• 한국세라믹학회지
• /
• 제56권2호
• /
• pp.184-190
• /
• 2019

To improve resistance in thermal shock of zirconia setter which is frequently and repeatedly exposed to high temperature, high degree of porosity and control of thermal expansion are needed for which the fused CSZ (CaO stabilized zirconia) is used to produce the zirconia setter. In the present study, the effects of sintering temperature, cool down condition, addition of CaO stabilizer, and addition of other additives on phase transition and thermal expansion behavior of the fabrication process of zirconia setter, were examined. The zirconia setter, fabricated with fused CSZ at 1550℃, exhibited 20.4 MPa of flexural strength, 6.8% of absorbance, and 27.9% of apparent porosity. The rapid change in thermal expansion of zirconia setter is observed at temperature around 800℃, and it was reduced by low firing temperature, slowed cooled down, and addition of CaO.

• 한국결정학회:학술대회논문집
• /
• 한국결정학회 2002년도 정기총회 및 추계학술연구발표회
• /
• pp.12-12
• /
• 2002

Lanthanum manganites have been extensively studied for the application to magnetic devices since the colossal magnetoresistance of these compounds has been observed [1]. The critical temperatures, Tc, of manganites La/sub 0.7/Ca/sub 0.3-x/Ba/sub x/MnO₃ increased as the content of Ba increased except the abrupt jump near the critical concentration. The step like behavior of the critical temperature for a similar compound has been known to be related to the structural phase transition [2]. To understand the step like behavior of Tc, the EXAFS technique is applied to the La/sub 0.7/Ca/sub 0.3-x/Ba/sub x/MnO₃ compound system. The ordering between the manganese and oxygen was examined by this method. The EXAFS analysis shows that the coordination numbers were not changed before and after the phase transition, the bonding distance between manganese and oxygen is about 1.94 ± 0.02 Å, which is consistent with other work [3] and the Debye waller parameters were about σ²= 0.0037 ± 0.0005 Ų for x=0.0 and x=3.0, respectively. The value of Debye-Waller parameter for x=0.09 is about σ² = 0.0050 ± 0.0005 Ų in about phase transition concentration. Based on the Debye-Waller parameters, it is shown that the ordering between manganese and oxygen is significantly reduced near the phase transition concentration.

• 한국세라믹학회지
• /
• 제44권1호
• /
• pp.18-22
• /
• 2007

The phase transition behavior of $Ge_2Sb_2Te_5$ (GST) thin film, which is a candidate material of recording layer for phase change random access memory (PRAM), has been evaluated using an in-situ reflectance measurement method. The experimental data have been analyzed by using johnson-mehl-avrami-kolomogorov (JMAK) model. JMAK model can be used only in isothermal state. However, temperature changes with time during the operation of PRAM. To apply JMAK equation to PRAM simulation, it has been assumed that the temperature increases stepwise and isothermally. By using JMAK equation and assumption for the transient state, the phase transition behavior of GST thin film has been predicted under $3^{\circ}C/min$ heating rate in this study. The simulation result agrees well with the experimental results. Therefore, It can be concluded that JMAK equation can be used far the PRAM simulation model.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2013년도 제44회 동계 정기학술대회 초록집
• /
• pp.266-266
• /
• 2013

We show a set-up of poly (4,4'-aminotriphenylene hexafluoroisopropylidenediphthalimide) (6F-TPA PI)/Al sample in which holes are injected by photoelectron emission process instead of direct charge carrier injection via metal electrode. In this process, an irreversible electrical phase transition of 6F-TPA PI is found in contrast to the Al/6F-TPA PI/Al structure, leading to a write-once-readmany behavior. The photoelectron spectroscopy results measured before and after the switching process revealed that the irreversible electrical phase transition of 6F-TPA PI is attributed to the chemical modification of the carbonyl group in phthalimide moiety.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2000년도 하계학술대회 논문집
• /
• pp.491-494
• /
• 2000

Conductive Langmuir-Blodgett(LB) films have recently attracted much interest from the viewpoint of ultrathin film conductors at the molecular level. The result shows that the Maxwell-displacement-current(MDC) measuring technique is useful in the detection of phase-transition over the entire range of molecule areas. At the liquid-solid phase transition, a striking feature in the present current measurement was observed; the I-A isotherm for a DPPC monolayer has sharp bend. Dynamic behavior of monolayers in the presence of an external field was also investigated using the current-measuring technique. Dynamic behavier of DPPC monolayer was measured by displacement current when the molecules are stimulated by pressure velocity. As result, it is known that current is generated of higher current pe마 as compression velocity become faster. Also, in order to clarify the reorganization of the lipid monolayers, it is instructive to plot the relationship between I and 1/$A^2$.

