• Korean Journal of Air-Conditioning and Refrigeration Engineering
• /
• v.25 no.9
• /
• pp.477-483
• /
• 2013

A numerical analysis of solid-liquid phase change was performed on a heat transfer module which consisted of circulating water path (BRINE), heat transfer plate (HTP) and phase change material (PCM) layers, such as high temperature PCM (HPCM, $78{\sim}79^{\circ}C$) and low temperature PCM (LPCM, $28{\sim}29^{\circ}C$). There were five arrangements, consisting of BRINE, HTP, LPCM and HPCM layers in the heat transfer module. The time and heat transfer rate for melting/solidification was compared to their arrangements, against each other. As results, the numerical time without convection was longer than the experimental one for melting/solidification. Moreover, the melting/solidification with the BRINE I-LPCM-BRINE II-HPCM arrangement was faster(10 hours) than the others; HPCM-BRINE-LPCM, BRINE I-HPCM-LPCM-BRINE II one.

• Journal of Adhesion and Interface
• /
• v.6 no.1
• /
• pp.11-18
• /
• 2005

The capsules were prepared from a phase change material (PCM) of octadecane as a core material and melamine formaldehyde resin as a shell material. The PCM capsule size was varied in the range of $3{\sim}25{\mu}m$. The core contents and sizes of the PCM capsule, were determined by DSC and SEM, respectively. An acrylic coating material which contains butyl acrylate (BA), methyl metacrylate (MMA) and acrylic acid (AA) were synthesized by emulsion polymerization. The films were prepared from the acrylic emulsion and PCM capsules which have various capsule sizes. From the results of SEM experiment, it was observed that the PCM capsules were well dispersed inside the film and the surface of the film became less rough when the PCM capsule size was small. The swelling ratio of the films were not significantly affected by the PCM capsule size. However, the tensile strength and elongation of the films were greatly decreased with increasing the PCM capsule size.

• Proceedings of the Korean Society of Dyers and Finishers Conference
• /
• 2008.10a
• /
• pp.151-152
• /
• 2008

PCM has the ability to change their state, these materials absorb energy during the heating process as a body contact and release energy during a reverse cooling process as phase change take place. Using the thermal energy storage of PCM which has a melting point 15 to $35^{circ}C$ is one of the most effective ideas for utilization in textile finish. In this study, microencapsulated PCM(MCPCM) were synthesized by sol-gel method using the octadecane(or nonadecane) as PCM and the silica as microcapsule materials. To develop smart temperature adaptable textile, coating process was applied to textile substrate using a composition included MCPCM.

• 한국태양에너지학회:학술대회논문집
• /
• 2011.04a
• /
• pp.162-167
• /
• 2011

Thermal storage plays an important role in building energy saving, which is greatly assisted by the incorporation of latent heat storage in building materials. A phase change material is a substance with a high heat of fusion which, melting and solidifying at a certain temperature, can be storing and releasing large amount of energy. Heat is stored or released when the material changes from solid to liquid. Integration of building materials incorporating PCMs into the building envelope can result in increased efficiency of the built environment. The aim of this research is to identify thermal performance of PCMs impregnated building materials which is applied to interior of building such as gypsum and red clay. In order to analyze thermal performance of phase change materials, test-cell experiments and simulation analysis were carried out. The results show that micro-encapsulated PCM has an effect to maintain a constant indoor temperature using latent heat through the test-cell experiments. PCM wallboard makes it possible to reduce the fluctuation of room temperature and heating and cooling load by using EnergyPlus simulation program. Phase change material can store solar energy directly in buildings. Increasing the heat capacity of a building is capable of improving human comfort by decreasing the frequency of indoor air temperature swings so that the interior air temperature is closer to the desired temperature for a long period of time.

• Applied Science and Convergence Technology
• /
• v.23 no.1
• /
• pp.34-39
• /
• 2014

The programmable switches which control the delivery of electrical signals in programmable logic devices are fabricated using memory technology. Although phase change memory (PCM) technology is one of the most promising candidates for the manufacturing of the programmable switches, the threshold switching material should be added to a PCM cell for realization of the programmable switches based on PCM technology. In this work, we report the impurity-doped $Ge_2Sb_2Te_5$ (GST) chalcogenide alloy exhibiting threshold switching property. Unlike the GST thin film, the doped GST thin film prepared by the incorporation of In and P into GST is not crystallized even at the postannealing temperature higher than $200^{\circ}C$. This specific crystallization behavior in the doped GST thin film is attributed to the stabilization of the amorphous phase of GST by In and P doping.

