• Proceedings of the Korea Concrete Institute Conference
• /
• 2004.05a
• /
• pp.292-295
• /
• 2004

Recently, polymer-clay hybrid materials have received considerable attention from both a fundamental research and application point of view. This organ-inorganic hybrid, which contains a nanoscale dispersion of the layered silicates, is a material with greatly improved thermal and mechanical characteristics. Two classes of nanocomposites were synthesized using an unsaturated polyester resin as the matrix and sodium montmorillonite as well as an organically modified montmorillonite as the reinforcing agents. X -ray diffraction pattern of the composites showed that the interlayer spacing of the modified montmorillonite were exfoliated in polymer matrix. The mechanical properties also supported these findings, since in general, tensile strength, modulus with modified montmorillonite were higher than the corresponding properties of the composites with unmodified montmorillonite. Adding organically modified clay improved the tensile strength of unsaturated polyester by $22\%$ and the tensile modulus of unsaturated polyester was also improved by $34\%$.

• Macromolecular Research
• /
• v.13 no.2
• /
• pp.96-101
• /
• 2005

Thin-film humidity sensors were prepared using inorganic/organic hybrid polyelectrolytes, which were prepared from the sol-gel reaction of copolymers of [2-(methacryloyloxy)ethyl]dimethylpropylammonium bromide (MEPAB), n-butyl methacrylate (BMA), and 3-(trimethoxysilyl)propyl methacrylate (TSPM) with tetraethyl ortho-silicate (TEOS). The humidity-sensitive polyelectrolytes were composed of the copolymers having the following mole ratios of MEPAB, BMA, and TSPM: 60/30/10, 55/30/15, and 50/30/20. We found that the impedance varied with the content of MEPAB or TEOS; it ranged from $10^{7} to 10^{3}\Omega$ between 20 and $95\%$ relative humidity, which is the range required for a humidity sensor operating at ambient humidity. In addition we investigated a number of characteristics of these humidity sensors, such as their hysteresis, response time, temperature dependence, frequency dependence, water durability, and long-term stability.

• Journal of the Semiconductor & Display Technology
• /
• v.16 no.4
• /
• pp.1-4
• /
• 2017

Encapsulation of organic based devices is essential issue due to easy deterioration of organic material by water vapor. Atomic layer deposition (ALD) is a promising solution because of its low temperature deposition and quality of the deposited film. Moisture permeation has a mechanism to pass through defects, Thin Film Encapsulation using inorganic / organic / inorganic hybrid film has been used as promising technology. $Al_2O_3$ / Polymer / $Al_2O_3$ multilayer film has shown excellent environmental protection characteristics despite of thin thicknesses of the films.

• Journal of the Korean Electrochemical Society
• /
• v.8 no.4
• /
• pp.177-180
• /
• 2005

A series of inorganic-organic hybrid membranes were prepared with a systematic variation of titanium dioxide nano particles content. Their liquid uptake, methanol permeability and proton conductivity as a function of inorganic oxide content were investigated. The results obtained show that the inorganic oxide network decreases the proton conductivity and liquid uptake. It is also found that increase in inorganic oxide content leads to decrease of methanol permeability. In terms of the morphology, membranes are homogeneous and exhibit a good adhesion between inorganic domains and the polymer matrix. The properties of the composite membranes are compared with the standard nafion membrane.

• Polymer(Korea)
• /
• v.37 no.1
• /
• pp.34-40
• /
• 2013

Commercially available polyamide thermoplastic elastomer (PA-TPE) was blended with hybrid filler which was prepared by means of the reaction between polyhedral oligomeric silsesquioxane (POSS) containing amine group and toluene diisocyanate (TDI)-caprolactam (CL) to explore the effect of blending the hybrid filler with the TPE. The chemical structure of the filler was identified by using FTIR and $^1H$ NMR. The composites, PA-TPE/POSS-(TDI+CL), which were the blends of TDI+CL modified POSS filler and PA-TPE up to 7 wt%, showed better elastic recovery delivered from lower tension setting compared to the PA-TPE and the PA-TPE/octaphenyl POSS blend. In addition the tensile strength and the initial modulus increased with increasing the hybrid filled content. Consequently it was assumed that the POSS-(TDI+CL) filler was a suitable material for enhancing strength and modulus without loss of elastic properties for the original PA-TPE.

