Co-Fe-Al-O nano-granular thin films with high electrical resistivity, fabricated by radio frequency magnetron sputtering under an $Ar+O_2$ atmosphere, are found to show good soft magnetic properties in the GHz frequency range. The real part value of the relative permeability is 260 at low frequencies and this value is maintained up to the GHz frequency range. A non-integrated type noise filter on a coplanar waveguide transmission line is demonstrated by using the Co-Fe-Al-O nano-granular thin film with the dimensions of $4\;mm(l){\times}4\;mm(w){\times}0.1\;{\mu}m(t)$. The insertion loss is very low being less than 0.3 dB and this low value is maintained up to 2 GHz. At a ferromagnetic resonance frequency of 3.3 GHz, the degree of noise suppression is measured to be 3 dB. This level of noise attenuation is small for real applications, but there is much room for further improvement by increasing the magnetic volume and integrating the magnetic thin film into the CPW transmission line.

• 한국세라믹학회지
• /
• 제56권4호
• /
• pp.354-359
• /
• 2019

Information security films that can ensure personal privacy by reducing the viewing angle of display screens were fabricated by microlouver patterning and a ZnO nano-ink filling process. Optical simulation results demonstrated that all the microlouver films showed good security performances. Security performances were evaluated as calculated relative luminance ratios compared between the side and front. Based on the simulation results, microlouver films were fabricated by UV imprint lithography and nano-ink bar coating. However, distortion of the microlouver pattern occurred with the use of high-viscosity nano-inks such as ZrO₂ and TiO₂, and the CuO-filled microlouver film suffered from very low optical transmittance. Accordingly, the effects of ZnO filling height on security performance were intensively investigated through simulation and experimental measurements. The fabricated microlouver film with a 75-㎛-high ZnO filling exhibited a good relative luminance ratio of 0.75 at a 60° side angle and a transmittance of 44% at a wavelength of 550 nm.

• 한국정보디스플레이학회:학술대회논문집
• /
• 한국정보디스플레이학회 2002년도 International Meeting on Information Display
• /
• pp.754-758
• /
• 2002

In order to reach the high quality of organic thin films such as high mobility for device applications, it is strongly desirable to study the growth properties of pentacene film as a function of evaporation condition. Here, we report the structure and morphology of thermal evaporated pentacene thin film by AFM, SEM, and XRD as a function of the evaporation rate and substrate temperature. These results play a key role in determining the electric performance of organic thin film transistor devices.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2007년도 추계학술대회 논문집
• /
• pp.328-328
• /
• 2007

$SnO_2$ has a high potential for electric and electronic applications. We have anodized pure tin metal and nano porous tin oxide film was obtained on pure Sn. Nano porous tin oxide were grown by anodization in nonaqueous-base electrolytes at different potentials between 5 V and 100 V. Pore size of ~100nm was observed by FE-SEM. Pore sizes as a function of applied voltage and anodizing time were characterized. We obtained nano porous tin oxide film having an uniform pore size at low temperature. High specific surface area of $SnO_2$ will be very useful for gas sensor, lithium battery, and dye sensitized solar cell.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2005년도 하계학술대회 논문집 Vol.6
• /
• pp.120-122
• /
• 2005

An alumina membrane with nano-sized pore array by anodic oxidation using thin film aluminum deposited on silicon wafer was fabricated. It is important that the sample prepared by metal deposition method has a flat aluminum surface and a good adhesion between the silicon wafer and the thin film aluminum. The oxidation time was controlled by observation of current variation. While the oxalic acid with 0.2M was used for low voltage anodization under 100V, the chromic acid with 0.1M was used for high voltage anodization over 100V. The nano-sized pores with diameter of 60~120nm was obtained by low voltage anodization of 40~90V and those of 200~300nm was obtained by high voltage anodization of 120~160V. Finally, the sample was immersed to the phosphoric acid with 0.1M concentration to etching the barrier layer. The sample will be applied to electronic sensors, field emission display, and template for nano-structure.

