• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09b
• /
• pp.1211-1212
• /
• 2006

The electrophoretic deposition process of Ni nano-particles was employed for self-repairing of heat exchanger tubes. For electrophoretic deposition of Ni nano-particles on pitted Ni alloy specimen, a constant electric field of 100 V $cm^{-1}$ was applied to the specimen for 180 s in Ni-dispersed solution. It was found that as electrophoretic deposition proceeded, the size of the pit remarkably decreased due to the agglomeration of Ni nano-particles at the pit. This strongly suggests that the electrophoretic mobility of the charged particles is larger for the pit with a higher current value rather than outer surfaces with a lower current value.

• Journal of Powder Materials
• /
• v.16 no.6
• /
• pp.424-430
• /
• 2009

Electromagnetic wave energies are consumed in the form of thermal energy, which is mainly caused by magnetic loss, dielectric loss and conductive loss. In this study, CNT was added to the nanocrystalline soft magnetic materials inducing a high magnetic loss, in order to improve the dielectric loss of the EM wave absorption sheet. Generally, the aspect ratio and the dispersion state of CNT can be changed by the pre-ball milling process, which affects the absorbing properties. After the various ball-milling processes, 1wt% of CNTs were mixed with the nanocrystalline $Fe_{73}Si_{16}B_7Nb_{3}Cu_1$ base powder, and then further processed to make EM absorption sheets. As a result, the addition of CNT to Fe-based nanocrystalline materials improved the absorption properties. However, the increase of ball-milling time for more than 1h was not desirable for the powder mixture, because the ballmilling caused the shortening of CNT length and the agglomeration of the CNT flakes.

• Transactions on Electrical and Electronic Materials
• /
• v.11 no.2
• /
• pp.61-64
• /
• 2010

In this paper, we investigate the quality difference of SiC crystals grown by a conventional physical vapor transport method using various SiC powders. While the growth rate was revealed to be dependent upon the particle size of the SiC powder, the growth rate of SiC bulk crystals grown using SiC powder with a smaller particle size (20 nm) was definitely higher than those using lager particle sizes with $0.1-0.2\;{\mu}m$ and $1-10\;{\mu}m$, respectively. All grown 2 inch SiC single crystals were proven to be the polytype of 6H-SiC and the carrier concentration levels of about $10^{17}\;cm^3$ were determined from Hall measurements. It was revealed that the particle size and process method of SiC powder played an important role in obtaining a good quality, high growth rate, and to reduce growth temperature.

• Korean Journal of Materials Research
• /
• v.18 no.8
• /
• pp.411-416
• /
• 2008

In this research, fine-structure TiO2 bulks were fabricated in a combined application of magnetic pulsed compaction (MPC) and subsequent sintering and their densification behavior was investigated. The obtained density of $TiO_2$ bulk prepared via the combined processes increased as the MPC pressure increased from 0.3 to 0.7 GPa. Relatively higher density (88%) in the MPCed specimen at 0.7 GPa was attributed to the decrease of the inter-particle distance of the pre-compacted component. High pressure and rapid compaction using magnetic pulsed compaction reduced the shrinkage rate (about 10% in this case) of the sintered bulks compared to general processing (about 20%). The mixing conditions of PVA, water, and $TiO_2$ nano powder for the compaction of $TiO_2$ nano powder did not affect the density and shrinkage of the sintered bulks due to the high pressure of the MPC.

• Bulletin of the Korean Chemical Society
• /
• v.30 no.1
• /
• pp.183-187
• /
• 2009

The structure of nano-crystalline $MnFe_2O_4$ was determined and refined with electron powder diffraction data employing the Rietveld refinement technique. A nano-crystalline sample (with average crystal size of about 10.9 nm) was characterized by selected area electron diffraction in an energy-filtering transmission electron microscope operated at 120 kV. All reflection intensities were extracted from a digitized image plate using the program ELD and then used in the course of structure refinements employing the program FULLPROF for the Rietveld analysis. The final structure was refined in space group Fd-3m (# 227) with lattice parameters a=8.3413(7) $\AA$. The reliability factors of the refinement are $R_F$=7.98% and $R_B$=3.55%. Comparison of crystallographic data between electron powder diffraction data and reference data resulted in better agreement with ICSD-56121 rather than with ICSD-28517 which assumes an initial structure model.

