• Applied Chemistry for Engineering
• /
• v.17 no.2
• /
• pp.150-157
• /
• 2006

The alternate plating method was suggested by a tin-cobalt alloy plating process which has excellent mechanical characteristics and also favorable to environment. Tin-cobalt alloy plating has many advantages such as nontoxicity, variable color-tone, and no post-treatment process. In this study, the plating conditions such as temperature, pH, current density, plating time, and amount of additive (glycine) were determined in the tin-cobalt alloy plating process through Hull-cell test and surface analysis. As the result of Hull-cell analysis, brightness became superior as the amount of glycine increased. It was found that the optimum alloy ratio was 0.03 M of $SnCl_{2}{\cdot}2H_{2}O$ and 0.05 M of $CoSO_{4}{\cdot}7H_{2}O$ at $50^{\circ}C$, pH 8.5, and $0.5A/dm^2$. The optimum amount of additive was 15 g/L of glycine and 0.1 g/L of organic acid. Then, the solution including glycine was recommended as an optimum plating solution for a chromium plating process.

• Journal of the Korean institute of surface engineering
• /
• v.47 no.5
• /
• pp.269-274
• /
• 2014

Electroless plating process as a solution deposition method is a viable means of preparing conductive metal films on non-conducting substrates through chemical reactions. In the present study, the preparation and properties of electroless Ni-plating on flexible silicone rubber are described. The process has been performed using a conventional Ni(P) chemical bath. Additives and complexing agents such as ammonium chloride and glycine were added and the reaction pH was controlled by NaOH aqueous solution. Ni deposition rate and crystallinity have been found to vary with pH and temperature of the plating bath. It was shown that Ni-films having the high crystallinity, enhanced adhesion and optimum electric conductivity were formed uniformly on silicone rubber substrates under pH 7 at $70^{\circ}C$. The conductive Ni-plated silicone rubber showed a high electromagnetic interference shielding effect in the 400 MHz-1 GHz range.

• Journal of environmental and Sanitary engineering
• /
• v.17 no.3
• /
• pp.37-45
• /
• 2002

The Purpose of this study is to reduce environmental problems caused by landfill of bituminous coal fly ash emitted from the power plant and to reuse it. First of all, we experimented that Al and Si elements were extracted from fly ash and investigated that extracted Al and Si elements night use a coagulant. The extraction was carried out under various conditions ; concentration of the extraction solution, calcination temperature and calcination time. As the results, it was found that the optimum conditions of the extraction of Al and Si elements from fly ash were as follows, concentration of NaOH was 5N for both of them, calcination temperature was $700^{\circ}C$ and $600^{\circ}C$ and calcination time was 1hr and 1.5hr, respectively The extracted solution was used as a coagulant to treat the diluted metal-plating solutions which contained Pb and Cu, respectively. As the result of treatment on the diluted Pb-plating solution with 315NTU, the removal efficiency of turbidity was more than 90%, and the removal efficiency of Pb was about 80%. As for treatment of the non-turbid diluted Cu-plating solution, the removal efficiency of Cu was about 98%.

• Journal of the Korean institute of surface engineering
• /
• v.24 no.4
• /
• pp.206-214
• /
• 1991

In the basic study of selective electroless Ni plating of Si wafers, plating rate and physical properties are investigated to obtain optimum conditions of contact hole filling. Si wafers are excellently activated in the concentration of 0.5M IF, 1mM PdCl2, 2mM EDTA at $70^{\circ}C$, 90sec. The optimum condition of Ni-B deposition on p-type Si wafers is 0.1M NiSO4, 0.11M Citrate, $70^{\circ}C$, pH6.8, 8mM DMAB. The main factor in the sheet resistences variation of films is amorphous and on heat treating matrix was transformed into a stable phase (Ni+Ni3B) at $300-400^{\circ}C$. But pH or DMAB concentration in the plating solution doesn't play role of heat-affected phase change.

