• Journal of the Korean Society for Heat Treatment
• /
• v.21 no.4
• /
• pp.219-224
• /
• 2008

• Korean Journal of Metals and Materials
• /
• v.47 no.10
• /
• pp.629-634
• /
• 2009

The effects of processing parameters on the surface properties of the hardened layers processed by the low temperature plasma nitrocarburizing and the low temperature two-step plama treatment (carburizing+nitriding) were investigated. The nitrogen-enriched expanded austenite structure (${\gamma}_N$) or S phase was formed on all of the treated surface. The surface hardness reached up to 1200 $HV_{0.025}$, which is about 5 times higher than that of untreated sample (250 $HV_{0.1}$). The thickness of hardened layer of the low temperature plasma nitrocarburized layer treated at $400^{\circ}C$ for 40 hour was only $15{\mu}m$, while the layer thicknesss in the two-step plama treatment for the 30 hour treatment increased up to about $30{\mu}m$. The surface thickness and hardness increased with increasing treatment temperature and time. In addition, the corrosion resistance was enhanced than untreated samples due to a high concentration of N on the surface. However, higher treatment temperature and longer treatment time resulted in the formation of $Cr_2N$ precipitates, which causes the degradation of corrosion resistance.

• Corrosion Science and Technology
• /
• v.6 no.5
• /
• pp.251-256
• /
• 2007

Plasma nitriding is a surface treatment process which is increasingly used to improve wear, fatigue and corrosion resistance of industrial parts. Active screen plasma nitriding (ASPN) has both the advantages of the classic cold wall and the hot wall conventional dc plasma nitriding (DCPN) method and the parts to be nitrided are no longer directly exposed to the plasma. In this study, AS plasma nitriding has been used to nitride the UNS S31803 duplex stainless steel, AISI 304 and AISI 316 austenitic stainless steel, and AISI 420 martensitic stainless steel. Treated specimenswere characterized by means of microstructural analysis, microhardness measurements and electrochemical tests in NaCl aerated solutions. Hardness of the nitride cases of AISI 420 stainless steel by Knoop test can get up to 1300 HK0.1. From polarization tests, the corrosion current densities of AISI 420 and UNS S31803specimens ASPN at $420^{\circ}C$ were generally lower than those of their untreated substrates. The corrosion resistance of UNS S31803 duplex stainless steel can be enhanced by plasma nitriding at $420^{\circ}C$ Cowing to the formation of the S-phase.

• Korean Journal of Materials Research
• /
• v.9 no.11
• /
• pp.1102-1107
• /
• 1999

FeAl matrix composite was fabricated successfully by hot-pressing. The mechanical properties of FeAl alloys have been widely studies, but their behaviors of surface hardening effect by plasma nitriding has not yet been studied. This study was to analysis the relationship between microstructure of the sintered composite by hot-pressing and surface hardening at plasma nitriding treatment. Surface hardening of FeAl base alloys was improved by plasma nitriding with increasing plasma treatment time. Excellent surface hardness in the FeAl alloys could be obtained by plasma nitriding($\textrm{H}_{\textrm{v}}$ 100gf, diffusion layer: 1100~1450kg/$\textrm{mm}^2$, matrix : 330~360kg/$\textrm{mm}^2$). Diffusion layer size increased with increasing plasma nitriding times and decreased with increasing Sic, content.

• Journal of the Korean Society for Heat Treatment
• /
• v.21 no.5
• /
• pp.265-273
• /
• 2008

• Journal of the Korean Society for Heat Treatment
• /
• v.14 no.1
• /
• pp.8-16
• /
• 2001

The effects of gas composition, pressure, temperature and time on the case thickness, hardness and nitride formation in the surface of tool steels(STD11 and STD61) have been studied by micro-pulse plasma nitriding. External compound layer and internal diffusion layer and the diffusion layer were observed in the nitrided case of tool steels. The relative amounts and kind of phases formed in the nitrided case changed with the change of nitriding conditions. Generally, only nitride phases such as ${\gamma}(Fe_4N)$, ${\varepsilon}(Fe_{2-3}N)$, or $Cr_{1.75}V_{0.25}N_2$ phases were detected in the compound layer, while nitride and carbide phases such as ${\varepsilon}-nitride(Fe_{2-3}N)$, $(Cr,Fe)_{\gamma}C_3$ or $Fe_3C$ were detected in the diffusion layer by XRD analysis. The thickness of compound layer increased with the increase of nitrogen content in the gas composition. Maximum case depth was obtained at gas pressure of 200Pa.

