• The Korean Journal of Ceramics
• /
• v.2 no.2
• /
• pp.95-101
• /
• 1996

Variations of the leakage current behaviors and interface potential barrier $({\Phi}_B)$ of rf-sputter deposited (Ba, Sr)$TiO_3$ (BST) thin films with thicknesses ranging from 20 nm to 150nm are investigated as a function of the thickness and bias voltages. The top and bottom electrodes are dc-sputter-deposited Pt films. ${\Phi}_B$ critically depends on the BST film deposition temperature, postannealing atmosphere and time after the annealing. The postannealing under $N_2$ atmosphere results in a high interface potential barrier height and low leakage current. Maintaining the BST capacitor in air for a long time reduces the ${\Phi}_B$ from about 2.4 eV to 1.6 eV due to the oxidation. ${\Phi}_B$ is not so dependent on the film thickness in this experimental range. The leakage conduction mechanism is very dependent on the BST film thickness; the 20 nm thick film shows tunneling current, 30 and 40 nm thick films show Shottky emission current.

• Journal of information and communication convergence engineering
• /
• v.3 no.4
• /
• pp.179-183
• /
• 2005

A photodiode capable of obtaining a sufficient photo/ dark current ratio at both forward bias state and reverse bias state is proposed. The photodiode includes a glass substrate, an aluminum film formed as a lower electrode over the glass substrate, an alumina film formed as an insulator barrier over the aluminum film, a hydrogenated amorphous silicon film formed as a photo conduction layer over a portion of the alumina film, and a transparent conduction film formed as an upper electrode over the hydro-generated amorphous silicon film. A good quality alumina $(Al_2O_3)$ film is formed by oxidation of aluminum film using electrolyte solution of succinic acid. Alumina is used as a potential barrier between amorphous silicon and aluminum. It controls dark-current restriction. In case of photodiodes made by changing the formation condition of alumina, we can obtain a stable dark current $(\~10^{-12}A)$ in alumina thickness below $1000{\AA}$. At the reverse bias state of the negative voltage in ITO (Indium Tin Oxide), the photo current has substantially constant value of $5{\times}10^{-9}$ A at light scan of 100 1x. On the other hand, the photo/dark current ratios become higher at smaller thicknesses of the alumina film. Therefore, the alumina film is used as a thin insulator barrier, which is distinct from the conventional concept of forming the insulator barrier layer near the transparent conduction film. Also, the structure with the insulator thin barrier layer formed near the lower electrode, opposed to the ITO film, solves the interface problem of the ITO film because it provides an improved photo current/dark current ratio.

• Korean Journal of Materials Research
• /
• v.9 no.1
• /
• pp.73-80
• /
• 1999

The effect of alloy compositions of the bond coating on the plasma sprayed-thermal barrier coatings was investigated. The performance of the coating composed of Rene80/NiCrAl/ZrO$_2$-CeO$_2$-Y$_2$O$_3$ and Rene80/CoNiCrAlY/ZrO$_2$-CeO$_2$-Y$_2$O$_3$was evaluated by isothermal and thermal cyclic test in an ambient atmosphere at 115$0^{\circ}C$. The failure of Rene80/NiCrAl/ZrO$_2$-CeO$_2$-Y$_2$O$_3$ coatings was occurred at the bond coating/ceramic coating interface while Rene80/CoNiCrAlY/ZrO$_2$-CeO$_2$-Y$_2$O$_3$ coating was failed at the substrate/bond coating interface after thermal cyclic test. The lifetime of Rene80/NiCrAl/ZrO$_2$-CeO$_2$-Y$_2$O$_3$coatings was longer than Rene80/CoNiCrAlY/ZrO$_2$-CeO$_2$-Y$_2$O$_3$coating. The oxidation rate of the NiCrAl bond coating examined by TGA was lower than CoNiCrAlY bond coatings. In summary, these results suggest that Rene80/CoNiCrAlY/ZrO$_2$-CeO$_2$-Y$_2$O$_3$system as thermal barrier coating be not suitable considering the durability of the coating layer for high temperature oxidation and thermal stress.

