• 한국염색가공학회지
• /
• 제2권1호
• /
• pp.21-30
• /
• 1990

In order to obtain high dye uptake initially, polyethylene terephthalate (PET) filaments were dyed with C.I.Disperse Orange 3 and Red 1 in mixed solvents of tetrachloroethylene acidic solvent, ethyl alcohol and tetrachloroethylene basic solvent, DMF. The dyeing behavior in the mixed solvent of tetrachloroethylene and basic solvent, DMF, the initial uptake of disperse dyes increased rapidly. The shrinkage of PET increased when the solubility parameter values of PET fiber and mixed solvent approached graduately.

• 폴리머
• /
• 제25권6호
• /
• pp.811-817
• /
• 2001

용매와 비용매의 다양한 비율에 따라서 bisphenol A polycarbonate(PC)의 무정형에서 결정성의 상변화를 확인하였다. 용매로 chloroform을, 비용매로 isopropanol을 사용하였다. 결정화된 PC는 광학현미경과 SEM, XRD, DSC를 이용하여 조사하였고, DSC와 XRD의 측정값은 PC의 결정화도를 판단하는데 이용하였다. 용해도 상수는 PC의 결정화도를 조절하는데 중요한 인자로 PC 결정화도 차이는 혼합용매의 용해도 상수 차이로 설명하였다. 용매와 비용매 비율이 75/25 wt%의 PC 용액에서 고결정화도를 가진 PC powder로 얻을 수 있었다. 이런 결과는 혼합용매의 용해도 상수(9.85)가 PC의 용해도 상수(9.9)와 유사하였기 때문이라고 판단된다.

• Archives of Pharmacal Research
• /
• 제20권3호
• /
• pp.269-274
• /
• 1997

Solubilities of oleanolic acid and ursolic acid in aqueous surfactant solutions, liquid polyethylene glycols (PEG), and solvents of various polarity were measured. The results showed that the solutes were slightly or moderately solubilized in the surfactant solutions and the liquid PEGS. It was also revealed that the solutes were slightly soluble in the solvent of either extreme polarity or nonpolarity, but moderately soluble in solvents of intermediate polarity of which solubility parameters are around 10. The solubility parameters of these solutes were calculated from the group contribution to be 10.2 for both of them. Of the solvents tested, tetramethylurea was exceptionally effective in solubilizing the solutes. The solutes were also moderately soluble in the aqueous cosolvents containing tetramethylurea. This suggests that the mixed systems of tetramethylurea could be employed for the solubilization in the formulation of these compounds as an aqueous system.

• 멤브레인
• /
• 제31권2호
• /
• pp.153-159
• /
• 2021

최근 들어 여러 산업 분야에 활발히 사용되고 있는 고분자 분리막은 화학구조의 제어나 제막공정에서의 물리적 특성 제어뿐만 아니라 다양한 소재와 혼합된 복합막 제조를 통해서 고유의 특성을 부여할 수 있는 장점을 가지고 있다. 본 연구에서는 분리막 제조 시에 누에(Bombyx mori)가 생산한 친환경 천연소재로 활용 가능성이 넓은 실크 고분자의 복합막 제조 시 다른 소재와의 혼화성 지표로 사용할 수 있는 용해도 파라미터를 분자동역학을 이용하여 계산하였다. 역시 친환경성 및 생체적합성을 갖고 있는 polyvinylalcohol (PVA)의 용해도 파라미터를 분자동역학을 이용하여 계산 후 서로 비교하였을 때 두 고분자 소재가 비슷한 용해도 파라미터 값을 갖는 것을 확인하였다. 결론적으로, 두 고분자가 서로 잘 혼합될 수 있음을 이론적으로 증명하였고, 실제 실험을 통해서도 이를 확인할 수 있었다.

• 한국염색가공학회지
• /
• 제15권6호
• /
• pp.55-62
• /
• 2003

Wool fabrics were dyed with the aqueous solution of C. I. Red Acid 114 mixed with methanol dissolving three kinds of barely water soluble ketones, acetophenone, 2-pentanone, and 3-pentanone. The steric hinderance and the orientation of the bigger hydrophobic part of the solvated dye molecules to the fiber slowed down the dying rate, however, loosening the wool molecule, say a little swelling, disaggeregating the dye molecules, and attaining the higher dye concentration on the fiber surface by the added solvents increased the amount of dye on the fabric. The higher concentration or/and the higher dyeing temperature helped loosen fiber molecules and made it easier for the solvated dye molecules to penetrate into the inside of the fiber. Acetophenone, the most influential solvent used, showed that the ability to loosen fiber molecules was the most important of all the three positive solvent actions mentioned above. The considered mechanism provided before reflected the fact that the dye uptake on the fabric dyed with the solvents included, except for 0.034M and 0.051M of acetophenone, was even lower than that without any solvents at $50^\circ{C}$, but all the solvents added to the dye bath increased the dye uptake on the fiber at $70^\circ{C}$.

