• Journal of Dental Rehabilitation and Applied Science
• /
• v.22 no.3
• /
• pp.211-220
• /
• 2006

Need of porcelain-repair system is largely demanding as dental porcelain restorations are increased in clinical dentistry. This study investigated shear bond strength of commercial porcelain-repair systems on dental porcelain and their reliability. Experimental groups were as follows; Group A Super Bond C&B, Group B Porcelain repair kit, Group C Ceramic repair, and Group D Spectrum system as a control. Porcelain disks were fired and embedded in epoxy resin. Porcelain surface were ground using 220 grit SiC disk, then cleaned in ultrasonic bath. Then porcelain specimens were treated with each repair system. A clear polystyrene cylinder 3.5 mm in internal diameter was filled with composite resin. Then the resin cylinder was polymerized with a visible light curing unit. Thirty one specimens at each group were prepared and stored at $37^{\circ}C$ distilled water for 48 h. Specimens were tested in an Instron testing machine according to ISO TR 11405. Mean shear bond strength and standard deviation of each group was $15.7{\pm}4.1MPa$ (Group A), $12.8{\pm}4.9MPa$ (Group B), $7.2{\pm}3.0MPa$ (Group C) and $9.6{\pm}2.2MPa$ (Group D). ANOVA and Tukey HSD post-hoc test showed that there were significant differences between groups (p<0.05). Data of bond strength were analyzed with two-parameter Weibull distribution. Confidence interval of Weibull modulus (m-parameter) at 95% of Group A (3.5-6.3) and Group D (3.6-6.0) were significantly higher than Group B (2.2-3.7) and Group C (2.0-3.4). There was little correlation between mean shear bond strength and Weibull modulus. Results indicated that acid-etching of porcelain surface increased porcelain-resin shear bonding strength.

• The Journal of Korean Academy of Prosthodontics
• /
• v.28 no.2
• /
• pp.147-163
• /
• 1990

Although dental porcelain demonstrates lasting esthetic results, it suffers from inherent brittle fractures. Various techniques and materials for intraoral porcelain repair has been suggested. This study investigated the in vitro shear strength of three porcelain repair systems according to aspects of the porcelain fractures. The purpose of this study was to evaluate the shear bond strength of three porcelain repair systems(All-bond, Clearfil, Scotchprime) according to fractured surface of porcelain - fused - to - metal restorations. For this study specimens were divided into five groups : group 1 represented fracture occurred at body porcelain layer, group 2 represented fracture occurred at opaque porcelain layer, group 3 represented fracture including 1/3 of metal exposure, group 4 represented fracture including 2/3 of metal exposure, and group 5 represented all metal surface was exposed. Specimens were stored in double deionized water(24Hr, $37^{\circ}C$) and thermocycling was performed(24Hr, 1080cycles), and subjected to a shear force parallel to the repair resin and porcelain interface by use of an University Testing Machine. The results of this study were obtained as follows : 1. In group 1 and 2, bond strength was relatively high, and bond strength showing reducing tendency as exposure of metal was increased. 2. In group 1, bond strength was relatively high, and no significant differences in porcelain repair system. 3. In group 2, 3 and 4, All-bond and Clearfil provided significantly higher bond strength than scotchprime. 4. In group 5, bond strength was the lowest among all groups and especially in case if Scotchprime. 5. Cohesive failure was observed in group 1 and 2, adhesive failure was observed in group 5, and cohesive / adhesive failures were observed in group 3 and 4.

• The Journal of Korean Academy of Prosthodontics
• /
• v.43 no.2
• /
• pp.149-157
• /
• 2005

