• 대한금속재료학회지
• /
• 제48권7호
• /
• pp.630-638
• /
• 2010

The present investigation has been performed on the mixing behavior and microstructural development during fabrication of Fe micro-nano powder feedstock for a micro-powder injection molding process. The mixing experiment using a screw type blender system was conducted to measure the variations of torque and temperature during mixing of Fe powder-binder feedstock with progressive powder loading for various nano-powder compositions up to 25%. It was found that the torque and the temperature required in the mixing of feedstock increased proportionally with increasing cumulative powder loading. Such an increment was larger in the feedstock containing higher content of nano-powder at the same powder loading condition. However, the maximum value was obtained at the nano-powder composition of not 25% but 10%. It was owing to the 'roller bearing effect' of agglomerate type nano-powder acting as lubricant during mixing, consequently leading to the rearrangement of micro-nano powder in the feedstock. It is concluded that the improvement of packing density by rearrangement of nano-powders into interstices of micro-powders is responsible for the maximum powder loading of about 71 vol.% in the nano-powder composition of 25%.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2005년도 봄학술 발표회 논문집(II)
• /
• pp.13-16
• /
• 2005

Nanoscale materials are of great interest due to their unique optical, electrical and magnetic properties. Due to the recent amazing achievements in nano technology, new materials were developed. But these nano technology is not apply to the construction part in spite of exellent properties of nano size material. The purpose of this study is to apply to nano technology into building materials. To develop the high performance concrete, nano cement particles is prepared by mechanical method. In the results of this study, the nano silica powder increase effect according to increase of the mixing amount, appeared that compressive strength increased but is limit in increment. For the production of high-strength concrete, nano silica powder was suitable the binder ratio from 20$\%$. And, the compressive strength of concrete are especially dependent on the curing temperature.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2007년도 추계학술대회 논문집
• /
• pp.138-139
• /
• 2007

The microstructure and micro-hardness of high velocity oxygen fuel-sprayed (HVOF) WC-CoCr coatings are comparatively studied for both before and after laser heat-treatment (LT) of the coatings. The results indicate that compared to HVOF WC-CoCro coating, the laser treatment has eliminated the pores almost entirely providing a more homogeneous and densified microstructure. And the compact interface of the coating with substrate is achieved by laser treatment. The thickness of the coating has decreased from 300 ${\mu}m$ to 225 ${\mu}m$ As a result, the average porosity is five times higher in HVOF coating than in the coating by laser treatment. The laser treatment has produced a considerable increment in the hardness of the coating near surface whose average value increases from Hv0.2=1262.4 in the HVOF-sprayed coating to Hv0.2=1818.7 in the coatings treated with laser.

• Journal of Ceramic Processing Research
• /
• 제13권spc2호
• /
• pp.394-397
• /
• 2012

In this work, we studied the influence of the dopant elements concentration on the properties of SnO2 thin films deposited by pulsed laser deposition. X-ray diffraction (XRD), field emission scanning electron microscopy (FE-SEM), Hall effect measurement and UV-Vis studies were performed to characterize the deposited films. XRD results showed that the films had polycrystalline nature with tetragonal rutile structure. FE-SEM micrographs revealed that the as deposited films composed of dense microstructures with uniform grain size distribution. All the films show n-type conduction and the best transparent conductive oxide (TCO) performance was obtained on 6 wt% Sb2O5 doped SnO2 film prepared at pO2 of 60mtorr and Ts of 500 ℃. Its resitivity, optical transmittance, figure of merit are 7.8 × 10-4 Ω cm, 85% and 1.2 × 10-2 Ω-1, respectively.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2012년도 제43회 하계 정기 학술대회 초록집
• /
• pp.79-79
• /
• 2012

A high temperature and a low temperature plasma process technologies were developed and demonstrated for synthesis, hybrid formation, surface treatment and CVD engineering of nano powder. RF thermal plasma is used for synthesis of spherical nano particles in a diameter ranged from 10 nm to 100 nm. A variety of nano particules such as Si, Ni, has been synthesized. The diameter of the nano-particles can be controlled by RF plasma power, pressure, gas flow rate and raw material feed rate. A modified RF thermal plasma also produces nano hybrid materials with graphene. Hemispherical nano-materials such as Ag, Ni, Si, SiO2, Al2O3, size ranged from 30 to 100 nm, has been grown on graphene nanoplatelet surface. The coverage ranged from 0.1 to 0.7 has been achieved uniformly over the graphene surface. Low temperature AC plasma is developed for surface modification of nano-powder. In order to have a three dimensional and lengthy plasma treatment, a spiral type of reactor has been developed. A similar plasma reactor has been modfied for nano plasma CVD process. The reactor can be heated with halogen lamp.

