• Journal of Advanced Marine Engineering and Technology
• /
• 제22권5호
• /
• pp.702-711
• /
• 1998

The characteristics of corrosion resistance for the surface of medium high carbon steels and low alloy steels utilizing as manufacturing the machinery structures and machining tools and treating by plasma/ion nitriding process have been studied in terms of electrochemical polarization behav-iors including corrosion potential(Ecorr) anodic polarization trends and polarization resistance(Rp) The seven base materials showed a clear passivation behavior for the polarization tests in the ASTM standard solution 1N ${H_2){SO_4}$ Although the treated surface by plasma nitriding for the seven test materials showed a significant increase in hardness the treatment gave a detri-mental effect in corrosion resistance. The various characteristics including corrosion potential polarization curves microstructures corrosion current polarization resistance among non-treat-ed nitriding and/or soft-nitriding treated specimens have been investigated and some of the mechanisms discussed.

• Corrosion Science and Technology
• /
• 제4권6호
• /
• pp.217-221
• /
• 2005

In the present investigation, holographic interferometry was utilized for the first time to monitor in situ the thickness of the oxide film of aluminium samples during anodization processes in boric acid solutions. The anodization process (oxidation) of the aluminium samples was carried out by the technique of the electrochemical impedance spectroscopy(EIS), in different concentrations of boric acid (0.5-5.0% $H_3BO_3$) at room temperature. In the mean time, the real-time holographic interferometry was used to measure the thickness of anodized (oxide) film of the aluminium samples in solutions. Consequently, holographic interferometry is found very useful for surface finish industries especially for monitoring the early stage of anodization processes of metals, in which the thickness of the anodized film of the aluminium samples can be determined without any physical contact. In addition, measurements of electrochemical values such as the alternating current (A.C) impedance(Z), the double layer capacitance($C_{dl}$), and the polarization resistance(Rp) of anodized films of aluminium samples in boric acid solutions were made by the electrochemical impedance spectroscopy(EIS). Attempts to measure electrochemical values of Z, Cdl, and Rp were not possible by holographic interferometry in boric acid especially in low concentrations of the acid. This is because of the high rate of evolutions of interferometric fringes during the anodization process of the aluminium samples in boric acid, which made measurements of Z, Cdl, and Rp are difficult.

• Corrosion Science and Technology
• /
• 제7권6호
• /
• pp.319-323
• /
• 2008

The polarization resistance of mild steel in 0.5M hydrochloric acid has been evaluated by using impedance (Z) and linear polarization (LPR) techniques and compared to the noise resistance obtained from electrochemical noise data. The degree of localization of this general corrosion has also been discussed by evaluating localization index and power spectral density. Polarization resistance obtained by LPR technique ($28\Omega$) was higher than that obtained by impedance technique ($15\Omega$). Noise resistance ($11\Omega$) was much lower than polarization resistance measured by both of above techniques. Higher polarization resistance obtained by LPR technique is generally caused by passivation effect in the presence of scales or deposits which can introduce an increased resistance as can low conductivity electrolytes. The reason why noise resistance is lower than polarization resistance is the effect of background noise detected by using three platinum electrodes cell in 0.5M hydrochloric acid. Slope($-\beta$) of power spectral density (PSD) obtained from analysis of noise data ($-\beta$ = 3.3) was much higher than 2 which indicates mild steel corroded uniformly. Localization index (LI) calculated from statistical analysis (LI=0.08) is much lower than 1 which indicates that mild steel did not corroded locally. However, LI value is still higher than $1x10^{-3}$ and this indicates that mild steel corroded locally in microscopic point of view.

• Corrosion Science and Technology
• /
• 제3권6호
• /
• pp.251-256
• /
• 2004

Exposure of zinc samples in simulated acid rain solution (SARS) was investigated under a periodic wet-dry conditions using an AC impedance technique. The periodic wet and dry exposure consisted of the immersion of zinc samples in SARS for one hour followed by exposure to 7 hours drying at 60% RH. Phases of the corrosion products were indentified by X-ray diffraction (XRD). The influence of relative humdiity (RH), temperature, and surface inclination on the atmospheric corrosion of zinc is described. The reciprocal of polarization resistance (1/Rp) decreases rapidly during the initial stages then slowly and eventually attains a steady state as exposure time progresses. The average of reciprocal of polarization resistance per cycle, (ARPR) was calculated and found to decrease as number of exposure cycle increases. An increase of temperature enhances the corrsion rate of zinc. The values of ARPR, of a sample inclined at 30 o are lower than those for a sample oriented horizontally. The experiment result shows a pronounced dependence of reciprocal of polarization resistance on RH. Exposure in the presence of carbonate anions gives rise to more protective corrosion products than in nitrate anion solution. The corrosion mechanism during the initial stages of atmospheric zinc corrosion under wet-dry cyclic conditions is suggested.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2002년도 가을 학술발표회 논문집
• /
• pp.63-67
• /
• 2002

The induced chemical and salt solution in water or admixture are originated to the corrosion process of the steeo rebar. These liquids penetrate into concrete as the accompanied by the chemical reaction and cause to attack the steel rebar in concrete. Concrete surfaces which it exposed to deicing, water and sea water is allowed to enter the chlorides in the structures. To prevent from the source of corrosion and deterioration Is subjected to put an end to corrode or reduce to contaminate on the steel rebar. As this reason the MCI 2022 products are applied to the surface of concrete and steel rebar. The concrete samples were made of to the kind of four, i.e. RF, MR, MS, and MM. Corrosion inhibitor is applied to coat on the surface of concrete after it had been cured for 28days. Specimen were immersed in a 3.5％ sodium chloride solution. Concrete specimen were tested to determine the changes of the resistance polarization, Rp, over a 22 weeks period. MCI 2022 is significantly shown the corrosion inhibition of steel rebar in 3.5% NaCl solution. In the each different concrete sample, MS and MM is seemed to be better than others. The results are proofed that MCI 2022 is promised to maintain the inhibition of corrosion with high resistance polarization of the steel rebar in concrete.