Statement of problem. Dental ceramics exhibit excellent esthetic property, compressive strength, chemical durability biocompatibility and translucency. However, it suffers from inherent brittle fractures. Various techniques and materials for intraoral porcelain repair has been suggested. Purpose. This study is to compare the tensile bond strength of four commonly used porcelain repair systems (Vivadent, Bisco, Ulttadent, Voco) and to insure the best system for the clinical application to the fractured porcelain. Materials and methods. A total of fifty specimens were fabricated. Specimens were stored in $37^{\circ}C$ distilled water for 7 days and thermocycling was performed(1000 cycles), and subjected to a tensile force parallel to the repair resin and porcelain interface by use of an Universal Testing Machine. Result. 1. Voco showed the highest tensile bond strength. In decreasing order, the tensile bond strength of the other materials was as follows : Ultradent, Bisco, Vivadent. 2. There was a statistically significant difference between the porcelain repair systems(Voco, Ultradent > Bisco, Yivadent) (p<0.05). 3. SEM examination of prepared porcelain surfaces revealed that the surface treated with Voco showed brittle fracture. However, Ultradent, Bisco and Vivadent showed ductile fracture. 4. All specimens treated with four porcelain repair systems showed adhesive failure between porcelain and composite resin.

• The Journal of Korean Academy of Prosthodontics
• /
• v.45 no.4
• /
• pp.419-430
• /
• 2007

Purpose: This in vitro study evaluated shear bond strengths of surface treatment porcelains with four porcelain repair systems simulating intraoral bonding of composite resin to feldspathic porcelain or pressable porcelain. Material and methods: Eighty Porcelain disks were prepared. Group A: forty disk specimens were fabricated with Feldspathic Porcelain($Omega^{(R)}900$, Vident, Menlo Park, CA, USA). Group B: forty disk specimens were fabricated with Pressable Porcelain(IPS Empress 2 ingot, Ivoclar-Vivadent, Schaan, Liechtenstein, Germany). Each groups was divided into 4 subgroups and composite resin cylinders were bonded to specimen with one of the following four systems: Clearfil Porcelain Bond(L. Morita, Tustin, CA, USA), Ulradent Porcelain Etch. (Ultradent, Salt Lake City UT, USA), Porcelain Liner-M(Sun Medical Co., Kyoto, Japan), Cimara Kit(Voco, Germany). After surface conditioning with one of the four porcelain repair systems substrate surfaces of the specimen were examined microscopically(SEM). Shear bond strengths of specimens for each subgroup were determined with a universal testing machine (5mm/min crosshead speed) after storing them in distilled water at $37{\pm}1^{\circ}C$ for 24 hours. Stress at failure was measured in $MP_a$, and mode of failure was recorded. Differences among four repair systems were analyzed with two way ANOVA and Duncan test at the 95% significance level. Results: In the scanning electron photomicrograph of the treated porcelain surface, hydrofluoric acid etched group appeared the highest roughness. The shear bond strength of the phosphoric acid etched group was not significantly(p>0.05) different between feldspathic porcelain and pressable porcelain. But in no treatment and roughened with a bur group, the shear bond strength of the feldspathic porcelain was significantly higher than that of the pressable porcelain. In hydrofluoric acid etched group, the shear bond strength of the pressable porcelain was significantly higher(p<0.05). Conclusion: 1. Treatment groups showed significantly greater shear bond strengths than no treatment group(p<0.05). 2. Group with more roughened porcelain surface did not always show higher shear bond strengths. 3. In phosphoric acid etched group, there was no significant difference in shear bond strength between feldspathic porcelain and pressable porcelain(p>0.05). However in the other groups, there were significant differences in shear bond strengths between feldspathic porcelain and pressable porcelain(p<0.05).

• The Journal of Advanced Prosthodontics
• /
• v.7 no.5
• /
• pp.343-348
• /
• 2015

PURPOSE. The purpose of this study was to evaluate the bond strength of composite resin on the fracture surface of metal-ceramic depending on the repair systems and surface roughening methods. MATERIALS AND METHODS. A total of 30 disk specimens were fabricated, 15 of each were made from feldspathic porcelain and nickel-chromium base metal alloy. Each substrate was divided into three groups according to the repair method: a) application of repair system I (Intraoral Repair Kit) with diamond bur roughening (Group DP and DM), b) application of repair system I with airborne-particle abrasion (Group SP and SM), and c) application of repair system II (CoJet Intraoral Repair System, Group CP and CM). All specimens were thermocycled, and the shear bond strength was measured. The data were analyzed using the Kruskal-Wallis analysis and the Mann-Whitney test with a significance level of 0.05. RESULTS. For the porcelain specimens, group SP showed the highest shear bond strength ($25.85{\pm}3.51MPa$) and group DP and CP were not significantly different. In metal specimens, group CM showed superior values of bond strength ($13.81{\pm}3.45MPa$) compared to groups DM or SM. CONCLUSION. Airborne-particle abrasion and application of repair system I can be recommended in the case of a fracture localized to the porcelain. If the fracture extends to metal surface, the repair system II is worthy of consideration.

