• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2017.05a
• /
• pp.222-223
• /
• 2017

In the automotive industry, such as scrap metal and plastic scrap process is being recycled. Although the glass beads are used as road paving or other additives and processing crushing, recycling is known that there are limits. The utilization of waste glass was evaluated as a concrete admixture by using powder characteristics and chemical composition of the glass. As a result of using waste-glass powder as an admixture, it is difficult to expect the pozzolanic effect, but it is found that it can increase the fluidity of concrete and ensure the durability performance in the appropriate amount range.

• Proceedings of the Korean Institute of Resources Recycling Conference
• /
• 2004.05a
• /
• pp.155-158
• /
• 2004

본 연구에서는 공냉(空冷)된 화력발전소 바닥재의 입도분포, 화학조성, 광물상 등 기초 특성과 압축강도비에 의해 포졸란 반응성을 측정하였다. 바닥재의 주요 성분은 $SiO_2$, $Al_2O_3,\;Fe_2O_3$로 이들의 합계가 91.2wt.%였으며, 주요 광물상은 mullite, quartz, cristobalite, tridymite, hematie 등이었다. 입도별 화학조성 변동은 거의 없었으나, 입도가 커짐에 따라 $SiO_2$는 quartz에서 cristobalite로 존재하는 비율이 증가하였다. 분쇄된 바닥재(blame 비표면적 $7,540cm^2/g$)의 양생 28일에서의 활성도 지수는 101을 나타내었다.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2015.05a
• /
• pp.84-85
• /
• 2015

The aim of this study is to develop crack self-healing concrete and repair materials with the sulfate resistance using geo-materials and by-products for practical industrial application. Research has been done on the healing of cracks in aged concrete, but it seems that very little is known about the actual healing mechanism and its conditions. In this research, the essential properties of geo-materials with pozzolanic reaction for self-healing were analyzed and discussed.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2017.11a
• /
• pp.30-31
• /
• 2017

The objective of this study is to evaluate the performance of polymer-modified surface preparation mortars with pozzolanic materials for corrosion prevention method in deteriorated sewage treatment structures. The prepackaged-type surface preparation mortars are prepared with a polymer-binder ratio of 10%, ground granulated blast furnace slag contents of 0, 15, 30%, a fly ash content of 15%. And, the specimens are tested for workability, adhesion in tension, water absorption, crack and impact resistance. As a result, the prepackage-type surface preparation mortars for sewage treatment structure are satisfied with quality requirements by KS F 4716, Japan sewage work agency(JS) and JIS A 6916 for surface preparation mortars.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2020.11a
• /
• pp.151-152
• /
• 2020

When concrete is exposed to fire, the thermal decomposition of hydrates of Portland cement paste results in critical damage to the concrete structure of a building. Recently, nanosilica arose as the effective nano-additive which can enhance the thermal resistance of the cementitious materials. However, the mechanism of the enhancement was not elucidated specifically. In this study, we investigated the properties of calcium silicate hydrates(C-S-H)of the nanosilica incorporated cement paste after heating to different heating temperatures (200℃, 500℃, and 800℃) by 29Si nuclear magnetic resonance. The results showed that the polymerization of C-S-H of nanosilica incorporated samples was larger than ordinary cement paste after heating to 200℃, and C-S-H formed during heating process to 500℃ due to the pozzolanic reaction during heating process.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2021.11a
• /
• pp.36-37
• /
• 2021

When the final finish of a building is designed with base concrete, complex deterioration occurs due to the harsh environment such as shrinkage and expansion due to external temperature changes, freezing and thawing, and the use of calcium chloride due to snow accumulation. Therefore, the pozzolanic reaction mechanism of blast furnace slag is clearly identified, and the causal relationship between the material properties and performance of the blast furnace slag is identified to present guidelines for mixing high-durability concrete.

