• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part2
• /
• pp.773-774
• /
• 2006

Gas surface treatment is considered to be effective for titanium because of its high reactivity. In this study, we investigated the gas nitriding mechanism in titanium sintered parts produced by metal powder injection molding (MIM) process. The microstructure and nitrogen content of sintered MIM parts were greatly affected by nitriding conditions. Nitriding process strongly depended on the specimen size, for example, the size of micro metal injection molding (${\mu}-MIM$) product is so small and the specific surface is so large that the mechanical and functional properties can be modified by nitriding.

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part2
• /
• pp.1157-1158
• /
• 2006

Internally nitrided dilute W-Ti alloy specimens having a heavily deformed surface microstructure were prepared by a multi-step internal nitriding at 1573-2073 K. Primary nitriding below their recrystallization temperature induced a precipitation of ultrafine TiN particles. After secondary and tertiary nitriding, those precipitates grew into rod-like TiN with a length of 20-60 nm. The recrystallization temperature after nitriding was elevated above 2073 K. The yield strength at 1773 K obtained from nitrided W-0.5 mass% Ti alloy was about 5 times as large as that of the recrystallized specimen. DBTT of the nitrided alloys was about 373 K.

• 산업기술연구
• /
• 제23권A호
• /
• pp.3-7
• /
• 2003

Effect of nitriding on fatigue crack initiation and growth rate has been studied on SNCM. Specimens were nitrided for 15 hr at $860^{\circ}C$. The fatigue limit of nitrided specimens was superior to that of annealed($860^{\circ}C$, 15 hr) specimens. Based on detailed observations of slip band and micro crack initiation, it is concluded that the excellent fatigue limit of nitrided specimens is attributed to improved slip initiation resistance by nitriding. The characteristic of fatigue crack growth rate of nitrided specimens was investigated and compared with those of annealed specimens. It was found that by nitriding the crack growth rate was markedly decreased and the threshold stress intensity factor range was improved. It is concluded that the excellent fatigue limit of nitrided specimens is also attributed to improved fatigue crack growth rate and threshold stress intensity factor range by nitriding.

• 한국표면공학회지
• /
• 제53권6호
• /
• pp.306-311
• /
• 2020

In this work, diamond-like carbon (DLC) films are coated onto plasma nitrided AISI 4140 steel by DC-pulsed PECVD. One problem of DLC films is their very poor adhesion on steel substrates. The purpose of the nitriding was to enhance adhesion between the substrate and the DLC films. The white layer formation is avoided. Plasma nitriding increased adhesion from 8 N for DLC coating to 25 N for duplex coating. Duplex plasma nitriding/DLC coating was proven to be more effective in improving the adhesion. The purpose of the bond layer was to enhance adhesion between the substrate and the DLC films.

• 열처리공학회지
• /
• 제23권3호
• /
• pp.150-155
• /
• 2010

Generally, plasma nitriding process has composed with a nitriding layer within glow discharge region occurred by energy exchange. The dissociations of nitrogen molecules are very difficult to make neutral atoms or ionic nitrogen species via glow discharge area. However, the captured electrons in which a double-folded screen with same potential cathode can stimulate and come out some single atoms or activated ionic species. It was showed an important thing that is called "hat is a dominant component in this nitriding process?" in plasma nitriding process and it can take an effective species for without compound layer. During a plasma nitriding process, it was able to estimate with analyzing and identification by optical emission spectroscopy (OES) study. And then we can make comparative studies on the nitrogen transfer with plasma nitriding and ATONA process using plasma diagnosis and metallurgical observation. From these observations, we can understand role of active species of nitrogen, like N, $N^+$, ${N_2}^+$, ${N_2}^*$ and $NH_x$-radical, in bulk plasma of each process. And the same time, during DC plasma nitriding and other processes, the species of FeN atom or any ionic nitride species were not detected by OES analyzing.

• Journal of Advanced Marine Engineering and Technology
• /
• 제32권2호
• /
• pp.262-267
• /
• 2008

Plasma immersion ion beam (PIIB) nitriding process is an environmentally benign and cost-effective process, and offers the potential of producing high dose of nitrogen ions in a way of simple, fast and economic technique for the high plasma flux treatment of large surface area with nitrogen ion source gas. In this report PIIB nitriding technique was used for nitriding on austenite stainless steel of AISI304 with plasma treatment at $250{\sim}500^{\circ}C$ for 4 hours, and with the working gas pressure of $2.67{\times}10^{-1}$ Pa in vacuum condition. This PIIB process might prove the advantage of the low energy high flux of ion bombardment and enhance the tribological or mechanical properties of austenite stainless steel by nitriding, Furthermore, PIIB showed a useful surface modification technique for the nitriding an irregularly shaped three dimensional workpiece of austenite stainless steel and for the improvement of surface properties of AISI 304, such as hardness and strength

