• Transactions on Electrical and Electronic Materials
• /
• v.13 no.5
• /
• pp.262-265
• /
• 2012

The Microstructure and nonlinear electrical properties of the ZPCCYT (ZnO-$Pr_6O_{11}$-CoO-$Cr_2O_3$-$Y_2O_3$-$Tb_4O_7$) varistors were investigated for different amounts of $Tb_4O_7$. The addition of $Tb_4O_7$ has a significant effect on microstructure and electrical properties. Analysis of the microstructure indicated that the ceramics consisted of ZnO grain as a main phase and a few secondary phases as a mix of $Pr_6O_{11}$, $Y_2O_3$, and $Tb_4O_7$. As the amount of $Tb_4O_7$ increased, the sintered densities of pellets increased from $\rho$ = 5.70 to $5.78g/cm^3$ and the average grain size decreased from d = 4.8 to $3.6{\mu}m$. The increase in the amount of $Tb_4O_7$ increased from $E_B$ = 7,473 to 10,035 V/cm and from ${\alpha}$ = 39.7 to 52.2. In particular, it was found that the ceramics modified with 1.0 mol% in the amount of $Tb_4O_7$ are suited for the varistors for high voltage in the light of a high sintered density and a high voltage gradient.

• Transactions of Materials Processing
• /
• v.7 no.3
• /
• pp.215-224
• /
• 1998

A semi-solid forming has a lot of advantages compared to the die casting. squeeze casting and conventional forging. therefore, semi-solid forming process is now becoming industrial interest for the production of metal components and metal matrix composites. However the material behaviour in the semi-solid temperature range is not sufficiently known although it controls the whole process through forces and geometry evolutions because the behaviour of metal slurries is complex. The semi-solid materials(SSMs) fabricated under electric-magnetic stirring condition is necessary to be applicated in forming process. A reheating conditions were studied with the reheating time holding time and reheating temperatures. The microstructure of SSM(specimen size : d39${\times}$h85) at the condition of heating time 10min and heating temperature 590${\circ}C$ is the most globular and finest one. The microstructure of SSM(specimen size : d76${\times}$h60) reheated under the three step reheating conditions is most globular and finest.

• Journal of Welding and Joining
• /
• v.11 no.4
• /
• pp.57-69
• /
• 1993

In the present study, the microstructure and Charpy V notch toughness of multipass $CO_2$ FCA weldment in three different heat inputs(1-3KJ/mm)were investigated. The weldments using two different domestic FCAW wires(AWS E71T-1 and E71T-5 equivalent) in C-Mn steel were chemically analysed. The following conclusions can be inferred. 1. T-1 wire Showed a stable arc transfer, less spatter and harsh, a better bead spreading and easy slag removal, whereas T-5 wire suffered from the arc stability, which tended to increase spatter and produce a more convex bead. 2.The microsturctures of the top beads of the weldments in three different heat inputs consisted of coarse-grained boundary ferrite and Widmanstatten ferrite side plate with increasing heat inputs. The modest fraction of acicular ferrite in the two wire weldments was observed in the 2KJ/mm heat input. 3.The fine-grained reheated zones of both welds consisted of a duplex microstructure of polygonal ferrite and second phases. 4. The basic flux weldment of T-5wires showed a higher Charpy impact property than that of T-1 wires because of a higher fraction of acicular ferrite in the weld microstructure.

• Journal of the Korean Ceramic Society
• /
• v.48 no.1
• /
• pp.106-109
• /
• 2011

In order to fabricate 8YSZ thick film by silk screen printing, YSZ(yttria-stabilized zirconia) commercial powder was used as starting materials. Paste for screen printing was made by mixing 8YSZ powder and organic vehicles. 8YSZ thick film was formed on $Al_2O_3$ substrate. The crystal structure, and microstructure were investigated. Grain size of 8YSZ was increased with increasing calcination temperature and rapid grain growth was shown after calcination at $1300^{\circ}C$. Microstructure showed the mixture of large and small grain size after $1400^{\circ}C$ sintering. Shrinkage rate of 8YSZ thick film sintered at $1400^{\circ}C$ was more than 40%.

• Journal of Korea Foundry Society
• /
• v.16 no.6
• /
• pp.537-549
• /
• 1996

This study aims at investigating the correlation of microstructure and mechanical properties of the AZ91 Mg/Al borate whisker composites fabricated by squeeze csting technique with a variation of applied pressure. Microstructure observation and in-situ fracture tests were conducted on the composites to identify the microfracture process. Detailed microstructural analyses indicated that the grain refinement could be achieved with applied pressure and the little change in volume fraction on reinforcing whiskers could be carried out. It was also found clearly from in-situ observation of crack initiation and propagation that in the composite processed by the lower applied pressure, microcracks were initiated earily at whisker/matrix interfaces, thereby resulting in the drop in strength. In the composite processed by the higher applied pressure, on the other hand, planar slip lines were well developed in the matrix, and then propagated through whiskers without whisker/matrix decohesion. Thus, the effect of the applied pressure on microstructure and mechanical properties can be explained by grain refinement, increased amounts of reinforcements, and improvement of whisker/matrix interfacial strength as the applied pressure in increased.

