• 한국구조물진단유지관리공학회 논문집
• /
• 제6권1호
• /
• pp.205-212
• /
• 2002

The deterioration rate of concrete structures in urban area is accelerated due to rapid urbanization and environmental pollution. Repair materials and methods newly introduced in Korea should be investigated whether they are appropriate for the urban environment in Korea. The creek concrete structures are exposed in severe environmental condition than others. Based on these background in mind, the study is focused on evaluation of performance on repair materials used to rehabilitate creek concrete structures. To evaluate the performance of repair materials, four kinds of repair materials were selected based on polymer emulsion. This experimental study was conducted on fundamental performance such as setting time, compressive strength, bending strength, bonding strength, thermal expansion coefficient, and durability performance such as chloride diffusion, carbonation, chemical attack, and steel corrosion rate. On the basis of this study, the optimal repair material which is proper to the environment condition can be selected and service life of creek concrete structures can be extended. As a result, the life cycle cost can be reduced and the waste of material resources will be cut down.

• 펄프종이기술
• /
• 제30권3호
• /
• pp.29-37
• /
• 1998

In order to set up a proper AKD quantification method for studing AKD hydrolysis, a quantitative analysis method using Uv/vis spectroscopy was evaluated and compared to the conventional GC-MS analysis. Hydrolysis rates of AKD emulsions during storage at 4$0^{\circ}C$ were measured by the UV/vis analysis. Owing to its simplicity and capability of measuring the unreacted AKD significantly even in a small amount, UV/vis method proved to be more suitable for studing AKD hydrolysis than GC-MS analysis. AKD hydrolysis was affected by the types of emulsifiers. Polymer stabilized AKD emulsion hydrolyzed more rapidly than starch stabilized AKD.

• Archives of Pharmacal Research
• /
• 제27권1호
• /
• pp.1-12
• /
• 2004

Initial burst is one of the major challenges in protein-encapsulated microparticle systems. Since protein release during the initial stage depends mostly on the diffusional escape of the protein, major approaches to prevent the initial burst have focused on efficient encapsulation of the protein within the microparticles. For this reason, control of encapsulation efficiency and the extent of initial burst are based on common formulation parameters. The present article provides a literature review of the formulation parameters that are known to influence the two properties in the emulsion-solvent evaporation/extraction method. Physical and chemical properties of encapsulating polymers, solvent systems, polymer-drug interactions, and properties of the continuous phase are some of the influential variables. Most parameters affect encapsulation efficiency and initial burst by modifying solidification rate of the dispersed phase. In order to prevent many unfavorable events such as pore formation, drug loss, and drug migration that occur while the dispersed phase is in the semi-solid state, it is important to understand and optimize these variables.

• Bulletin of the Korean Chemical Society
• /
• 제33권10호
• /
• pp.3208-3212
• /
• 2012

Controlled drug delivery systems employing microparticles offer lots of advantages over conventional drug dosage formulations. Microencapsulation technique have been conducted with biodegradable polymers such as poly(lactic-co-glycolic acid) (PLGA) and poly(lactic acid) (PLA) for its adjustable biodegradability and biocompatibility. In this study, we evaluated two techniques, oil-in-water (o/w) emulsion solvent evaporation and spray drying, for preparation of polymeric microparticles encapsulating a newly synthesized drug, SS-AG20, for the long-term drug delivery of this low-molecular-weight drug with a very short half-life. Drug-loaded microparticles prepared by the solvent evaporation method showed a smoother morphology; however, relatively poor encapsulation efficiency and drastic initial burst were discovered as drawbacks. Spray-dried drug-loaded microparticles had an imperfect surface with pores and distorted portions so that its initial burst was critical (70.05-87.16%) when the preparation was carried out with a 5% polymeric solution. By increasing the concentration of the polymer, the morphology was refined and undesirable initial burst was circumvented (burst was reduced to 35.93-74.85%) while retaining high encapsulation efficiency. Moreover, by encapsulating the drug with various biodegradable polymers using the spray drying method, gradual and sustained drug release, for up to 2 weeks, was achieved.

• 디지털융복합연구
• /
• 제13권8호
• /
• pp.369-374
• /
• 2015

본 연구에서는 초음파매개물의 1차적인 목적이외에 부가적인 특징을 조합하여 새로운 초음파매개물의 개발 가능성을 모색하였다. 임의 제조된 각 제형에 따른 유동학적 특징과 제조비용을 기성품 제제와 비교 분석하였다. 초음파전파매개물은 제형에 따라 각기 다른 기능적 특성을 지니게 되며, 저점도에멀전과 오일젤에서 유동성이 가장 우수하였다. 제조비용에서는 수화젤 제형이 물성분이 많을수록 제조비용이 가장 낮았으며, 에멀전과 오일젤 제형에서는 오일의 함유량이 높을수록 제조비용에 많은 차이가 있었다. 본 연구는 초음파의 다양한 영역의 전문성을 겸비한 새로운 초음파매개물의 연구에 대한 초석을 이룰 수 있을 것으로 사료된다.

