• Progress in Superconductivity
• /
• 제5권1호
• /
• pp.65-69
• /
• 2003

Many researches on fabrication process for BSCCO precursor powders have been developed for high J$_{c}$ BSCCO-2223 tape. Spray pyrolysis method for fabrication of precursor powder has many advantages, such as high purity, fine particle size and low carbon content of BSCCO precursor powder. Fine, spherical powders were prepared by ultrasonic spray pyrolysis from the aqueous solution of metal nitrates. BSCCO precursor powders were synthesized with various solutes concentration and heat treatment conditions. Average particle size for spray pyrolysis powders was $1.5∼3\mu\textrm{m}$. Bi-2223/Ag tape was prepared by PIT method and followed by various sintering conditions. BSCCO precursor powders were characterized by XRD, SEM, EDS, Carbon content and particle size analysis.s.

• Progress in Superconductivity
• /
• 제6권2호
• /
• pp.124-128
• /
• 2005

Homogeneous and fine powders for Bi-2223 tape were prepared by ultrasonic spray pyrolysis (SP) method from an aqueous solution of metal nitrates. Bi-2223 precursor powders were synthesized with various solutes concentration and pyrolysis temperature. The synthesized precursor powders had a narrow particle size distribution and an average particle size was $\~{\cal}um$. The reactivity of precursor powder by SP method is very high, attributed to the fine and narrow particle size distribution. Bi-2223/Ag tape was prepared using PIT method and followed by various sintering conditions. The precursor powder by SP method promoted a very quick formation of the Bi-2223 phase for short sintering time while the secondary phase such as large AEC phase and $Ca_2PbO_4$ were minimized for SP tapes.

• 한국초전도ㆍ저온공학회논문지
• /
• 제15권2호
• /
• pp.39-43
• /
• 2013

$MgB_2$ bulk samples are synthesized through solid state reaction route using Mg precursors with different particle size by keeping the boron precursor unchanged. Scanning electron microscopy study of the fractured surface for all the samples depicts quite distinct structure depending on the Mg precursor. Big size of Mg precursor resulted in to largely elongated and deep pores while smaller one gave roughly ellipsoidal and shallow pore structure. Influence of the Mg particle size on the grain to grain connectivity reflected in the critical current density value which was greater for samples with smaller Mg precursor. All the synthesized samples undergo a superconducting transition at around 36.5 K irrespective of different Mg precursor particle size.

• Journal of Magnetics
• /
• 제20권1호
• /
• pp.21-25
• /
• 2015

Fine Nd-Fe-B-type particles were prepared by ball milling of different types of Nd-Fe-B precursor materials, such as die-upset magnet, HDDR-treated material, and sintered magnets. Coercivity dependence on the grain and particle size of the powder was investigated. Coercivity of the milled particles was reduced as the particle size decreased, and the extent of coercivity loss was dependent upon the precursor material. Coercivity loss in the finely milled particles was attributed to the surface oxidation. The extent of coercivity loss in the fine particles was closely linked to grain size of the precursor materials. Coercivity loss was more profound for the fine particles with larger grain size. Contrary to the fine particles from the sintered magnets with larger grain size the fine particles (~10 um) from the die-upset magnet and HDDR-treated material with much finer grain size still retained high coercivity (> 10 kOe for die-upset magnet, > 4 kOe for HDDR-treated material).

• 한국분말재료학회지
• /
• 제10권2호
• /
• pp.123-128
• /
• 2003

$TiO_2$ nanopowder was synthesized by chemical vapor condensation (CVC) process and its photocatalytic property depending on microstructure was considered in terns of decomposition rate of organic compound. In order to control microstructure of $TiO_2$ nanopowder such as particle size and degree of agglomeration, precursor flow rate representing number concentration was changed as a process variable. In TEM observation, spherical $TiO_2$ nanoparticles with average size of 20 nm showed gradual increases in particle size and degree of agglomeration with increase of precursor flow rate. Also decomposition rate of organic compound increased with decreasing precursor flow rate. Thus, it was concluded that photocatalytic property was enhanced by targe surface area of disperse $TiO_2$ nanoparticles synthesized at lower precursor flow rate condition in CVC process.

