Poly(butylene terephthalate-co-oxybenzoate) (PBOT ) was synthesized by melt trans-esterification of poly(butylene terephthalate)(PBT) and p-acetoxybensoic acid (ABA) at 250, 260, and 27$0^{\circ}C$ with the compositions of PBT/ABA of 4/6, 5/5, 6/4. The sequence analysis of PBOT with a $^1$H FT-NMR indicated that the number of consecutive oxybenzoate units ranges from 1.2 to 1.5, which is larger than that of the corresponding poly(ethylene terephthalate)(PET)/ABA (PEOT) obtained at the same reaction conditions as the PBOT. The difference in the block length influenced the thermal degradation behavior: Polyoxybezoate (POB), PBT and PEOT showed one-step degradation whereas PBOT exhibited two-step degradation. The results suggested that PBOT consisted of three phases of PBT-rich phase, random phase of PBT and ABA, and ABA-rich phase.

• Polymer(Korea)
• /
• v.24 no.1
• /
• pp.16-22
• /
• 2000

Poly(butylene terephthalate- co-oxybenzoate)(PBOT) containing mesogenic oxybenzoate units in the main chain was synthesized through ester exchange reaction by melt mixing of poly(butylene terephthalate)(PBT) and p-acetoxybenzoic acid (ABA). From the kinetics of the copolymerization reaction, the activation energies and the rate constants of homopolymerization and copolymerization, k$_{h}$ and k$_{c}$, could be determined. From the reaction conditions of different compositions, 4/6, 5/5, and 6/4 of PBT/ABA, at 250, 260, and 27$0^{\circ}C$, it was revealed that copolymerization between PBT and ABA proceeds on a pseudo-second order reaction if the ABA content and its conversion are low. In this case, the ratio of rate constants of homopolymerization to copolymerization was in the range from 1.08 to 3.17, indicating that the copolymer with more notable block character was obtained at the higher mole fraction of ABA and at higher temperature.e.e.