• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2005년도 하계학술대회 논문집 Vol.6
• /
• pp.290-291
• /
• 2005

A high Tc superconducting with a nominal composition of $Bi_2Sr_2Ca_2Cu_3O_Y$ was prepared by the citarte method. The solid precursor produced by the dehydration of the gel at $120^{\circ}C$ for 12h is not in the amorphous state as expected but in a crystalline state. X-ray diffraction peaks of nearly the same angular position as the peaks of high Tc phase were observed in the precursor. After pyrolysis at $400^{\circ}C$ and calcination at $840^{\circ}C$ for 4h. the (001)peak of the high Tc phase was cleary observed. Experimental results suggest that the intermediate phase formed before the formation of the superconducting phase may be the most important factor in determining whether it is easy to form the high Tc phase or not. because the nucleation barriers of the two superconducting phase may be altered by the variation of the crystal structures of those intermediate phase.

• Bulletin of the Korean Chemical Society
• /
• 제21권8호
• /
• pp.817-822
• /
• 2000

Crack-free hard coating siIica films were prepared by sol-gel processfrom twokinds of silicon alkoxide (tetra-ethoxysilane and methyltrimethoxysilane) and two kinds of alcohol (methanol and isopropyl alcohol) with an acid catalyst,acetic acid. A silicate framework of the precursor solution was investigated by infrared spectros-copy (IR) in the process of hydrolysis and condensation. Theextent of the condensation in the intermediates was elucidated by gel permeation chromatography (GPC) and 29Si-NMR spectroscopy. The hard coating films werecharacterized by IR,scanning electron microscope (SEM), thermo gravimetric analyzer (TGA) and dif-ferential scanning calroimeter (DSC). The synthetic condition for the crack-free and transparent silica film for-mation was optimized interms of starting materials for the precursor solution as well as preparation method of the silica film.

• Bulletin of the Korean Chemical Society
• /
• 제33권9호
• /
• pp.3025-3032
• /
• 2012

Carbon microcapsules containing silicon nanoparticles (Si NPs)-carbon nanotubes (CNTs) nanocomposite (Si-CNT@C) have been fabricated by a two step polymerization method. Silicon nanoparticles-carbon nanotubes (Si-CNT) nanohybrids were prepared with a wet-type beadsmill method. A polymer, which is easily removable by a thermal treatment (intermediate polymer) was polymerized on the outer surfaces of Si-CNT nanocomposites. Subsequently, another polymer, which can be carbonized by thermal heating (carbon precursor polymer) was incorporated onto the surfaces of pre-existing polymer layer. In this way, polymer precursor spheres containing Si-CNT nanohybrids were produced using a two step polymerization. The intermediate polymer must disappear during carbonization resulting in the formation of an internal free space. The carbon precursor polymer should transform to carbon shell to encapsulate remaining Si-CNT nanocomposites. Therefore, hollow carbon microcapsules containing Si-CNT nanocomposites could be obtained (Si-CNT@C). The successful fabrication was confirmed by scanning electron microscopy (SEM) and X-ray diffraction (XRD). These final materials were employed for anode performance improvement in lithium ion battery. The cyclic performances of these Si-CNT@C microcapsules were measured with a lithium battery half cell tests.

• Progress in Superconductivity
• /
• 제9권1호
• /
• pp.91-95
• /
• 2007

[ $YBa_2Cu_3O_{7-{\delta}}$ ] films have been prepared on $LaAlO_3$ (100) single-crystal substrates by the metal organic deposition using dichloroacetate precursors (DCA-MOD). DCA precursor solutions with different composition such as; Yttrium-excess(15 at%), barium-poor(25 at%), and a stoichiometric(Y:Ba:Cu=1:2:3) were prepared in order to investigate the effects of precursor composition on the properties of YBCO films prepared by DCA-MOD method. Coated films were calcined at low temperature up to $500^{\circ}C$ in flowing humid oxygen atmosphere. Conversion heat treatment was performed $800^{\circ}C$ for 2 h in flowing Ar gas containing 1000 ppm oxygen with a humidity of 9.45%. For the film prepared using excess yttrium composition, high critical current density ($J_c$) of $>2MA/cm^2$ was obtained whereas, for the films prepared using barium-poor composition, $J_c$ was lower than $1MA/cm^2$.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2006년도 추계학술대회 논문집 Vol.19
• /
• pp.35-36
• /
• 2006

The influence of the concentration of precursor solution and the number of solution coatings on the densification of the Pb($Zr_xTi_{1-x}$)$O_3$(PZT) thick films was studied. PZT powder and PZT precursor solution were prepared by sol-gel method and PZT thick films were fabricated by the screen-printing method on the alumina substrates. The powder and solution of composition were PZT(70/30) and PZT(30/70), respectively. The coating and drying procedure was repeated 4 times. And then the PZT precursor solution was spin-coated on the PZT thick films. A concentration of a coating solution was 0.5 to 2.0 mol/L[M] and the number of coating was repeated from 0 to 6. The relative dielectric constant of the PZT thick film was increased with increasing the number of solution coatings and the thick films with 15M, 6-time coated showed the 698. The remanent polarization of the 1.5M, 6-time coated PZT thick films was 38.3 ${\mu}C/cm^2$.

