• Korean Journal of Materials Research
• /
• v.9 no.12
• /
• pp.1205-1210
• /
• 1999

Far infrared ceramic/aluminum composite powders for thermal spray were fabricated by spray drying method and investigated the characteristics of the plasma sprayed coating layers, I.e. microstructure, phases, thermal shock resistance and spectral emissivity. The shape of the spray dried composite powder was spherical and the particle size distribution was 34~105${\mu}m $. Aluminum was distributed homogeneously in the spray dried composite powder. Spectral emissivity of the plasma sprayed coating layer ranges from 3 to 14${\mu}m $ whereas spectral emissivity of the raw ceramic powder ranges from 8 to 14${\mu}m $. And then spectral emissivity of the coatings was better than that of the raw powder but spectral emissivity was decreased with increasing aluminum content. It was found that aluminum content ranging from 20 to 30wt% was suitable for fabricating far-infrared radiator by plasma spraying method.

• Journal of the Korean Society for Industrial and Applied Mathematics
• /
• v.15 no.3
• /
• pp.223-231
• /
• 2011

During spray coating, especially in an air plasma spray (APS), pores, cracks, and splat boundaries are developed and those factors exert influence on thermomechanical properties such as elastic modulus, thermal conductivity, and coefficient of thermal expansion. Moreover, the thermo mechanical properties are crucial elements to determine the thermoelastic characteristics, for instance, temperature distribution, displacements, and stresses. Two types of thermal barrier coating (TBC) model, the dense and porous microstructures, are taken into account for the analysis of microstructural characterizations. $TriplexPro^{TM}$-200 system was applied to prepare TBC samples, and the METECO 204 C-NS powder is adopted for the relatively porous microstructure and METECO 204 NS powder for the dense microstructure in the top coat of TBCs. Governing partial differential equations were derived based on the thermoelastic theory and approximate estimates for the thermoelastic characteristics were obtained using a finite volume method for the governing equations.

• Korean Journal of Materials Research
• /
• v.11 no.11
• /
• pp.965-971
• /
• 2001

The objective of this study is to investigate the characteristics - microstructure, hardness, adhesive strength and friction coefficient - of the coatings with aging - treatment after optimizing internal- plasma spraying parameters for Al-30wt%Si powder as a basic research to manufacture the cylinder block bore for Al engine composed of Al-30wt%Si alloy on Al alloy, The optimum internal-plasma spraying parameters of Al-30wt%Si alloy are summarized as follows: voltage: 37.5V, current: 160A, working distance: 25mm, gun traverse speed: 4.5mm/s, rotating speed: 518m/min. The primary Si particles grew aggressively with increasing heat-treating temperature. The hardness of the as-sprayed coating was about Hv=275 but this value was abruptly decreased with increasing heat-treating temperature. And average friction coefficient of the coating was below 0.08 after heat treatment for 48h at $175^{\circ}C$.

• Journal of Ocean Engineering and Technology
• /
• v.23 no.6
• /
• pp.99-104
• /
• 2009

PTFE has good mechanical and chemical stability at a wide range of temperatures and demonstrates a low friction coefficient value. PTFE is being used for self-lubricating parts in industry. But it shows a high wear rate. Thus, PTFE and nano-diamond powder were mixed into a composite and the wear properties of a PTFE coating layer on Al6061 was investigated. A ball-on-disk type of wear tester was used under a dry condition and different temperatures of oil. After the wear test, the wear track wasexamined by optical microscope. The PTFE-diamond showed the lowest friction coefficient (0.02) of all the lubricants in the experiments. The friction coefficient was shown to be directly related to the diamond powder in the PTFE coating. Adhesion estimations were performed by a scratch test, which is mainly used for coatings. The critical load between the coating and substrate was defined through analyses of the friction load, normal load curve, and acoustic emissions, along with optical microscope observations. The scratch test results showed that an import item (SWISS) gave the highest critical load values.

• Korean Journal of Materials Research
• /
• v.16 no.5
• /
• pp.285-291
• /
• 2006

Copper powders have been widely used in electrically conductive coatings, electrode materials et al. and are very prospective since they are cheaper than noble metal powders such as silver or palladium. In this study, copper powders for metal filler of EMI shielding have been prepared using a solvothermal process from $CuSO_4$, NaOH, Glucose, mixed solvent ($H_2O$: Ethanol) and hydrazine which was used as a reducing agent at various reaction conditions. The prepared copper powders showed finely dispersed spherical shape without agglomerate, uniform morphology, narrow size distribution, high purity and were about 400-700 nm in size. The prepared powders were characterized using XRD, SEM, TGA, XPS, particle size measurement and EMI shielding efficiency.