• 한국초전도저온공학회:학술대회논문집
• /
• 한국초전도저온공학회 2003년도 추계학술대회 논문집
• /
• pp.99-102
• /
• 2003

Many researches on synthesis process for BSCCO precursor powders have been developed for high J$_{c}$ BSCCO-2223/Ag tape. Spray pyrolysis method for fabrication of precursor powder has many advantages, such as high purity, fine particle size of BSCCO precursor powder. Fine, spherical powders were prepared by ultrasonic spray pyrolysis from the aqueous solution of metal nitrates. BSCCO precursor powders were synthesized with 0.1 M concentration and heat treatment conditions. Average particle size for spray pyrolysis powders was 1.5 ~ 3 ${\mu}{\textrm}{m}$. BSCCO -2223/Ag tape was prepared by PIT method and followed by various sintering conditions. The critical current density of BSCCO-2223/Ag tape sintered in low oxygen partial pressure was ~ 23 kAcm$^{-2}$.

• 멤브레인
• /
• 제26권5호
• /
• pp.372-380
• /
• 2016

본 연구에서는 입자크기가 다른 3가지 ${\alpha}$-알루미나 분체로부터 주입성형법과 소결법을 혼용하여 튜브형 ${\alpha}$-알루미나 지지체를 제조하여 초기 ${\alpha}$-알루미나 분체의 입자크기와 소결 온도가 지지체의 기공구조와 기체투과 특성에 미치는 영향을 고찰하였다. 평균입경이 0.2, 0.5, $1.7{\mu}m$인 ${\alpha}$-알루미나 분체를 사용했을 시 제조된 ${\alpha}$-알루미나 지지체는 각각 약 80, 130, 200 nm의 평균 기공경을 가졌으며 평균 기공경은 소결 온도 보다는 초기 알루미나 분체의 입자크기에 의존하였다. 모든 시편에서 소결 온도가 증가할수록 지지체의 부피 밀도는 증가하였고 겉보기 기공률은 감소하였다. He, $N_2$, $O_2$, $CO_2$에 대하여 $30^{\circ}C$에서 단일기체 투과 특성을 평가한 결과, 기체 투과도는 기공경 제곱에 비례하여 증가하였고 기공률이 증가함에 따라서 직선적으로 증가하였다. 이를 토대로 제조된 ${\alpha}$-알루미나 지지체의 기체 투과는 점성유동(viscous flow)에 의하여 이루어지며, ${\alpha}$-알루미나 지지체의 기체 투과 특성은 초기 ${\alpha}$-알루미나 분체의 입자크기와 소결온도를 제어함으로써 조절될 수 있음을 확인할 수 있었다.

• 한국초전도학회:학술대회논문집
• /
• 한국초전도학회 2003년도 High Temperature Superconductivity Vol.XIII
• /
• pp.77-77
• /
• 2003

• 센서학회지
• /
• 제10권2호
• /
• pp.118-124
• /
• 2001

입자들이 용액에 녹아있을 때 pH에 따라서 다른 zeta-potential을 가지게 되며, 이것은 입자의 분산상태에 영향을 주게 된다. NO 센서에서 $WO_3$ 입자의 크기는 감도에 큰 영향을 끼치므로 Sol-Coprecipitation법에 의한 $WO_3$ 센서 제조 시에 $WO_3$ precursor 상태에서의 pH의 영향을 알아보았다. 먼저 $WO_3$ precursor의 전기적 포텐셜을 측정하여 pH가 2에서 7로 변함에 따라 mobility가 증가하여 7일 때에 가장 큰 분산도를 가진 것을 알 수 있었고, 이는 powder 제조 후 입도 분석, 감지막의 XRD peak, 표면사진으로부터 확인 할 수 있었다. 결과적으로 감도 특성에도 영향을 끼쳐 pH=7에서 제조한 센서가 다른 pH에서 제조한 센서보다 감도가 우수한 것으로 나타났다.

• Bulletin of the Korean Chemical Society
• /
• 제33권10호
• /
• pp.3331-3337
• /
• 2012

Ru-modified Pt nanoparticles of various sizes on platelet carbon nanofiber toward methanol oxidation were investigated in terms of particle size effect. The sizes of Pt nanoparticles, prepared by polyol method, were in the range of 1.5-7.5 nm and Ru was spontaneously deposited by contacting Pt nanoparticles with the Ru precursor solutions of 2 and 5 mM. The Ru-modified Pt nanoparticles were characterized using transmission electron microscopy, X-ray photoelectron spectroscopy and cyclic voltammetry. The methanol oxidation activities of Ru-modified Pt nanoparticles, measured using cyclic voltammetry and chronoamperometry, revealed that when the Pt particle size was less than 4.3 nm, the mass specific activity was fairly constant with an enhancement factor of more than 2 at 0.4 V. However, the surface area specific activity was maximized on Pt nanoparticles of 4.3 nm modified with 5 mM Ru precursor solution. The observations were discussed in terms of the enhancement of poison oxidation by Ru and the population variation of Pt atoms at vertices and edges of Pt nanoparticles due to selective deposition of Ru on the facets of (111) and (100).