• 한국초전도저온공학회:학술대회논문집
• /
• 한국초전도저온공학회 2002년도 학술대회 논문집
• /
• pp.3-4
• /
• 2002

The stainless steel sheathed MgB$_2$ tapes with Cu addition were fabricated by PIT method without heat treatment. The $J_{c}$ value of 5,600 A/ $cm^{2}$and 16,000 A/$cm^{2}$ at 4.2 K and 5 T were obtained for the $MgB_{2}$ tape and 10 vol % of Cu added $MgB_{2}$ tape respectively. The $J_{c}$-B curve shows enhancement in J$_{c}$ under magnetic field, which suggests enhancement in flux pinning property with Cu addition.n.

• 전기학회논문지
• /
• 제61권2호
• /
• pp.339-341
• /
• 2012

The high Tc superconductor of YBCO system with the nominal composition of precursor was prepared from mixed powders of $Y_2O_3$, $BaCO_3$, CuO and $TiO_2$ by the thermal pyrolysis method. The effect of $TiO_2$ doping to Y based ceramics superconductors fabricated by the thermal pyrolysis reaction, to investigate the effect of the dopant on the superconductivity. The voltage appearing across the field-cooled HTS sample increased with external magnetic field. The improvement of critical current property as well as the mechanical property is important for the application. The improvement of the critical current can be achieved by forming the nano size defect working as a flux pining center inside the superconductor. We simply added $TiO_2$ to starting materials to dope $TiO_2$ and observed an increase in the trapped field and the critical current density up to at least 5 wt % $TiO_2$. The $TiO_2$ was converted to fine $BaTiO_3$ particles which were trapped in YBCO matrix during the sintering process. We observed a peak effect of Jc that can be attributed to $TiO_2$ doping and results suggest that introducing a proper amount of pinning centers can significantly enhance current density.

• 한국재료학회지
• /
• 제17권10호
• /
• pp.526-531
• /
• 2007

The sintering behavior and electrical property of $Ce_{0.8}Gd_{0.2}O_{1.9}$ ceramics were investigated with the iron oxide concentration ranging from 0 to 5 mol%. Both the sintered density and grain size were found to increase up to 2 mol% $Fe_2O_3$, and then to decrease with further additions. At a higher $Fe_2O_3$ content above 3 mol%, grain size decreased by a pinning effect induced by different shape grains. The electrical conductivity was also increased with increasing $Fe_2O_3$ content up to 2 mol%. Total conductivity of 2 mol% $Fe_2O_3-added$ specimen showed the maximum conductivity of $2{\times}10^{-2}{\Omega}{\cdot}cm^{-1}$ at $500^{\circ}C$. The addition of $Fe_2O_3$ was found to promote the sintering properties and electrical conductivities of $Gd_2O_3-dope\;CeO_2$.

• 한국전산유체공학회:학술대회논문집
• /
• 한국전산유체공학회 2010년 춘계학술대회논문집
• /
• pp.551-555
• /
• 2010

Electrowetting is a versatile tool to handle tiny droplets and forms a backbone of digital microfluidics. Numerical analysis is necessary to fully understand the dynamics of electrowetting, especially in designing electrowetting-based devices, such as liquid lenses and reflective displays. We developed a numerical method to analyze the general contact-line problems, incorporating dynamic contact angle models. The method is based on the conservative level set method to capture the interface of two fluids without loss of mass. We applied the method to the analysis of spreading process of a sessile droplet for step input voltages and oscillation of the droplet for alternating input voltages in electrowetting. The result was compared with experimental data. It is shown that contact line friction significantly affects the contact line motion and the oscillation amplitude. The pinning process of contact line was well represented by including the hysteresis effect in the contact angle models. In level set method, in the mean time, material properties are made to change smoothly across an interface of two materials with different properties by introducing an interpolation or smoothing scheme. So far, the weighted arithmetic mean (WAM) method has been exclusively adopted in level set method, without complete assessment for its validity. We viscosity, thermal conductivity, electrical conductivity, and permittivity, can be an alternative. I.e., the WHM gives more accurate results than the WAM method in certain circumstances. The interpolation scheme should be selected considering various characteristics including type of property, ratio of property of two fluids, geometry of interface, and so on.

• 한국분말재료학회지
• /
• 제15권6호
• /
• pp.471-476
• /
• 2008

Sintered Nd-Fe-B magnets have been widely used due to their excellent magnetic properties, especially for driving motors of hybrid and electric vehicles. The microstructure of Nd-Fe-B magnets strongly affects their magnetic properties, in particular the coercivity. Therefore, a post-sintering process like heat-treatment is required for improving the magnetic properties of Nd-Fe-B sintered magnets. In this study, cyclic heat treatment was performed at temperatures between $350^{\circ}C$ and $450^{\circ}C$ up to 16 cycles in order to control microstructures such as size and shape of the Nd-rich phase without grain growth of the $Nd_{2}Fe_{14}B$ phase. The 2 cycles specimen at this temperature range showed more homogeneous microstructure which leads to higher coercivity of 35 kOe than as-sintered one.

