• Transactions on Electrical and Electronic Materials
• /
• v.9 no.4
• /
• pp.143-146
• /
• 2008

In this study the thermal impact characteristics by forest fire are extensively investigated using temperature controlled ovens. The test conditions for thermal impact damage are simulated according to the characteristics of natural forest fire. The test pieces are suspension porcelain insulators made by KRI in 2005 for transmission lines. In the thermal impact cycle tests with $300\;^{\circ}C$ thermal impact gradient (-70 to $230\;^{\circ}C$), cycling in 10 minute periods, no critical failures occurred in the test samples even with long cycle times. But in tests with thermal impact gradient from room temperature to $200-600\;^{\circ}C$, cycling in 10 to 30 minute periods, there were critical failures of the porcelain insulators according to the thermal impact gradient and quenching method. In the case of thermal impact by forest fire, it was found of that duration time is more important than the cycling time, and the initiation temperature of porcelain insulator failures is about $300\;^{\circ}C$, in the case of water quenching, many cracks and fracture of the porcelain occurred. It was found that the thermal impact failure is closely related to the displacement in the cement by thermal stress as confirmed by simulation. It was estimated that the initiation displacement by the thermal impact of $300\;^{\circ}C$ is about 0.1 %. Above 1% displacement, it is expected that the most porcelain insulators would fail.

• Economic and Environmental Geology
• /
• v.51 no.2
• /
• pp.121-130
• /
• 2018

The KURT (KAERI Underground Research Tunnel) is a research tunnel which is located in KAERI (Korea Atomic Energy Research Institute) site. At KURT, researches on engineering and natural barrier system, which are the most important components for geological disposal system for high level radioactive waste, have been conducted. In this study, we synthesized the site characteristics obtained by various types of site investigation to introduce the geological model for KURT site, and induced the 3-D hydrogeological model for KURT site from the geological model. From the geological investigation at the surface and boreholes, four geological elements such as subsurface weathered zone, upper fractured rock, lower fractured rock and fracture zones were determined for the geological model. In addition, the geometries of these geological elements were also analyzed for the geological model to be three-dimensional. The results from 3-D geological model were used to construct the hydro-geological model for KURT site, which is one of the input data for groundwater flow modeling and safety assessment.

• Journal of Biomedical Engineering Research
• /
• v.28 no.1
• /
• pp.108-116
• /
• 2007

Recently, it has been reported that the posterior stabilized implant, which is clinically used for the total knee replacement (TKR), may have failure risk such as wear or fracture by the contact pressure and stress on the tibial post. The purpose of this study is to investigate the influence of the mal alignment of the posterior stabilized implant on the tibial post by estimating the distributions of contact pressure and von-Mises stress on a tibial post and to analyze the failure risk of the tibial post. Finite element models of a knee joint and an implant were developed from 1mm slices of CT images and 3D CAD software, respectively. The contact pressure and the von-Mises stress applying on the implant were analyzed by the finite element analysis in the neutral alignment as well as the 8 malalignment cases (3 and 5 degrees of valgus and varus angulations, and 2 and 4 degrees of anterior and posterior tilts). Loading condition at the 40% of one whole gait cycle such as 2000N of compressive load, 25N of anterior-posterior load, and 6.5Nm of torque was applied to the TKR models. Both the maximum contact pressure and the maximum von-Mises stress were concentrated on the anterior-medial region of the tibial post regardless of the malalignment, and their magnitudes increased as the degree of the malalignment increased. From present result, it is shown that the malalignment of the implant can influence on the failure risk of the tibial post.

• International Journal of Industrial Entomology and Biomaterials
• /
• v.24 no.2
• /
• pp.63-68
• /
• 2012

Osteoporosis is characterized by the reduced density of mineralized bone matrix. The loss of bone has been attributed to an imbalance between bone formation and bone resorption. The silkmoth is one of the famous traditional tonic medicines. Silkworm pupa was evaluated for its antiosteoporotic activity in an ovariectomized rat model of osteoporosis. The rats were ovariectomized at 6weeks of age and divided into 7 groups. All the groups were fed without calcium diet. The OVX rats were treated with water and silkworm powder for 6 weeks. In OVX rats, the body weight, feeding and water intake quantity did not show a significant change, but the silkworm pupa powder immediately before the eclosion of Yeonrokjam was significantly increased the bone mineral density in the femoral bone. The silkworm pupa powder increased the bone with increasing calcium in serum. These results also showed its protective action through promotion of bone formation. The silkworm pupa powder has a definite antiosteoporotic effect; similar to estrogen, it is especially effective for the prevention of bone fracture induced by estrogen deficiency. The silkworm pupa powder is a promising anti-osteoporotic agent that can prevent bone fractures in osteoporotic patients. The silkworm pupa powder does not show serious side effects because natural herbal medicine origin.

