• Bulletin of the Korean Chemical Society
• /
• v.30 no.10
• /
• pp.2227-2232
• /
• 2009

Novel polythiol materials of urethane lens series for plastic optical lens were synthesized from polyol materials via thioisouronium of thiourea with c-HCl in refluxing aqueous solution, in which polythiol material was carried out from hydrolysis of thioisouronium by ammonia water. Their structure properties were identified by EA, EI-MS, FT-IR, $^1H\;and\;^{13}C$ NMR spectroscopies and TGA. Their ophthalmic lenses as polythiourethane material were prepared by thermal curing to an injected glass mold using the evenly solutions of diisocyanates series (TDI, XDI, HDI or IPDI) with polythiols. Polythiourethane shows that the strong stretching mode for SH group of polythiol disappeared in FT-IR spectra after thermosetting polymerization. Thermal deformation starting temperature of ophthalmic lenses was determined by TMA. Ophthalmic lenses made from characteristic polythiol and diisocyanate series have transparency, colorless and good impact strength, in which thermal resistance and impact strength of ophthalmic lenses were influenced by diisocyanate series. Physical properties of ophthalmic lens have contrast thermal resistance with impact strength. The property of thermal resistance and impact strength for respective ophthalmic lenses was examined by TMA and drop ball test.

• Polymer(Korea)
• /
• v.27 no.5
• /
• pp.470-476
• /
• 2003

In order to obtain high refractive plastic materials, 1,2 -ethylenedisulfanylbis(2-mercaptomethyl-1-ethanthiol) (ESTT) was newly prepared in good yield by the reaction of 1,2-ethylenedisulfanylbis(2-bromomethyl-1-ethanthiol) (ESTB) with thiourea followed by hydrolysis using an aqueous ammonia solution and characterized by $^1$H-NMR (-SH at 1.7 ppm), $\^$13/C-NMR(-CH$_2$SH at 28.4 ppm) and FT-IR (-SH at 2540 cm$\^$-1/) spectroscopy, etc. Polythiourethanes (PTU) were obtained from the combinations of ESTT with each of 4,4＇-methylenebis(phenylisocyanate) (MDI), tolyene 2,4-diisocyanate (TDI), isophorone diisocyanate (IPDI), mxylene diisocyanate (XDI), and 1,6-diisocyanatohexane (HMDI) in the presence of dibutyltin dilaurylate as a catalyst, in a casting mold, and characterized by FT-IR (existence of N=C=O) spectroscopy and elemental analyzer (sulfur content). Accordingly, their thermal, mechanical and optical properties were investigated by using DSC, TGA, hardness tester and refractometer: both the melting point on DSC and crystallinity on X -ray diffraction (XRD) for specimens of PTUs were not observed. PTUs with T$\_$g/s above 110 $^{\circ}C$ showed good hardness (Shore D) in the range of 86 to 89. Thermal stabilities of PTUs obtained by using ESTT and each of diisocyanates containing aromatic rings were especially good. Also, the optical transmittances of amorphous PTUs through UV-visible source in the range of 400 to 600 nm were good. PTUs showed refractive indexes above 1.60, and their refractive indexes gradually increased with increase of sulfur contents.