• International Journal of Highway Engineering
• /
• v.15 no.2
• /
• pp.65-71
• /
• 2013

PURPOSES : The objective of this study is to evaluate the effect of physical characteristics of emulsion asphalt and aggregate on performance of chip seal pavements. METHODS : In order to evaluate the performance of chip seal materials, the sweep tests and Vialit Plate Shock tests were conducted on the mixtures with five emulsion asphalt binders and three aggregate types. The sweep tests was intended to investigate the change of bonding properties between emulsion asphalt and aggregate with curing time. The Vialit Plate Shock test was used to evaluate the bonding properties of chip seal materials at low temperatures. RESULTS : Results from sweep tests showed that polymer modified emulsion asphalt can reduce the curing time by 1.5 hour comparing with typical emulsion asphalt. It is also found that the Flakiness Index of aggregates and absorption rate of binder are the major factors affecting the bonding properties of chip seal materials. The Vialit Plate Shock test results showed that the average aggregate loss of CRS-2 is ten times higher than CRS-2P No.2 indicating that the use of polymer additives in emulsion asphalt can improve the performance of chip seal materials in low temperature region. CONCLUSIONS : The use of polymer in emulsion asphalt can decrease the curing time of chip seal materials and increase the bonding properties between aggregates and asphalt binder. It is also concluded that the lower Flakiness Index and absorption rate of aggregates can improve the performance of chip seal pavement.

• International Journal of Highway Engineering
• /
• v.19 no.2
• /
• pp.75-85
• /
• 2017

PURPOSES : The purpose of this study was to determine the optimum mix design of the content of 100 % reclaimed asphalt pavement (RAP) for spray injection application with different binder types. METHODS : Literature review revealed that spray injection method is the one of the efficient and economical methods for repairing a small defective area on an asphalt pavement. The Rapid-Setting Polymer modified asphalt mixtures using two types of rapid setting polymers-asphalt emulsion and a quick setting polymer asphalt emulsion-were subjected to the following tests to determine optimum mix designs and for performance comparison: 1) Marshall stability test, 2) Retained stability test, 3) Wet track abrasion test, and 4) Dynamic stability test. RESULTS and CONCLUSIONS : Type A, B, and C emulsions were tested with different mix designs using RAP aggregates, to compare the performances and determine the optimum mix design. Performance of mixtures with Type A emulsion exceeded that of mixtures with Type B and C emulsion in all aspects. In particular, Type A binder demonstrated the highest performance for WTAT at low temperature. It demonstrated the practicality of using Type A mixture during the cold season. Furthers studies are to be performed to verify the optimum mix design for machine application. Differences in optimum mix designs for machine application and lab application will be corrected through field tests.

• Elastomers and Composites
• /
• v.49 no.2
• /
• pp.134-143
• /
• 2014

Polymers are introduced to neat asphalt to prepare self-healing asphalt. The polymers are Surlyn, Nylon and polyethyleneterephtalate(PET). Since they are known as having high intermolecular force, they have high processing temperature. Therefore they are hardly introduced into the asphalt as bulk state. So in this study, they are introduced as solutions. Polymer-modified asphalts showed excellent modification effect and also healing effect. 5% polymer added asphalt showed more than 18% increased tensile strength. This tensile strength increment can be explained by polymer's intermolecular forces. Especially Surlyn interacts with asphalt molecules by hydrogen bonding and also with metals in asphalt by ionic bonding. When it comes to healing aspect the healing efficiency of Surlyn increased to 138% based on tensile strength. That of PET increased to 141% based on complex modulus and in case of Nylon it increased to 131% based on impact strength. This tells that in dealing with healing efficiency the important considering factors are not only the intermolecular forces of the polymers but also the interaction between the polymer and asphalt molecules.

• International Journal of Highway Engineering
• /
• v.18 no.6
• /
• pp.41-50
• /
• 2016

OBJECTIVES : In this study, microstructural components of crumb rubber modified asphalt (CRMA) binder were investigated using environmental scanning electron microscope (ESEM). To clearly understand the elemental composition of the CRMA binder, energy dispersive X-ray spectroscopy (EDX) was employed on the ESEM samples. METHODS : CRMA binders were produced using open blade mixers at $177^{\circ}C$ for 30 min. The binders were artificially aged through a series of accelerated aging processes. Sample preparation was done by making a mold shape on the glass slide. Thereafter, the morphology of the CRMA binder was observed using the ESEM coupled with the EDX. RESULTS : The images captured from the ESEM indicate that the unaged CRMA binder appears to have a single-phase continuous nonuniform structure after the addition of crumb rubber particles, whereas the artificially aged CRMA binder was observed to have two different phases. ESEM coupled with EDX shows detailed internal structure of the modified binders compared to other technologies (i.e., optical microscopy, atomic force microscopy, and conventional scanning electron microscope). CONCLUSIONS : The captured images resemble the internal structures such as the viscous properties of the unaged CRMA binder and the interaction between the rubber particles and the base binder at aged condition. ESEM is a powerful instrument and with the introduction of EDX, it provided more details of the network microstructure of the asphalt binder. ESEM coupled with EDX is recommended for use in future investigation of microstructure of asphalt binders.

• Journal of the Korea Institute of Building Construction
• /
• v.17 no.5
• /
• pp.437-444
• /
• 2017

In the composite waterproofing method in which a polyurethane coating waterproofing material is applied on the modified asphalt waterproofing sheet, the organic solvent is diluted in the coating waterproofing material in order to improve the workability. However, since the organic solvent is not volatilized before the curing of the polyurethane coating waterproofing material, the organic solvent causes dissolution of asphalt layer, thereby causing oil leakage. As a result, a polyamide film having a high dissolution resistance property was laminated on modified asphalt sheet, and through testing the dissolution resistance was visually confirmed and quantitative analysis of the polyamide film by SEM-EDX analysis was also used to confirmed the dissolution resistance of the polyamide film.