• Journal of the Society of Naval Architects of Korea
• /
• v.51 no.3
• /
• pp.246-253
• /
• 2014

Liquid natural gas is stored and transported inside cargo tank which is made of specially designed cryogenic materials such as 9% Ni steel, Al5083-O alloy and SUS304 and so on. The materials have to keep excellent ductile characteristics under the cryogenic environment, down to -163oC, in order to avoid the catastrophic sudden brittle fracture during the operation condition. High manganese steel is considered to be the promising alternative material that can replace the commonly used materials mentioned above owing to its cost effectiveness. In line with this industrial need, the mechanical properties of the high manganese steel under both room and cryogenic environment were investigated in this study focused on its tensile and fatigue behavior. In terms of the tensile strength, the ultimate tensile strength of the base material of the high manganese steel was comparable to the existing cryogenic materials, but it turned out to be undermatched one when welding is involved in. The fatigue strength of the high manganese steel under room temperature was as good as other cryogenic materials, but under cryogenic environment, slightly less than others though better than Al 5083-O alloy.

• Journal of Advanced Marine Engineering and Technology
• /
• v.9 no.2
• /
• pp.126-142
• /
• 1985

The plane bending corrosiion fatigue test for the welded metal parats was performed in the air and in the natural sea water with and without applying cathodic protection. The specimens tested were the weld of SM41 steel plates, SM58 steel plates and of SM41 to SM58, which were all prepared by submerged arc welding. The main results obtained from the experiment are summarized as follows: (1) In case with SM41 and SM58 steel plates, lower value of impact strength, higher value of hardness and more noble electrode potential were observed in the welded metal part than in the HAZ and base metal. Also the lowest hardness zone in the HAZ was observed with SM58 which was not found with SM41. In case with weld specimen of SM41 to SM58, the impact strength and the electrode potential of the welded metal part showed again the lowest and most noble value but the hardness value was located between those of SM41 and SM58 base metal. (2) In the fatigue test, the specimens tested in the air and under the cathodic protection were both cracked in a purely mechanical mode, but the specimens tested without cathodic protection were cracked by the combination of mechanical fracture and electro-chemical corrosion. (3) The corrosion fatigue limit of the welded metal parts of the specimen was increased by the cathodic protection. As the protection potential was varied down to -800 mV vs. SCE the fatigue limit was increased to the value tested in the air, and the maximum fatigue limit appeared at the -1, 000 - -1, 200 mV vs. SCE. However, as the protection potential was further decreased below -1, 200 mV vs.SCE, the fatigue limit of weld of SM58 and of SM41-SM58 joining was decreased but the limit was almost constant in the case of weld of SM41. (4) It is suggested that when designing steel ship the corrosion fatigue limit of welded metal parts should be stressed as a designing strength of the structure of steel ship in addition to the conventional basis considering simply tensile strength of steel and safety factor.

• Transactions of the Korean Society of Automotive Engineers
• /
• v.13 no.5
• /
• pp.127-133
• /
• 2005

Rotary swaging is one of the incremental forming process which is a chipless process using the reduction of cross-sections of bars, tubes and wires. The TDS(Tube Drive Shaft) of monobloc used in automotive has been developed by the rotary swaging process. The mechanical characteristics of swaged parts such as the hardness, thickness and roughness are also estimated to conduct experimental analyses of rotary swaging process with the materials of 34Mn5 Furthermore the change in the vibration mode of TDS due to design parameters, which are the tube length, diameter and thickness, has been investigated and analysed. The weight of the TDS product is smaller by about $12.8\%$ than that of SDS with the same performance. It could be evidently found that the TDS is designed to be much lighter than SDS (Solid Drive Shaft). This advantage might give some possibility to improve the NVH (Noise-Vibration-Harshness) characteristics. A maximum torque and a total number of torsional repetitions for the TDS is checked and measured to know the torsional intensity and fatigue strength through the static torsion test and torsional durability test, respectively. A total number of the torsional repetitions up to the fracture for the TDS is greater than 250,000 times.