• Transactions of Materials Processing
• /
• v.29 no.5
• /
• pp.251-256
• /
• 2020

The purpose of this study is to investigate the effect of sintering condition on the microstructure evolution and tensile properties of the Ti-6Al-4V alloy sample processed by metal injection molding (MIM) in terms of the sizes of the alpha morphology and pore found in the matrix. For this purpose, a series of MIM were conducted on this sample at various sintering temperatures ranging from 1173 to 1373 K for three hours followed by furnace cooling, observed by the scanning electron microscopy. The microstructures sintered in this study showed that, with increasing sintering temperature over beta transus temperature, the transformation of the equiaxed alpha into transformed beta was attained while the size of pores would tend to decrease. Thus, the strength remained unchanged significantly in the tension while ductility increased to some extent as sintering temperature increased. Such mechanical behavior would be explained in relation to the microstructure evolution of the Ti-6Al-4V sample via the MIM.

• Journal of Korea Foundry Society
• /
• v.23 no.1
• /
• pp.40-46
• /
• 2003

Semisolid forming requires alloys with non-dendritic microstructure of the thixotropy. Recently, low pouring temperture method without stirring, i.e. liquidus casting has been found out new fabrication method of the semisolid metals. Effects of melt superheat and mold conditions on the globulization of primary Al of $AlSi_7Mg$ alloy were investigated in gravity casting process without stirring. The microstructures of primary Al as function of melt superheat and mold temperature show globular, rosette and dendritic shapes. The conditions for globular microstructure of primary Al were low melt superheat < 35 K and low mold temperature < 500 K. The thermal conditions for globular microstructure of primary Al were undercooled melt at early solidification stages and slow cooling < 0.6 K/s. It was found that the initial microstructure was maintained throughout the solidification and the globules of primary Al can be obtained by high nucleation of fine and spherical nuclei due to enhanced undercooling of melt.

• KIEE International Transactions on Electrophysics and Applications
• /
• v.3C no.4
• /
• pp.140-145
• /
• 2003

The influence of microstructure nonuniformity on the electrical characteristics of ZnO varistors was analyzed with the added amount of $Al_2$O$_3$ dopants. $Al_2$O$_3$ doping can effectively inhibit grain growth. When $Al_2$O$_3$ content is in the range between 0-0.1 %, the average grain size and the standard deviation decrease quickly and the grain growth is strongly inhibited. Therefore, it is possible to increase the microstructure uniformity by accurate addition of $Al_2$O$_3$ to the ZnO varistor. The breakdown voltage increases with the decrease of standard deviation. The greater the uniformity of the Zno varistor means the higher the global breakdown voltage. The $Al_2$O$_3$ dopants having about 0-0.023 wt% content can effectively improve the voltage ratio, and the voltage ratio reaches a minimum value of 2.32 at an $Al_2$O$_3$ content of 0.005 wt%.

• Nuclear Engineering and Technology
• /
• v.47 no.3
• /
• pp.323-331
• /
• 2015

Zirconium alloys are widely used in nuclear reactors as structural materials. During the operation, they are exposed to fast neutrons. Ion irradiation is used to simulate the damage introduced by neutron irradiation. In this article, we briefly review the neutron irradiation damage of zirconium alloys, then summarize the effect of ion irradiation on microstructural evolution, mechanical and corrosion properties, and their relationships. The microstructure components consist of dislocation loops, second phase precipitates, and gas bubbles. The microstructure parameters are also included such as domain size and microstrain determined by X-ray diffraction and the S-parameter determined by positron annihilation. Understanding the relationships of microstructure and properties is necessary for developing new advanced materials with higher irradiation tolerance.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2007.10a
• /
• pp.322-325
• /
• 2007

Precipitation characteristics of the Fe-36Ni based high strength Invar alloy for power transmission wire was investigated in this study. High strength can be obtained in this alloy through solution hardening, precipitation hardening and strain hardening by cold working. In the present study, ingots of Fe-36Ni based Invar alloys with the contents of C, Mo and V varied. Microstructure observations by OM, SEM, and TEM were carried out to validate the simulation results. BCC phase and $FeNi_3$ phase are also expected at lower temperatures below $500^{\circ}C$. Aging treatments were carried out at temperatures ranging from 400 to $900^{\circ}C$ for time intervals from 3 min to 100hrs. Peak aging condition was obtained as $400^{\circ}C$ and 1 hr. With temperature increased, peak strength was decreased abruptly. Microstructure observation was conducted by optical microscopy, scanning electron microscopy, and transmission electron microscopy.