• 한국인쇄학회지
• /
• 제21권1호
• /
• pp.81-90
• /
• 2003

To understand the thermoresponsive volume phase transition of an N-isopropyl acrylamide(NIPA) gel on water, the solubility parameter of neutral NIPA gel was determined by swelling the gel with various solvents. Water was found not to be a good solvent for NIPA gel. Equilibrium swelling curves of NIPA gel were respectively obtained by immersing in pure water, ethanol, n-propanol and some mixed solvents. On adding a small amount of alcohols to water, volume phase transition of NIPA gel in water was changed. Phase transition temperature of this gel was decreased with the increase of the carbon number of alcohol.

• Elastomers and Composites
• /
• 제43권4호
• /
• pp.230-240
• /
• 2008

분산중합법에 의해 무기물을 포함하는 고분자 미립자를 합성하기 위해 styrene과 n-butyl methacrylate가 알루미나와 함께 중합되었다. Styrene과 n-butylmethacrylate의 무게 비는 3:1이었고, 입자안정제는 poly(N-vinyl pyrrolidon), 중합 개시제로는 2,2'-azobis(isobutyronitrile)를 사용하여 개시제의 농도, 분산매의 종류, 분산매의 혼합 용해도 상수 (${\delta}_{mix}$), 커플링제의 종류와 농도에 따른 입자경을 조사하였다. 개시제의 농도가 증가함에 따라 입자경이 소폭 상승하였고 분산매의 극성이 증가할수록 입경이 증가하였고, 분산매로서, 이소프로판올과 이온교환수를 조성비에 따라 사용한 경우, $[{\delta}_{mix}]^{-4.01}\;{\propto}$ 평균 입자경과 $[{\delta]_{mix}]^{-0.83}\;{\propto}$ 입경 분포의 관계를 얻을 수 있었다. 커플링제의 종류와 농도변화에 따른 입자경 및 입자경 분포는 뚜렷한 차이가 없었다.

• Bulletin of the Korean Chemical Society
• /
• 제10권1호
• /
• pp.34-39
• /
• 1989

The relationship between the solute retention and physical parameters describing the interaction between the solute and mobile phase was investigated to predict the solute retention easily in RPLC. The retention data of monosubstituted benzenes were measured on the $\mu$-Bondapak C18 and phenyl columns with methanol-water systems. The linear relationship between dielectric increment($\epdilon'$) and retention data was observed. When the solute form hydrogen bonding with solvent molecules, the slope of the ln k' vs. $\epdilon'$ plot is changed as the compositions is varied. The quadric relationship between mixed solvent solubility parameter ($\delta$M) and retention data was observed.

• 한국식품과학회지
• /
• 제23권2호
• /
• pp.235-240
• /
• 1991

Twin-screw extruder를 사용하여 인산제분 제조실험을 실시하였다. 옥수수 전분에 sodiumtripolyphosphate(STPP) 수용액을 분무하여 전분건물에 STPP 함량이 2%가 되도록 혼합하고, 원료투입속도 20 kg/hr 및 extrusion 온도 $130^{\circ}C$의 조건하에서 추가가수하여 조절한 process parameters 중 원료수분함량(23,25,30,35%) 및 스크류 회전속도(200,250,300,350 rpm)변화에 따라 압출되면서 측정한 system parameters(기계적 소모에너지, 압출물의 수분함량)와 압출된 인산전분의 특성인 target parameters(치환도, 호화도 및 분산액의 점도 및 겔 특성)와의 관계를 반응표면 분석하여 인산전분 제조공정을 검토하였다. 이 때 치환도는 수분함량이 클 수록 증가 하였고 스크류 회전속도 250rpm에서 최고의 값을 나타내었다. 호화도는 수분함량이 감소하고 스크류 회전속도가 증가할 수록 높았다. 주사전자현미경에 의한 전분입자의 미세구조는 입자의 붕괴가 크게 일어났으며 결과적으로 고유점도가 감소되었으나 용해도는 증가하였다. 또한, 겔의 노화속도는 치환도가 크고 점도가 낮을수록 지연되는 결과를 보였다.