• 한국염색가공학회지
• /
• 제19권2호
• /
• pp.36-43
• /
• 2007

Dyeing and fastness properties of a dyeable PP fiber were examined with four different types of disperse dyes. It was found that the dyed PP fiber could be cleared by soaping without using sodium hydrosulphite, and that the heat setting above $140^{\circ}C$ resulted in the melting of the PP fiber. The rates of dyeing and the extents of exhaustion of three primary E type dyes were different with each other, the apparent color strength did not increase with increasing dye concentration, and color fastness to washing was not satisfactory. In the cases of both high wash fastness and high light fastness dyes, the rates of dyeing were slow and the extents of exhaustion were very low. On the other hand, the dyeing rates of three primary S type dyes were similar and the build-up properties were good with good color fastnesses. It might be concluded that the best disperse dyes for the dyeable PP fiber were S type dyes.

• 콘크리트학회논문집
• /
• 제18권1호
• /
• pp.83-90
• /
• 2006

본 연구는 PP 및 CL 섬유 혼입량 변화에 따라 제작한 고성능 K 기둥부재를 대상으로 화재를 상정한 내화시험 후 폭열 방지 및 내화성능을 검토한 것으로, 그 실험결과를 요약하면 다음과 같다. 굳지않은 콘크리트의 특성으로, PP 및 CL섬유 혼입량 증가에 따른 유동성은 섬유의 엉킴현상 등에 의해 플레인보다 저하하였고, 공기량은 다소 증감의 차이는 있으나 모두 목표 공기량의 범위를 만족하였으며, 경화 콘크리트의 압축강도는 섬유 혼입량 변화에 따라 50 MPa 전후의 고강도로 나타났다. 내화시험 후 RC 기둥부재의 폭열특성으로, 섬유를 혼입하지 않은 플레인은 전체적으로 심한 파괴폭열이 발생하여 철근이 노출되었고, PP섬유를 혼입한 경우는 내부 수증기압의 효과적인 배출로 폭열이 방지되었으며, CL섬유는 플레인보다 폭열 방지효과는 있으나, 모서리 부분에서 일부 파괴폭열이 발생하였다. 또한, 내화시험 후 폭열깊이는 표면보다 모서리에서 더 깊게 나타났고, 폭열발생면적율은 폭열방지 성능과 관계하여 PP섬유를 혼입한 경우가 가장 양호하였으며, 중성화깊이는 $6{\sim}8mm$ 전후의 유사한 깊이로 나타났다. 내화시험 후 잔존 압축강도율은 PP섬유를 혼입한 경우 40% 전후로 플레인의 20% 보다 크게 나타났고, CL섬유를 혼입한 경우는 25% 전후로 플레인과 큰 차이가 없었다.

• 유변학
• /
• 제10권2호
• /
• pp.57-64
• /
• 1998

A pultrusion resin impregnation (PRI) die, which has been developed recently in our laboratory, was used to pre-pare various composite system. The continuous fiber reinforced composites of glass fiber/polypropylene(GFPP) and glass fiber/polyamide 6 (GFPA) were first manufactured by means of the PRI die and then cut into chopped pellets of predet-ermined length. These pellets and either virgin or modified thermoplastic resin were melt-mixed by a twin screw extruder to prepare GF/PA/PP and GF/PA/PPMA system. The mechanical properties of these blends were investigated and discussed in terms of their morphological observations. These preliminary results revealed that this new impregnation die could be suc-cessfully applied to produce prepregs suitavle for the final shaping process.

