• 한국건축시공학회지
• /
• 제18권6호
• /
• pp.559-567
• /
• 2018

외단열 마감 공법에서 사용되는 바탕조정재는 화재가 발생하는 경우 얇은 마감과 폴리머의 연소로 인해 표면부가 급속하게 붕괴되어 화재에 취약한 소재이다. 본 연구에서는 열적 성능이 우수한 팽창 흑연을 사용할 경우 바탕조정재의 성능을 개선할 수 있을 것으로 기대하였다. 실험결과, 팽창흑연을 사용한 바탕조정재는 부착강도 저하 및 물흡수계수 등의 감소가 발생하는 문제점이 있으나 플라이애시와 실리카흄을 사용하여 물리적 성능이 향상되는 것으로 나타났다. 팽창흑연을 사용한 바탕조정재는 복합 단열 시험체 표면의 페놀폼은 화염에 의한 표면 뚫림이 나타나지 않아 열원의 투과를 감소시킬 수 있을 것으로 나타났다.

• 국제학술발표논문집
• /
• The 3th International Conference on Construction Engineering and Project Management
• /
• pp.1630-1636
• /
• 2009

Nine alkali-activated (AA) mortars were mixed and cured at water or air-dried conditions to explore the significance and limitation for the application of the combination of Ba and Ca ions as an alkali-activator. Ground granulated blast-furnace slag (GGBS) was used for source materials, and calcium hydroxide (Ca(OH)₂) and barium hydroxide (Ba(OH)₂) were employed as alkali activators. Test results clearly showed that the water curing condition was more effective than the air-dried curing condition for the formation of the denser calcium silicate hydrate (C-S-H) gels that had a higher molar Si/Ca ratio, resulting in a higher strength development. At the same time, the introduction of Ba(OH)₂ led to the formation of 2CaO·Al₂O₃·SiO₂·8H₂O (C₂ASH₈) hydrates with higher molar Si/Al and Ca/Al ratios. Based on the test results, it can be concluded that the developed cementless mortars have highly effective performance and high potential as an eco-friendly sustainable building material.

• 콘크리트학회논문집
• /
• 제29권3호
• /
• pp.275-281
• /
• 2017

본 연구는 물-결합재비(water-to-binder ratio, W/B) 및 인산염-결합재비(phosphate-to-binder ratio, P/B)가 마그네시아-인산칼륨 시멘트(magnesium-potassium phosphate cement, MKPC) 모르타르의 플로, 응결시간, 압축강도발현 및 pH 변화에 미치는 영향성에 대한 평가이다. MKPC 모르타르의 P/B가 0.3 및 0.5일 때 W/B 범위 20~40%에 대하여 10 배합의 모르타르 실험을 실시하였으며, X-선 회절 분석(X-ray diffraction, XRD), 전자현미경(scanning electron microscope, SEM) 및 수은압입법(mercury intrusion porosimetry, MIP) 분석을 위해 MKPC의 반응생성물 및 미세공극분포를 평가하였다. 실험결과, MKPC 모르타르의 플로 및 응결시간은 P/B의 증가에 따라 감소하였으며, P/B가 0.3에서 0.5로 증가함에 따라 종결시간은 약 24% 감소하였다. MKPC 모르타르의 초기 압축강도 발현 기울기의 경우 콘크리트 구조기준에서 제시하는 시멘트 콘크리트 대비 높은 수준에 있었다. 재령 28일의 압축강도 30 MPa 이상 및 pH 9.0 이하를 만족하기 위해 MKPC 모르타르의 P/B 및 W/B는 각각 0.5이상 및 30% 이하가 추천된다. MKPC의 반응생성물인 스트루바이트(struvite)-K의 결정은 MKPC의 P/B 및 W/B가 높을수록 증가하였는데, 이로 인해 거대 모세관 공극은 감소하였다.

