• The Journal of the Korea Contents Association
• /
• v.11 no.8
• /
• pp.468-474
• /
• 2011

Reducing agent was used as process variable for Pt catalyst production process. By using six sigma the optimum operating variables condition for particle size and ICP yield were deduced. With the help of fractional factorial design the major variables were reduction temperature and process time. Also, the optimum number of reduction process, reduction temperature, quantity of reducing agent and process time were 1, $67-88^{\circ}C$, 0.5 ml and 10minutes, respectively.

• Carbon letters
• /
• v.11 no.4
• /
• pp.332-335
• /
• 2010

The photodegradation of the model compounds Quinol, an aromatic organic compound and Acid blue FFS, an acid dye of chemical class Triphenylmethane was studied by using illumination with UV lamp of light intensity 250W. $TiO_2$ and $TiO_2$ doped with Boron and Nitrogen was used as catalyst. The sol-gel method was followed with titanium isopropoxide as precursor and doping was done using Boron and Nitrogen. In photocatalytic degradation, $TiO_2$ and doped $TiO_2$ dosage, UV illumination time and initial concentration of the compounds were changed and examined in order to determine the optimal experimental conditions. Operational time was optimized for 360 min. The optimum dosage of $TiO_2$ and BN doped $TiO_2$ was obtained to be 2 $mgL^{-1}$ and 2.5 $mgL^{-1}$ respectively. Maximum degradation % for quinol and Blue FFS acid dye was 78 and 95 respectively, at the optimum dosage of BN-doped $TiO_2$ catalyst. It was 10 and 4% higher than when undoped $TiO_2$ catalyst was used.

• Bulletin of the Korean Chemical Society
• /
• v.21 no.12
• /
• pp.1233-1238
• /
• 2000

$Mo/{\gamma}-Al_2O_3catalysts$ modified with Fe, Co, and Ni were prepared by impregnation method and catalytic activity for water gas shift reaction was examined. The optimum amount of Mo loaded for the reaction was 10 wt% $MoO_3$ to ${\gamma}-Al_2O_3.$ The catalytic activity of $MoO_3/{\gamma}-Al_2O_3was$ increased by modifying with Fe, Co, and Ni in the order of Co${\thickapprox}$ Ni > Fe. The optimum amounts of Co and Ni added were 3 wt% based on CoO and NiO to 10 wt% $MoO_3/{\gamma}-Al_2O_3$, restectively. The TPR (temperature-programmed reduction) analysis revealed that the addition of Co and Ni enganced the reducibility of the catalysts. The results of both catalytic activity and TPR experiments strongly suggest that the redox property of the catalyst is an important factor in water gas shift reaction on the sulfided Mo catalysts, which could be an evidence of oxy-sulfide redox mechanism.

• Journal of the Korean Chemical Society
• /
• v.68 no.2
• /
• pp.87-92
• /
• 2024

The commercialization of rechargeable metal-air batteries is extremely desirable but designing stable oxygen reduction reaction (ORR) catalysts with non-noble metal still has faced challenges to replace platinum-based catalysts. The nonnoble metal catalysts for ORR were prepared to improve the catalytic performance and stability by the thermal decomposition of ZIF-8 with optimum cobalt loading. The porous carbon was obtained by the calcination of ZIF-8 and different loading amounts of Co nanoparticles were anchored onto porous carbon forming a Co/PC catalyst. Co/PC composite shows a significant increase in the ORR value of current and stability (500 h) due to the good electronic conductive PCN support and optimum cobalt metal loading. The significantly improved catalytic performance is ascribed to the chemical structure, synergistic effects, porous carbon networks, and rich active sites. This method develops a new pathway for a highly active and advantageous catalyst for electrochemical devices.

• Journal of Korean Society of Water and Wastewater
• /
• v.13 no.3
• /
• pp.101-106
• /
• 1999

This research aims to compare immobilized catalysts prepared by various methods and determine suitable $TiO_2$ catalyst for water purification. Sol-gel method by Anderson and powder coation method by Tanaka ate famous in the methods to immobilize catalyst. Therefore, the $TiO_2$ catalyst for this research was prepared by sol-gel method and powder coating method. Its structure was tested by X-ray diffractometer (XRD), Scanning electron microseope (SEM). Durability of a catalyst-support couple in an solution was investigated. too. Experimental results were summarized as following; i) Optimum ratio of Ti : $H_2O$ : $H^+$ to obtain stable sol was 1 : 10 : 0.1 and the XRD patterns of $TiO_2$ film immobilized by sol-gel method which were fired at $700^{\circ}C$ showed that the catalyst had an anatase structure. ii) The particle size of $TiO_2$ prepared by sol-gel method was less than $5{\mu}$, but it was observed that coated side was not unifiom. iii) Sol-gel method was very effective to obtain $TiO_2$ catalyst of thin film, but spreadability and durability of a catalyst-support couple in a solution were than $TiO_2$ film immobilized by powder coating method. iv) The particle size of $TiO_2$ immobilized by powder coating method was a little larger than it prepared by sol-gel method, but spreadability and uniformity of $TiO_2$ film and durability of a catalyst-support couple in a solution were better than it immobilized by sol-gel method.