• Computers and Concrete
• /
• v.17 no.3
• /
• pp.337-351
• /
• 2016

This paper presents the properties of pervious concrete containing high-calcium fly ash. The water to binder ratios of 0.19, 0.22, and 0.25, designed void ratios of 15, 20, and 25%, and fly ash replacements of 10, 20, and 30% were used. The results showed that the use of fly ash as partial replacement of Portland cement enhanced the mixing of paste resulting in a uniform mix and reduced amount of superplasticizer used in the mixture. The compressive strength and flexural strength of pervious concrete were slightly reduced with an increase in fly ash replacement level, while the abrasion resistance increased due mainly to the pozzolanic and filler effects. The compressive strength and flexural strengths at 28 days were still higher than 85% of the control concrete. The aggregate size also had a significant effect on the strength of pervious concrete. The compressive strength and flexural strength of pervious concrete with large aggregate were higher than that with small aggregate.

• International Journal of Concrete Structures and Materials
• /
• v.8 no.2
• /
• pp.157-164
• /
• 2014

Ground granulated blast-furnace slag (GGBS) is a green construction material used to produce durable concrete. The secondary pozzolanic reactions can result in reduced pore connectivity; therefore, replacing partial amount of Portland cement (PC) with GGBS can significantly reduce the risk of sulfate attack, alkali-silica reactions and chloride penetration. However, it may also reduce the concrete resistance against carbonation. Due to the time consuming process of concrete carbonation, many researchers have used accelerated carbonation test to shorten the experimental time. However, there are always some uncertainties in the accelerated carbonation test results. Most importantly, the moisture content and moisture profile of the concrete before the carbonation test can significantly affect the test results. In this work, more than 200 samples with various water-cementitious material ratios and various replacement percentages of GGBS were cast. The compressive strength, electrical resistivity, chloride permeability and carbonation tests were conducted. The moisture loss and microstructure of concrete were studied. The partial replacement of PC with GGBS produced considerable improvement on various properties of concrete.

• Journal of Ocean Engineering and Technology
• /
• v.23 no.3
• /
• pp.20-29
• /
• 2009

This study investigated the shear strength characteristics of waste tire powder-added lightweight soil (WTLS), which were developed to recycle dredged soil, bottom ash, and waste tires. The WTLS used in this experiment consisted of dredged soil, bottom ash, waste tire powder, and cement. Test specimens were prepared with various contents of waste tire powder ranging from 0% to 100% at 25% intervals and bottom ash contents of 0% or 100% by the weight of the dry dredged soil. In this study several series of direct shear tests were carried out, which indicated that the shear properties of WTLS were strongly influenced by the mixing conditions, such as the waste tire powder content and bottom ash content. The unit weight, as well as the shear strength of the WTLS, decreased with an increase in waste tire powder content. The shear strength of WTLS with bottom ash was 1.34 times greater than that of WTLS without bottom ash. An average increase in cohesion of 30 kPa was obtained in WTLS with the inclusion of bottom ash due to the bond strength induced from the pozzolanic reaction of the bottom ash. In this test, the maximum value of the internal friction angle was obtained with a 25% content of waste tire powder.

• Computers and Concrete
• /
• v.25 no.1
• /
• pp.83-94
• /
• 2020

The use of fly ash in modern-day concrete technology aiming sustainable constructions is on rapid rise. Fly ash, a spinoff from coal calcined thermal power plants with pozzolanic properties is used for cement replacement in concrete. Fly ash concrete is cost effective, which modifies and improves the fresh and hardened properties of concrete and additionally addresses the disposal and storage issues of fly ash. Soft computing techniques have gained attention in the civil engineering field which addresses the drawbacks of classical experimental and computational methods of determining the concrete compressive strength with varying percentages of fly ash. In this study, models based on soft computing techniques employed for the prediction of the compressive strengths of fly ash concrete are collected from literature. They are classified in a categorical way of concrete strengths such as control concrete, high strength concrete, high performance concrete, self-compacting concrete, and other concretes pertaining to the soft computing techniques usage. The performance of models in terms of statistical measures such as mean square error, root mean square error, coefficient of correlation, etc. has shown that soft computing techniques have potential applications for predicting the fly ash concrete compressive strengths.