• Journal of Surface Science and Engineering
• /
• v.37 no.5
• /
• pp.289-295
• /
• 2004

A dense palladium-nikel (Pd-Ni) alloy composite membrane has been fabricated on microporous nickel support mixed with submicron/micron nickel powder instead of mesoporous stainless steel support. Plasma treatment process is introduced as pre-treatment process instead of HCI activation. Pd-Ni alloy composite membrane prepared by electro plating was fairly a uniform and dense surface morphology. The membrane was characterized by permeation experiments with hydrogen and nitrogen gases at temperature 773 K and pressure 2.2 psi. The results showed that hydrogen ($H_2$) permeance was 27 ml/$\textrm{cm}^2$ㆍatmㆍmin and hydrogen/ nitrogen ($_H2$$N_2$) selectivity was 8 at 773 K.

• Proceedings of the Membrane Society of Korea Conference
• /
• 1999.07a
• /
• pp.43-47
• /
• 1999

Pd-ceramic composite membranes and catalytic membrane reactors(CMR) have been studied for hydrogen purification and recovery in th fusion reactor fuel cycle. The development of techniques for coating microporous ceramic tubes with Pd and Pd/Ag layers is described: composite membranes have been produced by electroless deposition (Pd/Ag film of 10-20${\mu}{\textrm}{m}$) and rolling of thin metal sheet (Pd and Pd/ Ag membranes of 50-70 ${\mu}{\textrm}{m}$). Experimental results on electroless membranes showed that the metallic film presented some defects and the membranes had not complete hydrogen selectivity . Then the catalytic membrane reactors with electroless membranes can be applied for some industrial processes that do not require a complete separation of the hydrogen (i.e. in the dehydrogenation of hydrocarbons). The rolled thin Pd/Ag membranes separated the hydrogen from the other gas with a complete selectivity and exhibited a slightly larger (about a factor 1.7) mass transfer resistance with respect to the electroless membranes. Experimental tests confirmed the good performances in terms of durability.

• Korean Membrane Journal
• /
• v.1 no.1
• /
• pp.1-7
• /
• 1999

Pd-ceramic composite membranes and catalytic membrane reactors(CMR) have been studied for hydrogen and its isotopes (deuterium and tritium) purification and recovery in the fusion reactor fuel cycle. Particularly a closed-loop process has been studied for recovering tritium from tritiated water by means of a CMR in which the water gas shift reaction takes place. The development of the techniques for coating micro-porous ceramic tubes with Pd and Pd/Ag thin layers is described : P composite membranes have been produced by electroless deposition (Pd/Ag film of 10-20 $\mu$m) and rolling of thin metal sheets (Pd and Pd/Ag membranes of 50-70 $\mu$m). Experimental results of the electroless membranes have shown a not complete hydrogen selectivity because of the presence of some defects(micro-holes) in the metallic thin layer. Conversely the rolled thin Pd and Pd/ag membranes have separated hydrogen from the other gases with a complete selectivity giving rise to a slightly larger (about a factor 1.7) mass transfer resistance with respect to the electroless membranes. Experimental tests have confirmed the good performances of the rolled membranes in terms of chemical stability over several weeks of operation. Therefore these rolled membranes and CMR are adequate for applications in the fusion reactor fuel cycle as well as in the industrial processes where high pure hydrogen is required (i.e. hydrocarbon reforming for fuel cell)

• Proceedings of the KIEE Conference
• /
• 1999.11b
• /
• pp.442-445
• /
• 1999

In this work, to detect of hydrogen in DI water in the generator area of nuclear power plants was fabricated Pd/Pt gate MISFET sensor using Pd membrane. $H_2$ permeation through Pd accounts for external mass transfer, surface adsorption and desorption, transitions to and from the bulk metal, and diffusion within the metal. The identification of pinholes in the generator area of plant is an important safety consideration, as hydrogen build-up gives rise to explosion. For this type of application the sensor needs to be isolated in DI water, accordingly, a Pd membrane was used to separate the DI water. The hydrogen in the DI water was then absorbed on the Pd thin film and diffused into the oil through the thin film. The Pd/Pt gate MISFET sensor, encapsulated by oil, will thereby detect permeated hydrogen.

• Journal of Surface Science and Engineering
• /
• v.37 no.5
• /
• pp.243-248
• /
• 2004

A palladium-nikel(Pd-Ni) alloy composite membrane has been fabricated on microporous nickel support formed with nickel powder. Plasma surface treatment process is introduced as pre-treatment process instead of HCI activation. Pd coating layer was prepared by dc magnetron sputtering deposition after $H_2$ plasma surface treatment. Palladium-nickel alloy composite layer had a fairly uniform and dense surface morphology. The membrane was characterized by permeation experiments with hydrogen and nitrogen gases at temperature of 773 K and pressure of 2.2psi. The hydrogen permeance was 6 ml/minㆍ$\textrm{cm}^2$ㆍatm and the selectivity was 120 for hydrogen/nitrogen($H_2$/$N_2$) mixing gases at 773 K.

