• Journal of the Korean Ceramic Society
• /
• v.26 no.1
• /
• pp.31-36
• /
• 1989

In order to synthesize AlN-polytypes from AlN-SiO2-Al2O3 system, composition A (AlN/SiO2/Al2O3=1/0.3/0.05, mole ratio) and composition B(AlN-SiO2-Al2O3=1/0.2/0.05, mole ratio) were used. AlN-polytypes were produced by nitriding the mixture at 175$0^{\circ}C$~190$0^{\circ}C$ under N2 atmosphere. For lower reaction temperature, 15R phase was produced and in the case of higher reaction temperature, AlN phase was only produced. As each composition was heated at 185$0^{\circ}C$ in N2 atmosphere, produced main phases were 15R phase for composition A and 21R phase for composition B respectively. The fracture surfaces of produced reactants showed porous skeleton structure.

• Journal of Powder Materials
• /
• v.10 no.2
• /
• pp.118-122
• /
• 2003

Alpha-SiAlON ceramics having various compositions and modifying cations were investigated with respect to their phase stability, transformation kinetics. and resulting microstructures. Each composition was heat treated at 150$0^{\circ}C$ for 1h and measured the $\alpha$-SiAlON transformation. The phase-boundary composition in the single-phase $\alpha$-SiAlON region showed sluggish transformation from $\alpha$-$Si_3N_4$ to $\alpha$-SiAlON compared to the phase-center composition in the diagram. Using the different rare earth modifying cations, dependence of transformation kinetics on the phase stability in a fixed composition was also explained. By changing size of the stable u-phase region with exchanging cations, systematic change in transformation was observed. Transformation rate of $\alpha$-SiAlON at low temperature has an important role on controlling the final microstructure. Less transformation gives more chances to develop elongated grain in the microstructure.

• Journal of KIISE:Databases
• /
• v.36 no.2
• /
• pp.123-138
• /
• 2009

In recent years, the web services composition search has become an issue of great interest. The web services composition search is the process of integrating individual web services to yield desired behavior. Through the web services composition search, more sophisticated functionalities can be provided. Current solutions can be classified into three main classes: forward chaining approach, backward chaining approach and two-phase approach. However one-way chaining approaches, such as forward chaining approach and backward chaining approach have limitations of searching irrelevant web services. And two-phase approach has limitations of including redundant web services. In this paper, we propose an unredundant web services composition search based on the two-phase algorithm. The algorithm consists of a forward phase and a backward phase. In the forward phase, the candidate web services participating composition will be found efficiently by searching the Link Index. In the backward phase, unredundant web services compositions will be generated from candidate web services by using the Token Manager. The experimental results show that our proposed algorithm is more efficient than one-way chaining approaches. The experimental results also show that our algorithm can provide more solutions than previous two-phase approach and is comparable to previous one in execution time.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.17 no.3
• /
• pp.353-359
• /
• 2004

In this study. porcelain insulator samples which have a different alumina composition were manufactured in order to test electrical and mechanical properties and make an analysis of the propagation phenomena of micro cracks on porcelain body. From XRD quantitative analysis the crystalline phases were different with alumina composition, sample C and D which have about l7wt％ Corundum phase without the Cristobalite phase shows better electrical and mechanical properties than sample A and B which have the Cristobalite phase. In dielectrics test on porcelain samples with below l7wt％ alumina composition, it was found that the amount of glass phase(SiO$_2$) have an main effect to decrease the dielectric loss(tan$\delta$), and the dielectric breakdown voltage of aluminous porcelain insulators was largely affected by its relative density. As a micro tracks analysis, HRB were measured, then the intensity of HRB increased with the amount of alumina composition. On the other hand, the propagation behaviors of cracks was fairly influenced by the distribution of pores.

• Biotechnology and Bioprocess Engineering:BBE
• /
• v.9 no.1
• /
• pp.47-51
• /
• 2004

Ceramide III was prepared by the cultivation of Saccharomyces cerevisiae. Ceramide III was partitioned from the cell extracts by solvent extraction and analyzed by Normal Phase High Performance Liquid Chromatography (NP-HPLC) using Evaporative Light Scattering Detector (ELSD). We experimentally determined the mobile phase composition to separate ceramide III with NP-HPLC. Three binary mobile phases of n-hexane/ethanol, n-hexane/lsoprophyl Alcohol(IPA) and n-hexane/n-butanol and one ternary mobile phase of n-hexane/IPA/methanol were demonstrated. For the binary mobile phase of n-hexane/ethanol, the first mobile phase composition, 95/5(v/v), was step-increased to 72/23(v/v) at 3 min. In the binary mobile phase, the retention time of ceramide III was 7.87min, while it was 4.11 min respectively in the ternary system, where the mobile phase composition of n-hexane/IPA/methanol, 85/7/8(v/v/v), was step-increased to 75/10/15(v/v/v) at 3 min. However, in the ternary mobile phase, the more peak area of ceramide III was observed.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1999.05a
• /
• pp.65-68
• /
• 1999

