• Journal of the Korean institute of surface engineering
• /
• v.27 no.1
• /
• pp.12-18
• /
• 1994

The plasma spray process was used to deposit coatings of $ZrO_2$-8wt%Y2O3 powders on mild steel sub-strate, and the characteristics of as-deposited and heat treated coatings have been investigated. Particulary, the variations of porosity, wear resistance, thermal barrier and thermal shock resistance in $ZrO_2$-8wt% $Y_2O_3$coatings after heat treatment under vacuum circumstance have been investigated. The porosity of the coating layer was increased with increased spray distance. In the case of the arc current of 450A and at the spray distance of 50mm, it was obtained the lowest amount of porosity. After heat treatment, the amount of porosity was found to be decreased, and the wear resistance, microhardness and thermal shock resistance were im-proved. However, the thermal barrier was decreased.

• Proceedings of the KIEE Conference
• /
• 1994.07b
• /
• pp.1606-1608
• /
• 1994

A performance of the torch greatly depends on the plasma gas and the cooling gas. The plasma gas constricted by the nozzle concentrates electric power and momentum, so it can eject molten metal from a cut. As an electric arc constricted in a nozzle is more constricted through thermal pinch by the cooling gas, it is possible to transfer larger thermal concentration to the workpiece. The optimized parameter value in this study was given below. Plasma gas pressure is $4[kgf/cm^2]$ and gas mass flow is $30[{\ell}/min]$. Cooling gas pressure is $6[kgf/cm^2]$ and gas mass flow is $120[{\ell}/min]$.

• Composites Research
• /
• v.36 no.2
• /
• pp.101-107
• /
• 2023

In this study, aluminum nitride (AlN) reinforced aluminum (Al) matrix composites are fabricated via plasma arc melting under a nitrogen atmosphere. Within a minute of the chemical reaction between Al and N, dispersed AlN with the shape of transient and lamellar layers is in situ formed in the Al matrix. The composite contains 10 vol.% AlN reinforcements with low thermal resistance and strong bonding at the interfaces, which leads to the unique combination of thermal expansivity and conductivity in the resulting composites. The coefficient of thermal expansion of the composite can be further reduced when Si was alloyed into the Al matrix, which proposes the potential of the in situ Al matrix composites for thermal management applications.

• 한국전산유체공학회:학술대회논문집
• /
• 2010.05a
• /
• pp.201-207
• /
• 2010

In this study, we calculated arc discharges happened in high-voltage circuit breakers for understanding the complex physics and the probability of thermal breakdown. The four main parts of arc model for this virtual-reality are radiation, PTFE abaltion, Cu evaporation and turbulence. Among these important parts the turbulence model can be critical to the reliability of computation results during high-current period because the plasma flow is affected by high eat energy and mass momentum. Two kinds of turbulence model, zero-equation model and two-equation model, are applied for these calculations and are compared with the measured pressure data inside a chamber.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2012.02a
• /
• pp.498-498
• /
• 2012

직류 아크 토치를 이용하여 열플라즈마를 발생시키는 방법은 전극의 구성에 따라 크게 비이송식(non-transferred)과 이송식(transferred)의 2가지 형태로 나눌 수 있다. 1950년대 H. Maecker 등에 의해 이론적 기초가 형성되기 시작한 이송식 아크 플라즈마 발생장치는 처리 대상물질을 전극으로 사용하여 양극에서의 에너지 전달을 직접 이용할 수 있으므로 열효율이 매우 높기 때문에 이를 이용한 고출력 토치에 관한 활발한 연구가 지속되고 있다. 본 연구에서는 대기압 아르곤 자유연소아크 방전에 의해 발생되는 열플라즈마의 열유동 특성을 수치적으로 해석하기 위하여 아크 기둥의 온도, 압력 및 속도 특성을 Navier-Stokes 방정식과 Maxwell 방정식을 연계 계산하였다. 또한 아크-전극 상호작용(arc-electrode interaction) 모델링을 통한 양극(anode)인 처리 대상물질로의 에너지 플럭스 유입을 고려하여 전극 내부의 온도분포를 계산하였다. 해석결과를 검증하기 위하여 음극과 양극 사이 플라즈마 기둥(column)의 중심축 온도는 Haddad & Farmer(1984)의 실험데이터와 비교하였고, 양극으로의 에너지 플럭스 및 온도분포 데이터는 Bini 등(2006)의 실험 및 해석데이터와 비교하여 만족스런 일치를 확인하였다.