• 한국초전도학회:학술대회논문집
• /
• 한국초전도학회 1999년도 High Temperature Superconductivity Vol.IX
• /
• pp.315-318
• /
• 1999

Bi$_{2}Sr_{2}CaCu_{2}O_{\delta}$ superconducting films were rapidly fabricated on copper tape by liquid reaction between a Cu-free precursor and Cu tape (LiReac-PreCu) method. Those thick films were well oriented along the c-axis. The precursor was made by melt-quenched technology using twin roller. The melt-quenched films were transparent and glossy yellow in appearance. These films which were the compostion of Bi$_2SrCaO_y$, Bi$_3Sr_2CaO_z$ were placed on copper tape and then heated at various temperatures for several minutes in air. They were analyzed using X-ray powder diffraction, SEM, a DC four-probe method. The mechanism of superconducting phase formation . from the melt-quenched precursor on Cu tape was studied

• 한국진공학회지
• /
• 제8권4A호
• /
• pp.425-431
• /
• 1999

$Pb(Zr_{0.52}, Ti_{0.48})O_3$ (PZT) thick films as an actuating material with conducting oxides, $(La_{0.5}Sr_{0.5}) CoO_3$ (LSCO), have been fabricated by sol-gel method for Optical Micro-Electro-Mechanical System (MEMS) devices, in which PZT/LSCO/SiO2 structures were used. In order to improve the adhesion to LSCO solution in order to enhance the wetting behavior of a water-based LSCO precursor solution and further to improve the adhesion between LSCO and $SiO_2$ layers. PZT films were made using 1-3 propanediol based precursor solution which has a high viscosity and a boiling point appropriate for thick film fabrication. In the precursor solution, Ti-propoxied and Zr-propoxied are partially substituted with acetylacetone to achieve the solution stability while maintaining reactivity. Crack free PZT films (0.8~1$\mu\textrm{m}$) have been successfully fabricated at crystallization temperatures above $700^{\circ}C$. Dielectric constants and dielectric losses of the PZT films were 900~1200and 2~5%, respectively. Piezoelectric constant $d_{33}$ of the PZT films constrained by a substrate were 200pm/V at 100kV/cm.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2003년도 하계학술대회 논문집 Vol.4 No.2
• /
• pp.732-734
• /
• 2003

A solvothermal synthetic method to $BaTiO_3$ nanoparticle has been investigated in toluene solution with $BaTi(OR)_6$ as precursor. A precursor prepared from barium metal with toluene, isopropanol and titanium isopropoxide was used as a starting material. Weight ratio of precursor to solvent prepared in the mixture are 5/100, 10/100, 20/100 and 50/100wt%. At the weight ratio of 50/100wt%, $BaTiO_3$ butterfly twin crystalline(${\fallingdotseq}100nm$) was obtained after synthesis at $250^{\circ}C$ for 20hrs in an autoclave. X-ray diffraction and transmission electron microscopy showed that the product of 50/100wt% has crystallization. At 5/100, 10/100, and 20/100wt%, however, red colloidal solution was obtained after synthesis and crystalline phase of $BaTiO_3$ was not produced.

• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2004년도 춘계학술대회
• /
• pp.382-387
• /
• 2004

Nanoindentation technique has been used to measure the mechanical properties of aluminium alloy foam cell walls. Al-Si-Cu-Mg alloy foams of different compositions and different cell morphologies were produced using powder metallurgical method. Cell morphology of the foam was controlled during production by varying foaming time and temperature. Mechanical properties such as hardness and Young's modulus were calculated using two different methods: a continuous stiffness measurement (CSM) and an unloading stiffness measurement (USM) method. Experimental results showed that hardness and Young's modulus of Al-5%(wt.)Si-4%Cu-4%Mg (544 alloy) precursor and foam walls are higher than those of Al-3%Si-2%Cu-2%Mg (322 alloy) precursor and foam walls. It was noticed that mechanical properties of cell wall are different from those of precursor materials.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2005년도 하계학술대회 논문집 Vol.6
• /
• pp.270-271
• /
• 2005

A high Tc superconducting with a nominal composition of $Bi_2Sr_2Ca_2Cu_3O_Y$ was prepared by the citarte method. The solid precursor produced by the dehydration of the gel at $120^{\circ}C$ for 12h is not in the amorphous state as expected but in a crystalline state. X-ray diffraction peaks of nearly the same angular position as the peaks of high Tc phase were observed in the precursor. After pyrolysis at $400^{\circ}C$ and calcination at $840^{\circ}C$ for 4h, the (001)peak of the high Tc phase was cleary observed. Experimental results suggest that the intermediate phase formed before the formation of the superconducting phase may be the most important factro in determining whether it is easy to form the high Tc phase or not. because the nucleation barriers of the two superconducting phase may be altered by the variation of the crystal structures of those intermediate phase.