• Fibers and Polymers
• /
• 제1권2호
• /
• pp.92-96
• /
• 2000

A high molecular weight polyhydroxyamide (PHA) solution in N, N-dimethyl acetamide (DMAc) was prepared from 3, 3'-dihydroxybenzidine and isophthalic chloride (IPC), which was used for spinning PHA fiber. Before spinning, the diffusion property of DMAc into various coagulants was examined. The fiber was well formed in coagulants such as water/ethanol with a composition of 5/5, ethanol, and ethanol/isopropanol with a composition of 7/3 and 5/5. However, the PHA fiber spun in the water/ethanol mixture contained voids. After the fiber spun in ethanol was annealed at over $350^{\circ}C$, the ultimate stress and initial modulus of the fiber increased from 75.5 MPa and 3.22 GPa to 369 MPa and 29.5 GPa, respectively. These properties of the PHA fiber spun by the dry spinning method were also enhanced, attaining 154 MPa and 5.56 Gpa, respectivel.

• 한국섬유공학회:학술대회논문집
• /
• 한국섬유공학회 2001년도 가을 학술발표회 논문집
• /
• pp.359-360
• /
• 2001

헤테로고리 방향족 polybenzoxazole(PBO)은 대표적인 내열성 고분자로서, 고온에서의 열적안정성 및 내화학성, 기계적 물성, 방염성 등에서 우수한 성질을 나타낸다. 그러나 황산과 같은 강산에만 용해되기 때문에 가공성 면에서 단점을 가지고 있어 사용하는데 있어 제약이 따른단 현재 이러한 단점을 보완하기 위해 polyhydroxyamide(PHA)와 같은 전구체 고분자에 대한 연구가 많은 연구자들에 의해 진행되고 있다. (중략)

• Elastomers and Composites
• /
• 제55권3호
• /
• pp.205-214
• /
• 2020

A series of wholly aromatic polyhyroxyamide (PHA) copolymers were prepared by direct polycondensation reaction of isophthalic acid and diacids containing bulky units with 3,3'-dihydroxybenzidine. The inherent viscosities of the PHAs measured at 35℃ in DMAc solution were in the range of 0.31-0.56 dL/g. The solubility study revealed that the PHAs were readily soluble in aprotic solvents such as, dimethylacetamide (DMAc), dimethyl sulfoxide (DMSO), and N-methyl-2-pyrrolidone (NMP) at room temperature and in less polar solvent such as pyridine. However, the polybenzoxazole (PBO) copoymers were quite insoluble in all organic solvents except partially soluble in concentrated sulfuric acid and partially soluble in NMP containing LiCl. The PBO copolymers showed maximum weight loss temperature in the range of 593-632℃ and high char yields in the range of 65.0-71.2% at 900℃ in a nitrogen atmosphere.

• Elastomers and Composites
• /
• 제46권4호
• /
• pp.295-303
• /
• 2011

3,3'-dihydroxybenzidine 과 2,2-bis (3-amino-4-hydroxyphenyl)hexafluoro-propane을 포함하는 두가지 타입의 bis(o-aminophenol)s 과 imide-diacids 를 직접 축 중합하여 imide 고리를 포함한 새로운 방향족 polyhydroxyamides(PHAs)을 합성하였다. 모든 중합체들은 FT-IR, FT-NMR, DSC 및 TGA를 이용하여 조사하였다. 중합체들의 고유점도는 $35^{\circ}C$의 DMAc 용액에서 측정하였으며, 0.49-1.13 dL/g 을 보였다. PHA 1을 제외한 PHA 2 와 3은 DMF, DMAc, NMP 등 극성 용매에 잘 용해되었으며, 6F 그룹이 포함된 PHA 4, 5, 및 6은 극성이 낮은 용매에 대해서도 좋은 용해도를 보였다. 반면에 polybenzoxazoles(PBOs)은 황산에 일부 용해되는 것 외에 다양한 용매에도 용해되지 않았다. 질소분위기 하에서 PBO 1, 2, 3의 최대 열분해온도는 $650-656^{\circ}C$ 범위의 값들을 보였고, char 수득율도 57.4-61.9 %로 비교적 높은 값을 보였다. 이로부터 고분자 주 사슬에 imide 혹은 diimide 고리의 도입은 PHA 혹은 PBO의 열안정성을 높이는데 효과적임을 알 수 있었다.