• Corrosion Science and Technology
• /
• 제9권5호
• /
• pp.223-232
• /
• 2010

NiTi alloy has been used for orthodontic wire due to good mechanical properties, such as elastic strength, friction resistance, and high corrosion resistance. Recently, these wire were coated by polymer and ceramic materials for aesthetics. The purpose of this study was to investigate electrochemical characteristics of tooth colored NiTi wire using various instruments. Wires (round type and rectangular type) were used, respectively, for experiment. Polymer coating was carried out for wire. Specimen was investigated with optical microscopy (OM), field emission scanning electron microscopy (FE-SEM) and energy dispersive x-ray spectroscopy (EDS). The corrosion properties of the specimens were examined using potentiodynamic tests (potential range of -1500 ~ 2000 mV) and electrochemical impedance spectroscopy (frequency range of 100 kHz ~ 10 mHz) in a 0.9 % NaCl solution by potentiostat. From the results of polarization behavior, the passive region of non-coated NiTi wire showed largely, whereas, the passive region of curved NiTi wire showed shortly in anodic polarization curve. In the case of coated NiTi wire, pitting and crevice corrosion occurred severely at interface between non-coated and coated region. From the results of EIS, polarization resistance(Rp) value of non-coated round and rectangular NiTi wire at curved part showed $5.10{\times}10^5{\Omega}cm^2$ and $4.43{\times}10^5{\Omega}cm^2$. lower than that of coated NiTi wire. $R_p$ of coated round and rectangular NiTi wire at curved part showed $1.31{\times}10^6{\Omega}cm^2$ and $1.19{\times}10^6{\Omega}cm^2$.

• Journal of Advanced Marine Engineering and Technology
• /
• 제23권6호
• /
• pp.761-769
• /
• 1999

In this paper the effect of aging heat treatment to the Corrosion behavior for the Nimonic 80A superalloy was studied by AC Impedance methods. Tested solution was 3.5% with tempera-ture $25^{\circ}C$ Electro-chemical corrosion test were carried out for the Nimonic 80A super-alloy which solution heat treated at $1080^{\circ}C$ for 8 hours followed by aging heat treated at $650^{\circ}C,\;700^{\circ}C,\;750^{\circ}C\;800^{\circ}C$ and $850^{\circ}C$ with 16hours under vacuum environment. The obtained results were as follows; 1. Base metal and solution-treated materials were exhibited similar corrosion tendency as Ran-dle equivalent cell. The value of passive film resistance was 579 ohms for the base metal and 124,770 ohms for the solutionized metal such a difference was arose by the ${{\gamma}_^'}$ precipitate on the metal surface during heat treatment. 2. The measure value of $R_p$ for heat-treated at $650^{\circ}C,\;700^{\circ}C,\;800^{\circ}C$and $850^{\circ}C$ were 97,943, 93, 111, 26,961, 15,798 and 11,780ohm respectively. Which indicated that the passive film resistance Rp was reduced as aging temperature increased due to the growth of grain size and sensitization at the grain boundary. 3. The similar tendency was exhibited for corrosion behavior of the electro-chemical corrosion polarization method and AC impedance method and confirmed that AC impedance method was useful tool for corrosion research.

• 한국구조물진단유지관리공학회 논문집
• /
• 제23권7호
• /
• pp.1-8
• /
• 2019

본 연구는 시멘트 모르타르 속에 매입된 철근이 3wt.% NaCl 전해질 수용액에 8시간 침지 및 대기 중에서 16시간 건조가 반복되는 환경에 있을 때 교류 임피던스법을 이용하여, 10kHz에서 용액저항, 10mHz에서 전하이동저항을 측정하여, 그 값의 차이로부터 분극저항을 계산하여 부식속도를 측정하였다. 부식속도를 제어하기 위해 포화 Ca(OH)₂ 용액에서 일정시간 전착하여, 그 효과를 관찰하였다. 철근의 부식속도는 용존산소의 확산속도 증가에 의해, 침지보다는 건조 환경에서 가속되었으며, 이것은 모르타르 두께가 얇을수록 명확히 측정되었다. 침지 및 건조 반복횟수가 증가함에 따로, 철근의 부식속도는 부동태에서 Low-middle 상태로 가속되었으며, 그 기준은 다수의 연구자들이 사용한 기준을 사용하였다. 이 기준에 의해 철근의 부식속도가 Low-middle 상태가 되면, 포화 Ca(OH)₂ 용액에서 -10 uA/㎠ 전류밀도를 사용하여 철근에 전착을 진행하고, 5일간 건조시킨 후, 3wt.% NaCl 용액에서 침지-건조 반복실험을 다시 진행하면서, 부식속도를 측정하였다. 측정결과, 모르타르의 두께가 얇은 경우, 부식속도의 감소를 명확히 관찰하였다. 또한, 전착에 의한 철근의 부식속도 감소는 침지상태에서 보다 철근이 건조과정에 놓일 때, 더욱 크게 측정되었다. 전착처리에 따라 칼슘은 철근표면과 모르타르 계면에 존재하는 Porous rust layer의 void를 메우는 것으로 보인다. 시험체가 건조과정에 놓일 때, 철근표면에 형성된 다공질의 녹층속에 농축된 Ca²⁺가 침지과정보다 쉽게 CO₃^2-와 결합되어, CaCO₃가 형성됨으로서 철근의 부식속도를 더욱 감소시킨 것으로 생각된다.