• 한국인쇄학회지
• /
• 제14권1호
• /
• pp.17-29
• /
• 1996

N-substituted acrylamide hydrogel is reported to have the feature of bing transparent and sensitive enough to response to a temperature stimulus below the temperature of phase transition. Especially at the near of 35 C it becomes shrunk and opaque very quickly. It has also the characteristic of reversing swelling and shrinking. The experiment showed that it is possible to produce a functional gel of super water absorption with the process of free radical polymerizing PVA(polyvinylalcohol) and PAA(polyacrylamide), and crosslinking. The ratio of shrinking and swelling caused by copolymerization rises 10% to 80% at the each temperature of 20 C, 30 C, 40 C, respectively. Phase transition temperature of this gel by copolymerization is50 C while that of ordinary N-substituted acrylamides is between 32~35 C. This temperature reaches the rearing limit of animals and plants so that volumetric transition polymer gel can be ulilized in varying fields such as agriculture/gardening which are water-using field, on-off switch sensing temperature and volumetric variation, processing of liquid wastes and civil engineering works, architecture and electronics. We have no doubt that this material will be the high-functional resin in the hi-tech age of the near future.

• Nuclear Engineering and Technology
• /
• 제34권6호
• /
• pp.574-585
• /
• 2002

The microstructural characteristics and its related mechanical properties of RPV cladding have been investigated using small punch (SP) tests. SA508 Cl.3 RPV steel plates were overlay cladded with the type ER309L welding consumables by submerged arc welding process. Although the RPV clad material had a small portion of 5 ferrite phase, it still showed the ductile to brittle transition behavior The transition temperature was determined by the SP test and it depended on the content of $\sigma$ phase, specimen size, and determination methods. The fracture appearance of SP specimen was changed from circumferential to radial cracking as test temperature became low, and below the transition temperature region, ER309L cladding usually fractured along the 6 ferrite by the low temperature failure of ferrite phase.

• 한국자기학회지
• /
• 제8권4호
• /
• pp.179-184
• /
• 1998

일반적으로 페로브로스카이트 구조의 망간 산화물에서 많이 관찰되어온 초거대 자기 저항 현상은 임계점 (큐리온도) 부근에서 온도 변화에 의한 상자성-강자성 상전이와 동반한 전기 전도 기수 변화에 따른 급격한 저항 변화와 매우 밀접한 광계가 있다. 본 논문에서는 이러한 전기 저항-온도 거동을 모사하기 위해, 온도에 따른 상분율 변화 함수를 유효매질 이론(effective media theory)을 이용하여 모형식을 마련하엿다. 미 모형식은 실제 La0.7Ca0.3MnO3의 저항-온도 거동을 매우 정확하게 모사하였다.

• Journal of Korean Vacuum Science & Technology
• /
• 제7권1호
• /
• pp.13-17
• /
• 2003

The influence of structural transition on the resistance and impedance behavior of Ni$_2$MnGa alloy was investigated. The temperature-dependent resistance and impedance were measured in a temperature range of 4 - 350 K and 185 - 300 K, respectively. The dependence of temperature coefficient of resistivity on temperature shows a kink at 220 K, which is related to the structural transition. The change in dominant scattering mechanism results in the observed kink. Significant increases were also observed around the transition temperature for both real and imaginary parts of impedance. It is thought that this phenomenon originates from disappearance of the martensite twin boundaries during the structural transformation.

• Bulletin of the Korean Chemical Society
• /
• 제26권12호
• /
• pp.2027-2032
• /
• 2005

This paper demonstrates details of thermal behavior of Langmuir-Blodgett (LB) film of poly(tert-butyl methacrylate) (PtBMA) by using the principal component analysis based two-dimensional correlation spectroscopy (PCA2D) through eigenvalue manipulating transformation (EMT). By uniformly lowering the power of a set of eigenvalues associated with the original data, the smaller eigenvalues becomes more prominent and the subtle contribution from minor components is now highlighted much more strongly than the original data. Thus, the subtle difference of thermal behavior of LB film of PtBMA from minor components, which is not readily detectable in the conventional 2D correlation analysis, is much more noticeable than the original data. PCA2D correlation spectra with EMT operation for the temperature-dependent IR spectra of LB film of PtBMA reveal the hidden property of phase transition processes during heating.