• Particle and aerosol research
• /
• v.9 no.3
• /
• pp.127-132
• /
• 2013

Recently, Aerosol Deposition method has attracted considerable attention because of its advantages to produce ceramic coatings on various substrates at room temperature. This method is strongly dependent on the raw powder, which should have high mobility with carrier gas and moderate mechanical strength to be crushed onto the substrate. In this report, the effects of the ceramic granules' compressive strength on the ceramic coating formation are discussed. The ceramic granules were prepared by spray-drying method and heat treated at various temperatures. It was found that at the moderate mechanical strength of ceramic granules gave more effective film formation behavior during Aerosol Deposition method.

• Journal of the Korean Ceramic Society
• /
• v.40 no.2
• /
• pp.123-127
• /
• 2003

The effects of process parameters on coating formation and coating properties were investigated using a fused and crushed Ti $O_2$powder by the Taguchi method and L$_{9}$(3$^4$) orthogonal array. The Taguchi analysis was conducted through the results of the coating properties affected strongly by plasma spraying parameters and Ti $O_2$powder was sprayed on Ti-6Al-4V alloy substrate. The coating properties were characterized by thickness, microhardness, porosity and surface roughness using optical microscopy, image analyzer and surface roughness tester respectively. An observed optimum condition of plasma spraying process could be found for potential use as a bioceramic coating.

• Korean Journal of Materials Research
• /
• v.27 no.2
• /
• pp.119-126
• /
• 2017

WC-CrC-Ni coatings were prepared by nine processes of the Taguchi program with three levels for the four spray parameters: spray distance, flow rates of hydrogen and oxygen, and powder feed rate. The optimal coating process (OCP) was oxygen flow rate of 38 FMR, hydrogen flow rate of 53 FMR, powder feed rate of 25 g/min, and spray distance of 7 inches. Hardness of 1150 Hv and porosity of 1.2 %, were obtained by OCP; these are better results compared with the highest 1033 Hv and the lowest 1.5 % porosity obtained by nine processes of the Taguchi program. Friction coefficient of the WC-CrC-Ni coating decreased from $0.36{\pm}0.07$ at $25^{\circ}C$ to $0.23{\pm}0.07$ at $450^{\circ}C$. These values were smaller than those of the EHC (electrolytic hard chrome) plating at both temperatures due to lubrication from the oxide debris. The wear trace and wear depth of the coating are smaller than those of the EHC at both temperatures. Pitting was not found in the WC-CrC-Ni coating sample, while it did appear in the EHC sample.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2009.05a
• /
• pp.278-281
• /
• 2009

Selective laser sintering(SLS), a kind of rapid prototyping technology, can provide a process to form many types of coatings. Coated layers by selective laser melting are highly influenced by substrate, powder and laser parameters such as laser power, scan rate, fill spacing and layer thickness. Therefore an attempt to fabricate Fe-Ni-Cr coating on AISI H13 tool steel has been performed by selective laser sintering. In this study, Fe-Ni-Cr coating was produced by experimental facilities consisting of a 200W fiber laser which can be focused to 0.08mm and atmospheric chamber which can control atmospheric pressure with Ar. With power increase or energy density decrease, line width was decreased and line surface quality was improved with energy density increase. Surface quality of coating layer was improved with fill spacing optimization or layer thickness decrease.

• Journal of Powder Materials
• /
• v.12 no.2 s.49
• /
• pp.106-111
• /
• 2005

The effect of post-heat treatment on the coating characteristics and the fatigue strength of the gas flame thermally sprayed Stellite alloy coatings on $0.35\%$ carbon steel were investigated. The fatigue fracture surfaces of the heat treated samples were observed using SEM (Scanning Electron Microscopy). For as-sprayed samples, there was considerable scattering in the fatigue life due to the presence of the pores in the coating. After the post-heat treatment to improve the microstructural characteristics of the coating layer, the fatigue strength of the specimens was greatly improved, increasing with increasing the coating thickness. For the specimens with the 0.3mm and 0.5mm thick coating, the fatigue cracks originated in the substrate region just below the interface. On the contrary, for the specimens with the 1.0mm thick coating, they nucleated at the pore within the coating, and the fatigue strength was 2.6 times higher than that of the substrate due to the high fatigue resistance of the coating.