• The korean journal of orthodontics
• /
• v.20 no.3 s.32
• /
• pp.583-591
• /
• 1990

If the bond strength is sufficient to resist orthodontic force, orthodontic brackets can be bonded to restorations. Orthodontic brackets were bonded to composite resin and glass ionomer cement restorations with no-mix adhesive or glass ionomer cement. The shear bond strength of adhesives bonded to restorations was studied in vitro. Orthodontic brackets were bonded to 10 extracted natural teeth, 40 composite resin restorations and 40 glass ionomer restorations. The surfaces of composite resin restorations were roughened or applied with bonding agent (Scothbond) after surface roughening. The surfaces of glass ionomer cement restorations were conditioned with acid etching or applied with Scotchbond to etched surface. The adhesive was no-mix resin or glass ionomer cement. The shear bond strength was measured. The results were as follows: 1. Orthodontic brackets could be bonded to composite resin restorations effectively as they could be bonded to acid etched enamel with no-mix adhesive. The shear bond strength was sufficient to resist orthodontic force and was not affected by bonding agent greatly. 2. The shear bond strength of no-mix adhesive bonded to acid etched glass ionomer cement restorations was sufficient to resist orthodontic force. However. the fracture risk of glass ionomer cement restorations was increased during debonding. The bonding agent couldn't increase the shear bond strength greatly. 3. The shear bond strength of glass ionomer cement bonded to glass ionomer cement restorations was lower than that of no-mix adhesive. The shear bond strength was sufficient to resist orthodontic force and was greatly decreased by bonding agent. 4. The shear bond strength of glass ionomer cement bonded to composite resin restorations was too low to resist orthodontic force.

• Geophysics and Geophysical Exploration
• /
• v.18 no.1
• /
• pp.21-30
• /
• 2015

Induced seismicity has been observed in the relation with lots of anthropogenic influence and at variety of geological conditions over the last several decades. This paper reviews those induced earthquakes and compares with each other as well as with natural tectonic earthquakes. Hydraulic fracturing is commonly used to enhance the permeability through new cracks in the rock formation. The process triggers the induced seismicity, which can give crucial information on the fracture network and oil/gas migration. In the similar way, unintentionally induced events during the production procedure of the field, dam reservoir, minig activity, or wastewater injection can be used to give insight into various hydrodynamic processes and changes of reservoir properties at a various scales. The general conclusion summarizes the uncertainty or limitations of knowledge up to date and presents some issues to be dealt with in the future research.

• Journal of Periodontal and Implant Science
• /
• v.30 no.1
• /
• pp.91-104
• /
• 2000

Many synthetic bone materials have been studied for their potential of regenerative effects in periodontal tissue. Safflower seeds have been traditionally used as a drug for the treatment of fracture and blood stasis in oriental medicines. The purpose of this study was to assess and compare the osseous responses in rat calvarial defects between bone substitutes such as calcium carbonate and bovine-derived hydroxyapatite and feeding of safflower seeds. The calvarial defects were made with 8 mm trephine bur in 24 Sprague-Dawley rats. Two graft materials were implanted in each experimental groups, whereas the control and safflower seed feeding groups were sutured without any other treatment. And then the rats of safflower seed feeding group were supplied with 3 g/day of safflower seeds. Each group was sacrificed at 4 weeks and 8 weeks. To study a histopathology related to bone healing and regeneration, Goldner's Masson Trichrome stain was done at each weeks. The tissue response was evaluated under light microscope. There were more osteoblastic activity, new bone formation, dense bony connective tissues in bovine-derived hydroxyapatite group compared to other groups at 8 weeks. The osseous defect area of safflower seed feeding group was filled with prominent fibrous tissues, where less inflammatory infiltration and new capillary proliferation. In the early phase of bone healing, safflower seed feeding reduces the inflammatory response and promotes the proliferation of connective tissue. These results suggest that natural bovine-derived HA and safflower seed feeding could enhance the regenerative potential in periodontal defects.