• Journal of Surface Science and Engineering
• /
• v.45 no.6
• /
• pp.248-256
• /
• 2012

A Pd-based hydrogen membranes for hydrogen purification and separation need high hydrogen perm-selectivity. The surface roughness of the support is important to coat the pinholes free and thin-film membrane over it. Also, The pinholes drastically decreased the hydrogen perm-selectivity of the Pd-based composite membrane. In order to remove the pinholes, we introduced various surface pre-treatment such as alumina powder packing, nickel electro-plating and micro-polishing pre-treatment. Especially, the micro-polishing pretreatment was very effective in roughness leveling off the surface of the porous nickel support, and it almost completely plugged the pores. Fine Ni particles filled surface pinholes with could form open structure at the interface of Pd alloy coating and Ni support by their diffusion to the membrane and resintering. In this study, a $4{\mu}m$ surface pore-free Pd-Cu-Ni ternary alloy membrane on a porous nickel substrate was successfully prepared by micro-polishing, high temperature sputtering and Cu-reflow process. And $H_2$ permeation and $N_2$ leak tests showed that the Pd-Cu-Ni ternary alloy hydrogen membrane achieved both high permeability of $13.2ml{\cdot}cm^{-2}{\cdot}min^{-1}{\cdot}atm^{-1}$ permation flux and infinite selectivity.

• Membrane Journal
• /
• v.20 no.1
• /
• pp.69-75
• /
• 2010

Cermet membrane was fabricated with tantalum as hydrogen-permeable metal and $Y_2O_3$-stabilized $ZrO_2$ (YSZ) as ceramic supporter. Ta/YSZ cermet membrane was prepared through pre-sintering in He atmosphere and then main sintering under high vacuum and the impurities to originate from sintering and brazing could be removed by mechanical polishing. As-prepared membrane showed dense structure with continuous channel of tantalum. Hydrogen permeation experiment was conducted in the region of $200{\sim}350^{\circ}C$ using Ta/YSZ membrane coated with Pd for hydrogen dissociation. The crack in membrane was formed at $300^{\circ}C$ and the Pd coating layer has flaked off in spots. XRD results showed that tantalum reacted with hydrogen to form $Ta_2H$. The lattice expansion by $Ta_2H$ caused deterioration for membrane.

• Bulletin of the Korean Chemical Society
• /
• v.23 no.5
• /
• pp.674-678
• /
• 2002

The dehydrogenation of propane to propylene has been studied in an isothermal high-temperature shell-and-tube membrane reactor containing a Pd-coated ${\psi}$-Al2O3 membrane and a Pt/K/Sn/Al2O3 packed catalyst . A tubular Pd-coated ${\psi}$-Al2O3 membrane was prepared by an electroless plating method. This membrane showed high hydrogen to nitrogen permselectivities (PH2N2 = 10-50) at 400 $^{\circ}C$ and 500 $^{\circ}C$ with various transmembrane pressure drops. The employment of a membrane reactor in the dehydrogenation reaction, which selectively separates hydrogen from the reaction mixture along the reaction path, can greatly increase the conversion and enable operation of the reactor at lower temperatures. High hydrogen permselectivity has been confirmed as a key factor in determining the reactor performance of conversion enhancement.

• Journal of Hydrogen and New Energy
• /
• v.27 no.3
• /
• pp.270-275
• /
• 2016

A simple solid state incorporation method was employed in order to incorporate Pd nanocatalyst into a Nafion film for polymer electrolyte membrane fuel cell (PEMFC) via the reduction of palladium (II) bis (acetylacetonate), $Pd(acac)_2$. It was sublimed, penetrated into Nafion film and then reduced to Pd nanoparticles simultaneously in a glass reactor of N2 atmosphere at $180^{\circ}C$ for 1, 3 and 5 min. This reaction was took place without any reducing agent and any solvent. The morphology of the Pd nanoparticles was observed by transmission electron microscopy (TEM), and Pd distribution was analyzed by scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS). And 23% modification of tensile strength of Pd/Nafion composite film was measured by universal testing machine and I-V curve was estimated by using a unit cell with $5{\times}5cm^2$ active area.

• Applied Chemistry for Engineering
• /
• v.20 no.1
• /
• pp.104-108
• /
• 2009

In this study, for the flow of carbon dioxide/hydrogen mixture through a tubular type Pd-Ag membrane, hydrogen partial pressure, velocity profile, and concentration profile were simulated as a function of inlet flow rate using computational fluid dynamics (CFD) technique. The simulation results indicated that the mole fraction of carbon dioxide increased slowly in the longitudinal direction as the flow rate increased. In addition, the effects of inlet flow rate and the length of membrane on hydrogen recovery were investigated. At lower flow rate and for longer membrane, the hydrogen recovery was larger.