• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09b
• /
• pp.786-787
• /
• 2006

The magnetic inductance of nanocrystalline $Fe_{73}Si_{16}B_7Nb_3Cu_1$ and an amorphous FeSiB powder sheet has been investigated to identify RFID performance. The powder was mixed with binder and solvent and tape-casted to form films. Results show annealing significantly influenced on the inductance of the material. The surface oxidation of the particles was the main reason for the reduced inductance. The maximum inductance of $Fe_{73}Si_{16}B_7Nb_3Cu_1$ alloy was about $88{\mu}H$ at 17.4 MHz, about 65% greater compared to the FeSiB alloy. The higher inductance in the nanocrystalline alloy indicates it may be used as a potential replacement of current RFID materials.

• Journal of Magnetics
• /
• v.16 no.3
• /
• pp.211-215
• /
• 2011

The dynamic magnetostriction characteristics of an Fe-based nanocrystalline FeCuNbSiB alloy are investigated as a function of the dc bias magnetic field. The experimental results show that the piezomagnetic coefficient of FeCuNbSiB is about 2.1 times higher than that of Terfenol-D at the low dc magnetic bias $H_{dc}$ = 46 Oe. Moreover, FeCuNbSiB has a large resonant dynamic strain coefficient at quite low Hdc due to a high mechanical quality factor, which is 3-5 times greater than that of Terfenol-D at the same low $H_{dc}$. Based on such magnetostriction characteristics, we fabricate a new type of transducer with FeCuNbSiB/PZT-8/FeCuNbSiB. Its maximum resonant magnetoelectric voltage coefficient achieves ~10 V/Oe. The ME output power reaches 331.8 ${\mu}W$ at an optimum load resistance of 7 $k{\Omega}$ under 0.4 Oe ac magnetic field, which is 50 times higher than that of the previous ultrasonic-horn-substrate composite transducer and it decreases the size by nearly 86%. The performance indicate that the FeCuNbSiB/PZT-8/FeCuNbSiB transducer is promising for application in highly efficient magnetoelectric energy conversion.

• Journal of Magnetics
• /
• v.14 no.4
• /
• pp.155-160
• /
• 2009

This study examined the effects of a decrease in thickness of magnetic alloy flakes on the electromagnetic wave absorption characteristics of nanocrystalline $Fe_{73.5}Cu_1Nb_3Si_{15.5}B_7$ (at.%) alloy flakes/polymer composite sheets available for a quasi-microwave band. The thickness of FeCuNbSiB alloy flakes decreased to 1-2 $\mu$m with increasing milling time up to 24 h, and the composite sheet including alloy flakes milled for 24 h exhibited considerably enhanced power loss properties in the GHz range compared to the sheets having non-milled alloy powders. Although a considerable increase in loss factor upon milling was observed in the narrow frequency range of 4-6 GHz, there was no correlation between the complex permeability and flake thickness. However, the complex permittivity increased with increasing milling time, and there was good agreement between the milling time and the frequency dependences of the complex permittivity and power loss.

• Journal of Magnetics
• /
• v.19 no.4
• /
• pp.327-332
• /
• 2014

The effect of minor element additions (Ca, Al) on microstructural change and magnetic properties of Fe-Nb-Cu-Si-B alloy has been investigated, in this paper. The Fe-Si-B-Nb-Cu(-Ca-Al) alloys were prepared by arc melting in argon gas atmosphere. The alloy ribbons were fabricated by melt-spinning, and heat-treated under a nitrogen atmosphere at $520-570^{\circ}C$ for 1 h. The soft magnetic properties of the ribbon core were analyzed using the AC B-H meter. A differential scanning calorimetry (DSC) was used to examine the crystallization behavior of the amorphous alloy ribbon. The microstructure was observed by X-ray diffraction (XRD), transmission electron microscope (TEM) and scanning electron microscope (SEM). The addition of Ca increased the electrical resistivity to reduce the eddy current loss. And the addition of Al decreased the intrinsic magnetocrystalline anisotropy $K_1$ resulting in the increased permeability. The reduction in the size of the ${\alpha}$-Fe precipitates was observed in the alloys containing of Ca and Al. Based on the results, it can be concluded that the additions of Ca and Al notably improved the soft magnetic properties such as permeability, coercivity and core loss in the Fe-Nb-Cu-Si-B base nanocrystalline alloys.

• Journal of the Korean Magnetics Society
• /
• v.5 no.5
• /
• pp.507-510
• /
• 1995

A heat-treatment method of pre-annealing and then flash annealing(FA) has been used to improve the soft magnetic properties of nanocrystalline $Fe_{76}CuSi_{13}B_{10}$ and $Fe_{74}CuNb_{3}Si_{12}B_{10}$ alloys. Outstanding magnetic properties of nanocrystalline $Fe_{74}CuNb_{3}Si_{12}B_{10}$ alloy were attained by flash-annealing in air after annealed at $500^{\circ}C$ for 0.5hr below the crystallization temperature. The same results were obtained for $Fe_{74}CuSi_{13}B_{10}$ alloy. The measurment of relief of stress and X-ray diffraction were used to analyze the effect of flashannealing.

• Journal of the Korean Magnetics Society
• /
• v.3 no.2
• /
• pp.130-134
• /
• 1993

The magnetic properties of the amorphous $Fe_{73.5-X}Co_{X}Cu_{1}Nb_{3}Si_{13.5}B_{9}(x=2,\;4)$ alloys, fabricated by a single roll rapid quenching technique and annealed at $400~650^{\circ}C$, have been investigated. The optimum annealing temperature is $550^{\circ}C$ for the amorphous $Fe_{71.5}Co_{2}Cu_{1}Nb_{3}Si_{13.5}B_{9}$ alloy. The properties of the nanocrystalline $Fe_{71.5}Co_{2}Cu_{1}Nb_{3}Si_{13.5}B_{9}$ alloy show the relative permeability of $1.1{\times}10^{4}$ and the coercive force of 0.22 Oe at 1 kHz. When annealed at $600^{\circ}C$, the nanocrystalline $Fe_{69.5}Co_{4}Cu_{1}Nb_{3}Si_{13.5)B_{9}$ alloy shows the relative permeability of $1.0{\times}10^{4}$ and the coercive force of 0.19 Oe at 1 kHz. From the X-ray measurement, it is found that the remarkably improved soft magnetic properties are the effect of the formation of $\alpha$-Fe(Si) grain. By the results of FMR exper-imeIlt, the optimum annealing condition is just below temperature which the peak-to-peak line width of FMR spectrum increase rapidly.

• Proceedings of the Korean Magnestics Society Conference
• /
• 2003.06a
• /
• pp.86-87
• /
• 2003

• Proceedings of the Korean Magnestics Society Conference
• /
• 1995.10a
• /
• pp.62-63
• /
• 1995

• Proceedings of the Korean Magnestics Society Conference
• /
• 1991.11a
• /
• pp.24-25
• /
• 1991

• Proceedings of the Korean Magnestics Society Conference
• /
• 2004.06a
• /
• pp.184-185
• /
• 2004