• Journal of the Korean Ceramic Society
• /
• v.42 no.3 s.274
• /
• pp.198-204
• /
• 2005

Fluosilicate salts based hydration heat reducer(SWP-HR), used in this study, is composed of fluosilicate salts, soluble silica, aromatic polymer condensate and nitrate salt based inorganic compound with latent heat property. Effects of SWP-HR addition on the hydration heat and anti-crack property of cement mortar were investigated. Adiabatic hydration temperature and drying shrinkage length of SWP-HR added cement mortar had a tendency to decrease compared to those of cement mortar without SWP-HR addition. Also, it was confirmed through crack pattern experiment of plate-form specimen for elucidating crack-reducing characteristic that anti-crack property of SWP-HR added cement mortar was improved.

• Journal of the Korea Concrete Institute
• /
• v.18 no.6 s.96
• /
• pp.737-742
• /
• 2006

Strengthening concrete structures with fiber reinforced polymer materials have grown to be a widely used method over most parts of the world today, which FRP was developed in 1960. A method to apply prestressing force to FRP is developed newly in these days, which can use the maximum performance of FRP materials. This paper presents the results of a study on improvement in flexural capacities of RC beams strenthened with near surface mounted prestressed CFRP rod and plate. Experimental variables include type of CFRP, prestressing level. Tests show that prestressed beams exhibit a higher crack-load as well as a higher steel-yielding load compared to non-prestressed strengthened beams.

• Earthquakes and Structures
• /
• v.15 no.2
• /
• pp.113-122
• /
• 2018

This study presents a new beam-column model comprising material nonlinearity and joint flexibility to predict the nonlinear response of reinforced concrete structures. The nonlinear behavior of connections has an outstanding role on the nonlinear response of reinforced concrete structures. In presented research, the joint flexibility is considered applying a rotational spring at each end of the member. To derive the moment-rotation behavior of beam-column connections, the relative rotations produced by the relative slip of flexural reinforcement in the joint and the flexural cracking of the beam end are taken into consideration. Furthermore, the considered spread plasticity model, unlike the previous models that have been developed based on the linear moment distribution subjected to lateral loads includes both lateral and gravity load effects, simultaneously. To confirm the accuracy of the proposed methodology, a simply-supported test beam and three reinforced concrete frames are considered. Pushover and nonlinear dynamic analysis of three numerical examples are performed. In these examples the nonlinear behavior of connections and the material nonlinearity using the proposed methodology and also linear flexibility model with different number of elements for each member and fiber based distributed plasticity model with different number of integration points are simulated. Comparing the results of the proposed methodology with those of the aforementioned models describes that suggested model that only uses one element for each member can appropriately estimate the nonlinear behavior of reinforced concrete structures.

• Advances in nano research
• /
• v.9 no.4
• /
• pp.263-276
• /
• 2020

In this article, the acoustic responses of free vibrated natural fibre-reinforced polymer nanocomposite structure have been investigated first time with the help of commercial package (ANSYS) using the multiphysical modelling approach. The sound relevant data of the polymeric structure is obtained by varying weight fractions of the natural nanofibre within the composite. Firstly, the structural frequencies are obtained through a simulation model prepared in ANSYS and solved through the static structural analysis module. Further, the corresponding sound data within a certain range of frequencies are evaluated by modelling the medium through the boundary element steps with adequate coupling between structure and fluid via LMS Virtual Lab. The simulation model validity has been established by comparing the frequency and sound responses with published results. In addition, sets of experimentation are carried out for the eigenvalue and the sound pressure level for different weight fractions of natural fibre and compared with own simulation data. The experimental frequencies are obtained using own impact type vibration analyzer and recorded through LABVIEW support software. Similarly, the noise data due to the harmonically excited vibrating plate are recorded through the available Array microphone (40 PH and serial no: 190569). The numerical results and subsequent experimental comparison are indicating the comprehensiveness of the presently derived simulation model. Finally, the effects of structural design parameters (thickness ratio, aspect ratio and boundary conditions) on the acoustic behaviour of the natural-fibre reinforced nanocomposite are computed using the present multiphysical model and highlighted the inferences.

• Journal of Electrochemical Science and Technology
• /
• v.7 no.2
• /
• pp.132-138
• /
• 2016

In this study, we report the fabrication of functional complex fibers, which have been studied widely globally for numerous applications. Here, we fabricated conductive complex fibers with antibacterial properties by coating metal ions on the surface of plastic (polypropylene) fibers using the electroless and electrochemical deposition. First, we polished the polypropylene melt-blown fiber surface and obtained an absorbing Pd seed layer on its surface. Subsequently, we substituted the Pd with Cu. Bis-3-sulfopropyl-disulfide disodium salt (SPS), polyethylene glycol (PEG), and ethylene thiourea (ETU) were used as the brightener, carrier, and leveler, respectively for the electroplating. We focused on most achieving the stable plating condition to remove dendrites, which are normally during electroplating metals so that smooth layer is formed on the fiber surface. The higher the amount of SPS, the higher was the extent of irregular plate-like growth. Many irregularities in the form of round spheres were observed with increase in the amount of PEG and ETU. Hence, when the additives were used separately, a uniform coating could not be obtained. A stable coating was obtained when the three additives were combined and a uniform 5-9 μm thick copper layer with a stable morphology could be obtained around the fiber. We believe that our results can be applied widely to obtain conductive fibers with antibacterial properties and are useful in aiding research on conductive lightweight composite fibers for application in information technology and robotics.

