• 대한전기학회논문지:전기물성ㆍ응용부문C
• /
• 제48권1호
• /
• pp.19-22
• /
• 1999

N-doped and low-hydrogenated DLC thin films were coated on the Mo-tip FEAs in order to improve the field emission performance and their electrical properties were evaluated. The fabricated devices showed improved field emission performance in terms of turn-on voltage, emission current and current fluctuation. This result might be caused both by the shift of Fermi level toward conduction band by N-doping and by the inherent stability of DLC material. Furthermore, the transconductance of the DLC-coated Mo-tip FEA and electrical conductivity and optical band-gap of the deposited DLC films were investigated.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 1997년도 하계학술대회 논문집 C
• /
• pp.1244-1246
• /
• 1997

In conducting systems based on Langmuir - Blodgett (LB) films, tetracyanoquinodimethane(TCNQ) derivatives have been extensively studied as electron acceptor molecules. We have fabricated N-docosyl N'-methyl viologen diTCNQ (DMVT) anion radical LB film and investigated the FT-IR, ESR, and AFM images as the optical, magnetic properties and morphology of the LB film. We have measured in-plane electrical conductivity with number of layers. The in-plane conductivities are approximately $10^{-7}{\sim}10^{-6}\;S/cm$.

• 한국염색가공학회지
• /
• 제25권1호
• /
• pp.37-46
• /
• 2013

This paper surveys the ESD characteristics of the PANI added PU/MWNT film according to the manufacturing conditions such as variation of the loading contents of PANI and the mixture ratio of 2 dispersion solutions. For this purpose, PANI added PU/MWNT ground films were made with IPA/MWNT 3wt% dispersion solution and PANI/DMF dispersion solutions(5, 10, 15, 20, 25, and 30wt% contents of the PANI) by the mixture ratio of dispersion solution(10/50, 20/40, 30/30, 40/20, and 50/10part) in the PU (972DF) 100g, which was treated with 500rpm for 30min in the stirrer with condition of the dry temperature $120^{\circ}C$ for 2min. Totally, 36 kinds of PANI added PU/MWNT film specimens were prepared. The physical properties of the PANI added PU/MWNT films such as electrical resistivity, absorbancy by UV-Vis spectrometer, and triboelectricity were measured and discussed with surface characteristics of the PANI added PU/MWNT films by SEM. The dispersion property of PANI to the DMF showed best dispersion at the 25% of PANI content. The surface electrical resistivity of the PANI added PU/MWNT films was decreased with increasing the weight content of PANI/DMF dispersion solution, and it showed the lowest value $10^6{\Omega}$ at the mixing condition of PANI/DMF 20part and MWNT/IPA 40part with 30% PANI. Furthermore, it was shown that the electrical and physical properties of the PANI added PU/MWNT film such as electrical resistivity, and triboelectricity were better than those of PU/MWNT film prepared with no PANI, which was result obtained in previous paper.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 1998년도 추계학술대회 논문집
• /
• pp.81-84
• /
• 1998

New diagnostic techniques have been tried on the applications of chemical, physical and micro-structural methods because there was a limit to diagnose degradation in Korean Underground Residential Distribution (URD) power cables with the conventional electrical methods. In this study, non-electrical properties were carried out as such. Characterization of interface layer was analyzed by X-ray, characterization of insulator by water tree, degree of crosslinking, shrinkage as well as ${\mu}$ -FTIR, characterization of semiconductive layer by volume resistivity. Electrical properties were also performed by leakage current.

• Elastomers and Composites
• /
• 제30권3호
• /
• pp.218-228
• /
• 1995

To make filler loaded conducting rubber which has excellent electronical and physical properties, CR and NBR were mixed with barium ferrite(BaO.6Fe2O3). From the result of this study, vulcanization characteristics shows that curve is upgraded as the filler concentration increases and CR has higher torque than NBR. In physical properties, elongation being higher, modulus comes to decrease. Tear strength gradually decrease after showing the maximum point when is in the 100phr in CR. Resilience is not good to cause the increase in filler concentration. In electrical properties, conductivity becomes low when filler concentration increase. The increase of voltage makes a conductivity grown, but the rate change is weak. The influence of temperature hardly changes on increasing temperature. The morphology and the dispersion of a conductivity filler in vulcanizates through SEM were good. The more filler concentration increases, the shorter the particle interval is.