• Journal of the Korean Society for Heat Treatment
• /
• v.8 no.3
• /
• pp.187-196
• /
• 1995

TiN and AlN are ceramic materials with mechanical and chemical properties for use in structural applications at elevated temperature. The purpose of this research is to develop the technology for the synthesis of (Ti, Al)N power, which shows simultancously the excellent properties of TiN and AlN, from the mixed powder($Ti_{0.25}Al_{0.75}$, $Ti_{0.5}Al_{0.5}$ and $Ti_{0.75}Al_{0.25}$) by the direct nitriding method. The effects of variables such as temperature, mixing ratio of Al to Ti in raw material were investigated. The(Ti, Al)N powder can be easily synthesized from the mixed powder by the direct nitriding method. Among the mixed powdres, the nitriding behavior decreased with increasing the ratio of Al to Ti. This behavior is well explained by the nitriding mechanism presented in this research.

• Journal of the Korean Society for Heat Treatment
• /
• v.9 no.3
• /
• pp.219-227
• /
• 1996

The purpose of this research is to develop the technology for the synthesis of (Ti,Al)N powder, which shows simultaneously the excellent properties of TiN and AlN, from the Ti-Al intermetallic compounds by the direct nitriding method. The effects of variables such as temperature, Ti-Al intermetallic compounds ($TiAl_3$, TiAl and $Ti_3Al$) were investigated by TG, XRD and SEM. The (Ti,Al)N powder can be easily synthesized from the intermetallic compounds by the direct nitriding method. Among the intermetallic compounds, the nitriding behavior increased with TiAl> $Ti_3Al$ > $TiAl_3$, as the difference of diffusion coefficient for nitrogen in each materials. The ternary nitride such as $Ti_2AlN$ and $Ti_3Al_2N_2$ can be synthesized by the direct nitriding method, although the ternary nitride coexist with TiN and AlN. The ternary nitrides are stable below $1400^{\circ}C$, but these are gradually decomposed into TiN and AlN above $1400^{\circ}C$.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2015.11a
• /
• pp.289-290
• /
• 2015

In this experiment, nitriding treatment has been performed at $400^{\circ}C$ with various $N_2$ content and with changing processing time on AISI 420 martensitic stainless steel to investigate the expanded martensite layer (${\alpha}^{\prime}_N$ layer) formation behavior. Nitriding was implemented with changing $N_2$ content from 10% to 25% for 15 hrs and processing time was changed from 4hr to 15hr at 25% $N_2$ content. After treatment, the behavior of the ${\alpha}^{\prime}_N$ layer was investigated by optical microscopy, X-ray diffraction, and micro-hardness testing. Potentiodynamic polarization test was also used to evaluate the corrosion resistance of the samples. It was found that the surface hardness and ${\alpha}^{\prime}_N$ layer thickness increases with increasing $N_2$ percentage and processing time. Although their corrosion behaviors are worse than the bare sample.

• Journal of the Korean Society for Heat Treatment
• /
• v.11 no.4
• /
• pp.258-267
• /
• 1998

For the purpose of investigating the growth characteristics and composition of nitrides, gas nitridings of the austenitic stainless steel, STR 36 heat resisting steel and martensitic stainless steel are investigated at the temperature ranges between $500^{\circ}C$ and $675^{\circ}C$ for 5hours under the $75%NH_3+5%CO_2+20%$Air gas atmosphere. When gas nitriding the austentic stainless steel and STR 36 heat resisting alloy, the abnormal growth behavior of compound layer deviating from the conventional diffusion law with increasing temperature appears, while the compound layer of martensitic stainless steel shows the normal diffusional growth behavior. From the examination of microstructure, X-ray diffraction and hardness test, it is concluded that the abnormal growth behavior of compound layer with increasing temperature induces from the formation and dissolution of CrN and ${\gamma}^{\prime}-Fe_4N$ at the nitriding temperature ranges of $600{\sim}650^{\circ}C$.