• Journal of the Korean Society for Heat Treatment
• /
• v.33 no.1
• /
• pp.1-12
• /
• 2020

In this study, thin foil fabrication using Ni/Ni₃Al single crystal was performed by cold-rolling. It was found that the cold-rolling behavior was strongly dependent on the initial crystallographic orientation rather than morphology of Ni₃Al precipitates. The deformation banding was formed in the case of (100)[001]- and (210)[001]-oriented specimens at 83% reduction in thickness. However, the effects of Ni₃Al precipitates morphology on the microstructure evolution of Ni/Ni₃Al single crystals during cold-rolling were not so serious comparing with the effects of initial crystallographic orientation. Therefore, it could be concluded that the deformation behavior of Ni/Ni₃Al single crystals at serious strain level was strongly dependent on the initial crystallographic orientation rather than the morphology of Ni₃Al precipitates, whereas the initial deformation behavior was related to both crystallographic orientation and the morphology of Ni₃Al precipitates.

• Journal of the Korean Society for Heat Treatment
• /
• v.19 no.1
• /
• pp.10-19
• /
• 2006

Microstructure and morphology of precipitates in $Ni_3Al$- and TiAl-based intermetallics containing carbon have been investigated in terms of transmission electron microscopy(TEM). In an $L1_2$-ordered $Ni_3Al$ alloy with 4 mol.% of chromium and 0.2~3.0 mol.% of carbon, fine octahedral precipitates of $M_{23}C_6$ type carbide were formed in the matrix by aging at temperatures around 973 K after solution annealing at 1423 K. TEM examination revealed that the $M_{23}C_6$ phase and the matrix lattices have a cube-cube orientation relationship and keep partial atomic matching at the {111} interface. After prolonged aging or by aging at higher temperatures, the $M_{23}C_6$ precipitates then adopt a rod-like morphology elongated parallel to the <100> directions. In the $L1_0$-ordered TiAl containing 0.1~2.0 mol.% carbon, TEM observations revealed that needle-like precipitates, which lie only in one direction parallel to the [001] axis of the $L1_0$ matrix, appear in the matrix and preferentially at dislocations. Selected area electron diffraction(SAED) patterns analyses have shown that the needle-shaped precipitate is $Ti_3AlC$ of perovskite type. The orientation relationship between the $Ti_3AlC$ and the $L1_0$ matrix is found to be $(001)_{Ti3AlC}//(001)_{L10\;matrix}$ and $[010]_{Ti3AlC}//[010]_{L10\;matrix}$. By aging at higher temperatures or for longer period at 1073 K, plate-like precipitates of $Ti_2AlC$ with a hexagonal structure are formed on the {111} planes of the $L1_0$ matrix. The orientation relationship between the $Ti_2AlC$ and the $L1_0$ matrix is $(0001)_{Ti2AlC}//(111)_{L10\;matrix}$ and $_{Ti2AlC}//_{L10\;matrix}$.

• Journal of the Korean Society for Heat Treatment
• /
• v.10 no.1
• /
• pp.55-62
• /
• 1997

The morphology of deformation induced dislocations in polycrystalline $Ni_3$(Al, Cr) containing $M_{23}C_6$ precipitates has been investigated in terms of transmission electron microscopy(TEM). Fine Polyhedral precipitates of $M_{23}C_6$ appeared in the matrix by aging at temperatures around 973 K after solution annealing at 1423 K. TEM examination revealed that the $M_{23}C_6$ phase and the matrix lattices have a cube-cube orientation relationship and keep partial atomic matching at the {111} interface. After deformation at temperature below 973 K, typical Orowan loops were observed surrounding the $M_{23}C_6$ particles. At higher deformation temperatures, the Orowan loops disappeared and the morphology of dislocations at the particle-matrix interfaces suggested the existence of attractive interaction between dislocations and particles. The change of the interaction modes between dislocation and particles with increasing deformation temperature can be considered as a result of strain relaxation at the interface bet ween matrix and particles.

