• Journal of the Korean Society of Hazard Mitigation
• /
• v.4 no.4 s.15
• /
• pp.1-6
• /
• 2004

Fatigue tests were carried out for butt welded joints with SM520-TMC steel plate with thickness between 20mm and 80mm. The test results were analysed statistically and the effect of plate thickness on the fatigue strength investigated. The fatigue strengths based on nominal stress range satisfy the requirement of the standards. Due to misalignment of the specimens, the measured stresses are higher than the nominal stresses especially for 20mm thick plates. If fatigue strengths are evaluated based on the measured stresses, then the fatigue strengths are greater than those based on nominal stresses. The results show that the thickness effect is similar to the formula proposed by Gurney.

• Journal of Ocean Engineering and Technology
• /
• v.10 no.3
• /
• pp.24-33
• /
• 1996

Up to now, most of studies on mechanical properties in friction welded components are about tensile and bending strength. However the fatigue studies on the friction-welded components subjected to repeated stress are not available. The purposes of this study are the development of fundamental design and the development of in-process real-time weld quality evaluation technique by acoustic emission for the bar-to-bar dissimilar friction welding of hydraulic valve spool steels.

• Journal of the Korean Society for Heat Treatment
• /
• v.33 no.4
• /
• pp.161-172
• /
• 2020

The tensile property of A5082 and A6060 aluminium wrought alloys was investigated, in terms of the strain rate sensitivity on alloy conditions by heat treatment and bake hardenability on pre-strain prior to strain ageing. The tensile test was carried out in a range of strain rate of 4.17 × 10^-5 s^-1 ~ 4.17 × 10^-5 s^-1 in room temperature and the nominal range of pre-strain was 3.0 ~ 10.5%. The tensile deformation of A5082 alloys is characterized as typical case of dynamic strain ageing with negative strain rate sensitivity for all conditions, and the tensile strength indicates a similar level regardless of alloy conditions, except only in full annealed condition. The stress-relief annealing on A6060 alloys can induce practical decrease in strength level of over approximately 100 MPa without any ductility loss, compared to as-rolled condition, while a full annealed and aged condition leads remarkable strengthening effect with the decrease of tensile elongation. Additionally, the bake hardenability of A5082 alloy by strain ageing indicates a negative dependence upon the increase of pre-strain, while A6060 alloy exhibits a positive sign even in low level relatively compared with conventional SPCC.

• Composites Research
• /
• v.17 no.2
• /
• pp.34-39
• /
• 2004

In this paper, a modified and representative unit cell model was employed to study the tensile behaviour of closed-cell metallic foams with varying spatial density distribution as well as material imperfections. The density variation was assumed to follow a statistical probability distribution of the Gaussian type. A multiple cell finite element model, utilising the modified unit cell, was developed. The model exhibits deformation patterns similar to those observed in tensile testing. The nominal stress-strain curve obtained from quasistatic tensile of the foam was compared with experimental findings and was found to be in good agreement in the scheme of maximum strength only if the appropriate density distribution and volume fraction of internal imperfections are taken into account. Moreover, maximum tensile strength of the aluminium foam was found to be more sensitive to the volume fraction of imperfection than standard deviation of the density.

• Journal of Korean Society of Steel Construction
• /
• v.13 no.1
• /
• pp.19-28
• /
• 2001

The strength and ductility of steel flexural members are investigated experimentally in this study. As for the performance evaluation of flexural members. experimental studies on the 9 test specimens were carried out. Four specimens were fabricated from SM490 and five specimens were fabricated from SM570. The experimental results of the specimens were analyzed with focus on the flexural strength and ductility. The experimental results exhibited that all the specimens provided sufficient flexural strengthes which exceeded the nominal flexural strengthes specified in the current Limit State Design Specification by average ratio of 1.22. However. the experimental results showed that the compact-section specimens fabricated from SM570 did not provide the required rotational ductility. The yield-to-tensile strength ratio(YR) of SM570 of about 0.9 might be the causes of such insufficient capacities.