• 열처리공학회지
• /
• 제22권6호
• /
• pp.361-367
• /
• 2009

The two-step gas nitriding was adopted to increase the depth of surface hardening in 3%Cr-Mo-V steel. The two-step gas nitriding consisted of Step I; $520^{\circ}C{\times}20\;hrs$ and Step II; $550^{\circ}{\times}70\;hrs$. The layer of two-step gas nitriding showed better uniformity and deeper nitriding layer than one-step gas-nitriding layer. The maximum surface hardness showed the value of 850 Hv. The maximum depth of nitrogen permeation showed $750\;{\mu}m$ (350 Hv). X-ray diffraction analysis showed that compound layer was mainly consisted of CrN and $\varepsilon-Fe_3N$ phases. These phases were presumed contributing to surface hardening and wear resistance. However, the corrosion resistance of gas-nitrided Cr-Mo-V steel were not improved in the solution of 1 N HCl and NaOH. Therefore, it is necessary that the continuous study for improvement of corrosion resistance hereafter.

• 한국표면공학회지
• /
• 제48권6호
• /
• pp.269-274
• /
• 2015

In this experiment, post-nitriding treatment was performed at $400^{\circ}C$ on AISI 316 stainless steel which was plasma carburized previously at $430^{\circ}C$ for 15 hours. Plasma nitriding was implemented on AISI 316 stainless steel at various gas compositions (25% $N_2$, 50% $N_2$ and 75% $N_2$) for 4 hours. Additionally, during post nitriding Ar gas was used with $H_2$ and $N_2$ to observe the improvement of surface properties. After treatment, the behavior of the hybrid layer was investigated by optical microscopy, X-ray diffraction, and micro-hardness testing. Potentiodynamic polarization test was also used to evaluate the corrosion resistance of the samples. Meanwhile, it was found that the surface hardness increased with increasing the nitrogen gas content. Also small percentage of Ar gas was introduced in the post nitriding process which improved the hardness of the hardened layer but reduced the corrosion resistance compared with the carburized sample. The experiment revealed that AISI 316L stainless steel showed better hardness and excellent corrosion resistance compared with the carburized sample, when 75% $N_2$ gas was used during the post nitriding treatment. Also addition of Ar gas during post nitriding treatment degraded the corrosion resistance of the sample compared with the carburized sample.

• 열처리공학회지
• /
• 제19권2호
• /
• pp.90-95
• /
• 2006

Nitriding or carburizing of carbon steels results in good mechanical properties such as high surface hardness and wear resistance but it has no affection on the corrosion resistance. Corrosion properties of nitriding and carburizing steels could be deteriorated. So, recently, there have been great demand for oxi-nitriding to enhance both mechanical properties and corrosion resistance. In this study, the corrosion resistance of carbon steel, S35C, and free cutting steel, SUM222, are prepared by vacuum nitriding and vacuum post-oxidation were compared with those treated by nitriding. After vacuum post-oxidation, $5{\mu}m$ oxide layer was formed on the nitride layer with $20{\sim}30{\mu}m$ depth. Potentio-dynamic polarization curve in corrosion test showed that the corrosion potential after post oxidation was increased from 200 mV to 800 mV in S35C and from 600 mV to 1200 mV in SUM222. SEM analyses showed that pores was increased and surface roughness became rougher with post oxidation. However, the formation of $Fe_3O_4$ resulted in the enhanced corrosion resistance of steels.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2012년도 춘계학술발표회 논문집
• /
• pp.177-178
• /
• 2012

In this experiment, post-nitriding treatment has been performed at $400^{\circ}C$ on AISI 316 stainless steel which is plasma carburized previously at $430^{\circ}C$ for 15 hours. Plasma nitriding was implemented on AISI 316 stainless steel at various gas compositions (25% N2, 50% N2 and 75% N2) for 4 hours. Additionally, during post nitriding Ar gas was used with H2 and N2 to observe the improvement of treatment. After treatment, the behavior of the hybrid layer was investigated by optical microscopy, X-ray diffraction, and micro-hardness testing. Potentiodynamic polarization test was also used to evaluate the corrosion resistance of the samples. Meanwhile, it was found that the surface hardness increased with increasing the nitrogen gas content. Also small percentage of Ar gas was introduced in the post nitriding process which improved the hardness of the hardened layer but reduces the corrosion resistance compared with the carburized sample. The experiment revealed that AISI 316L stainless steel showed better hardness and excellent corrosion resistance compared with the carburized sample, when 75% N2 gas was used during the post nitriding treatment. Also addition of Ar gas during post nitriding treatment were degraded the corrosion resistance of the sample compared with the carburized sample.