• Journal of the Korean Society for Precision Engineering
• /
• v.26 no.8
• /
• pp.24-28
• /
• 2009

• Journal of the Society of Cosmetic Scientists of Korea
• /
• v.32 no.1 s.55
• /
• pp.45-51
• /
• 2006

In the field of makeup cosmetics, especially, powder-based foundations such as two-way cake, pact and face powder, the quality of which is known to be strongly influenced by the properties of powder, surface treatment technology is widely used as a method to improve the various characteristics of powder texture, wear properties, dispersion ability and so on. The two-way cake or pressed-powder foundation is one of the familiar makeup products in Asian market for deep covering and finishing purpose. In spite of the relent progress in surface modification method such as composition of powders with different characteristics and application of a diversity of coating ingredient (metal soap, amino acid, silicone and fluorine), this product possess a technical difficulty to enhance both of the adhesion power and spreadability on the skin in addition to potential claim of consumer about heavy or thick feeling. This article is covering the preparation and coating method of nano-vesicle that mimic the double-layered lipid lamellar structure existing between the corneocytes of the stratum corneum in the skin for the purpose of improving both of two important physical characteristic of two-way cake, spreadability and adhering force to skin, and obtining better affinity to skin. Nano-vesicle was prepared using the high-pressure emulsifying process of lecithin, pseudo ceramide, butylene glycol and tocopheryl acetate. This nano-sized emulsion was added to powder-dispersed aqueous phase together with bivalent metal salt solution and then the filtering and drying procedure was followed to yield the nano-vesicle coated powder. The amount of nano-vesicle coated on the powder was able to regulated by the concentration of metal salt and this novel powder showed the lower friction coefficient, more uniform condition of application and higher adhesive powder comparing with the alkyl silane treated powder from the test result of spreadability and wear properties using friction meter and air jet method. Two-wav cake containing newly developed coated powder with nano-vesicle showed the similar advantages in the frictional and adhesive characteristics.

• Journal of Powder Materials
• /
• v.11 no.6 s.47
• /
• pp.493-502
• /
• 2004

In this study, nano-sized indium oxide powder with the average particle size below 100 nm is fab-ricated from the indium chloride solution by the spray pyrolysis process. The effects of the reaction temperature, the concentration of raw material solution and the inlet speed of solution on the properties of powder were studied. As the reaction temperature increased from 850 to $1000^{\circ}C$, the average particle size of produced powder increased from 30 to 100 nm, and microstructure became more solid, the particle size distribution was more irregular, the intensity of a XRD peak increased and specific surface area decreased. As the indium concentration of the raw material solution increased from 40 to 350 g/l, the average particle size of the powder gradually increased from 20 to 60 nm, yet the particle size distribution appeared more irregular, the intensity of a XRD peak increased and spe-cific surface area decreased. As the inlet speed of solution increased from 2 to 5 cc/min., the average particle size of the powder decreased and the particle size distribution became more homogeneous. In case of the inlet speed of 10 cc/min, the average particle size was larger and the particle size distribution was much irregular compared with the inlet speed of 5 cc/min. As the inlet speed of solution was 50 cc/min, the average particle size was smaller and microstructure of the powder was less solid compared with the inlet speed of 10 cc/min. The intensity of a XRD peak and the variation of specific area of the powder had the same tendency with the variation of the average par-ticle size.

• Applied Chemistry for Engineering
• /
• v.24 no.4
• /
• pp.391-395
• /
• 2013

In this study, zinc oxide (ZnO) nano powder, well known as an UV absorbing material, was synthesized with three synthetic conditions by the hydrothermal method. After ZnO nano powder was surface-modified with various silane coupling agents to improve dispersion property, a dispersion sol was prepared with dispersant for 72 h by the ball-milling of surface-modified ZnO nano powder. The dispersion sol, prepared by modifying the surface of the ZnO nano powder with an average size of about 30 nm using 3-chloropropyl trimethoxy silane, showed an excellent dispersion stability with a high UV-shielding and visible trnasparency.

• Journal of Powder Materials
• /
• v.13 no.6 s.59
• /
• pp.396-400
• /
• 2006

The Ti-Ni alloy nanopowders were synthesized by a levitational gas condensation (LGC) by using a micron powder feeding system and their particulate properties were investigated by x-ray diffraction (XRD), transmission electron microscopy (TEM) and Brunauer-Emmett-Teller (BET) method. The starting Ti and Ni micron powders $150{\mu}m$ were incorporated into the micron powder feeding system. An ingot type of the Ti-Ni ahoy was used as a seed material for the levitation and evaporation reactions. The collected powders were finally passivated by oxidation. The x-ray diffraction experiments have shown that the synthesized powders were completely alloyed with Ti and Ni and comprised of two different cubic and monoclinic crystalline phases. The TEM results showed that the produced powders were very fine and uniform with a spherical particle size of 18 to 32nm. The typical thickness of a passivated oxide layer on the particle surface was about 2 to 3 nm. The specific surface area of the Ti-Ni alloy nanopowders was $60m^2/g$ based on BET method.