boundary sliding between recrystallized α-ferrite and reverted γ-austenite grains. The main reason for the increase in elongation with the number of the repetitive cold rolling and annealing process was the increase in fractions of fine recrystallized α-ferrite and reverted γ-austenite grains, which undergo grain boundary sliding.

• Journal of the Korean Society for Heat Treatment
• /
• v.34 no.4
• /
• pp.179-184
• /
• 2021

Two types of secondary hardening martensitic steels, 10Co-14Ni and 6Co-5Ni, were produced by vacuum induction melting to investigate the effect of ausforming process on mechanical properties. According to the results of present study, the alloy samples ausformed at low temperature indicated a rather low hardness level in overall aging time despite the refinement of martensite lath width. As the result can closely be related with the presence of primary carbides precipitated within the initial austenite matrix, we confirmed that, in ultrahigh strength secondary hardening martensitic alloy steels, the ausforming process can rather limit the degree of secondary hardening during the subsequent aging treatment.

• Corrosion Science and Technology
• /
• v.20 no.6
• /
• pp.367-372
• /
• 2021

The effect of carbon addition on the general corrosion behavior of high-chromium cast iron (HCCI) was studied by a scanning electron microscope with energy dispersive spectroscopy (SEM-EDS) or electron back-scattered diffraction (EBSD), or electrochemical polarization techniques in 0.1 mol dm^-3 H₂SO₄ + 0.05 mol dm^-3 HCl at room temperature. The addition of 2.1-2.8 wt% carbon to HCCI increased the fraction of eutectic austenite and eutectic carbide phases, while that of HCCI decreased the fraction of the primary austenitic phase. Potentiostatic polarization of the HCCI at -0.35 V_SSCE or 0.0 V_SSCE resulted in preferential general corrosion of the primary austenitic or eutectic austenitic phases, respectively. The decrease in corrosion current density and the shift in noble corrosion potential direction with increasing carbon content in the HCCI indicated that the fraction and the chemical composition of austenitic (primary and eutectic) and carbide phases were strongly related to the general corrosion behavior of the HCCI.

• Journal of Korea Foundry Society
• /
• v.16 no.2
• /
• pp.141-148
• /
• 1996

In high chromium cast iron, the control of matrix microstructure as well as carbide structure is important to the performance as a wear resistant material. In this study, 3.0% C-24.0% Cr white cast irons with various molybdenum contents(residual, 1.0%, 3.0% and 5.0%) were solidified conventionally and unidirectionally for studying their effects on the microstructure and hardness. In the conventional casting, two sets of castings were poured from each melt. One set of the castings consisted of cylindrical bars of 10 and 20mm by 155mm long. The second set of the castings was a cylindrical bar of 30mm by 200mm long. On the other hand, a pep-set mold set on the Cu plate was employed to make the solidification unidirectionally. X-ray diffraction method was used to observe retained austenite and carbides in the high chromium cast iron. The morphology of eutectic $M_7C_3$ carbides changed from needle-like type to nodular type with the increase of Mo content. And, the presence of $M_2C$ carbides was identified in the sample where Mo was added over 3.0 %. Primary and eutectic carbides appeared as rod type and corngrain type, respectively in the unidirectionally solidified samples which were cut to parallel to the solidification direction. In the EDX analysis, Cr concentration was higher in the primary and eutectic $M_7C_3$ carbides, Mo in the $M_2C$ carbides, and Fe in the matrix.

• 한국가스학회:학술대회논문집
• /
• 1997.09a
• /
• pp.45-52
• /
• 1997

The objective of this study is, with concept of fitness-for-purpose, to evaluate the fracture toughness in X-grooved weld HAZ(heat-affected zone) of QLT(quenching, lamellarizing and tempering)-processed $9\%$ Ni steel, qualitatively and quantitatively, and analyze the relation with the change of microstructure. In general, CTOD test is widely used to determine the fracture toughness of steel weldments. But several problem of accuracy has been brought up. Therefore, in this study, modified CTOD test was used for X-grooved weld HAZ for $9\%$ Ni steel. Additionally, microstructure of HAZ is observed and analyzed by OM, SEM and XRD. From the resulty, HAZ toughness of QLT-$9\%$ Ni steel decreased as the evaluated region approaches the fusion line. The decreased toughness was partly caused by reduction of the retained austenite content, resulted from decreased nucleation site of the retained austenite content, resulted from decreased nucleasion site for reverse transformation due to the increasing fraction of coarse grained region. On the other hand, unexpectedly, the increasing fraction of ductile weld did not increase the HAZ toughness. Therefore, in this X-grooved weld HAZ, the primary factor affecting fracture toughness was the fraction of coarse grained region, i.e., the weakest region.