• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.11a
• /
• pp.430-433
• /
• 2001

The 0.96MgTiO$_3$-0.04SrTiO$_3$+xCe(x=0∼1.6 wt%) ceramics were fabricated by the conventional mixed oxide method. The sintering temperature and time were 1300$^{\circ}C$, 2hr., respectively. From the X-ray diffraction patterns, it was found that the perovskite SrTiO$_3$ and ilmenite MgTiO$_3$ structures were coexisted in the 0.96MgTiO$_3$-0.04SrTiO$_3$+xCe(x=0∼1.6 wt%) ceramics. The dielectric constant($\varepsilon$$\sub$r/) was increased with addition of Ce. The temperature coefficient of resonant frequency($\tau$$\sub$f/) was gradually varied from positive value to the negative value with increasing the Ce. The temperature coefficient of resonant frequency of the 0.96MgTiO$_3$-0.04SrTiO$_3$+0.2Ce ceramics was near zero, where the dielectric constant, quality factor, and $\tau$$\sub$f/ were 20.68, 50, 272 and -0.5pm/$^{\circ}C$, respectively.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.06a
• /
• pp.323-324
• /
• 2006

저온동시 소결용 세라믹스, LTCC를 사용한 RF/MW용 고유전율 세라믹을 개발하기 위하여 300이상의 고유전율과 낮은 손실 계수를 가지는 것으로 알려진 $Ag(Nb_{1/4}Ta_{3/4})O_3$ 고용체와 $CaTiO_3$, $TiO_2$를 각각 혼합하여 공진주파수의 온도 계수가 0에 가까운 안정된 유전체 특성을 얻고자 하였다. 유전율의 온도 안정성을 도모하기 위해 음의 온도 계수를 갖는 $CaTiO_3$, $TiO_2$와 양의 온도계수를 갖는 $CaTiO_3$ 및 $TiO_2$를 일정 분율로 혼합한 복합체 구조의 시편을 제작하였다. LTCC 소자로의 적용을 위해 3wt.%의 CuO를 첨가하여 소결 온도를 낮추었으며, 소결 시편의 상 분석, 미세구조 및 전기적 특성을 조사하였다.

• Journal of the Korean Magnetics Society
• /
• v.16 no.5
• /
• pp.255-260
• /
• 2006

The basic composition of Ni-Zn ferrite was $(Ni_{0.35}Cu_{0.2}Zn_{0.45})_{1.02}(Fe_2O_3)_{0.98}$ (group A) and $(Ni_{0.4}Cu_{0.2}Zn_{0.4})_{1.02}(Fe_2O_3)_{0.98}$(group B) with additional 0.1 mol% $CaCO_3$ and 0.03 mol% $V_2O_5$. For high permeability and acceleration of grain growth, $CaCO_3$ and $V_2O_5$ was added. The mixture of the law materials was calcinated at $600^{\circ}C$ for 2 hours and then milled. The compacts of toroidal type were sintered at different temperature ($1,050^{\circ}C,\;1,070^{\circ}C,\;1,100^{\circ}C$) for 2 hours in air followed by an air cooling. Then, effects of various composition and sintering temperatures on the microstructure and physical properties such as density, resistivity, magnetic induction, coercive force, initial permeability, quality factor, and curie temperature of the Ni-Zn ferrite were investigated. The density of the Ni-Zn ferrite was $4.90{\sim}5.10g/cm^3$, resistivity revealed $10^8{\sim}10^{12}{\Omega}-cm$. The average grain size increased with the increase of sintering temperatures. The magnetic properties obtained from the aforementioned Ni-Zn ferrite specimens were 4,000 gauss for the maximum induction, 0.25 oersted for the coercive force, 2,997 for the initial permeability, 208 for the quality factor, and $202^{\circ}C$ for the curie temperature. The physical properties indicated that the specimens could be utilized as the core of microwave communication and high permeability deflection yoke of high permeability.