• 열처리공학회지
• /
• 제18권2호
• /
• pp.99-104
• /
• 2005

In this study, the effects of C and Si on damping capacity and mechanical properties of as-cast and as-rolled Fe-17%Mn alloys were investigated as a basic study for the purpose of the commercialization of the alloy. The $M_s$ temperature of ${\gamma}{\rightarrow}{\varepsilon}$ martensitic transformation in Fe-17%Mn alloy was decreased with increasing C and Si contents, resulting in the less volume fraction of ${\varepsilon}$ martensite. The damping capacity was also decreased with increasing alloying content because of less ${\varepsilon}$ amount and the reduction in mobility of the damping sources such as the stacking fault boundaries and ${\gamma}/{\varepsilon}$ interfaces due to the pinning effect by alloying elements. The mechanical properties of as-rolled alloys were superior to those of as-cast alloys probably because of finer ${\gamma}$ grains, larger amount of ${\varepsilon}$ martensite, and chemical homogeneity.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2011년도 제40회 동계학술대회 초록집
• /
• pp.436-436
• /
• 2011

Recently, spintronic devices with submicron structures are widely investigated to take advantage of their unique micromagnetic properties. In this work, we study the temperature dependence of exchange bias in bilayer anti-dot arrays made by depositing Co (40 nm)/Ni (5 nm) ferromagnetic bilayer on Si substrate to form anti-dot arrays with a diameter $1{\mu}m$. The anti-dot patterning was done only for the upper Co layer, while the Ni underlayer was kept unperforated. The temperature dependences of magnetoresistance (MR) and exchange bias were studied along magnetic easy and hard axes. The in-plane MR measurements were performed using a physical-property measurement system (PPMS ; Quantum Design Inc.) at various temperatures. The standard in-line four-point probe configuration was used for the electrical contacts. As temperature was varied, the MR data were obtained in which in-plane field (H=3 kOe) was applied in the directions along the hard and the easy axes with respect to the lattice plane. The temperature dependences of magnetic anisotropy and exchange bias were also studied along the magnetic easy and hard axes. As temperature decreases, the single peak splits into two peaks. While no exchange bias was observed along the magnetic easy axis, the exchange bias field steadily increased with decreasing temperature along the magnetic hard axis. These results were interpreted in connection with the magnetic anisotropy and the effect of the anti-dots in pinning domain wall motion along the respective direction.

• Journal of Magnetics
• /
• 제7권2호
• /
• pp.45-50
• /
• 2002

A magnetic field annealing is firstly used for nanostructured Sm-Co/Co films, prepared by magnetron sputtering method. The effects of magnetic field annealing on single-layered Sm-Co films are different from those on multi-layered Sm-Co/Co films. A detailed analysis of microstructures and magnetic properties is made by means of HRTEM, Auger electron spectroscopy, XRD and Physical Property Measurement System (PPMS). From magnetic properties and microstructure analysis, it was confirmed that these differences originate from the effects of magnetic field annealing on crystallization behavior of the films. The relationship between magnetic properties and microstructures explains a different demagnetization process of single-layered and multilayered films. For the single-layered Sm-Co films, magnetic-field-annealing makes the main phases change from $CaCu_5/ to Zn_2Th_{17}$ structure, resulting in a decrease of coercivity. The results show that the magnetic-field-annealing is useful to improve the properties of nanostructured Sm-Co(30 nm)/Co(10 nm) films, which ascribe to improving the pinning effectiveness in coercivity mechanism and decreasing the magnetostatic interaction of films. A very high coercivity about 0.7 T was obtained from nanoscaled multi-layered Sm-Co(30 nm)-/Co(10 nm) films.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2007년도 하계학술대회 논문집 Vol.8
• /
• pp.108-108
• /
• 2007

Inkjet printing is a non-contact and direct writing associated with a computer. In the industrial field, there have been many efforts to utilize the inkjet printing as a new way of manufacturing, especially for electronic devices. The etching resist used in this process is an organic polymer which becomes solidified when exposed to ultraviolet lights and has high viscosity of 300 cPs at ambient temperature. A piezoelectric-driven ink jet printhead is used to dispense $20-40\;{\mu}m$ diameter droplets onto the copper substrate to prevent subsequent etching. In this study, factors affecting the pattern formation such as printing resolution, jetting property, adhesion strength, etching and strip mechanism, UV pinning energy have been investigated. As a result, microscale Etch resist patterning of printed circuit board with tens of ${\mu}m$ high have been fabricated.

• 한국초전도ㆍ저온공학회논문지
• /
• 제25권2호
• /
• pp.5-9
• /
• 2023

The effect of La_0.7Sr_0.3MnO₃ (LSMO) addition on the superconducting property of Bi_1.6Pb_0.4Sr₂Ca₂Cu₃O_10+δ ((Bi, Pb)-2223) polycrystalline samples was studied. LSMO (0.3 wt.% to 2.0 wt.%) added (Bi, Pb)-2223 samples were prepared by using a solid-state reaction method. The XRD analyses show that as the LSMO addition increases, the volume fraction of the Bi-2223 phase is gradually decreased. The critical temperature (T_c) exhibits a gradual decrease with a single transition as the LSMO amount increases up to 1.0 wt.%, but a further addition of LSMO induces an abrupt decrease of T_c with a dual transition. The analyses on the local structure of the CuO₂ plane from the X-ray absorption fine structure (EXAFS) measurements showed that for the samples with low concentration of LSMO up to 1.0 wt.%, the Cu-O bond length and the CuO₂ plane ordering do not degrade from the values of pure (Bi, Pb)-2223, while they get worsen with a further increase of LSMO addition. These results open up the possibility of LSMO as artificial pinning centers of the (Bi, Pb)-2223 system for power application.