• 한국건축시공학회지
• /
• 제12권3호
• /
• pp.275-283
• /
• 2012

본 연구는 철근 콘크리트 구조물의 장수명화를 위해 고성능 다기능 폴리머 시멘트 복합체의 개발을 목적으로, 우수한 성능을 갖는 VA/E/MMA (Vinyl Acetate/Ethylene/Methyl Methacrylate) 터폴리머 분말수지와 아질산형 하이드로칼루마이트를 병용한 폴리머 시멘트 모르타르의 염화물이온 침투 저항성, 중성화 저항성, 건조수축 및 철근부식 촉진시험을 통하여 그 내구성과 방청성을 검토하는 것이다. 그 결과, 폴리머 결합재비에 관계없이 칼루마이트의 치환에 의해 폴리머 시멘트 모르타르의 내구성이 일부 저하하는 경향을 보였으나, 이는 폴리머 결합재비의 증가에 따라 크게 개선되었다. 방청성의 경우 VA/E/MMA 분말수지 사용으로 시멘트 매트릭스 내 생성된 폴리머 필름에 의한 이온 및 가스투과 저항성 증대와 칼루마이트의 이온교환반응에 따른 염화물 이온 흡착 및 아질산 이온을 방출하는 자기방청기능에 의하여 우수한 방청효과를 보였다. 따라서, 철근콘크리트 구조물의 장수명화를 위해 VA/E/MMA 터폴리머 분말수지와 아질산형 하이드로칼루마이트의 병용에 의해 우수한 방청성과 내구성을 갖는 폴리머 시멘트 복합체의 개발이 가능할 것으로 판단된다.

• 콘크리트학회논문집
• /
• 제27권1호
• /
• pp.75-83
• /
• 2015

본 연구는 다양한 천연물계 항균물질로부터 추출된 추출액(extract)들의 자체 항곰팡이 성능을 평가하고, 이를 적용한 항균모르타르의 항곰팡이 성능과 그 지속성능, 그리고 항균성능 등에 대해 종합적으로 고찰함으로써 효율적인 건축물 내 항균대책 및 친환경 항균 건자재(모르타르 포함) 개발을 위한 기초적 자료를 제공하고자 수행하였다. 시험결과, 마조람 추출액 및 이를 적용한 항균모르타르의 항곰팡이 성능은 현재 널리 사용되고 있는 유기계 화학 항곰팡이제 및 이를 적용한 모르타르와 동등수준의 높은 항곰팡이 성능을 나타내었다. 특히 마조람 추출액 5% 혼입 모르타르는 장기 항곰팡이 성능뿐 아니라 대장균, 녹농균 및 황색포도상구균에 대한 항균성능에서도 뛰어나 그 활용가능성이 크게 기대되었으며, 향후 이에 대한 보다 상세한 검토가 요구된다.

• 한국광물학회지
• /
• 제30권4호
• /
• pp.179-186
• /
• 2017

본 연구는 남한산성 한봉성 여장에 사춤으로 사용된 석회 모르타르를 분석하여 조선시대에 사용된 석회의 광물학적 특성을 파악하고자 하였다. 편광현미경 관찰 결과 여장의 모르타르는 기질에 석영, 장석, 운모, 휘석과 불투명 광물을 함유하고 있으며 XRD 분석을 통해 점토 광물인 녹니석, 카올린을 추가로 확인하였다. 입도 분석 결과 시료의 입도 분포가 넓고 크기가 균일하지 않으며 입도의 60%가 모래영역에 해당되었다. XRF 분석 결과 석회의 주성분인 Ca은 8.71-11.18%로 나타났으며 토양에서 확인되는 $SiO_2$, $Al_2O_3$, $Fe_2O_3$가 주요 성분으로 확인되었다. TG-DTA 분석 결과 약 $750^{\circ}C$ 부근에서 탄산칼슘의 탈탄산반응으로 인한 흡열피크와 약 10%의 중량감소율을 확인하였으며, SEM을 통한 미세조직 관찰 결과 조밀하게 응집된 비정질, 능면상의 방해석 결정이 관찰되었다. 이를 바탕으로 여장의 사춤재는 석회와 토양이 혼합된 모르타르이며 여장의 위치나 사용부위에 따른 광물 조성 차이는 보이지 않으므로 당시 한봉성 여장은 동일한 재료와 기법을 사용하여 개축된 것으로 판단된다.