• Macromolecular Research
• /
• 제17권12호
• /
• pp.969-975
• /
• 2009

This article describes the topical delivery and localization of budesonide through the hairless mouse skin. Two poly(ethylene oxide)-block-poly($\varepsilon$-caprolactone)-block-poly(ethylene oxide) (PEO-PCL-PEO) triblock copolymers (T 222 and T 252) having different CL:EO ratios were added in the preparation of budesonide particles stabilized with poly(vinyl alcohol) (PVA) and Tween 80 under ultrasonication. For comparison, a commercial PEO-PPO-PEO triblock copolymer (F68) was studied under the same condition. To demonstrate the effects of the triblock copolymer, the particle size of budesonide emulsion, entrapment efficiency, and in vitro release were measured and compared. The budesonide particles stabilized by the triblock copolymers had a diameter of ca. 350 nm with entrapment efficiencies of 66-76%. The In vitro release profiles of all samples showed an initial burst followed by sustained release. The skin penetration and permeation of budesonide were analyzed by using a Frantz diffusion cell. T 222 and T 252 exhibited higher total permeation amounts, but lower budesonide penetration amounts, than F68. The results suggest that the partitioning of budesonide in each skin layer can be adjusted in order to avoid skin thinning and negative immune response arising from the penetration of budesonide in blood vessels.

• Nuclear Engineering and Technology
• /
• 제5권2호
• /
• pp.103-114
• /
• 1973

본 실험은 방사선을 이용하여 Polyester 직포의 흡수성과 염색성 그리고 대전성을 증진시키기 위한 연구로서 실온하에서 함침법으로 Acrylic acid또는 4-vinylpyridine을 Polyester 직포에 접목시켰다. Polyester 직포를 25$^{\circ}$또는 7$0^{\circ}C$에서 Acrylic acid나 Acrylic acid와 4-vinylpyridine의 emulsion 용액에 함침시켰으며 함침된 Polyester 직포를 질소깨스 존재 하에서 Co-60의 l-rays로 조사시켰다. Acrylic acid가 접목된 Polyester 직포를 Sodium carbonate, Calcium acetate 또는 Potassium persulfate로 처리하였을 때 흡수율은 더욱 증가하였으며 직포 표면에 형성된 polyacrylic acid 는 0.1% NaoH 용액으로 대부분 추출되었다. 4-vinylpyridine과 Acrylic acid의 혼합용액을 함침용액으로 사용하였을 경우 4-VP/AA의 비율과 방사선 선량이 커짐에 따라 접목율은 점점 증가함을 보여주었다. 여러가지로 처리된 Polyester 직포 표면에 물방울을 떨어 뜨렸을 때의 Contact angle을 측정하여 보니 접목율이 증가함에 따라 대전성은 감소하였다. Acryli acid가 접목된 Polyester 섬유를 Salt로 처리하여 전자 현미경으로 관찰하여 본 결과 일련의 무정형 형태로 결합되어 있었다.

• 한국응용과학기술학회지
• /
• 제31권2호
• /
• pp.296-304
• /
• 2014

본 연구에서는 hard segment를 형성하고 있는 폴리우레탄을 합성한 다음 피혁산업에서 마감 코팅시 많이 사용되고있는 폴리에틸렌왁스의 적하량을 점차 증가시켜 필름 및 Lam skin에 코팅에 적용하여 변화하는 물성을 측정하였다. 내용제성 측정 결과 높은 내용제성 물성을 지닌 폴리우레탄 수지에 폴리에틸렌왁스의 함량에 따른 물성적 변화는 크게 나타나지 않았다. 인장 강도 측정치에서는 폴리우레탄 단독 필름의 측정치가 $1.235kg_f/mm^2$로 가장 높은 수치를 나타내었으며, 폴리에틸렌왁스의 함량이 제일 높은 PUD-EW3가 가장 낮은 인장력 $1.022kg_f/mm^2$를 나타내었다. 또한 내마모도 측정에서는 PUD가 제일 높은 52.22 5mg.loss로 우수한 물성변화를 나타내었고, 연실율의 경우 역시 우레탄 단독 코팅인 PUD가 698%로 가장 높은 수치를 나타내었다.

• 한국도로학회논문집
• /
• 제20권1호
• /
• pp.77-85
• /
• 2018

PURPOSES : The purpose of this study was to develop an urgent road-repair system and perform a field applicability test, as well as discover the optimum mix design for machine applications compared to the optimum mix design for lab applications. METHODS : According to reviews of the patent and developed equipment, self-propelled and mix-in-place equipment types are suitable for urgent pavement repair, e.g., potholes and cracks. The machine-application mix design was revised based on the optimum lab-test mix design, and the field application of a spray-injection system was performed on the job site. The mixture from the machine application and lab application was subjected to a wet-track abrasion test and a wheel-tracking test to calibrate the machine application. RESULTS and CONCLUSIONS : This study showed that the binder content could differ for the lab application and the machine application in the same setting. Based on the wet-track abrasion test result, the binder contents of the machine application exceeded the binder contents of the lab application by 1-1.5% on the same setting value. Moreover, the maximum dynamic stability value for the machine application showed 1% lower binder contents than the maximum lab-application value. Collectively, the results of the two different tests showed that the different sizes and operating methods of the machine and lab applications could affect the mix designs. Further studies will be performed to verify the bonding strength and monitor the field application.

• 공업화학
• /
• 제4권2호
• /
• pp.284-290
• /
• 1993

AN을 친수성 공단량체로 하고, KPS를 개시제로 하여 St/BD의 무유화제 유화중합을 해 본 결과, 전환율 50% 이하에서 Rp의 $[AN]^n$ 및 $[KPS]^n$에 대한 의존성은 각각 n=1.617-1.050 및 n=0.83-0.96을 보였으며, 입자수 밀도 (Np)의 $[AN]^n$ 및 $[KPS]^n$ 의존성은 n=1.533 및 n=0.733이었다. 그리고 pH=5, 총단량체 (g)/물(g)=0.5일 때 전환율이 가장 높았으며, 얻어진 SBR은 상용 SBR에 비해 가류속도가 훨씬 빠르고, tensile strength, 300% modulus, elongation 등 기본 물성에서 열세였다.