• Fibers and Polymers
• /
• v.6 no.4
• /
• pp.343-347
• /
• 2005

The purpose of this study was to investigate the appropriate amounts of phase change materials to give objective and subjective wear sensations. Vapor-permeable water-repellent fabrics with (WR-PCM) and without (WR) octadecane containing microcapsules were obtained by wet-porous coating process. Then, calculating the area of the WR-PCM treated clothes, we estimated the total calories of the clothing by multiplying the heat of fusion and heat of crystallization of PCM to the calculated area. Wear tests were conducted in both warm environment $(30^{\circ}C,\;65\%\;RH)$ and cold environment $(5^{\circ}C,\;65\%\;RH)$ with sports warm up style experimental garments made with WR and WR-PCM fabrics. Rectal, skin, and clothing microclimate temperatures, saliva and subjective evaluation measurements were done during the wear test. There was no difference of rectal and mean skin temperatures between WR and WR-PCM, but the clothing microclimate temperature of WR-PCM under warm environment was slightly lower than that of WR. In cold environment, WR-PCM showed much higher temperature than in WR. Saliva change did not appear between clothes, but did between two environments. Although subjective sensation between WR and WR-PCM was not significantly different, WR-PCM was rated as cooler than WR in warm environment and as warmer than WR in cold environment. The results of this study indicated that octadecane containing microcapsules in water-repellent fabric provide cooling effect.

• Journal of the Korean Chemical Society
• /
• v.65 no.2
• /
• pp.145-150
• /
• 2021

The present study describes a hands-on experiment to help students understand the concept of phase change or phase transition and its application in a phase change material (PCM). PCMs are substances that have the capability of storing and releasing large amounts of thermal energy. They act as energy storage materials that provide an effective way to save energy by reducing the electricity required for heating and cooling. Lauric acid (LA) was selected as an example of the PCM. Students investigated the temperature change of LA and the temperature (of air) inside the test tube. The differences in the temperatures of the systems helped students understand how PCMs work. A one-group pretest and posttest design was implemented with 34 grade-11 students in science and mathematics. Students' understanding was assessed using a multiple-choice test and a questionnaire. The findings revealed that the designed activity helped students understand the concept of phase change and its application to materials for thermal energy storage.

• Composites Research
• /
• v.30 no.5
• /
• pp.288-296
• /
• 2017

The focus of this study is to experimentally investigate the heat dissipation characteristics of poly (methyl methacrylate) (PMMA) composite films with phase change materials (PCM) to resolve heat build-up problems encountered in various electronic devices. In this study, two different types of phase change materials were used to fabricate the composite films by compression molding method and PCM paste sealing method then compared. It was observed in this study that the heat dissipation capability of PCM/PMMA composite films was remarkably enhanced by applying graphite sheet or graphene film into the composite due to their high thermal conductivity. These PCM/ PMMA composite films were attached on the hot spot inside smart phone and tested its surface temperature change according to time. The heat dissipation capability of PCM/PMMA composite film incorporated smart phone was increased 154% and hybrid PCM/PMMA composite film incorporated smart phone was increased 286% over the reference, respectively.

• Journal of the Korea Concrete Institute
• /
• v.28 no.6
• /
• pp.665-672
• /
• 2016

This study is conducted to investigate the effect of phase change materials (PCM) on hydration heat and strength characteristics of cement mortar. Two types of Barium and Strontium-based PCMs were used in this study and the addition ratio of each PCM to the cement mortar ranged from 1% to 5% by cement weight. Flow test, semi-adiabatic temperature rise test, compressive strength and flexural strength test were carried out to examine the PCM effect on heat and mechanical properties of cement mortar. Test results indicated that PCMs used in this study were effective to control hydration heat of cement mortar, and Barium-based PCM slightly reduce flow value. The compressive and flexural strength of cement mortar with PCM decreased with increasing the adding mount of PCM. The prediction model for compressive strength of cement mortar with different addition levels of PCMs are suggested in this study.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2016.02a
• /
• pp.322-322
• /
• 2016

Phase change memory (PCM) has attracted much attention as one of the most promising candidates for next-generation nonvolatile memory. In that regard, the purposes of the study are to propose reference of effective pulse parameter to control phase switching operation and to invest the effect of nitrogen doped in PCM materials for improved cycling stability and economic energy consumption. Switching operation of PCM is affected by electric pulse parameter and as shown in figure.1 are composed to RT(rising time), ST(setting time), FT(falling time) and the effect of these parameter was precisely investigated. Transmission electron microscope (TEM) was used to confirm fine structure and retention cycle test was conducted to confirm reliability. Finally improvement reliability and economic power consumption in quantitatively are obtainable by optimum pulse parameter and nitrogen doping in GST material. these study is related to the engineering background of other semiconductor industries and it have confirmed to possibility further applications.