• 한국안전학회지
• /
• 제19권4호
• /
• pp.8-13
• /
• 2004

The purpose of this paper is to investigate the welding residual stress distribution according to the constraint or non-constraint welding condition with titanium commonly using power station, aircraft, and ship. The measuring method of the residual stress was applied stress release rating method with strain gages and a potable strain meter. The x direction residual stress generally showed the tensile residual stress in case of res03int welding. On the other hand, the x direction residual stress under non-restraint welding were changed tensile stress into compressive stress on 15mm away from welding bead center. Also, the y direction residual stress generally showed the tensile residual stress in case of non-restraint welding and the y direction residual stress under restraint welding were changed tensile stress into compressive stress about 60mm away from welding bead center.

• Journal of Welding and Joining
• /
• 제10권2호
• /
• pp.43-50
• /
• 1992

This study was aimed at resolving uncertainties about lamellar tearing initiation temperatures and studying the effect of nonmetallic inclusions on the tear initiation. In order to measure the lamellar tearing initiation temperature, the slice bend test was conducted in the temperature range of 20.deg.C to 425.deg.C on A572 Grade 50 and A588 Grade A steels. In addition, the weld restrain test was carried out to measure directly the tear initiation temperature with A572 steel. In slice bend tests, A572 steel showed the most susceptible region to lamellar tearing to be in the range of 100 to 300.deg.C, where the steel showed the minimum ductility. The observed tear initiation by the weld restraint test was to be in the range of 200to 300.deg.C. The tears became narrower and less rounded at the susceptible temperatures. It was confirmed in this study that lamellar teraring initiated during cooling from welding in the range of 200 to 300.deg.C and they were initiated by strain aging embrittlement.

• 수산해양기술연구
• /
• 제36권4호
• /
• pp.329-336
• /
• 2000

정치망 어선에 사용하는 더블 캡스턴 드럼의 용접공정은, 순간적으로 집중투입되는 고온열원에 의해 상당 열응력과 열변형 거동이 시간의 경과에 따라 비정상적으로 발생한다. 유한요소법으로 이것들의 거동을 해석한 후 다음과 같은 결론을 얻었다. 1) 용접 초기에는 용접열원 위치에서 54∼48MPa의 상당 열응력을 나타내고, 캡스턴 드럼의 내부로 진행될수록 42∼18Mpa 정도의 열응력 분포를 보이며, 열응력 구배는 1mm당 3.6MPa의 기울기를 형성하고 있었다. 용접열원에서 0.004∼0.015mm정도의 미세한 변형량이 계산되었고 좌측 자유단으로 진행하면서 0.03∼0.033mm의 변형량은 용접초기에 열충격 현상으로 발생한 것으로 사료되므로 이에 대한 대비책이 있어야 한다. 2) 용접 중반부에서는 상당 열응력 크기는 용접 초기보다 다소 작아져서 최대 51MPa, 최소 11.3MPa을 보여주며 열응력 기울기도 다소 완화된다. 이것은 용접 열원이 이동하면서 발생하는 예열효과로 상당 열응력이 감소한 것으로 사료된다. 상당 열변형의 크기는 최대 0.04mm, 최소 0.0045mm 정도를 형성하고 있고, 용접열원의 진행으로 전체적인 변형 양상이 용접진행 방향과 동일하게 이동하고 있다. 3) 용접공정의 후반부는 상당 열변형량이 최소 0.005mm, 최대 0.045mm 정도이므로, 정밀한 용접가공을 위해 반대방향에 지그나 고정구를 설치해야 한다. 상당 열응력의 구배는 모재 내부로 진행된 양상을 보이고 있으나 열응력의 절대 크기는 최소 3MPa에서 최대 27MPa로 작아졌다. 이 것은 용접의 이동열원이 제거됨으로서 모재 내부의 열응력이 현저히 저하되었음을 의미하지만, 잔류 열응력이 존재하므로 뜨임처리와 같은 후처리가 요망된다.