• Journal of Powder Materials
• /
• v.15 no.5
• /
• pp.352-358
• /
• 2008

The present study focused on the synthesis of a bismuth-antimony-tellurium-based thermoelectric nanopowders using plasma arc discharge process. The chemical composition, phase structure, particle size of the synthesized powders under various synthesis conditions were analyzed using XRF, XRD and SEM. The powders as synthesized were sintered by the plasma activated sintering. The thermoelectric properties of sintered body were analyzed by measuring Seebeck coefficient, specific electric resistivity and thermal conductivity. The chemical composition of the synthesized Bi-Sb-Te-based powders approached that of the raw material with an increasing DC current of the are plasma. The synthesized Bi-Sb-Te-based powder consist of a mixed phase structure of the $Bi_{0.5}Sb_{1.5}Te_{3}$, $Bi_{2}Te_{3}$ and $Sb_{2}Te_{3}$ phases. This powder has homogeneous mixing state of two different particles in an average particle size; about 100nm and about 500nm. The figure of merit of the sintered body of the synthesized 18.75 wt.%Bi-24.68 wt.%Sb-56.57 wt.%Te nanopowder showed higher value than one of the sintered body of the mechanically milled 12.64 wt.%Bi-29.47 wt.%Sb-57.89 wt.%Te powder.

• 한국연소학회:학술대회논문집
• /
• 2005.10a
• /
• pp.64-68
• /
• 2005

Methane reforming processes to obtain hydrogen were investigated experimentally by using atmospheric plasma source. Among possible reforming processes, such as a $CO_2$ reforming(dry reforming), a partial oxidation (POx), a steam reforming(SR), and a steam reforming with oxygen(SRO or auto-thermal reforming), partial oxidation and the steam reforming with oxygen were considered. We choose a rotating arc plasma as an atmospheric plasma source, since it shows the best performances in our preliminary tests in terms of a methane conversion, a hydrogen production, and a power consumption. Then, the effects of a feeding flow-rate, an electrical power input to a plasma reaction, an $O_2/C$ ratio and a steam to carbon ratio in the case of SRO on the reforming characteristics were observed systematically. As results, at a certain condition almost 100% of methane conversion was obtained and we could achieve the same hydrogen production rate by consuming a half of electrical power which was used by the best results for other researchers.

• Proceedings of the Korean Society For Composite Materials Conference
• /
• 1999.11a
• /
• pp.77-82
• /
• 1999

탄소 fabric 표면을 각기 다른 농도의 인산용액으로 표면처리함으로써 2-D 카본/페놀릭 복합 재료에 미치는 물성과 내 산화성, Arc plasma Torch test를 통하여 내열성등을 알아보았으며 ESCA를 통하여 인산 표면 처리에 의한 표면 functionality를 측정하였다.

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.21 no.1
• /
• pp.22-27
• /
• 2022

In accordance with the growing trend of decommissioning nuclear facilities, research on the cutting process is actively proceeding worldwide. In general, a thermal cutting process, such as plasma cutting is applied to decommissioning a nuclear reactor pressure vessel (RPV). Plasma cutting has the advantage of removing the radioactive materials and being able to cut thick materials. However, when operating under water, the molten metal remains in the cut plane and re-solidifies. Hence, cutting is not entirely accomplished. For these environmental reasons, it is difficult to cut thick metal. The contact arc metal cutting (CAMC) process can be used to cut thick metal under water. CAMC is a process that cuts metal using a plate-shaped electrode based on a high-current arc plasma heat source. During the cutting process, high-pressure water is sprayed from the electrode to remove the molten metal, known as rinsing. As the CAMC is conducted without using a shielding gas, such as Argon, the electrode is consumed during the process. In this study, CAMC is introduced as a method for dismantling nuclear vessels and the relationship between the metal removal and electrode consumption is investigated according to the cutting conditions.

• Journal of Power System Engineering
• /
• v.9 no.4
• /
• pp.90-95
• /
• 2005

The wire-arc process is a low-cost thermal spray method simply utilizes electrical energy to melt the feedstock wire. It is more userful for field applications, especially to coat large surface area. In this paper, a special Fe-based alloy coatings by using the wire-arc process were developed. Nanoscale composite coatings were achieved either during spraying or through a post heat treatment. As-sprayed Fe-based alloy coatings had been an amorphous matrix structure, after heating to $700^{\circ}C$ for 10 minutes a solid state transformation occurred in the some fraction of amorphous matrix which resulted in the formation of nanostructured recrystallized phase. Scanning electron microscopy (SEM) and field emotional scanning electron microscope(FE-SEM) were applied to analyze the microstructure of the coatings. Additionally hardness and bend resistance of the Fe-based alloy coatings were examined, and these results were compared with those of partially stabilized zirconia(PSZ) coatings by using the plasma spray process.