• Journal of the Korean Ceramic Society
• /
• v.34 no.1
• /
• pp.88-94
• /
• 1997

The oxidation behavior of the NiCrAlY bond coat and thermal fatigue failure in the plasma-sprayed thermal barrier coating system, ZrO2.8wt%Y2O3 top coat/Ni-26Cr-5Al-0.5Y bond coat/Hastelloy X superalloy substrate, in commercial use for finned segment of gas turbine burner were investigated. The main oxides formed in the bond coat were NiO, Cr2O3, and Al2O3. It divided the oxide distribution at this interface into two types whether an Al2O3 thin layer existed beneath ZrO2/bond coat interface before operation at high temperature or not. While a continuous layer of NiO was formed mainly in the region where the Al2O3 thin layer was present, the absence of it resulted in the formation of mixture of Cr2O3 and Al2O3 beneath NiO layer. Analyses on the fracture surface of specimen spalled by thermal cycling showed that spalling occurred mainly along the ceram-ic coat near ZrO2/bond coat oxide layer interface, but slightly in the oxide layer region.

• Current Photovoltaic Research
• /
• v.3 no.3
• /
• pp.85-90
• /
• 2015

Two-step processes for preparing $Cu(In,Ga)Se_2$ absorber layers consist of precursor layer formation and subsequent annealing in a Se-containing atmosphere. Among the various deposition methods for precursor layer, the nonvacuum (wet) processes have been spotlighted as alternatives to vacuum-based methods due to their potential to realize low-cost, scalable PV devices. However, due to its porous nature, the precursor layer deposited on Mo substrate by nonvacuum methods often suffers from thick $MoSe_2$ formation during selenization under a high Se vapor pressure. On the contrary, selenization under a low Se pressure to avoid $MoSe_2$ formation typically leads to low crystal quality of absorber films. Although TiN has been reported as a diffusion barrier against Se, the additional sputtering to deposit TiN layer may induce the complexity of fabrication process and nullify the advantages of nonvacuum deposition of absorber film. In this work, Mo oxide layers via thermal oxidation of Mo substrate have been explored as an alternative diffusion barrier. The morphology and phase evolution was examined as a function of oxidation temperature. The resulting Mo/Mo oxides double layers were employed as a back contact electrode for $CuInSe_2$ solar cells and were found to effectively suppress the formation of $MoSe_2$ layer.

• Food Science and Preservation
• /
• v.20 no.5
• /
• pp.597-601
• /
• 2013

In this study, we searched for bioactive compounds from natural resources with a supercritical extract. We selected the extracts of Chrysanthemum zawadskii, Lufa cylindrica, Paeonia lactiflora, Gardenia jasminoides and Scutellaria baicalensis, as natural materials, and evaluated the effects of their skin barrier function. We found that these extracts increased the transactivation activity of the PPAR-responsive element (PPRE) and the anti-oxidation with different priorities, respectively. In addition, these extracts promoted the expression of proteins related to cornified envelope (CE) formation, such as involucrin. From these results, we suggest that natural materials from supercritical extracts will be pertinent candidates for the improvement of the epidermal permeability barrier function.

• Korean Journal of Metals and Materials
• /
• v.48 no.10
• /
• pp.901-906
• /
• 2010

The first stage blade of a gas turbine was operated under a severe environment which included both $1300^{\circ}C$ hot gas and thermal stress. To obtain high efficiency, a thermal barrier coating (TBC) and an internal cooling system were used to increase the firing temperature. The TBC consists of multi-layer coatings of a ceramic outer layer (top coating) and a metallic inner layer (bond coat) between the ceramic and the substrate. The top and bond coating layer respectively act as a thermal barrier against hot gas and a buffer against the thermal stress caused by the difference in the thermal expansion coefficient between the ceramic and the substrate. Particularly, the bondcoating layer improves the resistance against oxidation and corrosion. An inter-diffusion layer is generated between the bond coat and the substrate due to the exposure at a high temperature and the diffusion phenomenon. A thickness measurement result showed that the bond coat of the suction side was thicker than that of the pressure side. The thickest inter-diffusion zone was noted at SS1 (Suction Side point 1). A chemical composition analysis of the bond coat showed aluminum depletion around the inter-diffusion layer. In this study, we evaluated the properties of the bond coat and the degradation of the coating layer used on a $1300^{\circ}C$-class gas turbine blade. Moreover, the operation temperature of the blade was estimated using the Arrhenius equation and this was compared with the result of a thermal analysis.