• 공업화학
• /
• 제29권2호
• /
• pp.168-175
• /
• 2018

본 논문에서는 대나무 섬유(BF)의 화학처리가 BF 및 폴리프로필렌(PP)/대나무섬유(BF) 복합체의 물성에 미치는 영향을 고찰하기 위해, 알칼리 처리 전후의 BF에 대해 ${\gamma}$-aminopropyltriethoxysilane (APS), ${\gamma}$-glycidoxypropyl-trimethoxysilane (GPS) 그리고 ${\gamma}$-mercaptopropyltrimethoxysilane (MRPS)을 이용하여 실란 상용화제를 처리하였다. BF의 화학처리에 따른 형태학적 특성은 광학현미경(OM)과 주사전자현미경(SEM)을 통해 확인하였으며, 화학 구조의 변화는 FT-IR과 EDS를 통해 확인하였다. 실란처리 시 BF의 열안정성이 증가함을 TGA를 통해 확인하였다. 실란 처리한 PP/BF 복합체의 굴곡강도와 충격특성이 개선되는 것을 만능시험기(UTM)와 충격강도시험기(Izod impact test)를 통해 확인하였고, PP/BF 계면 접착특성이 개선되는 것을 인장시험 후 시편의 파단면을 SEM 사진을 통해 확인하였다.

• 공업화학
• /
• 제22권5호
• /
• pp.467-472
• /
• 2011

본 연구에서는 천연물을 이용한 기능성 섬유를 제조하기 위하여 미처리 및 불소화 일라이트를 첨가하여 일라이트/PP 복합섬유를 용융방사로 제조하고 그 물리적 특성을 고찰하였다. 복합필라멘트 형성 시 층상구조를 가지는 일라이트의 윤활특성으로 순수 PP 필라멘트에 비해 복합필라멘트의 직경이 감소하는 현상이 나타났으며, 불소화의 효과로 인한 계면 친화성 향상 및 분산성 향상으로 불소화 일라이트/PP 복합필라멘트의 직경이 순수 PP 필라멘트의 2/3 정도로 감소하였다. 미처리 및 불소화 일라이트 모두 일라이트/PP 복합필라멘트의 열안정성을 향상시키는 효과가 있는 것으로 확인되었다. 또한, 미처리 일라이트/PP 복합필라멘트는 연신 공정을 거칠 때 절사가 발생하여, 복합섬유로서 활용될 수 없었으나, 불소화 일라이트/PP 복합필라멘트는 연신 후 순수 PP 필라멘트와 비슷한 인장강도를 가지고, 50% 정도 증가한 탄성률을 가지는 것으로 보아 복합섬유로서 사용될 수 있음을 확인할 수 있었다. 일라이트/PP 복합필라멘트를 형성 시, 불소화를 통하여 일라이트/PP간의 계면 친화성이 향상되고 고분자 내 분산성은 향상이 되었으나, 층간 결합력이 강한 비팽윤성 일라이트 고유의 성질로 인하여 일라이트의 박리나 PP의 일라이트 내 층간삽입이 충분히 발생하지 않은 것으로 보아 나노복합체가 아닌 마이크로 복합체를 형성하는 것으로 여겨진다.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2011년도 추계 학술논문 발표대회
• /
• pp.119-120
• /
• 2011

Recently, the effects of high temperature and fiber content on the residual mechnical properties of high-strength concrete were experimentally investigated. In this paper, residual mechanical properties of concrete with water to cement (w/c) ratios of 55%, 42% and 32% exposed to high temperature are compared with those obtained in fiber reinforced concretes of similar characteristics with the ranging of 0,05% to 0,20% polypropylene (PP) fibers by volume of concrete, and considered factors include pre-load levels (20% and 40% of the maximum load at room temperature). Outbreak time and water contents were tested and were determined the compressive strength. In the result, it is showed that to prevent the explosive spalling of 50MPa grade concretes exposed to high temperature need more than 0.05Vol.% PP fibers. Also, the cross-sectional area of PP fiber can influence on the residual mechanical properties and the spalling tendency of fiber reinforced concrete exposed to high temperature. Especially, the external loading increases not only the residual mechanical properties of concrete but also the risk of spalling and the brittle tendency.