• Journal of Korean Association for Spatial Structures
• /
• v.21 no.2
• /
• pp.49-56
• /
• 2021

The damage to non-structural elements in buildings has been increasing due to earthquakes. In Korea, post-installed anchors produced overseas have been mainly used for seismic anchorage of non-structural components to structures. Recently, a new cast-in-place concrete insert anchor installed in concrete without drilling has been developed in Korea. In this paper, an experimental study was conducted to evaluate the tensile and shear strengths of the newly developed anchor under monotonic load. The failure modes of the tension specimens were divided into concrete breakout failure and steel failure, and all shear specimens showed steel failure. In both tension and shear, the maximum loads of specimens were greater than the nominal strengths predicted by the concrete design code (KDS 14 20 54). As a result, it is expected that the current code can also be used to calculate the strength of the developed cast-in anchor.

• Transactions of Materials Processing
• /
• v.8 no.3
• /
• pp.233-233
• /
• 1999

To investigate the effect of tungsten addition on mechanical properties, we prepared refractory (62χ)Nb-18Si-l00Mo-l0Ti-χW (χ=0, 5, 10 and 15 mol.%) in-situ composites by the conventional arc-casting technique, and then explored the microstructure, hardness and elastic modulus at ambient temperature and tensile properties at 1670 K. The microstructure consists of relatively fine (Nb, Mo, W, Ti)/sub 5/Si₃, silicide and a Nb solid solution matrix, and the fine eutectic microstructure becomes predominant at a Si content of around 18 mol.%. The hardness of (Nb, Mo, W, Ti(/sub 5/Si₃, silicide in a W-free sample is 1680 GPa, and goes up to 1980 GPa in a W 15 mol.% sample. The hardness, however, of Nb solid solution does not exhibit a remarkable difference when the nominal W content is increased. The elastic modulus shows a similar tendency to the hardness. The optimum tensile properties of the composites investigated are achieved at W 5 mol.% sample, which exhibits a relatively good ultimate strength of 230 MPa and an excellent balance of yield strength of 215 MPa, and an elongation of 3.7%. The SEM fractography generally indicates a ductile fracture in the W-free sample, and a cleavage rupture in W-impregnated ones.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2004.05a
• /
• pp.640-643
• /
• 2004

Synthetic lightweight aggregates are manufactured with recycled plastic and fly ash with 12 percent carbon. Nominal maximum-size aggregates of 9.5mm were produced with fly ash contents of 0 percent, 35 percent, and 80 percent by total mass of the aggregate. An expanded day lightweight aggregate and a normal-weight aggregate were used as comparison. Mechanical properties of the concrete determined included density, compressive strength, elastic modulus, and splitting tensile strength. Compressive and tensile strengths were lower for the synthetic aggregates; however, comparable fracture properties were obtained. Relatively low compressive modulus of elasticity was found for concretes with the synthetic lightweight aggregate, although high ductility was also obtained. As fly ash content of the synthetic lightweight aggregate increased, all properties of the concrete were improved.

• Journal of the Korea Concrete Institute
• /
• v.27 no.1
• /
• pp.11-20
• /
• 2015

An unbonded post-tensioned anchor using a 15.2 mm diameter 7-wire strand was developed based on finite element analysis and experimental testing. In order to evaluate its performance, static load tests and load transfer tests were conducted following KCI-PS101. The static load tests and additional strand tensile tests confirmed that the developed anchor had a capacity more than nominal tensile strength of a 7-wire strand without any damage or deterioration. According to the result of load transfer tests for many different reinforcing details, specimens with no additional reinforcing bars sustained at least 1.64 times the nominal tensile strength of the strand.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.21 no.1
• /
• pp.129-137
• /
• 2020

In designing a high strength bolted beam splice using steel for building structures, it is necessary to present the appropriate steel grade selection criteria for how to determine the cover plate steel grade. This study examined the difference in tensile behavior according to the steel grades through static tensile tests simulating the beam member high strength bolt joints flange. For this purpose, the specimens were designed and fabricated with the main variables, such as the thickness, steel grade and the strength of flange and cover plate, which are expected to affect the splice strength and behavior. The tensile test results for a total of 48 specimens showed that the tensile-load capacity exceeded the design tensile strength applied with a nominal strength of steel in all specimens. When the design strength of the cover plate exceeded 1.25 times that of the flange plate, the flange plate governed the behavior of splice. The change in maximum tensile load due to the change in flange steel grade is not very large, but there is a difference in deformation. The test results confirmed that the steel grade and thickness of the cover plate were the main factors affecting the beam splice behavior.