• Journal of Electrical Engineering and Technology
• /
• 제11권3호
• /
• pp.690-698
• /
• 2016

In this paper, a study is carried out to investigate the dielectric, physical and chemical properties of Palm Oil (PO) and Coconut Oil (CO) under open thermal ageing condition. The type of PO used in this study is Refined Bleached and Deodorized Palm Oil (RBDPO) Olein. The ageing experiment was carried out at 85 ℃ and 115 ℃ for 1, 3, 5, 7 and 14 days. Several parameters were measured such as AC breakdown voltage, dielectric dissipation factor, relative permittivity, resistivity, viscosity, moisture and acidity throughout the ageing duration. Based on the study, it is found that there are no significant changes on the AC breakdown voltages and relative permittivities for both RBDPO and CO. At ageing temperature of 115℃, there are clear reduction trends of dielectric dissipation factor for CO and resistivities for most of RBDPO. On the other hand, no clear trends are observed for viscosities, moisture and acidities of RBDPO and CO throughout the ageing duration.

• 대한전기학회논문지:전기물성ㆍ응용부문C
• /
• 제53권12호
• /
• pp.601-605
• /
• 2004

In this paper, we investigated ionic impurities and physical properties by change of carbon black content, which is asemiconductive material for underground power transmission. Specimens were made into sheet form with three existing resins and nine specimens for measurement. The ionic impurities of the specimens were measured using anICP-AES (Inductively Coupled Plasma Atomic Emission Spectrometer), and the density of specimens was measured by a density meter. Specific heat (Cp) was then measured using aDSC (Differential Scanning Calorimetry). The ranges of measurement temperature were from 0[$^{\circ}C$] to 200[$^{\circ}C$], and heating temperature was 4[$^{\circ}C$/min]. Ionic impurities were measured to be high according to increases in the content of carbon black from this experimental result and density was also increased according to these properties. In particular, the impurity content values of A1 and A2, and existing resins, were measured at more than 4000[ppm]. Specific heat from the DSC results was lowered according to augmentation in the content of carbon black. The ionic impurities of carbon black containing Fe, Co, Mn, Al and Zn are forms of rapidly passed kinetic energy that increase the number of times breaking occurs during unit time with the near particles according to an increase in the vibration of particles by the applied heat energy.

• The Korean Journal of Ceramics
• /
• 제6권4호
• /
• pp.390-395
• /
• 2000

Silicon, titanium, zirconium phosphates were synthesized by starting with appropriate chemical precursors in a solution. The synthetic procedure, chemical and physical structures were examined by FT-IR, liquid and solid state NMR, TGA, SEM, XRD, etc. The phosphates were examined for thermal and electrical properties. Advantages of the synthesis technique and the data on unique structures and thermal properties are reported.

• 대한전기학회논문지:전기물성ㆍ응용부문C
• /
• 제53권9호
• /
• pp.455-458
• /
• 2004

In this paper, we investigated impurities content and physical properties showing by changing the content of carbon black that is semiconductive materials for underground power transmission. Specimens were made of sheet form with the three of existing resins and the nine of specimens for measurement. Impurities content of specimens was measured by ICP-AES (Inductively Coupled Plasma Atomic Emission Spectrometer), and density of specimens were measured by density meter And then specific heat (Cp) was measured by DSC (Differential Scanning Calorimetry). A ranges of measurement temperature were from $0^{\circ}[C]$ to $200^{\circ}[C]$, and heating temperature was $4^{\circ}[C/min]$. Impurities content was highly measured according to increasing the content of carbon black from this experimental result, also density was increased according to these properties. Especially impurities content values of the Al and A2 of existing resins were measured more than 4000［ppm］. Specific heat from the DSC results was decreased according to increasing the content of carbon black. Because ionic impurities of carbon black having Fe, Co, Mn, Al and Zn are rapidly passed kinetic energy increasing the number of times breaking during the unit time with the near particles according to increasing vibration of particles by the applied heat energy.

• Carbon letters
• /
• 제22권
• /
• pp.25-35
• /
• 2017

The aim of the work was to investigate the thermo-electrical properties of low cost and rapidly produced randomly oriented carbon/carbon (C/C) composite. The composite body was fabricated by combining the high-pressure hot-pressing (HP) method with the low-pressure impregnation thermosetting carbonization (ITC) method. After the ITC method step selected samples were graphitized at $3000^{\circ}C$. Detailed characterization of the samples' physical properties and thermal properties, including thermal diffusivity, thermal conductivity, specific heat and coefficient of thermal expansion, was carried out. Additionally, direct current (DC) electrical conductivity in both the in-plane and through-plane directions was evaluated. The results indicated that after graphitization the specimens had excellent carbon purity (99.9 %) as compared to that after carbonization (98.1). The results further showed an increasing trend in thermal conductivity with temperature for the carbonized samples and a decreasing trend in thermal conductivity with temperature for graphitized samples. The influence of the thickness of the test specimen on the thermal conductivity was found to be negligible. Further, all of the specimens after graphitization displayed an enormous increase in electrical conductivity (from 190 to 565 and 595 to 1180 S/cm in the through-plane and in-plane directions, respectively).