• Korean Chemical Engineering Research
• /
• v.55 no.5
• /
• pp.690-697
• /
• 2017

In this study, styrene-isoprene-styrene (SIS)-styrene-butadiene-styrene (SBS) modified asphalt was prepared for waterproof-sheet to measure its properties including softening point, penetration, low temperature flexibility, viscosity and adhesion. Then the properties of SIS-SBS modified asphalt imparted with self-healing were optimized to seek for optimal compositions of SIS and SBS versus asphalt according to response surface methodology (RSM). As the content of SBS or SIS was increased, both properties of softening point and viscosity, measured at high temperature, were increased with a statistical significance. However, the increments of softening point and viscosity per unit content of SBS added, were observed to be greater than those per unit content of SIS added, respectively. It was due to the difference of thermal properties of SBS and SIS at high temperature that the cross-linking degree of SBS was increased by gelation accompanied with the increase of viscosity, while chain-entanglement of SIS was relatively reduced owing to a chain scission of poly(isoprene) blocks causing the decrease of viscosity. To the contrary, SIS-SBS modified asphalt showed a behavior of the least elasticity resulting in both the maximum of penetration and adhesion, measured at room temperature, as well as the lowest low temperature flexibility at the composition of SIS, 4 g and SBS, 8.5 g based on asphalt, 63 g.

• International Journal of Highway Engineering
• /
• v.14 no.5
• /
• pp.85-91
• /
• 2012

PURPOSES: In this study, various laboratory tests were performed to investigate the suitability of wasted vinyl as a modifier of asphalt binder. METHODS: Based on the ASTM specification, variations in material properties of asphalt binder such as penetration, flash point, softening point, ductility, penetration index (PI), and performance grade (PG) with vinyl content were tested and analyzed. RESULTS: Lavoratory tests revealed that penetration and ductility of the asphalt binder increased with the vinyl content. The flash point, softening point, and PI decreased, and PG changed from 64-22 to 70-22 with increase of the vinyl content. CONCLUSIONS: Wasted vinyl modified the material properties of the asphalt binder. However, the asphalt binder with vinyl content over 6.0% was unsuitable as a pavement material.

• International Journal of Highway Engineering
• /
• v.17 no.3
• /
• pp.69-76
• /
• 2015

PURPOSES : Performance evaluation of four types of asphalt concrete overlays for deteriorated national highways. METHODS : Pavement distress surveys for crack rate and rut depth have been conducted annually using an automated pavement survey vehicle since 2007. Linear and non-linear performance prediction models of the asphalt concrete overlays were developed for 43 sections. The service life of the asphalt overlays was defined as the number of years after which a crack rate of 30% or rut depth of 15mm is observed. RESULTS : The service life of the asphalt overlays was estimated as 17.4 years on an average. In 90.7% of the sections, the service life of the overlays was 15 years or more which is 1.5 times the life of conventional asphalt concrete overlays used in national highways. The performance of the overlays was dependent on the type of asphalt mixture, traffic volume levels, and environmental conditions. CONCLUSIONS : The usage of stone mastic asphalt (SMA) and polymer-modified asphalt (PMA) for the overlays provided good resistance to cracking and rutting development. It is recommended that appropriate asphalt concrete overlays must be applied depending on the type of existing pavement distress.

• International Journal of Highway Engineering
• /
• v.12 no.4
• /
• pp.53-60
• /
• 2010

Geogrid-reinforced asphalt pavement is a pavement type applicable to overlay for repair in addition to new construction. The geosynthetic materials are placed between the asphalt layers to stop or delay propagation of the cracking existing at lower layers and to reduce the rutting. In this study, the cracking, rutting, IRI, and deflection were investigated to compare the performance between geogrid-reinforced asphalt pavement and ordinary or polymer modified asphalt pavement. Based on field conditions, the 11 sections were classified into 3 groups; sections proper to compare, sections with restrictions to compare, sections with difficulties in comparing, and the data was statistically analyzed. Larger resistance to rutting and increased IRI were measured at the geogrid-reinforced asphalt pavement sections comparing to the ordinary or polymer modified asphalt pavement sections. However, the deflections of the pavements were similar and the resistance to the cracking could not be compared because of short pavement lives.

• International Journal of Highway Engineering
• /
• v.19 no.2
• /
• pp.87-95
• /
• 2017

PURPOSES : The objectives of this study are to evaluate moisture sensitivity of various asphalt mixtures and to suggest an alternate method for the dynamic immersion test, which is used to determine the application of anti-stripping agent, by analyzing bond strength. METHODS : The bond strength of various asphalt mixtures such as hot mix asphalt, warm mix asphalt, and polymer-modified asphalt was evaluated by the ABS test. In order to characterize moisture sensitivity at different temperatures of the mixtures, the ABS test was conducted at $-10^{\circ}C$, $5^{\circ}C$, $20^{\circ}C$, $40^{\circ}C$, and $54^{\circ}C$ under both dry and wet conditions. The concept of the bond strength ratio was applied for objective moisture sensitivity analysis. Moreover, the bond strength characteristic was compared to the dynamic immersion test to suggest an alternate method to determine the application of anti-stripping agent. RESULTS AND CONCLUSIONS : Overall, the polymer-modified asphalt demonstrates the highest bond strength characteristic regardless of moisture condition and temperature. The bond strength characteristic displays a highly reliable linear relationship from $5^{\circ}C$ to $40^{\circ}C$, and the relationship could be used to predict bond strength at any intermediate temperature. Based on the analysis of bond strength and retained asphalt ratio, the bond strength value of 1254 kPa could be applied as a criterion for anti-stripping agent.