• The Journal of Korean Academy of Prosthodontics
• /
• v.42 no.2
• /
• pp.133-141
• /
• 2004

Statement of problem : Porcelain restorations are widely used in restorative dentistry with a high degree of general success. However, porcelain is brittle and may fracture intraorally. Sometimes a repair may be attempted using composite resin and bonding system available. Color stability of porcelain repair resins affects esthetics and prognosis of prosthesis, so that provides important criteria for the choice of porcelain repair resins. Purpose : The purpose of this study was to investigate the color stability of composite resins used widely as porcelain repair system. Materials and method : Composite resins used for this study were Carisma(Kulzer, Germany), Tetric ceram(Ivoclar, Liechtenstein), Filtek Z250(3M, USA), and Arabesk Top(VOCO, Germany). Thirty disc-shaped specimens($10{\times}2mm$) were fabricated from each composite resin. Color changes of specimens after treatment using thermocycling system(KD-TCS30, Kwang-duk F.A. Korea) and after immersion in methylene blue(0.05% by Wt) were measured with colorimeter(Model Tc-6Fx, Tokyo Denshoku Co.) and obtained data were analyzed. Results and Conclusion: The results obtained from this study were as fo11ows. 1. The color change of Filtek Z250 was lesser than those of Tetric ceram and Arabesk Top after thermocycling (12000 times). 2. All of the composite resins in this study showed increase of color change according to increase of thermocycling frequency. 3. After treatment with methylene blue, the color change of Arabesk Top was greater than those of Carisma and Tetric ceram, and Tetric ceram was more stable than others.

• The Journal of Advanced Prosthodontics
• /
• v.12 no.3
• /
• pp.131-139
• /
• 2020

PURPOSE. The purpose of this study is to evaluate the repair bond strength of a nanohybrid resin composite to three CAD/CAM blocks using different intraoral ceramic repair systems. MATERIALS AND METHODS. Three CAD/CAM blocks (Lava Ultimate, Cerasmart, and Vitablocks Mark II) were selected for the study. Thirty-two specimens were fabricated from each block. Specimens were randomly divided into eight groups for the following different intraoral repair systems: Group 1: control group (no treatment); Group 2: 34.5% phosphoric acid etching; Group 3: CoJet System; Group 4: Z-Prime Plus System; Group 5: GC Repair System; Group 6: Cimara System; Group 7: Porcelain Repair System; and Group 8: Clearfil Repair System. Then, nanohybrid resin composite (Tetric Evo Ceram) was packed onto treated blocks surfaces. The specimens were thermocycled before application of repair systems and after application of composite resin. After second thermal cycling, blocks were cut into bars (1 × 1 × 12 ㎣) for microtensile bond strength tests. Data were analyzed using two-way ANOVA and Tukey's HSD test (α=.05). RESULTS. Cimara System, Porcelain Repair, and Clearfil Repair systems significantly increased the bond strength of nanohybrid resin composite to all CAD/CAM blocks when compared with the other tested repair systems (P<.05). In terms of CAD/CAM blocks, the lowest values were observed in Vitablocks Mark II groups (P<.05). CONCLUSION. All repair systems used in the study exhibited clinically acceptable bond strength and can be recommended for clinical use.

