Internally nitrided dilute W-Ti alloy specimens having a heavily deformed surface microstructure were prepared by a multi-step internal nitriding at 1573-2073 K. Primary nitriding below their recrystallization temperature induced a precipitation of ultrafine TiN particles. After secondary and tertiary nitriding, those precipitates grew into rod-like TiN with a length of 20-60 nm. The recrystallization temperature after nitriding was elevated above 2073 K. The yield strength at 1773 K obtained from nitrided W-0.5 mass% Ti alloy was about 5 times as large as that of the recrystallized specimen. DBTT of the nitrided alloys was about 373 K.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09b
• /
• pp.1161-1162
• /
• 2006

In order to overcome the recrystallization embrittlement and irradiation embrittlement of Mo, which are major problems for its fusion applications, internally nitrided Mo alloys were prepared by a novel multi-step internal nitriding. Neutron irradiation was performed in the Japan Material Testing Reactor (JMTR). After irradiation, nitrided Mo alloys exhibited $\iota$ ower ductile-brittle transition temperature than irradiated TZM. These results suggested that multi-step internal nitriding was effective to the improvement in the embrittlement by irradiation. Transmission electron microscope observation revealed that TiN particles precipitated by nitriding acted as a sink for irradiation-induced defects.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09b
• /
• pp.1163-1164
• /
• 2006

TZM alloy having elongated coarse-grain structure was developed by three-step internal nitriding treatment at 1423 to 1873 K in $N_2$ and subsequent recrystallization treatment at 2173 K in vacuum. Some specimens were subjected to re-nitriding treatment at 1873 K for 16 h. After the recrystallization treatment, aspect ratio (L/W) of grains for rolling direction was about 50 at the maximum. Yield stress obtained at 1773 K after re-nitriding treatment was about 6 times as large as that of recrystallized specimen. Re-nitriding was very effective in the improvement in strength of TZM alloy having elongated coarse-grain structure.