A well oriented Bi2212 superconductor thick films were fabricated by screen printing with a Cu-free Bi-Sr-Ca-O mixture powder on a copper plate and heat-treating at 820-88$0^{\circ}C$ for several minute in air. During the heat-treatment, the printing layer partially melted by reaction between the Cu-free precursor and CuO of the oxidizing copper plate. In the partial melting state, it is believed that the solid phase is Bi-free phase and Cu-rich phase and the composition of the liquid is around Bi : Sr : Ca : Cu = 2 : 2 : 0 : 1. Following the partial melting, the Bi2212 superconducting phase is formed at Bi-free phase/liquid interface by nucleation and grows. With decreasing the Bi composition in the precursor powder, the critical temperature(T$_{c}$) of the fabricated Bi2212 thick film increased to about 79 K.K.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.05e
• /
• pp.85-88
• /
• 2003

In this study, porcelain insulator samples which have a different alumina composition were manufactured in order to test electrical and mechanical properties and make an analysis of the propagation phenomena of micro cracks on porcelain body. From XRD quantitative analysis the crystalline phases were different with alumina composition, sample C and D which have about 17wt% Corundum phase without the Cristobalite phase shows better electrical and mechanical properties than sample A and 8 which have the Cristobalite phase. In dielectrics test on porcelain samples with below 17wt% alumina composition, it was found that the amount of glass phase$(SiO_2)$have an main effect to decrease the dielectric loss$(tan{\delta})$, and the dielectric breakdown voltage of aluminous porcelain insulators was largely affected by its relative density. As a micro cracks analysis, HRS were measured, then the intensity of HRS increased with the amount of alumina composition. On the other hand, the propagation behaviors of cracks was fairly influenced by the distribution of pores.

• Journal of the Semiconductor & Display Technology
• /
• v.10 no.3
• /
• pp.29-33
• /
• 2011

Film growth rate and composition variation are numerically analyzed during the selective area growth of InGaN on the GaN triangular stripe microfacet in this study. Both the vapor phase diffusion and the surface diffusion are considered to determine the In composition on the InGaN surface. To obtain the In composition on the surface, flux of In atoms due to the surface diffusion is added to the concentration determined from the Laplace equation which is governing the gas phase diffusion. The solution model is validated by comparing the growth rates from the analyses to the experimental results of GaN and InN films. The In composition and resulting wave length are increased when the surface diffusion is considered. The In content is also increased according to the increasing mask width. The effect of mask width to the In content and wave length is increasing in the case of a small open region.

• Journal of Welding and Joining
• /
• v.18 no.5
• /
• pp.90-97
• /
• 2000

Effect of alloy elements on joinability of insert metal for liquid phase diffusion bonding of heat resistant alloys was investigated in this study. Also, optimum chemical composition of insert metal was explained using interpolation method. The insert metals utilized was commercial Ni-base amorphous foils and newly developed Ni-base filler metals with B, Si and Cr in this study. Melting point and critical interlayer width(CIW) decreased with increasing additional amount of B, Si and Cr, melting point lowering element of the insert metal. Optimized chemical composition of insert metals could be estimated by interpolation method. The optimum amount of B, Si, Cr addition into the insert metal were found to be about 3%, 4% and 3%, respectively. The measured characteristic values, melting point, microhardness in the bonded interlayer and CIW of the insert metals were the almost identical to ones of the calculated results by interpolation method.

• Applied Microscopy
• /
• v.52
• /
• pp.14.1-14.10
• /
• 2022

An electron probe X-ray microanalyzer (EPMA) is an essential tool for studying chemical composition distribution in the microstructure. Quantifying chemical composition using standard specimens is commonly used to determine the composition of individual phases. However, the local difference in chemical composition in the standard specimens brings the deviation of the quantified composition from the actual one. This study introduces how to overcome the error of quantification in EPMA in the practical aspect. The obtained results are applied to evaluate the chemical com position of retained austenite in multi-phase steel. Film-type austenite shows higher carbon content than blocky-type one. The measured carbon contents of the retained austenite show good coherency with the calculated value from the X-ray diffraction.