• Journal of the Korean Ceramic Society
• /
• v.53 no.4
• /
• pp.381-385
• /
• 2016

Recently, white LEDs, especially, warm white LEDs have been intensively investigated due to outstanding optical properties, long term stability and low power consumption. In this study, mixed type and patterned type of remote phosphors were prepared by screen printing process employing green and red phosphor. Each type of remote phosphor exhibited distinctive photoluminescence spectrum. For example, the mixed type of remote phosphor exhibited unique spectrum, while the patterned type showed expectable spectrum depending on the concentration of phosphors. This indicates that a small amount of red phosphor dramatically reduced the green photoluminescence in the case of mixed-type remote phosphor, whereas the effect was negligible in the patterned-type remote phosphor. The possibility of undesirable chemical reaction was further investigated by using scanning electron microscopy and X-ray diffraction.

• Journal of the Korean Wood Science and Technology
• /
• v.42 no.4
• /
• pp.420-427
• /
• 2014

The physical and mechanical properties of sawdust-rice husk mixed ceramic were investigated with rice husk mixing ratios. The mixed ceramic board was produced with carbonization and resin impregnated sawdust-rice husk board at high temperature. At the same percentage of resin impregnation condition, density and bending strength of the mixed ceramic board increased with increasing the mixing rates of rice husk, whereas weight loss of the ceramic boards decreased. At the same temperature condition for the carbonization of resin impregnated sawdust-rice husk board, the density and bending strength were the highest with 40% of rice husk mixing ratio.

• Journal of the Korean Ceramic Society
• /
• v.32 no.1
• /
• pp.63-70
• /
• 1995

A crack-free ceramic composite membrane with micropores has been synthesized by the pressurized sol-gel coating technique using the mixed Al2O3-SiO2 sols. The mixed sols were prepared by mixing nanoparticulate SiO2 and boehmite sols. These sols were more stable at lower pH, but very unstable when their copositions were in the range of 50~75mol% of SiO2 at the same pH. The mixed Al2O3-SiO2 membrane prepared from the mixed sol (0.2mol/$\ell$ of solid content and pH=2) containing 40mol% of SiO2 had the mean pore radius of 0.80nm and the specific surface area of 280$m^2$/g. The nitrogen permeability through the coated Al2O3-SiO2 layer was 42$\times$107mol/$m^2$.s.Pa. It was found that the thermal stability of aluminosilicate membranes, even through similar to that of SiO2 membranes, was much improved in comparison with ${\gamma}$-alumina membranes.

• Journal of the Korean Ceramic Society
• /
• v.53 no.4
• /
• pp.435-443
• /
• 2016

Coal ash, a material generated from coal-fired power plants, can be classified as fly ash and bottom ash. The amount of domestic fly ash generation is almost 6.84 million tons per year, while the amount of bottom ash generation is 1.51 million tons. The fly ash is commonly used as a concrete admixture and a subsidiary raw material in cement fabrication process. And some amount of bottom ash is used as a material for embankment and block. However, the recyclable amount of the ash is limited since it could cause deterioration of physical properties. In Korea, the ashes are simply mixed and used as a replacement material for cement. In this study, an attempt was made to mechanically activate the ash by grinding process in order to increase recycling rates of the fly ash. Activated fly ash was prepared by controlling the mill types and the milling times and characteristics of the mortar containing the activated fly ash was analyzed. When the ash was ground by using a vibratory mill, physical properties of the mortar mixed with such fly ash were higher than the mortar mixed with fly ash ground by a planetary mill.

• Journal of the Korean Ceramic Society
• /
• v.39 no.10
• /
• pp.970-976
• /
• 2002

In this paper, the slump flow of the concrete, suspension, pH, corrosion effect, bleeding and the characteristics of coompressive strength were analyzed using antiwashout underwater admixture and antiwashout underwater agent+corrosion inhibitor mixed admixtures(1type). The results showed that there were no rare difference in physical properties but in the results of rapid corrosion tests there were lots of corrosion inhibitor ratio differences between concrete using only antiwashout underwater admixture and the corrosion inhibitor mixed(1type). In the case of only antiwashout underwater admixture 5.4%, the case corrosion inhibitor mixed(1type) 0.07%, the Antiseawater of the concrete which uses the Corrosion Inibitor Mixed(1type) appeared highly.

• Journal of the Korean Ceramic Society
• /
• v.24 no.4
• /
• pp.357-363
• /
• 1987

This study consists of two powder preparation process. One is that the synthesized Forsterite at 1400$^{\circ}C$ mixed with Zirconia powder. Another, theoretical Forsterite composition mixed with Zirconia. These two Forsterite bodies were heat-treated at 1400$^{\circ}C$, 1450$^{\circ}C$. Synthesized Foresterite composition showed higher density, strength than Forsterite composite which was directly mixed with Zirconia KIC value was measured by Microhardness Indentation method. It shows the highest value when 15 weight percent Zirconia dispersed.