• Korean Journal of Crystallography
• /
• v.17 no.1
• /
• pp.24-32
• /
• 2006

The microwave dielectric properties of $Zn_3Nb_2O_8\;with\;V_2O_5$ addition were investigated. The addition of $V_2O_5$ enhanced the sinterability of $Zn_3Nb_2O_8$, which resulted in high density of $Zn_3Nb_2O_8$ ceramic greater than 95% of the theoretical value when sintered at $900^{\circ}C$ for 4 hours. X-ray diffraction analysis of sintered $Zn_3Nb_2O_8$ ceramic showed no second phase with $V_2O_5$ addition. Dielectric permittivity(${\varepsilon}_r$) and quality factor($Q{\times}f$) varied with both density at different sintering temperature and $V_2O_5$ addition. Dielectric permittivity, quality factor and temperature coefficient($T_{cf}$) of the two mole of $V_2O_5\;added\;Zn_3Nb_2O_8$ that was sintered at $900^{\circ}C$ were 21.4, 40,000, $-54ppm/^{\circ}C$, respectively.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.20 no.1
• /
• pp.21-24
• /
• 2010

The effects of mole ratio(A/B) m and Ti-ion on the dielectric properties and microstructure of the microwave dielectric ceramics $(Ca_{0.7}Sr_{0.3})_m(Ti_yZr_{1-y})O_3$ were investigated. Ti ions substituted on Zr-sites in these modified $CaZrO_3$ composition strongly affect the sintering density and microstructure of the fired ceramic body. With increasing the amount of Ti substituted on Zr-sites, the sintered density rapidly increased and the dense microstructure was obtained for the compositions having mole ratio of 1.01, whereas the sintered density and microstructure are nearly constant with the content of Ti-ion for the compositions having mole ratio of 0.99. With increasing the content of Ti ion, the curve of TCC (Temperature Coefficient of Capacitance) as a function of temperature rotated clockwise and satisfied the COG characteristics for both of compositions with mole ratio of 0.99 and 1.01. The content of Ti ion seems to be more effective than mole with respect to the controlling of firing and TCC.

• Journal of the Korean Magnetics Society
• /
• v.17 no.6
• /
• pp.232-237
• /
• 2007

We have synthesized the low temperature sintered of Ni-Zn-Cu ferrite with nonstoichiometric composition a little deficient in $Fe_2O_3$ from $(Ni_{0.2}Cu_{0.2}Zn_{0.6})_{1+x}(Fe_2O_3)_{1-x}$. For low loss and acceleration of grain growth $TiO_2$ and $Li_2CO_3$ was added from 0.25 mol% to 1.0 mol%. The mixture of the law materials was calcinated and milled. The compacts of toroidal type were sintered at different temperature $(875^{\circ}C,\;900^{\circ}C,\;925^{\circ}C\;950^{\circ}C)$ for 2 hours in air followed by an air cooling. Then, effects of composition and sintering temperatures on the physical properties such as density, resistivity, magnetic induction, coercive force, initial permeability, and quality factor of the Ni-Zn-Cu ferrite were investigated. The density of the Ni-Zn-Cu ferrite was $4.85\sim5.32g/cm^3$, resistivity revealed $10^8\sim10^{12}\Omega-cm$. The magnetic properties obtained from the aforementioned Ni-Zn-Cu ferrite specimens were 1,300 gauss for the maximum induction, 4.5 oersted for the coercive force, 275 for the initial permeability, and 83 for the quality factor. The physical properties indicated that the specimens could be utilized as the core of high frequency range (involved microwave range) communication and deflection yoke of T.V.

• Journal of the Korean Ceramic Society
• /
• v.38 no.11
• /
• pp.1046-1054
• /
• 2001

Effects of B$_2$O$_3$and CuO addition on the microwave dielectric properties of the PbWO$_4$-TiO$_2$ceramics were investigated in order to use this material as an LTCC material for fabrication of a multilayered RF passive components module. We found that PbWO$_4$could be used as an LTCC material because of its low sintering temperature (8$50^{\circ}C$) and fairy good microwave dielectric properties($\varepsilon$$_{r}$=21.5, Q$\times$f$_{0}$=37200 GHz and $\tau$$_{f}$ =-31 ppm/$^{\circ}C$). In order to stabilize $\tau$$_{f}$ of PbWO$_4$, TiO$_2$was added to the PbWO$_4$and the mixture was sintered at 8$50^{\circ}C$. A near zero $\tau$$_{f}$ value (+0.2 ppm/$^{\circ}C$) was obtained with 8.7 mol% TiO$_2$addition. $\varepsilon$r and Q$\times$f$_{0}$ values were 22.3 and 21400 GHz, respectively. It was believed that the decrement of Q$\times$f$_{0}$ value with TiO$_2$addition was resulted from increasing grain boundary. In order to improve Q$\times$f$_{0}$, various amounts of B$_2$O$_3$and CuO were added to the 0.913PbWO$_4$-0.087TiO$_2$mixture. The optimum amount of CuO was 0.05 wt%. At this addition, the 0.913PbWO$_4$-0.087TiO$_2$ceramic showed $\varepsilon$$_{r}$=23.5, $\tau$$_{f}$ =-2.2ppm/$^{\circ}C$, and Q$\times$f$_{0}$=32900 GHz after sintered at 8$50^{\circ}C$. In case of B$_2$O$_3$addition, the optimum amount range was 1.0~2.5 wt% at which we could obtain following results; $\varepsilon$$_{r}$=20.3~22.1, Q$\times$f$_{0}$=48700~54700 GHz, and $\tau$$_{f}$ =+2.4~+8.2ppm/$^{\circ}C$.