• 한국복합재료학회:학술대회논문집
• /
• 한국복합재료학회 2001년도 추계학술발표대회 논문집
• /
• pp.137-140
• /
• 2001

Oragnic/inorganic hybrid materials prepared by sol-gel method have rapidly become a fasci nating research field in materials science. In this study, Polyimide/$\textrm{TiO}_2$ composites were synthesized from nano-sized anatase $\textrm{TiO}_2$ and two types of Polyimide (BTDA-PPD, PMDA-ODA) by Sol-gel method. Nano-sized $\textrm{TiO}_2$ particles were prepared from $\textrm{TiOEt}_4$ solution. The composites were charcaterized by using XRD, TGA, IR, TEM, and Atomic Force Microscope(AFM). $\textrm{TiO}_2$ nano particles were dispersed well in polyimide matrix and the thermal stability of polyimide was improved with $\textrm{TiO}_2$ nano-sized particles.

• Advances in nano research
• /
• 제13권3호
• /
• pp.247-257
• /
• 2022

Extraordinary properties of nanocomposites make them a primary replacement for many conventional materials. Anterior cruciate ligament (ACL) reconstruction, which is a frequent surgery in sport activities, is one of the fields in which nanocomposites could be utilized. In the present study, the mechanical properties of different porous scaffolds made from graphene nano-composites are presented ad load bearing capacity of these materials is calculated using finite element method. The numerical results are further compared with experimental published data. In addition, several geometrical and material parameters are analyzed to find the best configuration of nanocomposite scaffolds in reconstruction of ACL. Moreover, coating of detoxification chemicals are extremely easier on the nano-structured materials than conventional one. Detoxification potential of nano-composites in the injured body are also discussed in detail. The results indicated that nano-composite could be successfully used in place of auto- and allografts and also instead of conventional metallic screws in reconstruction of ACL.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2006년도 영호남 합동 학술대회 및 춘계학술대회 논문집 센서 박막 기술교육
• /
• pp.113-116
• /
• 2006

자발착화 연소반응법 (Glycine Nitrate Process)을 응용한 초음파분무열분해장치를 이용하여 이차전지의 양극재료인 Ni치환형 $LiMn_2O-4$ 분말을 합성하였고, 각각의 하소온도에 따른 분말의 특성을 평가하였다. 전구용액은 산화제로 $Mn(NO_3)_2{\cdot}6H_20$EX>, $LiNO_3$, $Ni(NO_3)_2{\cdot}6H_20$를 사용하였고, 자발착화 에너지를 공급하기 위한 연료로는 glycine를 사용하였다. 분말의 결정상을 확인하기 위해 X-선 회절 시험을 시행하였으며, 각각의 조성별로 ICP측정결과 여러 조성들($LiNi_xNm_{2-x}O_4\;0{\leq}x{\leq]0.5$) 중 $LiNi_{0.3}Nm_{1.7}O_4$의 분말이 비교적 우수한 특성을 나타내었지만, 전기화학적 특성 평가 결과 이론용량값에 미치지 못하는 용량값을 나타내었다. 이것은 분말 합성 시 미량의 미 반응된 유기물들이 분말 표면에 피복되어 전기적 성질을 변화시키고 있기 때문임을 확인하였다. 이러한 특성을 개선하고자 추가적으로 하소 공정을 실시하여 전지의 성능를 평가 하였다. 분말의 미세구조와 형태, 크기, 전기 화학적 특성을 관찰하여 하소 전 후의 분말을 비교하였다.

• 한국레이저가공학회지
• /
• 제15권3호
• /
• pp.16-19
• /
• 2012

We have successfully formed brown colored patterns inside of a transparent borosilicate glass generally known as BK7, laying the focus of near infrared Ti: sapphire femtosecond laser beam in the bulk BK7 glass. It is important to keep the laser power well below the damage threshold of BK7 in forming the color center. According to the low laser power, there was no laser induced mechanical damage such as cracks or threads in the color formed area. From the absorbance spectrum and its gaussian fitting, we found the band gap of BK7, 4.21eV, and three absorption edges.

• 한국분말재료학회지
• /
• 제13권3호
• /
• pp.187-191
• /
• 2006

Al-Cu alloy nano powders were produced by the electrical explosion of Cu-plated Al wires. The composition and phase of the alloy could be controlled by varying the thickness of Cu deposit on Al wire. When the Cu layer was thin, Al solid solution and $CuAl_2$ were the major phases. As the Cu layer becomes thicker, Al diminished while $Al_4Cu_9$ phase prevailed instead. The average particle size of Al-Cu nano powders became slightly smaller from 63 nm to 44 nm as Cu layer becomes thicker. The oxygen content of Al-Cu powder decreased linearly with Cu content. It is well demonstrated that the electrodeposition combined with wire explosion could be simple and economical means to prepare variety of alloy and intermetallic nano powders.