• 한국정밀공학회지
• /
• 제9권1호
• /
• pp.106-117
• /
• 1992

In this study, the propagation behaviour and the closure phenomena of physically small surface cracks were investigated by the techinque of the Kikukawa-unloading elastic compliance method using a back face strain gage. The surface cracks initiated and propagated from notched specimens under constant amplitude bending load. The crack shape (aspect ratio) with approximately semi-circular at the early stage was changed to semi-elliptical as the cracks grew larger. The crack depth (a) could be expressed uniquenly by the crack length (c). The dependence of the crack propagation rate on the stress ratio R was strongly related in the lower ${\Delta}K$ range. The deceleration of the surface crack propagation rate was prominent in lower R during the crack length was small. When the propagation rate was rearranged with the effective stress intensity factor range ${\Delta}$K_{eff} the dependence of the crack propagation rate on the stress ratio R was found to be diminshed. These were caused by the crack closure phenomena that was most prominent at the lower propagation rate. The mechanism of crack closure phenomena was dominated by the plasticity-induced mechanism.