• Proceedings of the Korean Society of Propulsion Engineers Conference
• /
• 2005.11a
• /
• pp.266-271
• /
• 2005

An experimental investigation of a microthruster using hydrogen peroxide as a monopropellant is described. The study comprises of preparation method of silver as a catalyst and performance evaluation of a catalytic reaction chamber. Silver was reduced in $H_2$ environment at $500^{\circ}C$. The catalytic reaction chamber was tested to determine the optimum configuration of the catalyst bed. The catalyst bed was made of a glass wafer substrate sputtered with silver and had a length of 20 mm. The conversion rate was measured with various residence time, catalyst bed temperature, catalytic coated area.

• Bulletin of the Korean Chemical Society
• /
• v.35 no.6
• /
• pp.1687-1691
• /
• 2014

This study reports on the synthesis of carbon nanofibers via chemical vapor deposition using Co and Cu as catalysts. In order to investigate the suitability of their catalytic activity for the growth of nanofibers, we prepared catalysts for the synthesis of carbon nanofibers with Cobalt nitrate and Copper nitrate, and found the optimum concentration of each respective catalyst. Then we made them react with Aluminum nitrate and Ammonium Molybdate to form precipitates. The precipitates were dried at a temperature of $110^{\circ}C$ in order to be prepared into catalyst powder. The catalyst was sparsely and thinly spread on a quartz tube boat to grow carbon nanofibers via thermal chemical vapor deposition. The characteristics of the synthesized carbon nanofibers were analyzed through SEM, EDS, XRD, Raman, XPS, and TG/DTA, and the specific surface area was measured via BET. Consequently, the characteristics of the synthesized carbon nanofibers were greatly influenced by the concentration ratio of metal catalysts. In particular, uniform carbon nanofibers of 27 nm in diameter grew when the concentration ratio of Co and Cu was 6:4 at $700^{\circ}C$ of calcination temperature; carbon nanofibers synthesized under such conditions showed the best crystallizability, compared to carbon nanofibers synthesized with metal catalysts under different concentration ratios, and revealed 1.26 high amorphicity as well as $292m^2g^{-1}$ high specific surface area.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.21 no.5
• /
• pp.447-452
• /
• 2008

We synthesized nano-sized $La_{1-x}Sr_xCoO_3$ ($x=0.1{\sim}0.4$) cathode catalyst for the zinc air secondary batteries by citrate method, And we measured the cathode's electrochemical characteristics according to content of strontium compose the cathode catalyst. We controlled the pH of precursor solution by 10 in the process of manufacturing the precursor, We heat treated the prepared precursor at various calcination temperature ($500{\sim}900^{\circ}C$), and examined the optimum calcinations temperature by XRD analysis and electrochemical evaluation. We examined the ORR (oxygen reduction reaction) and OER (oxygen evolution reaction) performance of the prepared $La_{1-x}Sr_xCoO_3$ catalyst powder. When we consider ORR and OER performance simultaneously, $La_{0.7}Sr_{0.3}CoO_3$ catalyst has shown the best performance because of its lowest voltage deference between charge and discharge.

• Journal of Korean Society of Environmental Engineers
• /
• v.27 no.4
• /
• pp.402-408
• /
• 2005

This investigation aimed at selecting the optimum catalyst and reaction conditions used in Fenton oxidation for landfill leachate treatment and was carried out at ambient temperature using a lab-scale experiment. The investigation led to the following results: 1) The optimum pH and dose for each iron catalyst were as follows: $Fe^{2+}\;=\;1,200\;mg/L$, $H_2O_2\;=\;1,200\;mg/L$, initial pH=3.0; $Fe^{3+}\;=\;1,200\;mg/L$, $H_2O_2\;=\;1,500\;mg/L$, initial pH=4.5; $Fe^0\;=\;1,200\;mg/L$, $H_2O_2\;=\;900\;mg/L$, initial pH=4.0, respectively. 2) The progress of Fenton oxidation could be instrumentally monitored by measuring redox potential evolution during leachate oxidation, thus, indicating the possibility of an on-line process monitoring. 3) A simple acid-base titration of Fenton-treated leachate proved that a relevant fraction of by- products formed during the treatment was made of acidic compounds in the optimum reaction condition for each catalyst used, thus demonstrating that the higher the extent of Fenton oxidation the greater was the amount of acids formed. 4) With the aim of selecting the optimum catalyst among $Fe^0$, $Fe^{2+}$ and $Fe^{3+}$, removal efficiency of each parameter in the optimum reaction conditions was considered. Although $Fe^{3+}$ was higher than other catalysts($Fe^0$, $Fe^{2+}$) in removal efficiency, $Fe^0$ was a optimum catalyst with a view of cost effectiveness.

• Journal of the Korean GEO-environmental Society
• /
• v.17 no.10
• /
• pp.5-11
• /
• 2016

In this study, the factors affecting commercialization of $Pt/TiO_2$ catalyst, which can oxidize HCHO at room temperature, was investigated. In order to determine the optimum noble metal loading, the catalytic activity was evaluated by varying the Pt loadings; the best catalytic activity was achieved for 1 wt% of Pt. In addition, the catalyst prepared under the reduction condition showed an excellent HCHO oxidation conversion at room temperature. Based on these results, it was confirmed that the activity could be changed by oxidation state of active metal, and in case of Pt, metallic Pt ($Pt^0$) species was more active on HCHO oxidation at room temperature. As a result of evaluating an effect of space velocity to determine the optimum operating condition, it was found that in the lower space velocity, conversion rate of HCHO was increased due to increase of catalyst bed. Catalytic activity was greater in the presence of moisture than in its absence. Through above results, the key factors for commercialization of oxidation catalyst, which was operated at room temperature even without any additional energy source was confirmed.