• International Journal of Concrete Structures and Materials
• /
• v.8 no.2
• /
• pp.173-182
• /
• 2014

An experimental investigation was carried out to evaluate the mechanical properties of concrete mixtures in which coarse aggregate was partially (30, 50 or 70 %) replaced with pre-washed municipal solid waste incineration (MSWI) bottom ash. Results indicated that bottom ash reduced the compressive strength, elastic modulus, and levels of heavy metals in leachate when used as a replacement for gravel, and that the maximum amount of MSWI bottom ash in concrete should not exceed 50 %. To analyze the effect mechanism of bottom ash in concrete, the degree of hydration and the following pozzolanic reaction characterized by the pozzolanic activity index, and the porosity distribution in cement mortar. The study indicates that improved properties of concrete are not solely later strength gain and reduced levels of heavy metals in leachate but also the progression of pozzolanic reactions, where a dense structure contains a higher proportion of fine pores that are related to durability.

• Bulletin of the Korean Chemical Society
• /
• v.27 no.10
• /
• pp.1562-1566
• /
• 2006

Mesoporous silica films with three different pore sizes were prepared by using cationic surfactant, non-ionic surfactant, or triblock copolymer as structure directing agents with tetramethylorthosilicate as silica source in order to control the pore size and wall thickness. They were synthesized by an evaporation-induced self-assembly process and spin-coated on Si wafer. Mesoporous silica films with three different pore sizes of 2.9, 4.6, and 6.6 nm and wall thickness ranging from $\sim$1 to $\sim$3 nm were prepared by using three different surfactants. These materials were optically transparent mesoporous silica films and crack free when thickness was less than 1 m m. The photoluminescence spectra found in the visible range were peaked at higher energy for smaller pore and thinner wall sized materials, consistent with the quantum confinement effect within the nano-sized walls of the silica pores.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2009.06a
• /
• pp.429-429
• /
• 2009

Nanoporous anodic alumina membranes (NAAM) with high-density through-hole pores fabricated by hard anodization of aluminum in 0.3 M oxalic acid under the applied voltage of 40 (mild anodization), 80, 100, 120 and 140 V were investigated. The current-time responses monitored using a PC-controlled anodization cell and the corresponding pore structures attainable from field-enhanced scanning electron microscopy (FE-SEM) were analyzed in order to establish the optimum fabrication process. The nanoporous structure can be produced for all the voltage conditions, while the stabilized through-hole pore formation seems to occur at 40, 80 and 140 V. The growth rate under 140 V hard anodization was over 30 times higher than under 40 V mild anodization (1.5 um/hr).

• Journal of the Korean Ceramic Society
• /
• v.29 no.11
• /
• pp.905-911
• /
• 1992

Model equations for the gas permeation through a ceramic composite membrane were derived for examining the existence of crack, the reproducibility, and the microstructural properties of composite membranes. From the results of analyzing the nitrogen permeability data through alumina-tube supported TiO2 and SiO2 composite membranes, the extent of cracking, and the formation and structure of membrane top-layers were modelled. It was proved that the crack-free and reproducible composite membranes could be easily prepared only by the pore-filled coating within pores of the support in the sol-gel coating process.

• Journal of the Korean Ceramic Society
• /
• v.29 no.4
• /
• pp.265-272
• /
• 1992

Role of CaO in the sintering of 12Ce-TZP ceramics was studied. The addition of small amounts of CaO increase the densification rate of 12Ce-TZP by altering lattice defect structure and the diffusion coefficient of the rate controlling species, namely cerium and zirconium cations. CaO also inhibits grain growth during sintering and allows the sintering process to proceed to theoretical density by maintaining a high diffusion flux of vacancies from the pores to the grain boundaries. The inhibition of grain growth is accomplished by the segregation of solute at the grain boundaries, causing a decrease in the grain boundary mobility. The segregation of calcium was revealed by AES study.