• 한국자기학회:학술대회 개요집
• /
• 한국자기학회 2008년도 Asian Magnetics Conference
• /
• pp.177.2-177.2
• /
• 2008

• 폴리머
• /
• 제35권4호
• /
• pp.289-295
• /
• 2011

망막조직공학을 위한 생체 재료는 기계적 안정성, 생체적합성, 낮은 분해속도 등을 포함하여 in vivo에서 잠재적인 유용성을 위한 몇 가지 중요한 특징이 입증되어야 한다. 실크 필름 생체재료는 이러한 기능적인 요구에 맞게 디자인되었다. 0, 10, 20, 40, 및 80 wt%의 실크가 함유된 천연합성물질과 하이브리드화된 silk/PLGA 필름을 용매 증발법으로 제조하였다. 1, 2, 및 3일 후에 부착된 세포 수를 확인하기 위해 MTT 분석을 하였고 SEM을 통해 필름에 부착된 세포 모폴로지를 확인하였다. 또한, mRNA 발현정도를 알아보기 위해 retinal pigment epithelitun(RPE) 세포의 프라이머인 RPE65를 사용하여 RT-PCR을 실시하였고 RPE 세포의 특정 단백질인 cytokeratin의 발현을 확인하고 세포의 증식을 비교하기 위해 면역화학염색을 실시하였다. 본 실험을 통해 실크/PLGA 필름에서 20~40 wt% 실크를 함유한 경우에 RPE 세포의 부착과 증식에 가장 좋은 영향을 미치는 것을 확인하였다.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2004년도 춘계학술대회 논문집 디스플레이 광소자분야
• /
• pp.189-192
• /
• 2004

To improvement life-time of the organic light emitting diodes(OLEDs). We investigate the inorganic composite film based on MgO and $SiO_2$ to protect from the moisture and oxygen. The inorganic composite films are added the base materials to the co-operate materials using the mixed process and it is deposited on plastic substrate by e-beam evaporator. In order to analyze as kinds of inorganic materials, Water Vapor method of Transmission Rate (WVTR) and Oxygen Transmission Rate (OTR) are measured by Permatran equipment(MOCON Corp.). For comparison. an MgD- and $SiO_2$-based composite film has lower values of WVTR and OTR than inorganic composite/compound films of ones. The results obtained here shows that this film is suitable for passivation layer to extend the life-time of OLEDs.

• 한국표면공학회지
• /
• 제42권4호
• /
• pp.152-156
• /
• 2009

Electroless plating is influenced by kinds of parameters including concentrations of electrolyte, plating time, temperature and so on. In this study, the Pt thin films were prepared on GaAs substrate by a 2-step electroless plating depending method. The small Pt catalytic particles by using Pt I bath exhibited islands-morphology dispersed throughout the substrate surface at $65^{\circ}C$, as function as a sensitized thin film, and then a thicker Pt film grew upon the sensitized layer by the second Pt II bath. As the growth of Pt film is strongly influenced by the plating time and temperature, the plating time of Pt II bath varied from 5 min to 40 min at $60{\sim}80^{\circ}C$ after Pt I bath at $60{\sim}80^{\circ}C$ for 5 min. It is found that the film grows with the increasing plating time and temperature. The resistivity value of Pt deposited layer was characterized to study the growth mechanism of 2-step plating.

• 한국인쇄학회지
• /
• 제29권3호
• /
• pp.17-30
• /
• 2011

The polarizer is an important optical element used in a variety of applications. Nano-wire grid polarizers in the form of sub-wavelength metallic gratings are an attractive alternative to conventional polarizers, because they provide high extinction ratio. This study has been carried out to fabrication of the 17inch area size nano-wire grid polarizer(NWGP) The master for NWGPs with a pitch of 200nm and the area size $730mm{\times}450mm$ were fabricated using laser interference lithography and aluminum sputtering and wet etching. And The NWGP fabrication process was using by the Roll to-Roll UV imprinting and was applied to flexible PET film. The results were a transmission of light (Tp) 46.7%, reflectance (Rs) 40.1% and Extinction ratio of above 16 for the visible light range.