• 한국세라믹학회지
• /
• 제34권12호
• /
• pp.1247-1253
• /
• 1997

Sinter-active yttria powders were prepared by a solution precipitation with using a self-decomposing precipitation agent NH2CONH2(urea). The cold-pressed powders can be sintered to full density and the microstructure of grains less than 200 nm at a temperature as low as 120$0^{\circ}C$. The activity of the yttria powder has been controlled by varying nucleation conditions during precipitation and by minimizing formation of aggregates. The type of precursor is decisive in preparation of a sinter-active oxide powder, and urea is desirable as a precipitation agent for an active yttrium oxide powder.

• 한국분말재료학회지
• /
• 제15권6호
• /
• pp.503-508
• /
• 2008

Ti(C,N) solid solutions in hot-pressed Ti($C_{x}N_{1-x}$) (x=0.0, 0.3, 0.5, 0.7, 1.0) and 40TiC-40TiN-20Ni (in wt.%) cermet were characterized in this study. For hot-pressed Ti(C,N)s, the lattice parameters and hardness values of Ti(C,N) were determined by using XRD (X-Ray Diffraction) and nanoindentation. The properties of hot-pressed Ti(C,N) samples changed linearly with their carbon or nitrogen contents. For the TiC-TiN-Ni cermet, the hardness of the hard phase and binder phase were determined by nanoindentation in conjunction with microstructural observation. The measured hardness values were ${\sim}8.7$ GPa for the binder phase and ${\sim}28.7$ GPa for the hard phase, which was close to the hardness of hot-pressed Ti($C_{0.7}N_{0.3}$).

• 한국세라믹학회지
• /
• 제26권5호
• /
• pp.637-644
• /
• 1989

Beta-sialon powder(Z=1) was synthesized by the simultaeous reduction and nitridation of the mixed powders of Hadong kaolin and silica. Silicon hydroxide was prepared from Si-alkoxide by a hydrolysis method and amorphous silica was obtained from the calcination of the prepared silicon hydroxide. Hadong kaolin was mixed with both the silicon hydroxide and amorphous silica, respectively. The average particle size was 4${\mu}{\textrm}{m}$ and the morphology of particle was rod-like and equiaxed in the case of beta-sialon powder prepared form Hadong kaolin and silicon hydroxide(COMPOSITION A), whereas the average particle size was 3${\mu}{\textrm}{m}$ and the morphology of particle was equiaxed in the case of beta-sialon powder prepared from Hadong kaolin and amorphous silica(COMPOSITION B). The synthesized beta-sialon powders were hot-pressed at 175$0^{\circ}C$ for 2 hours under 30 MPa in a nitrogen atmosphere after YAG composition(8wt%) was added to these powders as a sintering agent. The hot-pressed specimens were annealed a 140$0^{\circ}C$ for 4 hours in a nitrogen atmosphere. The mechanical properties of sintered bodies were investigated in terms of M.O.R., fracture toughness and hardness. The measured values are as follows. COMPOSITION A : M.O.R. 508MPa, KIC 3.5MN/m3/2, hardness 13.6GPa. COMPOSITION B : M.O.R. 653MPa, KIC 5.4MN/m3/2, hardness 13.5GPa.

• Nuclear Engineering and Technology
• /
• 제31권6호
• /
• pp.608-617
• /
• 1999

The powder mixture which has a bimodal size distribution, with a large mode corresponding to AUC-UO$_2$ powder and a small one corresponding to ADU-UO$_2$ powder, was prepared, pressed into compacts, and sintered at 1680t for 4 hours in hydrogen gas. The compact density of the powder mixture increases with increasing ADU-UO$_2$content within a content of 20 wt %, since small ADU-UO$_2$ particles can fill interstices between large AUC-UO$_2$particles. The UO$_2$ pellet made using the powder mixture has a lower open porosity than that made using AUC-UO$_2$ powder alone. The mechanism for the formation of a flake-like pore is proposed, and the decrease in open porosity may be ascribed to the decrease in the number of flake-like pores.

• 한국분말재료학회지
• /
• 제1권2호
• /
• pp.135-144
• /
• 1994

Silicon carbide powder was prepared from mixtures of Sangdong silica sand and carbon black by SHS (Self propagating High temperature Synthesis) method which utilizes magnesiothermic reduction of silica. In the powder preparation process, the reacted powder was leached by chloric acid to remove the magnesium oxide and was subsequently roasted to remove free carbon. The impurities were mostly eliminated by hot acid treatment. The resultant SiC powder showed the mean particle size of 0.22 ${\mu}{\textrm}{m}$ and the specific surface area of $66.55 m^2/g$. The SiC powder was mixed with 1 wt% of boron and of carbon to increase densification rate. The mixed powder was pressed and sintered pressurelessly at $2100^{\circ}C$ for 30 min in argon gas. The sintered body showed the hardness of $2550 kg{\cdot}f/mm^2$ and the fracture toughness, KIC of $3.47 MN/m^{3/2}$.

