• 한국입자에어로졸학회지
• /
• 제12권3호
• /
• pp.65-72
• /
• 2016

Nanoporous $SiO_2$ particles containing different pore volume and size were prepared from silicic acid by a spray pyrolysis. The pore size, pore volume and particle size could be controlled with varying the precursor concentration, reaction temperature, and amount of organic templates such as Urea and poly ethylene glycol (PEG). The pore size distribution, pore volume and specific surface area of as-prepared particles were analyzed by BET and BJH methods, and the average particle sizes were measured by a laser diffraction method. The nanoporous $SiO_2$ particles ranged $0.6-0.9{\mu}m$ in diameter were successfully synthesized and the average particle size increased as the silicic acid concentration increased. The morphology of nanoporous $SiO_2$ particles was spherical and pores ranged 1 - 40 nm in diameter were measured in the particles. In case of Urea added into silicic acid, it showed no much difference in the morphology, pore size and pore volume at different Urea concentration. On the other hand, when PEG was added, it was clearly observed that pore diameter and pore volume of the particles surface increased with respect to PEG concentration.

• 한국세라믹학회지
• /
• 제41권1호
• /
• pp.81-85
• /
• 2004

점토를 이용한 나노 다공성 촉매 제조를 목적으로 $Ni^{2+}$ 이온으로 피복된 $SiO_2$ 나노 졸 입자를 2차원 충상점토 화합물의 층간에 삽입, 가교화 시켜 비표면적 및 다공도가 우수한 $NiO-SiO_2$ 가교화 점토($NiO-SiO_2$-PILM)를 합성하였다. 나노 크기의 실리카 졸 입자는 tetraethyl orthosilicate(TEOS)를 가수분해하여 합성하였고, 여기에 $Ni^{2+}$ 수용액을 첨가한 다음 NaOH 용액을 적정하여 $Ni^{2+}-SiO_2$ 혼합 나노 졸입자를 완성하였다. 이렇게 제조된 혼합 졸 용액을 1wt%의 점토 수분산액에 첨가하여 $60{\circ}C$에서 5h 이온교환 반응을 통해 층간에 삽입, 수세, 건조 후 $40^{\circ}C$에서 2시간 열처리 하므로써 다공성 가교화 점토를 제조하였다. 나노 졸 입자의 가교화에 따라 점토의 층간거리($d_{001}$)는 $45{\AA}$ 정도 크게 증가하였고 $600^{\circ}C$까지도 다공구조가 안정하게 유지되었다. 또한 질소 흡착-탈착 등온선 분석 결과 비표면적($S_{BET}$)이 최대 $760m^2/g$으로 다공 구조가 매우 잘 발달되어 있음을 확인하였고, $NiO-SiO_2$ 졸 가교화 점토의 경우 $NiO-SiO_2$ 나노입자가 층간에 이중층으로 배열되어 있음을 알 수 있었다.

• Applied Science and Convergence Technology
• /
• 제24권6호
• /
• pp.262-267
• /
• 2015

We demonstrate the growth of single-walled carbon nanotubes (SWNTs) using ethylene-based chemical vapor deposition (CVD) and ferritin-induced catalytic particles toward growth temperature reduction. We first optimized the gas composition of $H_2$ and $C_2H_4$ at 500 and 30 sccm, respectively. On a planar $SiO_2$ substrate, high density SWNTs were grown at a minimum temperature of $760^{\circ}C$. In the case of growth using nanoporous templates, many suspended SWNTs were also observed from the samples grown at $760^{\circ}C$; low values of $I_D/I_G$ in the Raman spectra were also obtained. This means that the temperature of $760^{\circ}C$ is sufficient for SWNT growth in ethylene-based CVD and that ethylene is more effective that methane for low temperature growth. Our results provide a recipe for low temperature growth of SWNT; such growth is crucial for SWNT-based applications.