• International Journal of Concrete Structures and Materials
• /
• 제2권1호
• /
• pp.35-39
• /
• 2008

This experimental study examines the applicability of polymer mortar permanent forms using a methyl methacrylate (MMA) solution of waste expanded polystyrene (EPS) to develop effective recycling processes for the EPS, referring to the flexural behavior of a polymer-impregnated mortar permanent form with almost the same performance as commercial products. An MMA solution of EPS is prepared by dissolving EPS in MMA, and unreinforced and steel fiber-reinforced polymer mortars are mixed using the EPS-MMA-based solution as a liquid resin or binder. Polymer mortar permanent forms (PMPFs) using the EPS-MMA-based polymer mortars without and with steel fiber and crimped wire cloth reinforcements and steel fiber-reinforced polymer-impregnated mortar permanent form (PIMPF) are prepared on trial, and tested for flexural behavior under four-point (third-point) loading. The EPS-MMAbased PMPFs are more ductile than the PIMPF, and have a high load-bearing capacity. Consequently, they can replace PIMPF in practical applications.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2015년도 추계 학술논문 발표대회
• /
• pp.7-8
• /
• 2015

The purpose of this study is to investigate the expansion of alkali-activated geopolymer mortar containing reactive aggregate due to alkali-silica reaction. In addition, this study is particularly concerned with the behavior of these alkaline materials in the presence of reactive aggregates. The test method included expansion measurement of the mortar bar specimens and geopolymer compressive strength test. Major results that alkali-activated geopolymer mortars showed expansion due to the alkali-silica reaction. geopolymer mortars is safety for the expansion exhibited less than 0.2% at 14 day.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2001년도 가을 학술발표회 논문집
• /
• pp.239-244
• /
• 2001

Opens the construction market recently, the construction industry of Korea has faced up to the barrier of globalism, and has been enforced to follow the various global standards in many aspects. Accordingly, it is expected that the test method related to the cement and concrete will be changed to conform to the international standards in Korea. Therefore, in this study, the strength tests are executed for the cement mortars, made by KS and ISO standards respectively, and then obtains such results. 1) The flow of the cement mortar according to ISO is about 8% higher ,than that of KS. 2) The flexural strength of the cement mortar according to ISO is about 10~20% higher than that of KS, and the compressive strength is about 30% higher. 3) The compressive strength relation between the cement mortars of KS and ISO may be expressed in the first-order recurrence formula as follows: Y = 1.33X - 8 In which X is the compressive strength(kgf/$\textrm{cm}^2$) of the mortar according to KS and Y is the compressive strength(kgf/$\textrm{cm}^2$) of the mortar according to ISO.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 1994년도 가을 학술발표회 논문집
• /
• pp.235-239
• /
• 1994

Polymer mortars are mainly used as protective coatings in concrete, reinforced concrete, and more rarely, steel, while polymer concretes represent a new type of structural material capable of withstanding highly corrosive environments. The mechanical properties, chemical stability, and some other useful properties are the reasons research, design, and production organizations. However polymer mortars and polymer concretes have been introduced only recently, and many of their properties are still imperfectly known. And, the main technique in producing polymer concrete is to minimize void volume in the aggregate mass so as to reduce the quantity of the relatively impressive polymer necessary for binding the aggregate. In this study, compressive strength and flexural strength of unsaturated polyester resin concrete are related to quantity of resin and solid volume of aggregate. It was founded that the more solid volume of aggregate increase, the less using quantity of resin decrease with out reducing mechnical properties. When solid volume ratio of aggregate is 70.6%, using quantity of resin is minimized to 10wt.%.