Recently, it is on the increase interest for Al alloy with new material for ship application to substitute for FRP ship. The reason is thatAl alloy ship has beneficial characteristics such as high sea speed, increase of loadage and easy to recycle compared with FRP ship. In this paper, mechanical and electrochemical properties are investigated by slow strain rate test experiment in various applied potential condition. These results will provide as reference data to design ship by deciding optimum protection potential regard to hydrogen embrittlement and stress corrosion cracking. In general, Al and Al alloys are not corroded with forming film which has the corrosion resistance property in neutral solution. However, it was observed that formation and destruction of passive film by $Cl^-$ ion in sea water environment. At comparison of current density after 1200 sec in potentiostatic experiment, the current density in the potential range of -0.68 $\~$-1.5 V is shown low value. The low current density means protection potential range. Elongation in applied potential of 0 V was high. However, the corrosion protection application in this condition is impossible potential because the toughness is low value by decreasing strength by active dissolution reaction at parallel part of specimen. The film composed with $CaCO_3$ and $Mg(OH)_2$ has a corrosion resistance property. However, the uniform electrodeposition coating at below -1.6 V potential is not formed since the time to form the uniform electrodeposition coating is short. Therefore, it is concluded that mechanical property is poor because effect by hydrogen gas generation is larger than that of electrodeposition coating. It is concluded that the optimum protection potential range from comparison of_maxim urn tensile strength, elongation and time to fracture is -1.3$\~$0.7 V (SSCE).

• 한국표면공학회지
• /
• 제50권5호
• /
• pp.339-344
• /
• 2017

Highly corrosion resistance performance of CrAlSiN coatings were obtained by applying ultrathin $Al_2O_3$ thin films using atomic layer deposition (ALD) method. CrAlSiN coatings were prepared on Cr adhesion layer/SUS304 substrates by a hybrid coating system of arc ion plating and high power impulse magnetron sputtering (HiPIMS) method. And, ultrathin $Al_2O_3$ passivation layer was deposited on the CrAlSiN/Cr adhesion layer/SUS304 sample to protect CrAlSiN coatings by encapsulating the whole surface defects of coating using ALD. Here, the high-angle annular dark-field scanning transmission electron microscopy (HAADF-STEM) and energy dispersive X-ray spectrometry (EDX) analysis revealed that the ALD $Al_2O_3$ thin films uniformly covered the inner and outer surface of CrAlSiN coatings. Also, the potentiodynamic and potentiostatic polarization test revealed that the corrosion protection properties of CrAlSiN coatings/Cr/SUS304 sample was greatly improved by ALD encapsulation with 50 nm-thick $Al_2O_3$ thin films, which implies that ALD-$Al_2O_3$ passivation layer can be used as an effect barrier layer of corrosion.

• Corrosion Science and Technology
• /
• 제22권6호
• /
• pp.447-456
• /
• 2023

In this work, we performed a comparative study examining two coatings on Ti Gr.1 for use in fuel cell bipolar plates. The coatings consisted of carbon black as the conductor along with acrylic polymer and Ti Sol-Gel binder as the binder. Ti Sol-Gel that had precipitated as TiO₂ in areas impregnated between carbon black gaps, thereby acting as a binder for carbon black and serving as a polymer coating. Neither of the coatings peeled off during the 90° bend test to check formability. The contact resistance of the TiO₂ coating was found to be lower than that of the polymer binder coating. Moreover, due to coating shrinkage (denser) that occurred during the heat treatment process, the TiO₂ binder coating showed almost the same level of corrosion resistance, as measured by potentiostatic and EIS tests, despite being thinner than the polymer coating. However, both the polymer binder coating and the TiO₂ binder coating had many pores and irregularities internally (around 10 ~ 100 nm) and on the surface (0.1 ~ 2 ㎛). We considered that these pores and irregularities contributed to the lower corrosion resistance.

• 대한치과기공학회지
• /
• 제30권1호
• /
• pp.25-31
• /
• 2008

Cp-Ti and Ti-6Al-4V alloys commonly used dental implant materials, particularly for orthopaedic and osteosynthesis because of its suitable mechanical properties and excellent biocompatibility. This alloys have excellent corrosion behavior in the clinical environment. The first factor to decide the success of dental implantation is sufficient osseointegration and high corrosion resistance between on implant fixture and its surrounding bone tissue. In this study, in order to increase corrosion resistance and biocompatibility of Cp-Ti and Ti-6Al-4V alloy that surface of manufactured alloy was coated with TiN by RF-magnetron sputtering method. The electrochemical behavior of TiN coated Cp-Ti and Ti-6Al-4V alloy were investigated using potentiodynamic (EG&G Co, PARSTAT 2273. USA) and potentiostatic test (250mV) in 0.9% NaCl solution at 36.5 $\pm$ 1$^{\circ}C$. These results are as follows : 1. From the microstructure analysis, Cp-Ti showed the acicular structure of $\alpha$-phase and Ti-6Al-4V showed the micro-acicular structure of ${\alpha}+{\beta}$ phase. 2. From the potentiodynamic test, Ecorr value of Cp-Ti and Ti-6Al-4V alloys showed -702.48mV and -319.87mV, respectively. Ti-6Al-4V alloy value was higher than Cp-Ti alloy. 3. From the analysis of TiN and coated layer, TIN coated surface showed columnar structure with 800 nm thickness. 4. The corrosion resistance of TiN coated Cp-Ti and Ti-6Al-4V alloys were higher than those of the non-coated Ti alloys in 0.9% NaCl solution from potentiodynamic test, indicating better protective effect. 5. The passivation current density of TiN coated Cp-Ti and Ti-6Al-4V alloys were smaller than that of the noncoated implant fixture in 0.9% NaCl solution, indicating the good protective effect resulting from more compact and homogeneous layer formation.