• Transactions on Electrical and Electronic Materials
• /
• v.16 no.4
• /
• pp.190-193
• /
• 2015

Insulation breakdown characteristics of an inverter surge resistant enameled wire were investigated in a twisted pair prepared with organic/inorganic hybrid nanocomposite. Organic polymer was polyesterimide-polyamideimide (EI/AI) and inorganic material was a nano-sized silica. The enamel thickness was 50 μm and the diameters of enameled copper wires were 0.75, 1.024, and 1.09 mm, respectively. There were many air gaps in a twisted pair. Therefore, when the voltage was applied to the twisted pair, enamel erosion took place in the air gap area because of partial discharge according to Paschen’s law. The insulation lifetime of the hybrid wire (HW) was 41,750 sec, which was 515.4 times more than the 81 sec of EI/AIW. In addition, the shape parameter of HW was 2.58, which was 3.4 times higher than 0.75 of EI/AIW.

• Journal of Adhesion and Interface
• /
• v.2 no.1
• /
• pp.1-8
• /
• 2001

In this study, wasted stone powders (WSP) obtained from sludge and Wasted Tire Chips (WTC) as fillers have been used to formulate polymer hybrid composites based on Unsaturated Polyester (UPE) resin. To further enhance not only the interfacial bond between the inorganic filler and the polymer matrix, but also the filler dispersion by wetting the particulate surfaces to uniformly spread the resin during the mixing, silane coupling agent[${\gamma}$-methacryloxy propyl trimethoxy silane (${\gamma}$-MPS)] was used. The influences of organic recycled fillers contents and the concentrations of coupling agent in polymer hybrid composite formulations have been investigated from a mechanical and microstructural point o view through Mercury Porosimeter and SEM.

• Polymer(Korea)
• /
• v.36 no.1
• /
• pp.16-21
• /
• 2012

Organic-inorganic hybrid coating film using 1,2-bis(2,4-dimethyl-5-phenyl-3-thienyl)-3,3,4,4,5,5-hexafluoro-1-cyclopentene (BTHFC) as a photochromic material was prepared under various reaction conditions such as the amounts of tetramethoxysilane (TMOS), various silane coupling agents, and solvent. It was found that color-fading speed and absorbance of the coating film was strongly dependent upon the polarity of silane coupling agent and solvent. In addition, the mole ratio of TMOS and methacryloyloxypropyltrimethoxysilane (MPTMS) was an important factor to determine color-fading speed and absorbance of the coating film. With increasing TMOS contents in coating film, the pencil hardness was increased. On the other hands, the transmittance of coating film was relatively decreased with the increase of TMOS.

• Polymer(Korea)
• /
• v.35 no.5
• /
• pp.488-492
• /
• 2011

Three isocyanatopropyldimethoxysilylpolydimethylsiloxanes(IDMSi-PDMS) were synthesised from the reaction of isocyanatopropyltrimethoxysilane with monohydroxyl group termainated PDMS having different molecular weight($M_n$=5000, 10000, and 20000). Then PDMS modified polyurethane hybrid elastomer(PSMPH) were prepared from the reaction of IDMSi-PDMS with ${\alpha}$, ${\omega}$-hydroxyl group terminated polyurethane. PSMPH sealant was prepared by compounding PSMPH elastomer with additives such as plasticizer, adhesion promoter, crosslinking agent, vicosity increasing agent, inorganic filler, and catalyst at room temperature under nitrogen atmosphere. The methoxy group in the PSMPH sealant should be crosslinked with the hydroxyl group in the building stone or moisture by typical sol-gel reaction. The adhesive strength of the sealant having PDMS of $M_n$=5000 showed 40.28 kg of maxium load and 20.14 kg of break load. The shrinkage rate of the sealant having PDMS of $M_n$=20000 was 5.7% as the best result. Also, their skin over time, slump, oil content after 8 days under oil soaked paper and alkaline resistance characteristics show good results.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2007.02a
• /
• pp.124-124
• /
• 2007