• Korean Journal of Materials Research
• /
• v.7 no.10
• /
• pp.872-876
• /
• 1997

(1-x)CaTi $O_{3}$-xLa(Z $n_{1}$2/ $Ti_{1}$2/) $O_{3}$의 마이크로 유전특성을 조사하였다. x가 증가함에 따라 비유전율과 공진주파수의 온도계수는 감소하였으며, Qㆍ $f_{0}$는 증가하였다. 그 결과 x=0.5인 (C $a_{0.5}$L $a_{0.5}$)( $Ti_{0.75}$Z $n_{0.25}$) $O_{3}$의 조성에서 $\varepsilon$$_{r}$=51, Qㆍ $f_{0}$=38,000 (at 7 GHz), $\tau$$_{f}$=+5ppm/$^{\circ}C$의 유전특성이 나타났다. (C $a_{0.5}$L $a_{0.5}$)( $Ti_{0.75}$Z $n_{0.25}$) $O_{3}$조성의 소결온도를 저하시키기 위하여 B $i_{2}$ $O_{3}$를 주조성으로한 소결체를 첨가하여 소결 및 유전특성을 조사하였다. 1wt% 0.76B $i_{2}$ $O_{3}$-0.24NiO가 첨가된 경우 소결온도는 15$0^{\circ}C$ 낮아졌으며, 비유전율 ($\varepsilon$$_{r}$), 공진주파수의 온도계수($\tau$$_{f}$), Qㆍ $f_{0}$가 각각 50+5ppm/$^{\circ}C$, 35,000인 마이크로파 유전특성이 얻어졌다. 또한 3wt%의 0.76B $i_{2}$ $O_{3}$-0.24NiO가 첨가된 경우 소결온도는 20$0^{\circ}C$ 저하되었고, 비유전율 ($\varepsilon$$_{r}$)과 공진주파수의 온도계수 ($\tau$$_{f}$)는 변하기 않았으나, Qㆍ $f_{0}$값이 38,000에서 25,000으로 저하되었다. 25,000으로 저하되었다.되었다.되었다.되었다.

• Journal of the Korean Ceramic Society
• /
• v.42 no.2 s.273
• /
• pp.132-139
• /
• 2005

Sintering behavior of $BaO-Nd_{2}O_3-TiO_2$ with a Pb-based glassceramics frit were investigated in order to understand an effect of glassceramics as a low temperature sintering agent on dielectric ceramics. A green sheet form was fabricated through tape casting method with the glassceramic fut added $BaO-Nd_{2}O_3-TiO_2$. The dispersion properties, rheological properties and final density of dielectric composit slurry as a function of amount and composition of organic additives was examined. The dispersants' addition was effective in controlling dispersion of the ceramics in solution. The addition of excessive dispersant showed adverse effect on dispersion. The prepared slurries, containing ceramic : powders, glass-ceramics and various kinds of organic viechles, exhibited typical shear thinning behavior. The best properties of tape casting appeared powder to solvent ratio 65 : 35 and amount of the binder 6 wt$\%$ and plasticizer 3 wt$\%$. The viscosity of the slurry was 677 cps and green/sintered density in the tape was $3.3 g/cm^3,\;5.56 g/cm^3$ respectively.

• Applied Chemistry for Engineering
• /
• v.21 no.6
• /
• pp.694-696
• /
• 2010

We have synthesized boron (or phosphorous) doped silicon nanoparticles (Si-NPs) by a solution process. The surfaces of the Si-NPs were terminated with various alkyl groups to form a protecting layer. The Si-NPs were characterized by UV-Vis, PL, FTIR, and NMR. Through a microwave sintering process, the crystalline thin films of the Si-NPs were prepared by removing the surface alkyl groups. The TEM and SEM images reveal that contiguous films as large as $200{\mu}m$ in diameter were formed with a cubic structure. The electrical conductivity of the Si film was controlled by a doping type.