• Korean Journal of Materials Research
• /
• v.17 no.8
• /
• pp.420-424
• /
• 2007

Precipitation behavior has been studied in NiTi-based ordered alloy using transmission electron microscopy. The hardness after solution treatment is high in NiTi alloy suggesting the large contribution of solid solution strengthening in this alloy system. However, the amount of age hardening is not large as compared to the large microstructural variations during aging. At the beginning of aging, the $L2_1-type$ $Ni_2AlTi$ precipitates keep a lattice coherency with the NiTi matrix. By longer periods of aging $Ni_2AlTi$ precipitates lose their coherency and change their morphology to the globular ones surrounded by misfit dislocations. Misfit dislocations, which are observed on {100} planes of H-precipitates have the Burgers vector of a <100> with a pure edge type. The lattice misfits of $NiTi-Ni_2AlTi$ system is estimated from the spacings of misfit dislocations to be 1.3% at 1273 K. The lattice misfits decrease with increasing aging temperature in this system.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2006.11a
• /
• pp.31.2-31.2
• /
• 2006

• Korean Journal of Materials Research
• /
• v.16 no.4
• /
• pp.241-247
• /
• 2006

Structural studies have been performed on precipitation hardening discovered in $L1_2-ordered\;Ni_3(Al,Cr)$ containing 0.2 to 3.0 mol% of carbon using transmission electron microscopy (TEM). Fine octahedral precipitates of $M_{23}C_6$ appeared in the matrix by aging at temperatures around 973 K after solution treatment at 1423 K. TEM examination revealed that the $M_{23}C_6$ phase and the matrix lattices have a cube-cube orientation relationship and keep partial atomic matching at the {111} interface. After prolonged aging or by aging at higher temperatures, the $M_{23}C_6$ precipitates then adopt a rod-like morphology elongated parallel to the <100> directions. Deformation at temperature below 973 K, typical Orowan loops were observed surrounding the $M_{23}C_6$ particles. At higher deformation temperatures, the Orowan loops disappeared and the morphology of dislocations at the particle-matrix interfaces suggested the existence of attractive interaction between dislocations and particles. The change of the interaction modes between dislocation and particles with increasing deformation temperature can be considered as a result of strain relaxation at the interface between matrix and particles.

• Journal of the Korean Society for Heat Treatment
• /
• v.21 no.5
• /
• pp.251-258
• /
• 2008

A transmission electron microscope investigation has been performed on the morphology of dislocations in deformed ${\gamma}^{\prime}-Ni_3(Al,Ti)$ alloys containing fine dispersion of disordered ${\gamma}$ particles. Superlattice dislocations dissociate into fourfold Shockley partial dislocations in a uniform supersaturated solid solution of the ${\gamma}^{\prime}$ phase. Dislocations are attracted into the disordered ${\gamma}$ phase and dissociate further in the particles. At any stage of aging, dislocations cut through the particles and the Orowan bypassing process does not occur even in the over-aged stage of this alloy system. The work necessary to pull the dislocation away from the disordered particles into the ordered matrix should mainly contribute to increase the strength of the ${\gamma}^{\prime}$ phase containing fine dispersion of the disordered ${\gamma}$ phase.

• Korean Journal of Materials Research
• /
• v.8 no.12
• /
• pp.1165-1169
• /
• 1998

A single crystal cast blade was manufactured by CMSX 6, one of the first generarion nickel based single crystal superalloys by the selector method in a vacuum furnace. The single crystal has been grown with cooling rate of 2.5 mm/min, after pouring the molten alloy of 163$0^{\circ}C$ to the mold heated to 150$0^{\circ}C$. The cast structure could be classified into matrix (dendrite) and eutectic regions in ${\gamma}$'shape and size. The eutectic region showed higher Ti content. As the additional results of ${\gamma}$'precipitates by EPMA and CBED analysis the ${\gamma}$'size was less than 0.5~0.7$\mu\textrm{m}$, showing the chemical composition close to Ni$_3$Al of Ll$_2$ lattice structure. But ${\gamma}$'size has increased to bigger than 1.0$\mu\textrm{m}$, being near to eutectic region, changing its shape to bar or huge block types. These showed the chemical structure near to Ni$_3$Ti of D $O_{24}$ lattice structure. Therefore, ${\gamma}$'morphology of dendrite and eutectic regions depends absolutely on its chemical composition and lattice structure.