• Korean Chemical Engineering Research
• /
• v.45 no.4
• /
• pp.384-390
• /
• 2007

In this study, electroless plating of copper was performed on PET film by using the blend of supercritical $CO_2$ and plating solution. The optimum volumetric ratio of supercritical fluid and plating solution was found to be 1:9 and dispersion property was poor at $CO_2$ vol% langer than 10%. Electroless plating of copper was best at $25^{\circ}C$ and 15 MPa. Role of added supercritical $CO_2$ is not to increase solubility but to disperse and maintain Cu-particles as the 1st particles.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2000.11a
• /
• pp.1-2
• /
• 2000

In chip plating, several parameters must be taken into consideration. Current density, solution concentration, pH, solution temperature, components volume, chip and media ratio, barrel geometrical shape were most likely found to have an effect to the process yields. The 3 types of barrels utilized in chip plating industry are the onventional rotating barrel, vibrational barrel(vibarrel), and the centrifugal type. Conventional rotating barrel is a close type and is commonly used. The components inside the barrel are circulated by the barrel's rotation at a horizontal axis. Process yield has known to have higher thickness deviation. The vibrational barrel is an open type which offers a wide exposure to electrolyte resulting to a stable thickness deviation. It rotates in a vertical axis coupled with multi-vibration action to facilitate mixed up and easy transportation of components. The centrifugal barrel has its plated work centrifugally compacted against the cathode ring for superior electrical contact with simultaneous rotary motion. This experiment has determined the effect of barrel vibration intensity to the plating thickness distribution. The procedures carried out in the experiment involved the overall plating process., cleaning, rinse, Nickel plating, Tin-Lead plating. Plating time was adjusted to meet the required specification. All other parameters were maintained constant. Two trials were performed to confirm the consistency of the result. The thickness data of the experiment conducted showed thatbthe average mean value obtained from higher vibrational intensity is nearer to the standard mean. The distribution curve shown has a narrower specification limits and it has a reduced variation around the target value. Generally, intensity control in vi-barrel facilitates mixed up and easy transportation of components. However, it is desirable to maintain an optimum vibration intensity to prevent solution intrusion into the chips' internal electrode. A cathodic reaction can occur in the interface of the external and internal electrode. 2H20 + e $\rightarrow$M/TEX> 20H + H2.. Hydrogen can penetrate into the body and create pressure which can cause cracks. At high intensity, the chip's motion becomes stronger, its contact between each other is delayed and so plating action is being controlled. However, the strong impact created by its collision can damage the external electrode's structure there by resulting to bad plating condition.

• Journal of the Korean institute of surface engineering
• /
• v.26 no.5
• /
• pp.263-270
• /
• 1993

The effects of surfactants on electorless copper plating bath for PCB was studied. Basic bath composition was cuplic sulfate 10g/l, EDTA.2Na 40 g/l, formalin$ 3m\ell$/l and sodium hydroxide solution for pH adjust. After addition of accelerators, stabilizers and surfactants, the polarization curves in plating bath were carried out for presumption of the plating rate. From the plating rate in bath with the various concentration of additives, the optimum condition for manufacturing the electroless copper plating bath was confirmed. It was found that the addition of $\alpha$.$\alpha$'-dipyridyl, pyridine and polyxyethylene octylphenylether was good as stabilizer, accelerator and surfactants, respectively. With this additives, the maximum plating rate of $12\mu\textrm{m}$/h at $65^{\circ}C$ and $2\mu\textrm{m}$/h at $25^{\circ}C$ was obtained.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 1999.10a
• /
• pp.15-15
• /
• 1999

