• Advances in concrete construction
• /
• v.6 no.2
• /
• pp.199-220
• /
• 2018

In this study, the effects of sulphuric acid on the mechanical performance and the durability of Engineered Cementitious Composites (ECC) specimens were investigated. The carbon fiber reinforced polymer (CFRP) and basalt fiber reinforced polymer (BFRP) fabrics were used to evaluate the performances of the confined and unconfined ECC specimens under static and cyclic loading in the acidic environment. In addition, the use of CFRP and BFRP fabrics as a rehabilitation technique was also studied for the specimens exposed to the sulphuric acid environment. The polyvinyl alcohol (PVA) fiber with a fraction of 2% was used in the research. Two different PVA-ECC concretes were produced using low lime fly ash (LCFA) and high lime fly ash (HCFA) with the fly ash-to-OPC ratio of 1.2. Unwrapped PVA-ECC specimens were also produced as a reference concrete and all concrete specimens were continuously immersed in 5% sulphuric acid solution ($H_2SO_4$). The mechanical performance and the durability of specimens were evaluated by means of the visual inspection, weight change, static and cyclic loading, and failure mode. In addition, microscopic changes of the PVA-ECC specimens due to sulphuric acid attack were also assessed using scanning electron microscopy (SEM) to understand the macroscale behavior of the specimens. Results indicated that PVA-ECC specimens produced with low lime fly ash (LCFA) showed superior performance than the specimens produced with high lime fly ash (HCFA) in the acidic environment. In addition, confinement of ECC specimens with BFRP and CFRP fabrics significantly improved compressive strength, ductility, and durability of the specimens. PVA-ECC specimens wrapped with carbon FRP fabric showed better mechanical performance and durability properties than the specimens wrapped with basalt FRP fabric. Both FRP materials can be used as a rehabilitation material in the acidic environment.

• Textile Coloration and Finishing
• /
• v.31 no.4
• /
• pp.312-322
• /
• 2019

The mechanical properties of developed fabrics which were composed of soluble yarns and stretch fibers were analyzed using the Kawabata Evaluation System. The following findings were obtained from this investigation. Fabrics woven with lightweight yarns can be easily deformed by external forces. But when the fabric were woven using thick lightweight yarns reduced the slippage between the fibers, which makes it difficult to deform due to external force, thereby maintaining a certain space from the human body. As for the weight of the fabric per unit thickness, it was found that fabrics were compose of lightweight spun yarn was lightweight relatively. Lightweight yarns were more flexible than regular yarns because of the reduced bending and shear properties that greatly affect the lattice pattern. smoother, more flexible, and the better the bend was recovered. As fabrics increased content of using of lightweight spun yarn was increased flexible and smooth, and bending recovery.

• Journal of Korean Society of Environmental Engineers
• /
• v.27 no.9
• /
• pp.946-951
• /
• 2005

In this wort plasma treatment was evaluated as an alternative clean desizing technology. Size materials such as PVA(polyvinyl alcohol), PACL(polyacrylic acid esters) and their mixture on PET(polyethylene terephthalate) fabrics were treated by $N_2$ and $O_2$ plasma. $O_2$ plasma was more efficient in size removal than $N_2$ plasma, and the removal of PVA was higher than that of PACL. SEM(scanning emission microscopy) pictures of the plasma treated samples directly proved the disappearance of sizing agents. After $O_2$ plasma treatment, the PET fabrics were subjected to conventional desizing process. Compared with untreated fabrics, the desizing effluent from the treated fabrics gave lower TOC, COD and $BOD_5$ values. This indicates plasma treatment not only serves to directly remove sizing agents but also offered several advantages by changing the chemical properties of sizing agents. Lastly, the effect of plasma desizing process on dyeing was examined using color difference and dyeing fastness tests. The CCM(computer color matching) results showed rotor difference between PET fabric desized by $O_2$ plasma treatment for 20 min and reference PET fabric desized by the conventional wet desizing process was around 1. This suggests the treated PET fabric can be directly subjected to dyeing process without any additional process. The plasma treated fabric also gave a good result of dyeing fastness so that grades of laundering, crocking, heat and light fastness were same or even better than the reference PET fabric did.

• Journal of the Korean Society of Clothing and Textiles
• /
• v.10 no.3
• /
• pp.71-81
• /
• 1986

In order to control the formaldehyde release from D.P. finished fabric, cotton fabric was padded in DMDHEU resin bath containing either $Zn(NO_3)_2$ or $MgCl_2$ catalyst and a form-aldehyde scavenger like Glycerol, Sorbitol, Formamide, Polyvinyl alcohol (PVA, n= 2000) or diols, then dried and cured. The results are as follows : 1. When Lewis acid catalyst like $Zn(NO_3)_2$ or $MgCl_2$ was added in pad bath, the fabric finished with $Zn(NO_3)_2$ catalyst released the lower formaldehyde than with $MgCl_2$. 2. When the effect of pad bath pH was examined with varying the kinds of catalyst and the scavenger, it was found that the pad bath pH influenced on the amount of formaldehyde release and the optimum pad bath pH is at 4.3. Especially, in case of finishing at pad bath pH 4.3 with adding Formamide, the amount of formaldehyde release was decreased by about $45\~$35\%$ with $Zn(NO_3)_2$, while by about $20\~$45\%$ with $MgCl_2$ catalyst. In case of varying the concentration of a scavenger (Formamide), $1\%$ concentration of a scavenger was found to be the optimum level ana the higher the curing temperature up to $180^{\circ}C$, the lesser the amount of formaldehyde release were observed. 3. When the diol was used as scavenger, the amount of formaldehyde release was decreased by about $40\~$50\%$, but the longer the intramolecular length between OH groups, the lessor the amount of decrease of formaldehyde release were observed. 4. When the mixture of scavengers (Formamide and Glycerol) was added in the pad bath, .synergistic effect on formaldehyde release between the two scavengers wasn't observed. 5. The tensile strength of the resin finished fabric was reduced with increasing the pad lath pH and was influenced by the kind of scavengers, and the tensile strength was severely reduced when scavengers, especially Formamide, was added. The wrinkle recovery property is generally improved by resin finish on cotton fabric. When Formamide was added, the wrinkle recovery property is slightly decreased compared with that of the fabrics resin finished without a scavenger, and when polyol was added, the wrinkle recovery property showed almost no change.