• Journal of the Korean Society of Propulsion Engineers
• /
• v.1 no.1
• /
• pp.82-88
• /
• 1997

The goal is to assess the effect of fatigue loading on mechanical properties of Fiberite 934/T300 laminates of pressure vessel using the recent variational mechanics analysis. This analysis has been useful in providing fracture mechanics interpretation of matrix microcracking in cross-ply laminates. This paper describes using the new energy release rate analysis for a fracture mechanics based interpretation of microcrack formation during fatigue loading. The master plot by modified Paris-law gives a complete characterization of a material system's resistance to microcrack formation.

• Structural Engineering and Mechanics
• /
• v.17 no.1
• /
• pp.51-68
• /
• 2004

Since the linear elastic fracture analysis has been proved to be insufficient in predicting the failure of strain hardening materials, a number of fracture concepts have been studied which remain applicable in the presence of plasticity near a crack tip. This work thereby presents a new finite element model to predict the elastic-plastic crack-tip field and fatigue life of center-cracked panels(CCP) with ductile fracture under large-scale yielding conditions. Also, this study has been carried out to investigate the path-dependence of J-integral within the plastic zone for elastic-perfectly plastic, bilinear elastic-plastic, and nonlinear elastic-plastic materials. Based on the incremental theory of plasticity, the p-version finite element is employed to account for the accurate values of J-integral, the most dominant fracture parameter, and the shape of plastic zone near a crack tip by using the J-integral method. To predict the fatigue life, the conventional Paris law has been modified by substituting the range of J-value denoted by ${\Delta}J$ for ${\Delta}K$. The experimental fatigue test is conducted with five CCP specimens to validate the accuracy of the proposed model. It is noted that the relationship between the crack length a and ${\Delta}K$ in LEFM analysis shows a strong linearity, on the other hand, the nonlinear relationship between a and ${\Delta}J$ is detected in EPFM analysis. Therefore, this trend will be depended especially in the case of large scale yielding. The numerical results by the proposed model are compared with the theoretical solutions in literatures, experimental results, and the numerical solutions by the conventional h-version of the finite element method.

• Proceedings of the Korean Society of Propulsion Engineers Conference
• /
• 1996.11a
• /
• pp.45-52
• /
• 1996

The goal is to assess the effect of fatigue loading on mechanical properties of Fiberite 934/T300 laminates of pressure vessel using the recent variational mechanics analysis. This analysis has been useful in providing fracture mechanics interpretation of matrix microcracking in cross-ply laminates. This paper describes using the new energy release rate analysis for a fracture mechanics based interpretation of microcrack formation during fatigue loading. The master plot by modified Paris-law gives a complete characterization of a material system's resistance to microcrack formation.

• Proceedings of the Computational Structural Engineering Institute Conference
• /
• 1999.10a
• /
• pp.429-436
• /
• 1999

The best available solution to predict the fatigue life of structural steels is the implementation of EPFM approach based on the principles and techniques of elasto plastic fracture mechanics. To predict the fatigue life, the conventional Paris law has been modified by substituting the range of J-value denoted by ΔJ for ΔK that is calculated by the proposed p-version model. The proposed P-version finite element model is formulated by the incremental theory of Plasticity that consists of the constitutive equation fur elastic-perfectly plastic materials, Tresca/von-Mises yield criteria, and associated flow rule. The experimental fatigue test is conducted with five UP(Center Clucked Panels) specimens to validate the accuracy of the p-version finite element model. Also, the results obtained by LTM approach have been compared with those by EPFM approach.

• Proceedings of the KSME Conference
• /
• 2004.11a
• /
• pp.220-225
• /
• 2004

The mesh-insensitive structural stress procedure by Dong is modified to apply to the welded joints with local thickness variation and inignorable shear/normal stresses along local discontinuity surface. In order to make use of the structural stress based K solution for fatigue correlation of welded joints, a proper crack growth model needs to be developed. There exist some significant discrepancies in inferring the slope or crack growth exponent in the conventional Paris law regime. Two-stage crack growth model was not considered since its applications are focused upon the fatigue behavior in welded joints in which the load ratio effects are considered negligible. In this paper, a two-stage crack growth law considering high mean loading is proposed and proven to be effective in unifying the so-called anomalous short crack growth data.

• Proceedings of the Korean Society For Composite Materials Conference
• /
• 2005.11a
• /
• pp.39-44
• /
• 2005

The effects of aging of PSF/AS4 laminates on fatigue was studied using the new energy release rate analysis. The analysis by the variational mechanics has been useful in providing fracture mechanics interpretation of matrix microcracking in cross-ply laminates. This paper describes the changes of the critical energy release rate (microcracking toughness) according to the aging period under fatigue loading. The master plot by modified Paris-law gives a characterization of a material system's resistance to microcrack formation. PSF $[0/90_{s}]_{s}$ laminates were aged at four different temperature based on the glass transition temperature for 0 to 60 days. At all temperatures, the toughness decreased with aging time. The decrease of the toughness at higher temperature was faster than at lower temperature. To assess the effects of aging on fatigue, the unaged laminates were compared with the laminates which had been aged for 60 days at 170$^{\circ}C$ near 180 $^{\circ}C$ t$_g$. The slope of dD/dN versus ${\Delta}G_m$. of the aged laminates was lower than that of the unaged laminates. There was a significant shift of the aged data to formation of microcracks at the lower values of ${\Delta}G_m$.

