• Journal of the korean academy of Pediatric Dentistry
• /
• v.44 no.3
• /
• pp.335-340
• /
• 2017

Composite resin becomes an essential material in pediatric dentistry. However, incremental filling of composite resin to minimize the polymerization shrinkage takes time. To reduce the polymerization shrinkage, clinicians and researchers have focused on bulk-filling materials. Bulk-base composite resin is newly introduced as bulk-filling composite resin. The purpose of this study was to evaluate microhardness profile of bulk-base composite resin according to the depth of cure. A high flow bulk-base material and a low flow bulk-base material were used for experimental group, and a conventional composite resin was used for control group. Each group consist of 20 specimens, $3.5{\times}3.5{\times}5.0mm$ mold was used to make specimen. Specimens were sectioned at the 2 mm and the 3 mm depth with milling machine. Microhardness profile was measured at the surface, 2 mm depth, 3 mm depth, and 4 mm depth. Microhardness of control group showed statistically significant difference (p < 0.05) according to the polymerization depth. In contrast, experimental group showed no statistically significant difference, except between 0 mm and 4 mm at HFB, 0 mm and 2 mm, 0 mm and 3 mm at MFB. At the surface and the 2 mm depth, the control group showed higher microhardness than the experimental groups (p < 0.05). However, at the 4 mm depth, the experimental groups showed significantly higher microhardness (p < 0.05). The results from this study, the bulk-base composite resin showed higher microhardness at the 4 mm and lower microhardness at the surface and the 2 mm depth. Therefore, if bulk-base resin overcomes the mechanical weakness, it could be considered using in pediatric dentistry.

• Journal of Korean Ophthalmic Optics Society
• /
• v.18 no.4
• /
• pp.365-371
• /
• 2013

Purpose: In this study, we evaluated the physical and thermal properties of the compositions made by blending glass fiber (GF) of different contents into glass fiber polyamide-66, and investigated if the compositions applying to the glasses frame to replace the TR-90, which is polyamide-12 resin used as an injection-type spectacle frame material. Methods: To investigate the characteristics change of polyamide-66 (PA-66) compositions with the change of the content of glass fibers, we produced a composition of the content by using a twin-screw extruder. The mechanical strength of the composition production was measured and coating properties as well as cutting processability were evaluated. We evaluated the applicability of the glasses frame by comparison the results of new compositions with characterizations of traditional TR. Results: For the results of the characterization of Polyamide-66/GF composition, we found that the higher increase of content of the glass fiber, the less mold shrinkage rate, and the mechanical strength was increased. Tensile strength increased from $498kg/cm^2$ for 0 wt% of the content of the glass fibers to $849kg/cm^2$ for 30 wt% of the content of the glass fibers. As a result of a coating evaluation, the strength of coating was 4B in the GF 5wt% and 5B, which was extremely good coating characteristics, in the over than GF 5 wt%. Conclusions: In case that 30 wt% of the glass fiber was blended, the mechanical strength was greatly improved, the hardness was increased, injection temperature increased due to increase of the viscosity, and the flow mark of the product may occur. The paint coating of PA-66 blended with glass fiber was all excellent. With general evaluating physical properties and workability properties it was determined that around 10 wt% of the content of the glass fibers was possible to apply a spectacle frame.