• Korean Journal of Materials Research
• /
• v.14 no.9
• /
• pp.664-669
• /
• 2004

Anodic aluminum oxide (AAO) with pores of various diameter, density, and thickness values was obtained through control of the anodization parameters including voltage, temperature, pore widening time, anodization time, etc. The pore diameter was controlled by a pore widening in an etchant, and alumina templates having stepped nano-channels were fabricated by repetition of anodization and pore widening processes. Stepped carbon nanotubes (CNTs) were then grown on the stepped AAO templates by pyrolysis of acetylene without using the catalyst. High-resolution transmission electron microscopy images revealed that CNTs have a multi-wall structure made of graphite flakes of several nm sizes. The current-voltage characteristic of the sloped and linear CNTs were also examined.

• Journal of the Korean Society for Precision Engineering
• /
• v.21 no.4
• /
• pp.186-193
• /
• 2004

Porous anodic alumina has been used widely for corrosion protection of aluminum surfaces or as dielectric material in micro-electronics applications. It exhibits a homogeneous morphology of parallel pores which can easily be controlled between 10 and 400nm. It has been applied as a template for fabrication of the nanometer-scale composite. In this study, mechanical properties of the AAO structures are measured by the nano indentation method. Nano indentation technique is one of the most effective methods to measure the mechanical properties of nano-structures. Basically, hardness and elastic modulus can be obtained by the nano-indentation. Using the nano-indentation method, we investigated the mechanical properties of the AAO structure with different size of nano-holes. In results, we find the hole effect that changes the mechanical properties as size of nano hole.

• Journal of Powder Materials
• /
• v.19 no.5
• /
• pp.367-372
• /
• 2012

Single crystalline Cu nanowires with controlled diameters and aspect ratios have been synthesized using electrochemical deposition within confined nanochannels of a porous anodic aluminium oxide(AAO) template. The diameters of nano-sized cylindrical pores in AAO template were adjusted by controlling the anodization conditions. Cu nanowires with diameters of approximately 38, 99, 274 nm were synthesized by the electrodeposition using the AAO templates. The crystal structure, morphology and microstructure of the Cu nanowires were systematically investigated using XRD, FE-SEM, TEM and SAED. Investigation results revealed that the Cu nanowires had the controlled diameter, high aspect ratio and single crystalline nature.

• Architectural research
• /
• v.15 no.1
• /
• pp.53-58
• /
• 2013

High strength concrete is being used increasingly in mass structure projects. The purpose of this study is to investigate the influence of temperature during mixing, placing and curing on the strength development, hydration products and pore structures of high strength concrete in mass structures. The experiments were conducted with two different model walls, viz.: 1.5 m and 0.3 m under typical summer and winter weather conditions. The final part of this study deal with the clarification of the relationship between the long-term strength loss and the microstructure of the high strength concrete at high temperatures. Test results indicated that high elevated temperatures in mass concrete structures significantly accelerate the strength development of concrete at the early ages, while the long-term strength development is decreased. The long-term strength loss is caused by the decomposition of ettringite and increased the total porosity and amount of small pores.

• Journal of Powder Materials
• /
• v.21 no.5
• /
• pp.389-398
• /
• 2014

Macroporous ceramics with tailored pore size and shape could be used for well-established and emerging applications, such as molten metal filtration, biomaterial, catalysis, thermal insulation, hot gas filtration and diesel particulate filters. In these applications, unique properties of porous materials were required which could be achieved through the incorporation of macro-pores into ceramics. In this article, we reviewed the main processing techniques which can be used for the fabrication of macroporous ceramics with tailored microstructure. Partial sintering, replica templates, sacrificial fugutives, and direct foaming techniques was described here and compared in terms of microstructures and mechanical properties that could be achieved. The main focus was given to the direct foaming technique which was simple and versatile approach that allowed the fabrication of macro-porous ceramics with tailored features and properties.