• The Journal of Korean Academy of Prosthodontics
• /
• v.30 no.1
• /
• pp.73-83
• /
• 1992

Now composite resin restoration is clinically accepted in the repair of fractured PFM case, many mechanical surface treatment methods are performed to increase retentive force. The main purpose of this study was to compare the retentive force among the possible surface treatments and to insure the best method for the clinical application to the fractures porecelain and the exposed metal surface. To compare and to analyze the retentive force of repair resin, porcelain specimen were divided into 2 groups, etching group and non-etching group, and etching group were treated with 37% $H_3PO_4$, 1.23% APF, 10% HF and non-etching groups were treated with diamond bur, micro-sandblasasting. Also, metal specimens were divided by 2 groups : one was non-precious metal group which was treated with diamond bur, micro-sandblasting and tin plating and electrolytic etching, the other was precious metal group which was composed of micro-sandblasting treatment only and tin plating treatment with micro-sandblasting. Each specimen had been restored for 48 hours and the bond strength of each specimen was calculated with Universal testing machine. The results were as follows : 1. Porcelain specimen had higher bonding strength than metal specimen for the repair resin(P<0.01). 2. In porcelain specimen, 10% HF etching group had the highest bonding strength among etching and non-etching group. 3. Metal specimen treated with micro-sandblasting had highest bonding strength among the non-sandblasting had hightest bonding strength among the non-precious group, tin plating group had higher bonding strength than micro-sandblasting group between the precious metal groups. 4. Bonding strength of tin plating was increased in precious metal group only.

• The Journal of Advanced Prosthodontics
• /
• v.11 no.5
• /
• pp.297-304
• /
• 2019

PURPOSE. This in vitro study investigated the repair bond strength of the zirconia ceramic after different aging conditions. MATERIALS AND METHODS. In order to imitate the failure modes of veneered zirconia restorations, veneer ceramic, zirconia, and veneer ceramic-zirconia specimens were prepared and were divided into 4 subgroups as: control ($37^{\circ}C$ distilled water for 24 hours ) and 3000, 6000, 12000 thermal cycling groups (n=15). Then, specimens were bonded to composite resin using a porcelain repair kit according to the manufacturer recommendation. The repair bond strength (RBS) test was performed using a universal testing machine (0.5 mm/min). Failure types were analyzed under a stereomicroscope. Two-way ANOVA and Bonferroni test were used for statistical analysis. RESULTS. The RBS values of zirconia specimens were statistically significant and higher than veneer ceramic and veneer ceramic-zirconia specimens in control, 3000 and 6000 thermal cycling groups (P<.05). When 12000 thermal cycles were applied, the highest value was found in zirconia specimens but there was no statistically significant difference between veneer ceramic and veneer ceramic-zirconia specimens (P>.05). Veneer ceramic specimens exhibited cohesive failure types, zirconia specimens exhibited adhesive failure types, and veneer ceramic-zirconia specimens exhibited predominately mixed failure types. CONCLUSION. Thermal cycling can adversely affect RBS of composite resin binded to level of fractured zirconia ceramics.

• The Journal of Korean Academy of Prosthodontics
• /
• v.29 no.2
• /
• pp.117-127
• /
• 1991

The purpose of this study was to evaluate the effect of surface treatment of fractured metal-ceramic crown on bond strength of porcelain repair resin. The specimens were divided into two groups for metal specimens add five groups for porcelain specimens by surface treatment methods. the metal specimens were treated by 2 methods. : micro-sandblasting with $50{\mu}m$ aluminum oxide and grinding with diamond bur. The porcelain specimens were treated by 5 methods : micro-sandblasting with $50{\mu}m$ aluminum oxide, grinding with diamond bur, etching with porcelain etching agent, combination of micro-sandblasting and etching procedure, and combination of grinding and etching procedure. After surface treatment, each specimen was bonded with composite resin and the bond strength was measured and the surface texture was observed by scanning electromicroscope(SEM). The results were as follows : 1. There was significant difference in shear bond strength between metal specimen and prorcelain specimen. 2. Bood strength of metal specimens treated with diamond bur was higher than that treated with $50{\mu}m$ aluminum oxide sandblasting. 3. Bond strength of porcelain specimen treated with diamond bur was higher than that treated with $50{\mu}m$ aluminum oxide sandblasting and porcelain etching agent. 4. There was no significant difference in shear bond strength between the group treated with diamond bur and combined treatment groups respectively. 5. The large undercuts were observed in group treated with diamond bur by SEM.