• Polymer(Korea)
• /
• v.24 no.2
• /
• pp.237-244
• /
• 2000

Phenolic resin used as a precursor of carbonized matrix for carbon-carbon composites was modified by addition of molybdenum disilicide (MoSi$_2$) in various concentrations of 0, 4, 12 and 20% by weight to improve the anti-oxidation properties of the composites. The green body was manufactured by a prepreg method and was submitted to carbonization up to 110$0^{\circ}C$. In this work, the oxidation behavior of carbon-carbon composites with MoSi$_2$ as an oxidation inhibitor was investigated at the temperature range of 600-100$0^{\circ}C$ in an air environment. The carbon-carbon composites with MoSi$_2$ showed a significantly improved oxidation resistance due to both the reduction of the porosity formation and the formation of mobile diffusion barrier for oxygen when compared to those without MoSi$_2$. Carbon active sites should be blocked, decreasing the oxidation rate of carbon. This is probably due to the effect of the inherent MoSi$_2$ properties, resulted from a formation of the protective layer against oxygen attack in the composites studied.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2010.08a
• /
• pp.171-171
• /
• 2010

In this work, we investigated the effect of the oxidation temperature on the unipolar and bipolar resistance switching behaviors of the oxidized TiO-x films. TiOx films on Pt electrodes were fabricated by the oxidation of Ti films at $550^{\circ}C$ for 1 to 3 hours. The unipolar and bipolar resistance switching properties were investigated with the oxidation temperature and time. Also, the crystal structure and the physical properties such as chemical bonding states of TiOx layers were characterized in addition to the resistance switching characteristics. The resistance switching behaviors of TiOx films oxidized at above $450^{\circ}C$ and below $650^{\circ}C$ was shown. So, we investigated that the resistance switching behaviors of TiOx films oxidized at $550^{\circ}C$ with the oxidation time from 1 to 3 hour. The memory windows of unipolar switching in the oxidized TiOx films were reduced with increasing the oxidation time, but those of the bipolar switching were slightly enlarged. The enlargement of rutile TiO2 peak with increasing the oxidation time and temperature was studied by X-ray diffraction. An increase of non-lattice oxygen and Ti3+ in the TiOx films with the oxidation times was investigated by X-ray photoemission spectroscopy. It was expected that the uipolar and bipolar resistive switching of the oxidized TiOx film was strongly related with the migration of non-lattice oxygen anions and schottky barrier height, respectively.

• Journal of Soil and Groundwater Environment
• /
• v.17 no.2
• /
• pp.15-21
• /
• 2012

MTBE (Methyl tertiary-butyl ether) has been commonly used as an octane enhancer to replace tetraethyl lead in gasoline, because MTBE increases the efficiency of combustion and decreases the emission of carbon monoxide. However, MTBE has been found in groundwater from the fuel spills and leaks in the UST (Underground Storage Tank). Fenton's oxidation, an advanced oxidation catalyzed with ferrous iron, is successful in removing MTBE in groundwater. However, Fenton's oxidation requires the continuous addition of dissolved $Fe^{2+}$. Zero-valent iron is available as a source of catalytic ferrous iron of MFO (Modified Fenton's Oxidation) and has been studied for use in PRBs (Permeable Reactive Barriers) as a reactive material. Therefore, this study investigated the condition of optimization in MFO-PRBs using waste zero-valent iron (ZVI) with the waste steel scrap to treat MTBE contaminated groundwater. Batch tests were examined to find optimal molar ratio of MTBE : $H_2O_2$ on extent to degradation of MTBE in groundwater at pH 7 with 10% waste ZVI. As the results, the ratio of optimization of MTBE to hydrogen peroxide for MFO was determined to be 1:300[mM]. The column experiment was conducted to know applicability of MFO-PRBs for MTBE remediation in groundwater. As the results of column test, MTBE was removed 87% of the initial concentration during 120days of operational period. Interestingly, MTBE was degraded not only within waste ZVI column but also within sand column. It means the aquifer may affect continuously the MTBE contaminated groundwater after throughout the waste ZVI barrier. The residual products showed acetone, TBF (Tert-butyl formate) and TBA (Tert-butyl acetate) during this test. The results of the present study showed that the recycled materials can be effectively used for not only a source of catalytic ferrous iron but also a reactive material of the MFO-PRBs to remove MTBE in groundwater.