• 한국세라믹학회지
• /
• 제29권8호
• /
• pp.609-616
• /
• 1992

This study has been investigated on the milling of Aluminium Distearate (ADS) powder and characteristics of the ADS-doped UO2 pellets. As-received ADS powder of the agglomerated particles has not shown any milling effect because of heat generated during planetary milling. But the use of coolant to effectively remove heat generated during milling has been found an effective way in breaking up the agglomerates of ADS powder. The green density of the UO2 pellet decreases with the amount of ADS powder doped. Therefore, in order to get the sintered density of 95% pellet decreases with the amount of ADS powder doped. Therefore, in order to get the sintered density of 95% theoretical density, the 200 ppm ADS-doped UO2 pellet has to be pressed under higher compacting pressure of 3500~4000 kgf/$\textrm{cm}^2$ compared with the ADS-undoped UO2 pellet pressed under around 3000 kgf/$\textrm{cm}^2$. The ADS-dpoed UO2 pellet with even relatively low sintered density of 10.27 g/㎤ exhibits open porosity of 1% while open porosity of the ADS-undoped UO2 pellet is reduced to around 1% only after its sintered density increases to 10.43g/㎤. It is, therefore, concluded that doping of ADS powder significantly contributes to the decrease in open porosity of the UO2 pellet. The dilatometry of the ADS doped UO2 pellet shows the sintering rate curve with the bimodal mode, which could be attributed to a phase reaction between UO2 and ADS. The X-ray diffraction analysis indicates that there occurs not any new phase formed but the shift of the peaks. It would be expected that a phase reaction resulting in solid solution would happen in the temperature range of 130$0^{\circ}C$ to 150$0^{\circ}C$ between UO2 and ADS.

• 한국분말재료학회지
• /
• 제29권3호
• /
• pp.247-251
• /
• 2022

This study demonstrates the effect of the compaction pressure on the microstructure and properties of pressureless-sintered W bodies. W powders are synthesized by ultrasonic spray pyrolysis and hydrogen reduction using ammonium metatungstate hydrate as a precursor. Microstructural investigation reveals that a spherical powder in the form of agglomerated nanosized W particles is successfully synthesized. The W powder synthesized by ultrasonic spray pyrolysis exhibits a relative density of approximately 94% regardless of the compaction pressure, whereas the commercial powder exhibits a relative density of 64% under the same sintering conditions. This change in the relative density of the sintered compact can be explained by the difference in the sizes of the raw powder and the densities of the compacted green body. The grain size increases as the compaction pressure increases, and the sintered compact uniaxially pressed to 50 MPa and then isostatically pressed to 300 MPa exhibits a size of 0.71 m. The Vickers hardness of the sintered W exhibits a high value of 4.7 GPa, mainly due to grain refinement.

• 한국분말재료학회지
• /
• 제1권1호
• /
• pp.27-34
• /
• 1994

Commercial pure iron powder and iron powder of coated 0.45% phosphorus were mixed with graphite powder in dry mixer to control carbon content from 0 wt% to 0.8 wt%. Mixed powder was pressed in the mould under the pressure of 510 MPa. Compacts were sintered at 118$0^{\circ}C$ for 40 min. in cracked ammonia gaseous atmosphere. Some of these sintered specimens were quenched in oil, and tempered in Ar gas. All of these specimens were investigated for microstructure, density and hardness in relation to coated phosphorus and carbon content. The results obtained were as follows: (1) The microstructure of the sintered speciments revealed that the amount of pearlite was increased with increasing C content but decreased by P-addition. (2) The P-addition affected the microstructure of pores in which the pore shape became round and its mean size was decreased by P-addition. (3) After tempering of sintered specimens the structure of pearlite was changed from fine structure to coarse one in P added specimen. (4) Hardness was higher in P added specimens.

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part2
• /
• pp.1227-1228
• /
• 2006

The electrochemical properties of novel metal powders were investigated for the electrode materias of polymer electrolyte memebrane electrolysis. Two types of Pt black and $IrO_2$ powder electrodes were hot-pressed on the polymer electrolyte membrane to form membrane electrode assembly. The galvanodynamic polarization methode was used to characterize the electrochemical properties of both electrodes. From the experimental results, we concluded that the $IrO_2$ powder electrode exhibits better electrochemical performance than Pt black as cathode material for the electrolysis.

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part 1
• /
• pp.22-23
• /
• 2006

High velocity compaction (HVC) is a production technique with capacity to significantly improve the mechanical properties of powder metallurgy (PM) parts. Investigated here are green body data such as density, tensile strength, radial springback, ejection force and surface flatness. Comparisons are performed with conventional compaction using the same pressing conditions. Cylindrical samples of a pre-alloyed water atomized iron powder are used in this experimental investigation. The HVC process in this study resulted in a better compressibility curve and lower ejection force compared to conventional quasi static pressing. Vertical scanning interferometry measurements show that the HVC process gives flatter sample surfaces.