• Food Science and Biotechnology
• /
• v.14 no.5
• /
• pp.704-708
• /
• 2005

Poly-y-glutamate (${\gamma}$-PGA) has great potential as a biodegradable polymer in a broad range of industrial fields such as food, cosmetics, medicine and water treatment. In order to isolate ${\gamma}$-PGA producers that are suitable for specific industrial applications, 653 Bacillus-like strains were isolated from 439 varieties of three Korean fermented foods, Cheongkukjang, Doenjang, and Kochujang, which were collected from different regions across Korea. A very high level of ${\gamma}$-PGA production was demonstrated in 4.7%, 1.8%, and 3.0% of the Bacillus-like strains isolated from Cheongkukjang, Doenjang, and Kochujang samples, respectively, which produced a viscous substance to such extent that it overflowed to the lid of the plate on the glutamate-dependent ${\gamma}$-PGA production plates. On glutamate-independent ${\gamma}$-PGA production plates, 5.1%, 5.9%, and 6.1% of Bacillus-like strains isolated from Cheongkukjang, Doenjang, and Kochujang samples, respectively, showed high production. The maximum ${\gamma}$-PGA production yields were 32.5 g/L and 5 g/L, depending on the purification methods in the glutamate-dependent media, with the higher yield resulting from a simple precipitation of ${\gamma}$-PGA by either methanol or ethanol and dialysis. The viscous substance produced by each strain showed different morphological characteristics, suggesting that isolated ${\gamma}$-PGA producers could produce various types of ${\gamma}$-PGA.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.21 no.4
• /
• pp.425-433
• /
• 2001

A correlation between fatigue damage and acousto-ultrasonic (AU) parameters has been obtained from signals acquired during fatigue loading of the single-lap joints of a carbon-fiber reinforced plastic (CFRP) laminates and A16061 plate. The correlation showed an analogy to those representing the stiffness reduction $(E/E_0)$ of polymer matrix composites by the accumulation of fatigue damage. This has been attributed to the transmission characteristics of acoustic wave energy through bonded joints with delamination-type defects and their influence on the change of spectral content of AU signals. Another correlation between fatigue cycles and the spectral magnitude of acoustic emission (AE) signals has also been found during the final stage of fatigue loading. Both AU and AE can be applied almost in real-time to monitor the evolution of damage during fatigue loading.

• Applied Chemistry for Engineering
• /
• v.9 no.4
• /
• pp.481-485
• /
• 1998

Hydrated aluminum sulfate, an inorganic polymer, was synthesized from kaolin in $H_2SO_4$ solution using microwave energy. The maximum rates of alumina extracted from calcined kaolin were 72.8% in a conventional process ($80^{\circ}C$, 1M, and 180min) and 99.9% in a microwave process ($90^{\circ}C$, 1M, and 60 min). Compared with the conventional one, the hydrated aluminum sulfate synthesized under the microwave process had layer structure consisting of plate-shaped large grains. After synthesis and then calcination at $1100^{\circ}C$, both products on conventional and microwave processes were ${\gamma}-Al_2O_3$ with agglomerated powders of spherical shape. The specific area of the products in conventional and microwave processes were 113.5 and $106.6m^2/g$, and their average grain sizes were 46.5 an $26.3{\mu}m$, respectively.

• Applied Chemistry for Engineering
• /
• v.9 no.4
• /
• pp.536-541
• /
• 1998

The porous size alumina membrane was prepared by anodic oxidation with current method in an aqueous solution of oxalic acid. The aluminum metal plate was pretreated with thermal oxidation, chemical polishing and electropolishing before anodic oxidation. Membrane thickness and pore size distribution were investigated with several anodizing conditions; reaction temperature, cumulative charge, electrolyte concentration and current density. The porous alumina membrane obtained was $55{\sim}75{\mu}m$ thick with straight micropore of 45~100nm. Also, the porous alumina membrane has an uniform pore diameter and pore distribution. It was inorganic ultrafiltration membrane as a kind of the ceramic membrane.

• Journal of the Korean Society for Railway
• /
• v.12 no.5
• /
• pp.641-648
• /
• 2009

Concrete structures become more common in railway systems with an advancement of high speed train technologies. As the service life of concrete structures increases, structural strengthening for concrete structures may be necessary. There are several typical strengthening techniques using steel plate and fiber reinforced polymer (FRP) materials, which have their own inherent shortcomings. In order to enhance greater durability and resistance to fire and other environmental attacks, basalt fiber material attracts engineer's attention due to its characteristics. This study investigates bonding performance of basalt fiber sheet as a structural strengthening material. Experimental variables include bond width, length and number of layer. From the bonding tests, there were three different types of bonding failure modes: debonding, rupture and rip-off. Among the variables, bond width indicated more significant effect on bonding characteristics. In addition the bond length did not contribute to bond strength in proportion to the bond length. Hence this study evaluated effective bond length and effective bond strength. The effective bond strength was compared to those suggested by other researches which used different types of FRP strengthening materials such as carbon FRP.