• Proceedings of the KSME Conference
• /
• 2008.11a
• /
• pp.356-361
• /
• 2008

In characteristics of fatigue crack propagation, it is important that fatigue life is affected by crack closure phenomenon in thin sheet Al alloy. The purpose of this paper is to analyze the characteristics of fatigue crack propagation in constant loading condition for sheet Al 2024-T3 alloy of two sort of thickness and identify the difference of fatigue life in thin sheet specimen comparing experimental results of thin sheet specimen and relatively thick sheet specimen under same fatigue loading condition. In applying fatigue related material constants from fatigue crack propagation analysis, we attempt to operate the fatigue life estimating process of thin sheet specimen by modified Paris‘ law considering crack closure phenomenon and analyze the experimental and prediction results of fatigue life in thin sheet Al alloy.

• Transactions of the Korean Society of Pressure Vessels and Piping
• /
• v.11 no.2
• /
• pp.45-50
• /
• 2015

In many cases, the field fracture mechanism of the thermoplastic pipe is considered as either brittle or environmental fractures. Thus the estimation of the lifetime by modeling slow crack growth considering such fracture mechanisms is required. In comparison of the some conventional and empirical equations to explain the slow crack growth rate such as the Paris' law, the crack layer theory can be used to simulate the crack and process zone growth behaviors precisely, so the lifetime of thermoplastic pipe can also be accurately estimated. In this study, the modified crack layer theory for the stress corrosion cracking (SCC) of high density polyethylene is introduced with detailed algorithm. The oxidation induction time of the HDPE is also considered for the reduction of specific fracture energy during exposed to chemical environments. Furthermore, the parametric study for an important SCC parameter is conducted to understand the slow crack growth behavior of SCC.

• Advanced Composite Materials
• /
• v.16 no.2
• /
• pp.151-166
• /
• 2007

High-cycle fatigue characteristics of quasi-isotropic carbon fiber reinforced plastic (CFRP) laminates [-45/0/45/90]s up to $10^8$ cycles were investigated. To assess the fatigue behavior in the high-cycle region, fatigue tests were conducted at a frequency of 100 Hz, since it is difficult to investigate the fatigue characteristics in high-cycle at 5 Hz. Then, the damage behavior of the specimen was observed with a microscope, soft X-ray photography and a 3D ultrasonic inspection system. In this study, to evaluate quantitative characteristics of both transverse crack propagation and delamination growth in the high-cycle region, the energy release rate associated with damage growth in the width direction was calculated. Transverse crack propagation and delamination growth in the width direction were evaluated based on a modified Paris law approach. The results revealed that transverse crack propagation delayed under the test conditions of less than ${\sigma}_{max}/{\sigma}_b$ = 0.3 of the applied stress level.

• Korean Security Journal
• /
• no.47
• /
• pp.85-117
• /
• 2016

These days, ISIS terrorists have been expanding not only to european countries, but also to asian countries so South Korea is no longer safe from terrorists' attacks. Especially, 'soft target terrorism' makes many people maximizing fear of terrorism because it is caused by small groups - those who are armed with small arms and light weapons - and they are able to carry out hit and run attacks on civilian targets. It poses even more dangerous to kill massively. That is why November 2015 Paris attacks and January 2016 Jakarta attacks killed and injured many people because of 'soft target terrorism.' Therefore, the South Korea has also recognized the seriousness of terrorism by ISIS. The study has shown the precautionary measures about 'soft target terrorism' and how to defend against 'soft target terrorism' by looking through overseas examples. It is for the possibilities of 'soft terrorism' in South Korea because of the expansion of ISIS. As a result, 'soft target terrorism', caused by ISIS, could happen in South Korea. The counterplan is as in the following. First of all, 'soft target terrorism', which is collaborated with ISIS and domestic terrorists, could be caused by negative awareness of foreign residents and xenophobia so the public should change stereotypes about the foreign residents and there should be legislation about racial discrimination enacted by parliament and the government must practice the law. Second, the Korean anti-terrorism laws should be modified to minimize violations of human rights, related to the Korean citizens' personal information, and to stop the concentration of power into the hands of one law enforcement. Third, the government has to develop and to initiate the refuge&evacuation simulation, which prepares for 'soft target terrorism' and minimizes the damages if terrorists attack hot spots like central commercial areas or event halls.