In chip plating, several parameters must be taken into consideration. Current density, solution concentration, pH, solution temperature, components volume, chip and media ratio, barrel geometrical shape were most likely found to have an effect to the process yields. The 3 types of barrels utilized in chip plating industry are the conventional rotating barrel. vibrational barrel (vibarrel), and the centrifugal type. Conventional rotating barrel is a close type and is commonly used. The components inside the barrel are circulated by the barrel's rotation at a horizontal axis. Process yield has known to have higher thickness deviation. The vibrational barrel is an open type which offers a wide exposure to electrolyte resulting to a stable thickness deviation. It rotates in a vertical axis coupled with multi-vibration action to facilitate mixed up and easy transportation of components, The centrifugal barrel has its plated work centrifugally compacted against the cathode ring for superior electrical contact with simultaneous rotary motion. This experiment has determined the effect of barrel vibration intensity to the plating thickness distribution. The procedures carried out in the experiment involved the overall plating process., cleaning, rinse, Nickel plating, Tin-Lead plating. Plating time was adjusted to meet the required specification. All other parameters were maintained constant. Two trials were performed to confirm the consistency of the result. The thickness data of the experiment conducted showed that the average mean value obtained from higher vibrational intensity is nearer to the standard mean. The distribution curve shown has a narrower specification limits and it has a reduced variation around the target value, Generally, intensity control in vi-barrel facilitates mixed up and easy transportation of components, However, it is desirable to maintain an optimum vibration intensity to prevent solution intrusion into the chips' internal electrode. A cathodic reaction can occur in the interface of the external and internal electrode. $2HD{\;}+{\;}e{\;}{\rightarrow}20H{\;}+{\;}H_2$ Hydrogen can penetrate into the body and create pressure which can cause cracks. At high intensity, the chip's motion becomes stronger, its contact between each other is delayed and so plating action is being controlled. However, the strong impact created by its collision can damage the external electrode's structure thereby resulting to bad plating condition. 1 lot of chip was divided into two equal partion. Each portion was loaded to the same barrel one after the other. Nickel plating and tin-lead plating was performed in the same station. Portion A maintained the normal barrel vibration intensity and portion B vibration intensity was increased two steps higher. All other parameters, current, solution condition were maintained constant. Generally, plating method find procedures were carried out in a best way to maintained the best plating condition. After plating, samples were taken out from each portion. molded and polished. Plating thickness was investigated for both. To check consistency of results. 2nd trial was done now using different lot of another characteristics.

• Journal of Power System Engineering
• /
• v.5 no.2
• /
• pp.71-78
• /
• 2001

Using sodium hypophosphite as reducing agent, bath composition and plating condition of electroless copper plating on plating rate have been studied. The followings were determined as optimum, bath composition; $CuSO_4\;0.025M,\;NiSO_4\;0.002M,\;NaH_2PO_2\;0.4M$, sodium citrate 0.06M, $H_3BO_3$ 0.6M, thiourea or 2-MBT $0.2mg/{\ell}$, and operation conditions; pH $9{\sim}10$ at bath temperature rage of $60{\sim}70^{\circ}C$. A small amount of nickel ion($Ni^{2+}/Cu^{2+}$=0.002/0.025) to the hypophosphite reduced solution promotes autocatalysis and continuous plating. An additive such as thiourea or 2-MBT of a small amount($0.2mg/{\ell}$) can be used to stabilize the solution without changing plating rate much. The attivation energy between $20^{\circ}C\;and\;70^{\circ}C$ were calculated to be 11.3kcal/mol for deposition weight. Plating reaction had been ceased by the adjustment of pH above 13, temperature higher than $90^{\circ}C\;and\;under\;20^{\circ}C$. Deposited surface became worse in the case of increment of bath temperature above $80^{\circ}C$.

• Journal of the Korean institute of surface engineering
• /
• v.25 no.4
• /
• pp.189-206
• /
• 1992

The effect of activation and electroless nickel plating conditions on contact properties was investi-gated for selective electroless nickel plating of Si wafers in order to obtain an optimum condition of con-tact hole filling. According to RCA prosess, p-type silicon (100) surface was cleaned out and activated. The effects of temperature, DMAB concentration, time, and strirring were investigated for activation of p-type Si(100) surface. The optimal activation condition was 0.2M HF, 1mM PdCl2, 2mM EDTA,$ 70^{\circ}C$, and 90sec under ultrasonic vibration. In electroless nickel plating, the effect of temperature, DMAB concentra-tion, pH, and plating time were studied. The optimal plating condition found was 0.10M NiSO4.H2O, 0.11M Citrate, pH 6.8, $60^{\circ}C$, 30minutes. The contact resistance of films was comparatively low. It took 30minutes to obtain 1$\mu\textrm{m}$ thick film with 8mM DMAB concentration. The film surface roughness was improved with decreasing temperature and decreasing pH of the plating solution. The best quality of the film was obtained at the condition of temperature $60^{\circ}C$ and pH 6.0. The micro-vickers hardness of film was about 800Hv. Plating rate of nickel on the hole pattern was slower than that of nickel on the line pattern.