• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.11a
• /
• pp.392-393
• /
• 2006

Direct Printing Process is a suitable fabrication technique to develope pigment components whose dimensions are in nano. The success of this process depends on the sysmatic preparation of pigment millbase. Conventional millbase dispersions are constituted of the organic pigments, monomer, dispersant and solvents. An experimental study on the rheology of millbase dispersions is presented.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.20 no.5
• /
• pp.450-455
• /
• 2007

LCD color filters have been manufactured in a process called photolithography to date, but various printing methods have been studied currently in response to the trend of low-end LCD panels. Direct Printing Process is a suitable fabrication technique to develope pigment components whose dimensions are in nano. The success of this process depends on the systematic preparation of pigment millbase. Conventional millbase dispersions are constituted of the organic pigments, monomer, dispersant and solvents. An experimental study on the rheology of millbase dispersions is presented. Subsequently, this thesis attempts to find out the dispersive characteristics as well as the selection of pigments, monomers and dispersants in the part of millbase among the stages of manufacturing LCD color filters using the direct printing methods. The dispersive characteristics were shown through analytic devices such as PSA, Rheometer, etc.

• Clean Technology
• /
• v.14 no.1
• /
• pp.21-28
• /
• 2008

The properties of the dispersion of the red, green, and blue pigments were investigated for the manufacture of the millbase of LCD color filters. Their physical properties and viscosity were controlled to apply to the screen printing in order to substitute the existing photolithography method. The best dispersion properties were obtained with dispersant BYK-2000 and monomer EB-140. The millbase was pre-mixed at 500 rpm for 30 min, and dispersed at 4000 rpm for 5 - 6 hour by Torus Mill. The resulting particle sizes were $100{\sim}110\;nm$ for red, $50{\sim}70\;nm$ for green, and $60{\sim}80\;nm$ for blue. When the millbase viscosity was 200-300 cps in the low viscosity formulation, an efficient impact of the beads on pigments was achieved. The dispersion properties were confirmed from the rheological behavior and color characteristics.