• 한국화재소방학회논문지
• /
• 제23권4호
• /
• pp.1-6
• /
• 2009

고강도 콘크리트는 구조적인 장점에도 불구하고 화재 시 폭렬과 함께 취성적인 파괴를 나타내는 단점으로 인하여 실구조물에 적용 시 주의하여 사용하여야 한다. 고강도 콘크리트의 폭렬제어를 위하여 폴리프로필렌 섬유(PP섬유)의 혼입이 효율적인 것으로 콘크리트 공시체를 대상으로 한 여러 내화실험결과를 통하여 보고되었다. 또한 초고강도 콘크리트의 강도발현을 위하여 필수적으로 사용되는 실리카흄은 콘크리트의 수밀성을 높여 폭렬현상이 더욱 심하게 발생할 것으로 판단된다. 따라서 본 연구에서는 PP섬유의 혼입량과 실리카흄 치환율을 변수로 하는 고강도 철근콘크리트 기둥부재의 내화실험 및 잔존강도 실험을 수행하여 고온 시 각 변수들이 폭렬현상에 미치는 영향 및 잔존강도를 분석하였다. 실험결과 PP섬유 혼입량을 0%에서 0.2%까지 증가 시킬수록 기둥의 폭렬정도가 감소하고, 잔존 압축강도비는 증가하는 것으로 나타났으며, 실리카흄을 7%, 14% 및 21%로 증가시킬수록 기둥의 폭렬정도는 크게 변화하지 않았으나, 잔존 압축강도비는 감소하는 것으로 나타났다.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2009년도 춘계 학술논문 발표대회 학계
• /
• pp.61-64
• /
• 2009

This study is reviewed fire resistance characteristics of high strength concrete according to changes in PP fiber mixing ratio and type of fine aggregate, and the results can be summarized as follows. As fire resistance characteristics, all plain crushed sands prevented spalling regardless of increase in mixing ratio of PP fiber. Mixtures other than the plain showed satisfactory spalling prevention when 0.05 % or more of PP fiber was mixed. After the fire resistance experiment, the plain showed 5.5 % of mass loss rate when fiber was not mixed and others could not be measured. According to increase in mixing ratio of fiber, river sand with fineness modulus of 2.2 showed most satisfactory result of 34 %${\sim}$42 %. Mass loss rate after fire resistance experiment was most satisfactory at about 10 % in the plain crushed sand without mixing of fiber, and all other mixes with 0.05 % PP fiber or more showed 5${\sim}$10 % loss rate.

• 한국세라믹학회지
• /
• 제41권6호
• /
• pp.430-434
• /
• 2004

The values of fracture energy and mechanical flexural strength of Fiber Reinforced Cement (FRC) with polypropylene (PP) fiber modified by Ion Assisted Reaction (JAR), by which functional groups were grafted on the surface of PP fiber, was improved about 2 times as those of fracture energy and flexural strength of cement reinforced by untreated PP fiber. PP fiber was irradiated in O$_2$ environment by Ar$\^$+/ ion. The contact angle of PP treated by IAR decreased largely when compared with untreated PP. From this result, we expected that surface energy and interfacial adhesion force of treated PP fiber increased. The strain hardening occurred in the strain-stress curve of FRC including PP treated by IAR when compared with that of FRC with untreated PP. These enhanced mechanical properties might be due to strong interaction between hydrophilic group on modified PP fiber and hydroxyl group in cement matrix. This hydrophilic group on surface modified PP fiber was confirmed by XPS analysis. We clearly observed hydration products that were fixed at modified PP fiber due to the strong adhesion force of interface in cement reinforced modified PP by SEM (Scanning Electron Microscopy) study.

• Macromolecular Research
• /
• 제11권4호
• /
• pp.224-230
• /
• 2003

The blends of polypropylene (PP) with glass filled thermotropic liquid crystalline polymer (LCP-g) have been prepared by melt mixing techniques at different blend ratios. The thermal, dynamic mechanical, crystalline and morphological characteristics of these blends were investigated. Higher percent crystallinity was observed for 10% level of LCP-g in the blend in comparison to that of other blend ratios. The thermal stability increased with LCP-g concentration in the blend with PP. The variation of storage modulus, stiffness and loss modulus as a function of blend ratios suggested the phase inversion at the 50% level of LCP-g in the blend. The scanning electron microscopy (SEM) photographs showed the creation of voids and destruction of the fiber structures during the dynamic mechanical measurements. Processing behavior of the blends depended on the fiber forming characteristics of LCP-g, which again varied with the molding temperatures.