• Microbiology and Biotechnology Letters
• /
• v.23 no.6
• /
• pp.755-762
• /
• 1995

A phenolic resin industrial wastewater containing about 41,000 mg/l of phenol and 2,800 mg/l of formaldehyde was biologically treated by a mixed culture GE2 immobilized on ceramic beads. This study was carried out with three experimental groups : Control-only added the sludge of papermill wastewater ; GE2 treatment-added GE2 to Control ; Ceramic treatment-applied ceramic carrier to GE2 treatment. When the original wastewater was diluted 80 times with aerated tap-water, influent COD$_{Mn}$ WaS 1,140 mg/l and that of the effluent was in the range of 22-35 mg/l, which was not much different among the experimental groups. However, at 20-times dilution, influent COD$_{Mn}$ was 4,800 mg/l and the effluent COD$_{Mn}$ of Control, GE2 treatment and Ceramic treatment was 179, 128 and 94 mg/l, respectively. COD$_{Mn}$, removal efficiency by Ceramic treatment was the highest, at 98.0%. At this time, the effluent phenol concentration of Control, GE2 treatment and Ceramic treatment was 10.71, 7.93 and 5.60, respectively. As the dilution times decreased, the removal efficiency of COD$_{Mn}$ and phenol did not change much, but COD$_{Mn}$ and phenol concentration of the effluent increased. Consequently, it is likely that the phenolic industrial wastewater containing phenol and formaldehyde can be biologically treated using a GE2 and ceramic carrier and that at 40-times dilution, the effluent completely meets the effluent standards for industrial wastewater treatment plant.

• The Journal of Korean Academy of Prosthodontics
• /
• v.28 no.1
• /
• pp.203-216
• /
• 1990

The purpose of this study was to evaluate the cervical margin fitness in the collarless metal ceramic crowns formed by different techniques. Specimens were divided as follows : the metal ceramic crowns with metal butt margin as group I, the collarless metal ceramic crowns formed with resin binder technique as group II, and the collarless metal ceramic crowns formed with shoulder powder mixed with phosphate-bonded investment liquids on a refractory die as group III. Each group was made of five specimens, and their marginal fitness on each epoxy die was evaluated under scanning electron microscope of x200 magnification at three measuring points : mesial, central, distal. The following results were obtained. 1. The metal ceramic crowns with metal butt margin exhibited significantly better marginal fitness than the collarless metal ceramic crowns. The marginal fitness in descending order was group I, III, II. 2. The collarless metal ceramic crown formed with resin binder technique had the worst marginal fitness & showed cervical color variation and dermacation between the corrected porcelain & the dentin porcelain. 3. The collarless metal ceramic crowns formed with shoulder powder mixed with phosphate-bonded investment liquids on a refractory die exhibited significantly better marginal fitness & sharper marginal configuration than the other collarless group.

• The Journal of the Korea Contents Association
• /
• v.21 no.3
• /
• pp.602-608
• /
• 2021

For the comparison of bond strength between the Co-Cr alloy and ceramic, which are clinically used, test samples made with a traditional casting method as a control group), and Milling and SLM(3d printing group) samples were made as an experimental group. The metal-ceramic bond strength was measured with a universal testing machine. For the measurement, a three-point bending test was conducted. After the bond strength was measured, metal-ceramic interface was observed. According to the test result, casting group had 53.59 MPa, milling group had 45.90 MPa, and 3d printing group had 58.34 MPa. There was no statistical significance. With regard to failure pattern, most of the samples in two groups, showed mixed failure. This study showed a clinically applicable value when measuring the bond strength of alloy-ceramic material with an alloy produced by 3D printing.

• Journal of Physiology & Pathology in Korean Medicine
• /
• v.18 no.4
• /
• pp.1159-1162
• /
• 2004

We studied on the production of the ceramic by the mineral-Oriental medicine and the property of the clean active water depositting on the ceramic stone. The results are as follows: We properly mixed of maifanshi, mica, ochre, and added to a small amount cinnabar, and therefore formed the ceramic stone. By the plasticity process and the irradiating magnetic force recovered the disappeared a part of constitutent elements. The recovered effects were become higher the freshness, maintenance, deodoriztion, clean water. As well as having the ability on capture of the notoxious heavy metal on human. The ceramic powder were mixed proper dose maifanshi, mica. And the powder had ionization, absorption, adhesion by the plasticity process and magnetic force. The clean active water of depositting on the ceramic stone during 24hours were observed significant the content of micro element, dissolved oxygen, abstraction on Herbs.